• Corrosion Science and Technology
• /
• v.7 no.3
• /
• pp.145-151
• /
• 2008

Material degradation such as high temperature oxidation of metallic material is a severe problem in energy generation systems or manufacturing industries. The metallic materials are oxidized to form oxide films in high temperature environments. The oxide films act as diffusion barriers of oxygen and metal ions and thereafter decrease oxidation rates of metals. The metal oxidation is, however, accelerated by mechanical fracture and spalling of the oxide films caused by thermal stresses by repetition of temperature change, vibration and by the impact of solid particles. It is therefore very important to investigate mechanical properties and adhesion of oxide films in high temperature environments, as well as the properties in a room temperature environment. The oxidation tests were conducted for Ni and Ni-Co alloy under high temperature corrosive environments. The hardness distributions against the indentation depth from the top surface were examined at room temperature. Dynamic indentation tests were performed on Ni oxide films formed on Ni surfaces at room and high temperature to observe fractures or cracks generated around impact craters. As a result, it was found that the mechanical property as hardness of the oxide films were different between Ni and Ni-Co alloy, and between room and high temperatures, and that the adhesion of Ni oxide films was relatively stronger than that of Co oxide films.

• Journal of Korean Society for Atmospheric Environment
• /
• v.3 no.1
• /
• pp.41-46
• /
• 1987

Adsorption and reaction studies were made for the catalytic oxidation in aqueous slurries of activated carbon at room temperature and atmospheric pressure. In order to analyze the reaction rate, the mechanism was assumed by the steps of nonhomogeneous catalytic reaction. The experimental result show that oxidation rate was controlled by the reaction between adsorbed molecular oxygen and sulfur dioxide on the catalyst surface. Ar room temperature, the equat5ion of reaction rate was given as $ro_2 = 2.49 \times 10^{-7} P_O_2^{0.604}$.

• Tribology and Lubricants
• /
• v.16 no.4
• /
• pp.282-288
• /
• 2000

A sliding friction and wear test for silicon nitride (Si,N4) was conducted using a ball-on-disk specimen configuration. The material used in this study was HIPed silicon nitride. The tests were carried out from room temperature to 1000$^{\circ}C$ using self-mated silicon nitride couples in laboratory air. The worn surfaces were observed by SEM and the debris particles from the worn surfaces were analyzed for oxidation by XPS. The normal load was found to have a more significant influence on the friction coefficient of the silicon nitride than an elevated temperature. The specific wear rate was found to decrease along with the sliding distance. The specific wear rate at 29.4 N and 1000$^{\circ}C$ was 292 times larger than that at room temperature. The main wear mechanism from room temperature to 750$^{\circ}C$ was caused by brittle fracture whereas from 750$^{\circ}C$ to 1000$^{\circ}C$ the wear mechanism was mainly influenced by the oxidation of silicon nitride due to the increased temperature. The oxidation of silicon nitride at a high temperature was a significant factor in the wear increase.

• Journal of the Korean GEO-environmental Society
• /
• v.17 no.10
• /
• pp.5-11
• /
• 2016

In this study, the factors affecting commercialization of $Pt/TiO_2$ catalyst, which can oxidize HCHO at room temperature, was investigated. In order to determine the optimum noble metal loading, the catalytic activity was evaluated by varying the Pt loadings; the best catalytic activity was achieved for 1 wt% of Pt. In addition, the catalyst prepared under the reduction condition showed an excellent HCHO oxidation conversion at room temperature. Based on these results, it was confirmed that the activity could be changed by oxidation state of active metal, and in case of Pt, metallic Pt ($Pt^0$) species was more active on HCHO oxidation at room temperature. As a result of evaluating an effect of space velocity to determine the optimum operating condition, it was found that in the lower space velocity, conversion rate of HCHO was increased due to increase of catalyst bed. Catalytic activity was greater in the presence of moisture than in its absence. Through above results, the key factors for commercialization of oxidation catalyst, which was operated at room temperature even without any additional energy source was confirmed.

• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.155-161
• /
• 1999

The tribological behaviour of monolithic SiC as well as SiC-TiC and SiC-TiC-$TiB_2$ particulate composite materials has been investigated in unlubricated oscillating sliding tests against $Al_2O_3$ at temperature in the range from room temperature up to $600^{\circ}C$. At temperatures below $600^{\circ}C$ the wear rate of the systems with the composite materials was up to 20 times lower than the wear of the $Al_2O_3$/SiC system and was dominated by the oxidation of the titanium phases. At $600^{\circ}C$ the oxidation rate of the TiC and -TEX>$TiB_2$ grains becomes predominant resulting in an enhanced wear rate of the composite rate of the TiC and TiB2 grains becomes predominant resulting in an enhanced wear rate of the composite materials. The coefficient of friction shows similar values for all materials of investigation, increasing from 0.25…0.3 at room temperature to 0.7…0.8 $600^{\circ}C$. The wear of the $Al_2O_3$/SiC system is mainly abrasive at temperatures above room temperature and is characterised by an enhanced wear of the alumina ball at $600^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.182-182
• /
• 2009

