• Korean Journal of Metals and Materials
• /
• v.49 no.8
• /
• pp.642-648
• /
• 2011

This paper describes an experimental study on ultrasonic welding of similar and dissimilar metals. There are optimum welding conditions which are found for welding of Al/Al and Al/Cu. It evaluated weldability using tensile test, SEM observation and EDX-ray analysis. Both ultrasonic welding of Al/Al and Al/Cu have amplitude as the variable factor. Al/Cu welding was examined again with welding time as variable factor to find the best conditions. The more welding time or amplitude increase, the better weldability. The optimum conditions for ultrasonic welding of Al/Al were formed at pressure 0.25 MPa, welding time 0.25 sec, amplitude 90%. Pressure 0.25 MPa, welding time 0.4 sec, amplitude 80% are optimized for Al/Cu ultrasonic metal welding and solid-state diffusion generated by ultrasonic vibration and frictional heat is confirmed at the welded interface.

• Textile Coloration and Finishing
• /
• v.33 no.4
• /
• pp.309-316
• /
• 2021

Due to the rigid nature of the silicon carbide fiber(SiC), fiber damage occurs from the friction during the carding process. This damage not only lowers the spun yarn yield, but also lowers the heat resistance of the spun yarn, so that ultra-high heat resistant yarn cannot be manufactured. Therefore, in the carding process where the most friction between fiber and machine(wire, etc.) occurs, some factors were modified and tested, and as a result of measuring the change in physical properties, fiber damage decreased due to the wire angle or wire density, resulting in improved yield. The test method used to measure the yield of SiC fiber was the carbonization method, and the content of SiC fibers was calculated using the remaining amount after carbonization. Carbonization test was performed at air condition, 700℃, and for 2 hours. Analysis by SEM-EDX showed that the carbide was consistent with the composition of the SiC fiber.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.3
• /
• pp.123-133
• /
• 1994

Oxidation behavior of STS 304 and 430, produced by POSCO, Korea, was studied in order to study the surface defects formed during manufacturing processes. Oxidation experiments were carried out in a preheat-ed furnace at 850~$1, 250^{\circ}C$ in air and in a simulated coke oven gas(COG) atmosphere. The reaction products were examined by XRD, SEM and EDX on their surfaces and cross sections. Protective $Cr_2O_3$-primary oxide film was formed initially, but at critical point this film was broken and a duplex scale consisting of $Fe_2O_3$- and Fe$Cr_2O_4$- was formed. It was more severely attacked in a simulated COG atmosphere than in air, and STS 304 was superior to STS 430 in oxidation resistance.

• Journal of Veterinary Clinics
• /
• v.31 no.3
• /
• pp.250-252
• /
• 2014

After clinical and laboratory tests of a 12-year-old warmblood horse (castrated male, 540 kg) displaying symptom of pain, a diagnosis of intestinal obstruction due to foreign substances like sand was made and an abdominal section and enterotomy were conducted to confirm and extract the intestinal stone (enterolith) on the right dorsal part of the ascending colon. The extracted intestinal stone was around 2.9 kg and greenish brown rugby ball sized ($22cm{\times}10cm$) stone. Analysis of the element components (EDX) using a scanning electron microscope revealed percentages of C (30.08%), O (39.85%), Mg (3.89%), P (11.15%), and Ca (11.16%) at a magnification of 400. This was the first example of a successful extraction and treatment of intestinal stone in a horse domestically and thereby has its significance.

