• 한국산업융합학회 논문집
• /
• 제23권1호
• /
• pp.73-81
• /
• 2020

This study analyzed the causes of failure of SCM435 bolts that fix the springs of automobile air brakes that have been fractured during use. The cause of failure was analyzed using SEM, EDS, metallogical microscope and Vickers hardness tester. In the fracture, the ratchet mark began at the outer boundary of crack origin, and the grains at crack origin were found to have clear intergranular corrosion. One SCM435 bolt was subjected to a stress of 398 MPa, it's a stress of about 80% of the fatigue limit. As a result of such a large applied stress, cracks occurred at the corrosion origin and were fractured. In order to prevent the SCM435 bolt from fracture, it is necessary to use the correct composition, the accuracy of heat treatment, preventing damage by external impact, preventing corrosion of the damage part by moisture, and introduction a compressive residual stress by peening.

• 한국산업융합학회 논문집
• /
• 제22권6호
• /
• pp.649-655
• /
• 2019

Fracture behaviors of SCM435 high strength bolt have been studied including macroscopic and microscopic fracture observation, Energy Dispersive X-ray Spectroscopy, Vickers hardness test and applied stress evaluation. cracks (ratchet marks) were generated by the repetitive loads acting on the bolts, initial stress of bolt and the stress concentration. The applied stress was found to be slightly higher than the fatigue limit of the material. The initial stress of bolt must be removed, and the mold temperature during the process must be maintained by room temperature. Bolts are recommended to be peened to improve fatigue limit.

• 열처리공학회지
• /
• 제11권2호
• /
• pp.99-110
• /
• 1998

The effects of pre-heat treatment(Q/T) on microstructure and hardness of SCM435 structural steel nitrided by micro-pulse plasma was investigated. The quenching and tempering temperatures for obtaining matrix hardness of SCM435 steel on range of HRC30 to HRC40 desired for machine parts were about $860^{\circ}C$ and $500^{\circ}C$ respectively. The case depth of SCM435 nitrided at $480^{\circ}C$ for 5 hours was independent of pre-heat treatment condition and was approximately $150{\mu}m$. However, hardness and compactness of nitrified layer on Q/T treated specimen were more heigher than annealed specimen. The case depth increased linearly with the increase of nitriding temperature, however, the hardness of nitrified layer decreased with the temperature. Phase mixture of ${\gamma}^{\prime}$-phase($Fe_4N$) and ${\varepsilon}$-phase($Fe_3N$) were detected by XRD analysis in the nitrified layer formed at optimum nitriding condition, and only single ${\gamma}^{\prime}$-phase was detected in the nitrified layer formed at higher nitriding temperature such as $540^{\circ}C$. The optimum nitriding temperature was approximately $480^{\circ}C$ which is lower than tempering temperature for preventing softening behavior of SCM435 matrix during nitriding process and the surface hardness of nitrified layer obtained by optimum preheat treatment condition was about Hv930.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 제5회 압연심포지엄 신 시장 개척을 위한 압연기술
• /
• pp.317-326
• /
• 2004

This study investigated tile local austenite grain size (AGS) distribution In rolling of SCM435 steel which is commonly used for high strength bolt. To investigate AGS distribution, round-oval (R-O) and square-diamond (S-D) rolling experiments were carried out with pilot mill. In round-oval rolling, local AGS has a tendency to increase when it goes to outward. In square-diamond rolling, local AGS has a tendency to increase when it goes to free surface. To investigate relation between AGS and process parameter, three dimensional FE analysis was carried out along with rolling experiment. To validate accuracy of FE analysis, we compared deformed geometry with FE result. The AGS prediction combined AGS model with numerical analysis was also carried out for center node of S-D rolling. Although this study brought experimental observation and its qualitative analysis into focus and quantitative AGS prediction will be done as a further work.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2008년도 춘계학술대회 논문집
• /
• pp.439-443
• /
• 2008

We investigate the mechanical behavior of a pre-heat treated steel of ESW95, which is being used for automotive parts including tie-rods to save manufacturing cost and enhance product quality. SCM435 is also investigated to reveal the characteristics of the pre-heat treated steel tested. AFDEX/MAT is used to extract the true stress-strain curve over the large strain with higher accuracy. It has been found that ESW95 has very week strain-hardening behavior which can be negligible compared with SCM435 and that the initial yield strength is quite high and the toughness of ESW95 reaches nearly 75% of SCM435. ESW95 is characterized by the weak strain-hardening behavior and high yield strength that can be lead to minimization of post-processing including heat treatment and straightening. ESW95 and SCM435 are also compared by applying them to ball-stud forging by computer simulation. It is expected that a great deal of change may take place in production as well as in service if the pre-heated steels are adopted.