The effect of Re-oxidation on the PTCR properties of Sm-doped barium titanate ceramics was investigated by means of impedance spectroscopy. Electrical properties such as resistance vs. temperature, I-V curve were measured and microstructure was observed with SEM photography. Sample was fabricated with thick film process such as tape casting of green sheet, screen printing of electrode pattern, stacking, firing in reduced atmosphere and re-oxidation, etc. As the temperature of re-oxidation increases, resistance jump as a function of temperature enhances but resistance at room temperature increases. These behavior of resistance as a function of temperature, dependent on the re-oxidation condition, is analyzed with Cole-Cole impedance plot and is shown to be related with the degree of oxidation of grain boundary regardless of grain core during re-oxidation process of sample.

• Applied Chemistry for Engineering
• /
• v.29 no.6
• /
• pp.657-662
• /
• 2018

In this study, the effect of $Pt/TiO_2$ catalysts on the CO oxidation reaction at room temperature was investigated using various $TiO_2$ supports with different physical properties to compare and evaluate $Pt/TiO_2$ catalysts. Physicochemical properties of the catalyst were alanyzed using XPS, CO-chemisorption, BET, and CO-TPD. As a result, when the active particle diameter was smaller, while the metal dispersion and surface area were larger, the CO room temperature oxidation reaction was better. These physical properties increased the number of active sites, causing the target material to increase the adsorption amount of CO. In addition, when the $O_2$-consumption increased, the CO-room temperature oxidation reaction activity increased due to the excellent oxygen-transferring ability.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.89-95
• /
• 2001

The fretting wear characteristics of Zircaloy-4 tube at room and high temperature were Investigated experimentally. In this study, the number of cycles, slip amplitude and temperature were selected as main factors of fretting wear. The results of this research showed that the wear volume Increased with the Increase of slip amplitudes and the number of cycles but decreased with temperature and the coefficient of friction were observed different tendency between room and high temperature. According to SEM(EDS) only gross slip were observed on the surface of both specimens and compacted oxide were on worn surfaces. XRO patterns showed that the crystallization of ZrO$_2$ were observed on the worn surface at high temperature. The fretting wear were Investigated due to oxidation and accumulation of plastic flow.

• Corrosion Science and Technology
• /
• v.22 no.4
• /
• pp.257-264
• /
• 2023

Ti-6Al-4V alloys are mainly used as dental materials due to their excellent biocompatibility, corrosion resistance, and chemical stability. However, they have a low bioactivity with bioinertness in the body. Therefore, they could not directly bond with human bone. To improve their applications, their bone bonding ability and bone formation capacity should be improved. Thus, the objective of this study was to improve the bioinert surface of titanium alloy substrate to show bioactive characteristics by performing surface modification using wollastonite powder. Commercial bioactive wollastonite powder was successfully deposited onto Ti-6Al-4V alloy using a room temperature spray process. It was found that wollastonite-coated layer showed homogeneous microstructure and uniform thickness. Corrosion resistance of Ti-6Al-4V alloy was also improved by plasma electrolytic oxidation treatment. Its wettability and bioactivity were also greatly increased by wollastonite coating. Results of this study indicate that both plasma electrolytic oxidation treatment and wollastonite coating by room temperature spray process could be used to improve surface bioactivity of Ti-6Al-4V alloy substrate.

• 연구논문집
• /
• s.28
• /
• pp.183-192
• /
• 1998

The wear and oxidation resistance of two phase nickel aluminides was investigated. Wear tests of various heat-treated specimens at room temperature and at $500^{\circ}C$ were performed under no lubricant condition in air by using a ball-on-disk type tribotester. Isothermal oxidation tests were made at $1100^{\circ}C$ in air flowing at the rate of 70cc/min and at $1000^{\circ}C$ in air by using TGA. Experimental results from wear tests showed that nickel aluminide with a higher content of Al had an improved wear resistance at both temperatures. Also the examination of the wear tracks after wear test at both room temperature and $500^{\circ}C$ indicated that regardless of the alloy compositions the wear tracks of the two phase nickel aluminides showed an abrasive type wear The improved oxidation resistance observed in the Ni-34at%Al alloy could to be attributed to the microstructural difference between the aluminides. An accelerated oxidation along the thin layer of $Ni_3AL$ along the grain boundary observed in the microstructure of the Ni-32at%Al aluminide could be attributed to the poor oxidation resistance.