• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.11
• /
• pp.916-921
• /
• 2012

This research measured the dielectric properties of silicone rubber with various hardness in 100 Hz~3 MHz, $30{\sim}170^{\circ}C$ conditions. When the hardness increases from 65 degree to 75 degree, the dielectric loss increased within frequency range of 100 kHz~3 MHz and was a little change in dielectric loss within temperature range of $90^{\circ}C{\sim}170^{\circ}C$. Thermogravimetric Analysis (TGA) showed the weight change rate increased a little while heated until $800^{\circ}C$. Scanning Electron Microscope (SEM) measurement showed that Aluminium Trihydroxide($AlOH_3$) which acts as a reinforcement agent reduced the size of the particles as the hardness increased.

• Design & Manufacturing
• /
• v.17 no.2
• /
• pp.27-32
• /
• 2023

Liquid silicon rubber (LSR) has fine thermal compatibility and is widely used in various fields such as medical care and automobiles because it is easy to implement products with good fluidity. With the recent development of flexible sensors, the focus has been on manufacturing conductive elastomers, such as silicone as elastic materials, and carbon black, CNT, and graphene are mainly used as nanomaterials that impart conductive phases. In this study, mechanical behavior and curing behavior were measured and analyzed to manufacture a CB-LSR complex by adding Carbon Black to LSR and to identify properties. As a result of the compression test, the elastic modulus tended to increase as carbon black was added. When the swelling test and the compression set test were conducted, the swelling rate tended to decrease as the content of carbon black increased, and the compression set tended to increase. In addition, DSC measurements showed that the total amount of reaction heat increased slightly as the carbon black content increased. It is considered that carbon black was involved in the crosslinking of LSR to increase the crosslinking density and have a positive effect on oil resistance reinforcement.

• Geomechanics and Engineering
• /
• v.32 no.4
• /
• pp.361-373
• /
• 2023

This study aimed to investigate the engineering properties and mechanical behaviors of polymer-fibers treated sand. Para rubber (PR), natural fiber (NF), and geosynthetic fiber (GF) were used to reinforce poorly graded sand. A series of unconfined compressive and splitting tensile strength tests were performed to analyze the engineering behaviors and strength enhancement mechanism. The experiment results indicated that the PR-fibers mixture could firmly enhance the strength properties of sand. The stress-strain characteristics and failure patterns have been changed due to the increase of PR and fibers content. The presence of PR and fibers strengthened the sand and enhanced the stiffness and ductility behavior of the mixture. The stiffness of reinforced sand reaches an optimum state when both NF and GF are 0.5%, while the optimum PR contents are 20% and 22.5% for the mixture with NF and GF, respectively. An addition of PR and fiber into sand contributed to increasing interlocking zone and bonding of PR-sand interfacial.

• Elastomers and Composites
• /
• v.44 no.1
• /
• pp.47-54
• /
• 2009

EPDM(Ethylene-propylene-diene-terpolymer) compound reinforced with carbon black having four different particle size, acetylene black(thermal conductivity carbon black), and silica were manufactured by internal mix and open mill. To investigate the effect of particle size of filler and filler type on far-infrared vulcanization, intermal temperature of compound, degree of curing, infrared spectroscopy, and thermal analysis were measured. The thermal conductivity of far-infrared vulcanized EPDM compound increased with increasing particle size of carbon filler, but hot air vulcanized EPDM compound is not affected by particle size. The thermal conductivity was increased in the order of carbon black < silica < acetylene black(thermal conductivity carbon black).

• Journal of the Korean Geotechnical Society
• /
• v.28 no.9
• /
• pp.47-55
• /
• 2012

This paper investigates the shear properties of crumb rubber-bottom ash mixture reinforced by waste fishing net (WFN). Mixtures used in this experiment consist of crumb rubber and bottom ash (2mm~10mm) with the same weight ratio. In this study several series of direct shear tests were carried out on the five different specimens : unreinforced mixture, reinforced mixtures with 1 or 2 single-layered WFN, reinforced mixtures with 1 or 2 double-layered WFN. The experimental results indicated that the shear properties of reinforced crumb rubber-bottom ash mixture were strongly influenced by reinforcing layer of WFN. It was found that the shear strength and internal friction angle of the mixtures increased with an increase in reinforcing layer of WFN due to interlocking effect and friction between mixture and WFN.

• Elastomers and Composites
• /
• v.25 no.4
• /
• pp.280-290
• /
• 1990

The effect of surface treatment of kaolinite with silane coupling agent on the reinforcement of SBR was investigated. The possibility of the practical use of kaolinite as an organic filler was also scrutinized and it was found that the reinforcement of SBR was improved by modifying surface of the cheap inactive inorganic filler with organic silane coupling agents. 3-Chloropropyltrimethoxysilane(C-series), 3-mercaptopropyltrimethoxysilane(M-series) and 3-aminopropyltriethoxysilane(A-series) were used as coupling agents. To test the material properties of vulcanized and unvulcanized SBR, Mooney viscosity, modulus, elongation and fractured surface measurements by SEM were carried out by changing the amount of silane coupling agents. Torqe of the unvulcanized SBR following the measurement of the degree of vulcanization was to be increased as the amount of silane was increasing, and Mooney viscosity of M-series and A-series was also increased.