• Journal of Technologic Dentistry
• /
• v.27 no.1
• /
• pp.79-88
• /
• 2005

This study was performed to investigate the surface properties of electrochemically oxidized pure niobium by anodic oxide and hydrothermal treatment technique. Niobium specimens of $10\times10mm$ in dimension were polished sequentially from #600, #800, #1000 emery paper. The surface pure niobium specimens were anodized in an electrolytic solution that was dissolved calcium and phosphate in water. The electrolytic voltage was set in the range of 250 V and the current density was 10 $mA/cm^2$. The specimen was hydrothermal treated in high-pressure steam at 300$^{\circ}C$ for 2 hours using an autoclave. Then, specimens were immersed in the Hanks' solution with pH 7.4 at 37$^{\circ}C$ for 30 days. The surface of specimen was characterized by scanning electron microscope(SEM), energy dispersive X-ray microanalysis(EDX), potentiostat/galvanostat test, and cytotoxicity test. The results obtained was summarized as follows; According to the result of measuring corrosion behavior at 0.9% NaCl, corrosion resistance was improved more specimens treated with anodic oxide than in hydrothermal treated ones. The multi-porous oxide layer on surface treated through anodic oxidation showed a structure that fine pores overlap one another, and the early precipitation of apatite was observed on the surface of hydrothermal treated samples. According to the result of EDX after 30 days deposition in Hanks' solution, Ca/P was 1.69 in hydrothermal treated specimens. In MTT test, specimens treated through anodic oxidation and hydrothermal treated ones showed spectrophotometer similar to that of the control group. Thus no significant difference in cytotoxicity was observed (P>0.05).

• The Journal of Advanced Prosthodontics
• /
• v.6 no.4
• /
• pp.285-294
• /
• 2014

PURPOSE. The purpose of this study was to evaluate the properties of a porous zirconia scaffold coated with bioactive materials and compare the in vitro cellular behavior of MC3T3-E1 preosteoblastic cells to titanium and zirconia disks and porous zirconia scaffolds. MATERIALS AND METHODS. Titanium and zirconia disks were prepared. A porous zirconia scaffold was fabricated with an open cell polyurethane disk foam template. The porous zirconia scaffolds were coated with ${\beta}$-TCP, HA and a compound of ${\beta}$-TCP and HA (BCP). The characteristics of the specimens were evaluated using scanning electron microscopy (SEM), energy dispersive x-ray spectrometer (EDX), and x-ray diffractometry (XRD). The dissolution tests were analyzed by an inductively coupled plasma spectrometer (ICP). The osteogenic effect of MC3T3-E1 cells was assessed via cell counting and reverse transcriptase-polymerase chain reaction (RT-PCR). RESULTS. The EDX profiles showed the substrate of zirconia, which was surrounded by the Ca-P layer. In the dissolution test, dissolved $Ca^{2+}$ ions were observed in the following decreasing order; ${\beta}$-TCP > BCP > HA (P<.05). In the cellular experiments, the cell proliferation on titanium disks appeared significantly lower in comparison to the other groups after 5 days (P<.05). The zirconia scaffolds had greater values than the zirconia disks (P<.05). The mRNA level of osteocalcin was highest on the non-coated zirconia scaffolds after 7 days. CONCLUSION. Zirconia had greater osteoblast cell activity than titanium. The interconnecting pores of the zirconia scaffolds showed enhanced proliferation and cell differentiation. The activity of osteoblast was more affected by microstructure than by coating materials.

• Journal of Biosystems Engineering
• /
• v.39 no.3
• /
• pp.235-243
• /
• 2014

Purpose: The aim of this study was to prepare and evaluate a natural material extracted from germinated brown rice (GBR). Herein, we evaluated whether the natural material could positively activate the biological effects seen during bone formation, including enhancement of metabolic activity, osteogenesis, and the expression of vascular endothelial growth factor (VEGF), one of the growth factors in human osteoblast-like cells. Methods: The natural material was created by a hot water extraction process after being soaked for 2~3 days in tap water and dried at $50^{\circ}C$. The material was characterized using field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), and Fourier transformed infrared (FTIR) spectroscopy. The biological behaviors of the material were also investigated; we performed tests to assess cell cytotoxicity, metabolic activity, osteogenic markers related to bone formation, and VEGF. Results: The EDX, XRD, and FTIR results for the natural material indicated the presence of organic compounds. The natural material caused positive increases in cell metabolic activity and mineralized bone formation without cytotoxicity. The protein levels in the extract for the $6.25{\mu}g/mL$, $12.25{\mu}g/mL$, $25{\mu}g/mL$, $50{\mu}g/mL$, and $100{\mu}g/mL$ groups were significantly different from that for the control. Conclusions: The GBR-based natural material was easy to prepare and had characteristics of a potential biomaterial. The biocompatibility of this natural material was evaluated using in vitro techniques; our findings indicate that this novel material is promising for agricultural and biological applications.

