• The korean journal of orthodontics
• /
• v.27 no.3 s.62
• /
• pp.493-502
• /
• 1997

This study was conducted to evaluate the tensile bond strength by bonding the dental bracket with Super-bond after treating the surface of dental Nickel-Chromium alloy with sandblasting, sandblasting & tin-plating, respectively, and tin-plating. 10 pieces of Nickel-Chromium alloys with brackets bonded with Super-bond without their surface treatment were sampled as a control group, 20 pieces of Nickel-Chromium alloy brackets bonded with Super-bond after treating them with sandblasting as group I, 20 pieces of Nickel-Chromium alloys tin-plated and bonded with Super-bond after sandblasting as group II, and then 20 pieces of alloys with brackets bonded with Super-bond after tin-plating as group III. The result of those examination and comparison is summarized as follows: 1. Group I showed the mean tensile bond strength of $14.41{\pm}2.24MPa$ which was highest among 4 groups, followed by group III($13.59{\pm}.51MPa$), group II($12.27{\pm}.45MPa$), and control group($10.50{\pm}1.57MPa$), respectively. However, it was shown that there was no statistically significant difference between group I and III, group III and II, and group II and control group(p>0.05). 2. The main failure pattern of those brackets showed that $70\%$ of the control group had an adhesive failure at the bracket-Superbond interface, and $30\%$ at the Nickel-Chromium alloy-Superbond interface, while other groups did the adhesive failure at the bracket-Superbond interface. 3. When examined under SEM, it was shown that adhesives were mostly attached to the surface of the Nickel-Chromium alloy for all groups while a considerable quantity of adhesives were attached to the bracket base. Then, those samples treated only with sandblasting showed the most even and remarkable roughness of their surface.

• Journal of Periodontal and Implant Science
• /
• v.24 no.1
• /
• pp.131-143
• /
• 1994

For maintenance of exposed implant in healthy state, it is necessary to treat the surface of implant fixture and provide the surface adjustable to surrounding tissues. Variable techniques have been introduced such as citric acid and air-abrasive system to treat the failed implant. Although when the rough surface of HA coated implant was exposed to oral environment, the surface treatment method with citric acid or air-abrasive system is effective for removal of bacterial endotoxin, it is unsuccessful to prevent plaque deposition due to difficulty in removal of rough surface of HA coated implant. Thus, in this study the method that removes bacterial endotoxin and makes smooch surface without alteration of surface characteristics was studied. HA coated disc manufactured by IMZ Co. Was treated with high speed diamond bur, low speed diamond bur, stone bur, rubber point, jetpolisher. And then its surface state was examined with profilometer and SEM to evaluate the surface smoothness, and its surface component was analyzed with EDX to evaluate wheter the surface characteristics were altered or not. As a result, following results were obtained. When the surface roughness of each implant disc was measured by profilometer, the group I showed a $R_{max}\;2.11{\mu}m$ and the group II, III, IV, V showed a $R_{max2}\;4.17{\mu}m$, $7.28{\mu}m$, $8.61{\mu}m$ and $39.44{\mu}m$ respectively. That is, surface smoothness was highest in the group I and it has been gradually decreased in the group II, III, IV and V. Under the SEM examination, the group I showed relatively smooth surface and the group II showed slightly rougher surface than the group I due to partially remaining HA particles while most HA particle was removed. The group III and IV showed rough topography due to HA particles that was not grinded, and HA coated surface in group V showed very irregular surface with deep groove and prominence. In cross-sectional view, the group I showed uniform surface, and the group III, IV showed rough surface due to remaining HA particles but the thickness of HA coating was remarkably reduced. The group II has similar pattern in group I, and the group V showed about $40{\mu}m$ thickness although it was not constant. By analysis of surface component with EDX, the group II in which the grinding was effective showed a small quantity of calcium and phosphorous and the group III, IV, in which the grinding was incomplete showed calcium and phosphorus peak. In all experimental group, no other than titanium, aluminum, calcium, phosphorus was observed.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.6
• /
• pp.720-731
• /
• 2003

Statement of problem. The importance of fixture design and surface treatment. Purpose. The clinical success of dental in plants is affected by many factors such like as degree of osseointegration, the effective load dispersion for the prostheses, and a lot of attempts have been made to overcome the difficulties. In this study, efforts were made to find the possibility of clinical acceptance of the dental implants of newly designed surface and resorbable blast media surcace. Materials and methods. In this study, two groups of custom-made, screw-shaped implants were prepared. The first with the consisting of Branemark clone design and the other with the new design. These implants were divided into four groups according to the kinds of surface treatment. Four implants($AVANA^{(R)}$, Osstem, Busan, Korea)of each group were installed in twenty rabbits. Group A was consisted of Branemark done implant left as machined, Group B with Branemark clone implants with RBM(Resorbable blast media) surface, Group C with newly designed implants left as machined and Group D with newly designed implants with RBM surface. One of the twenty rabbits died from inflammation and the observation was made for six weeks. Specimens from four groups were observed using scanning electron microscopy with 40, 100, 1000 magnification power and microsurface structures were measured by white-light scanning interferometry for three dimensional surface roughness measurements(Accura $2000^{(R)}$, Intek-Plus, Korea.). Removal torque was measured in 17 rabbits using digital torque gauge(MGT 12R, Mark-10 corp., NY, U.S.A.) immediately after the sacrifice and two rabbits were used for the histologic preparation(EXAKT $310^{(R)}$, Heraeus Kulzer, wehrheim, Germany) of specimens and observed under light microscope. Resonance frequency measurement($Osstell^{(R)}$) was taken with the 19 rabbits at the beginning of the implant fixation and immediately after the sacrifice. Results. Following results were taken from the experiment. 1. The surface of the RBM implants as seen with SEM had rough and irregular pattern with reticular formation compared to that of fumed specimens showing different surface topographies. 2. The newly designed implant with RBM surface had high removal torque value among four groups with no statistical significance. The average removal torque was $49.95{\pm}6.70Ncm$ in Group A, $51.15{\pm}4.40Ncm$ in Group B, $50.78{\pm}9.37Ncm$ in Group C, $51.09{\pm}4.69Ncm$ in Group D. 3. The RFA values were $70.8{\pm}4.3Hz$ in Group A, $71.8{\pm}3.1Hz$ in Group B, $70.9{\pm}2.5Hz$, $72.7{\pm}2.5Hz$ in Group D. Higher values were noted in the groups which had surface treatment compared to the untreated groups with no statistical significance. 4. The results from the histomorphometric evaluation showed a mean percentage of bone-to-implant contact of $45{\pm}0.5%$ in Group A, $55{\pm}3%$ in Group B, $49.5{\pm}0.5%$ in Group C, and $55{\pm}3%$ in Group D. Quite amount of newly formed bone were observed at the surface RBM-treated implants in bone marrow space.