• Elastomers and Composites
• /
• v.50 no.3
• /
• pp.184-188
• /
• 2015

There is a need for light weight and high stiffness characteristics in the building structure as well as aircraft and cars. So fiber reinforced plastic with the addition of reinforcing agent such as glass fiber, carbon fiber, aramid fiber is utilized in this regard. In this study, mechanical strength, flow property and part shrinkage of glass fiber and carbon fiber reinforced PA6 were examined according to reinforcement content such as 10%, 20%, and 30%, and reinforcement type. The mechanical property was measured by a tensile test with specimen fabricated by injection molding and the flow property was measured by spiral test. In addition, we measured the part shrinkage of fiber reinforced PA6 that affects part quality. As glass fiber content increases, mechanical property increased by 75.4 to 182%, and flow property decreased by 18.9 to 39.5%. And part shrinkage decreased by 52.9 to 60.8% in the flow direction, and decreased by 48.2 to 58.1% in the perpendicular to the flow direction. As carbon fiber content increases, mechanical property increased by 180 to 276%, flow property decreased by 26.8 to 42.8%, and part shrinkage decreased by 65.0 to 71.8% and 69.5 to 72.7% in the flow direction and the direction perpendicular to the flow respectively.

• Elastomers and Composites
• /
• v.44 no.4
• /
• pp.455-465
• /
• 2009

In this study, Organo-montmorillonite(MMT) was synthesized by intercalation of various amine(Octylamine, Dodecylamine, Dimethyldodecylamine, Octadecylamine) compounds into layered silicate. Natural Rubber(NR)/MMT nanocomposites were prepared by reinforcement of Organo-MMT. X-ray diffraction(XRD) and Scanning electron microscope(SEM) were employed to characterize the layer distance of Organo-MMT and the morphology of the NR/MMT nanocomposites. The structures of the synthesized Organo-MMTs were analyzed by the measurement of FT-IR. Cure characteristics, surface free energy and mechanical properties such as tensile strength, modulus and hardness of NR/MMT nanocomposites were carefully studied by contact angle meter, ODR, UTM, and hardness tester. FT-IR analysis showed a insertion of the alkyl and amine chains into the interlayers of the MMT. It was shown that the cure time of the organo-MMT was more decreased than that of $Na^+$-MMT. Surface free energy and tensile strength of the NR/DDA-MMT nanocomposite were the highest. NR/ODA-MMT nanocomposite was the highest in hardness.

• Journal of Adhesion and Interface
• /
• v.13 no.1
• /
• pp.45-50
• /
• 2012

Recently developed polyketone fiber has various applications in the mechanical rubber goods as reinforcement because of its good mechanical properties. However, its surface is not suitable for good adhesion with the rubber matrix. Thus, a surface modification is essential to obtain the good interfacial adhesion. Plasma treatment, in this study, has been conducted to modify the surface of the polyketone fiber. The morphological changes of the fibers by oxygen plasma treatment were observed by using SEM and AFM. The chemical composition changes of PK fiber surface treated with oxygen plasma were investigated using an XPS (X-ray photoelectron spectroscopy). Finally, the effect of these changes on the interfacial adhesion between fiber and rubber was analyzed by using a microdroplet debonding test. By the plasma treatment, oxygen moieties on the fiber surface increased with processing time and power. The surface RMS roughness increases until the proper processing condition, but a long plasma processing time resulted in a rather reduced roughness because of surface degradation. When the treatment time and power were 60 s and 80 W, respectively, the highest interfacial shear strength (IFSS) was obtained between the PK fiber and natural rubber. However, as the treatment time and power were higher than 60 s and 80 W, respectively, the IFSS decreased because of degradation of the PK fiber surface by severe plasma treatment.

• Elastomers and Composites
• /
• v.29 no.1
• /
• pp.18-29
• /
• 1994

The purpose of this study is to investigate reinforced effect between silica treated by coupling agents and rubber matrix under the configuration chemical bonds, and the effect of silica particles coated by organic polymers using aluminum chloride as the catalyst. In vulcanization characteristies were tested by Curastometer. The M-series vulcanizates were reached to the fastest optimum cure $time(t_{90})$ and R-series vulcanizates with the same formula had the shorted optimum cure times. Tensile characteristics measuring with a tensile tester revealed that the M-series vulcanizate was the best in the physical properties, such as tensile strength. In 100% modulus, however, the S-series vulcanizates appeared to be better than the other vulcanizates. Also, hardness showed the following order : S-series>R-series>M-series with the order of elongation R-series>M-series>S-series. In SEM test, shapes of chemical treated silicas were observed. The dispersion of filler in the SBR composite appeard uniformly. In RDS test for the dynamic characteristics, G' indicates that S-3 shows the highest value with the next order M-3>R-3, and the order of damping values are as followe: M-3>M-3>R-3.