• 열처리공학회지
• /
• 제13권5호
• /
• pp.303-308
• /
• 2000

The ring gears of automobile parts are manufactured generally process chart of which is as follows : forging ${\rightarrow}$ annealing or normalizing ${\rightarrow}$ rough machining ${\rightarrow}$ hardening(Quenching-Tempering or carburizing process) ${\rightarrow}$ finish machining. Isothermal annealing process after forging is most effective in the side of improvment of machinability. On this study we selected two kinds of steel;SCM415, SCM435 of most universal and investigated microstructures to find out most suitable condition of heat treatment in proportion continuous cooling and isothermal annealing. As the cooling rate is $5^{\circ}C$ per minute in continuous cooling process, martensite and bainite are coexisted with ferrite and pearlite in SCM435 steel. If the cooling rate is slower than $5^{\circ}C$ per minute, microstructure were only ferrite and pearlite but formation of band structure can't be avoid. On the other hand, microstructure is only ferrite and pearlite regardless of cooling rate because carbon content of SCM415 steel is low. Moreover formation of band structure isn't exposed by faster cooling rate. Most optimal temperature of the isothermal annealing is from $650^{\circ}C$ to $680^{\circ}C$ in SCM435 steel. When holding time is 60 minute with $650^{\circ}C$, the identical ferrite and pearlite microstructures can be obtained.

• 한국재료학회지
• /
• 제11권12호
• /
• pp.1063-1067
• /
• 2001

The effect of the pulse parameters(pulse ratio and frequency) on the characteristics of the nitrided layer in the pulsed plasma nitrified SCM435 Steels was investigated. Material properties of the nitrided layer were analysed by employing optical microscope, scanning electron microscope(SEM), X-ray diffractometer(XRD) and micro-Vickers hardness tester. It was found that both the compound layer thickness and the surface hardness decreased with decreasing of pulse ratios. At high pulse ratio, the compound layer thickness and the surface hardness were rapidly decreased with decreasing frequency compared to lower pulse ratios.

• 한국재료학회지
• /
• 제12권6호
• /
• pp.427-430
• /
• 2002

Plasma nitrocarburizing treatment was performed for SCM 435 steel by using a plasma ion nitriding system. The effects of the variation of nitrogen and methan contents upon the hardened layer was investigated. Both the thickness of the compound layer and the amount of $\varepsilon$ phase in the compound layer increased with increasing nitrogen content. However, the thickness of the compound layer decreased due to unstable plasma for an atmosphere containing 90% $N_2$ gas content in the gas mixture. The amount of $\varepsilon$phase in the compound layer increased with increasing $CH_4$ gas content. For $CH_4$ gas content more than 2% in the gas mixture, the thickness of the compound layer decreased due to the formation of $\theta$ phase.

• 비파괴검사학회지
• /
• 제15권4호
• /
• pp.511-519
• /
• 1996

Cr-Mo강인 SNCM220, SCM435, SACM645 및 SCM415 강봉을 사용하여 ${\phi}31.2$ 봉 대 봉 동종재 마찰용접의 최적 조건을 실험적으로 구하였으며, 이를 위하여 이음부의 인장강도와 마찰용접 변수와의 정량적 상관식을 실험적으로 도출하였다. 한편 마찰용접시 음향방출시험을 병행하여, AE 누적총량과 마찰용접변수, 마찰용접부의 인장강도와 AE 누적총량과의 정량적 상관성을 도출하였다. 그리고, 마찰용접부의 인장파단면을 검토함으로써 용접품질을 확인하였다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2001년도 추계 학술발표강연 및 논문개요집
• /
• pp.104-104
• /
• 2001