• Korean Journal of Materials Research
• /
• v.20 no.8
• /
• pp.429-433
• /
• 2010

In this study, activated carbon (AC) as a carbon source was modified with different concentrations of cobalt chloride ($CoCl_2$) to prepare a Co-AC composite, and it was used for the preparation of Co-AC/$TiO_2$ composites with titanium oxysulfate (TOS) as the titanium precursor. The physicochemical properties of the prepared Co-AC/$TiO_2$ composites were characterized by $N_2$ adsorption at 77 K, X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive X-ray (EDX) analysis. The photocatalytic treatments of organic dyes were examined under an irradiation of visible light with different irradiation times. $N_2$ adsorption data showed that the composites had decreased surface area compared with the pristine AC, which was $389\;m^2/g$. From the XRD results, the Co-AC/$TiO_2$ composites contained a mixturephase structuresof anatase and rutile, but a cobalt oxide phase was not detected in the XRD pattern. The EDX results of the Co-AC/$TiO_2$ composites confirmed the presence of various elements, namely, C, O, Ti, and Co. Subsequently, the decomposition of methylene orange (MO, $C_{14}H_{14}N_3NaO_3S$) and rhodamine B (Rh.B, $C_{28}H_{31}ClN_2O_3$) in an aqueous solution, respectively, showed the combined effects of an adsorption effect by AC and the photo degradation effect by $TiO_2$. Especially, the Co particles in the Co-AC/$TiO_2$ composites could enhance the photo degradation behaviors of $TiO_2$ under visible light.

• Journal of Hydrogen and New Energy
• /
• v.23 no.3
• /
• pp.207-212
• /
• 2012

This study was performed to observe the change of stainless steel pipe interacting with alkaline solution. We used STS316L and STS304 as samples which were soaked in alkaline solution. We measured the samples by use of FE-SEM, EDX, SIMS to observe the surface and depth profile of both samples. The result showed that the precipitate appeared on the surface of both samples from 5 days. but the precipitate was confirmed to be decreased as time passes. but the quantitative change of precipitates at both samples was different as time passed. The EDX showed that the precipitate is Potassium from solution of Electrolysis. The result also showed that the primary elements of stainless steel pipeline and of Alkaline Solution were changed. The change of primary elements was severe between 5 days to 16 days and was stable around 40 days at both samples. The reaction of STS316L with alkaline solution was lower than STS304. We hoped that this study would be the foundation of developing the electrode of the alkaline hydrogen generator.

• Korean Journal of Materials Research
• /
• v.20 no.3
• /
• pp.117-124
• /
• 2010

Titanium dioxide ($TiO_2$) particles deposited on different quantitative Fe-treated carbon nanotube (CNT) composites with high photocatalytic activity of visible light were prepared by a modified sol-gel method using TNB as a titanium source. The composites were characterized by BET, XRD, SEM, TEM and EDX, which showed that the BET surface area was related to the adsorption capacity for each composite. From TEM images, surface and structural characterization of for the CNT surface had been carried out. The XRD results showed that the Fe-ACF/$TiO_2$ composite mostly contained an anatase structure with a Fe-mediated compound. EDX results showed the presence of C, O, and Ti with Fe peaks in the Fe-CNT/$TiO_2$ composites. The photocatalytic activity of the composites was examined by degradation of methylene blue (MB) in aqueous solution under visible light, which was found to depend on the amount of CNT. The highest photocatalytic activity among the different composites was related to the optimal content of CNT in the Fe-CNT/$TiO_2$ composites. In particular, the photocatalytic activity of the Fe-CNT/$TiO_2$ composites under visible light was better than that of the CNT/$TiO_2$ composites due to the introduction of Fe particles.