• 공업화학
• /
• 제25권4호
• /
• pp.352-356
• /
• 2014

${\alpha},{\omega}$-Aminopropylpolydimethylsiloxane을 bisphenol-A diglycidyl ether (DGEBA)계 이관능성 에폭시 수지와 반응시켜 polydimethylsiloxane (PDMS)의 양 말단에 에폭시가 도입된 실리콘 변성 에폭시 수지(EMPDMS)를 제조한 다음 alkylesteraminopropyl alkoxy silane (XD 5607)을 반응시켜 PDMS가 도입된 에폭시 hybrid 화합물(EMPDMSH)을 제조하고 이를 FT-IR, $^1H$-NMR 및 $^{29}Si$-NMR로 구조를 확인하였다. EMPDMSH base 수지에 용매를 혼합하여 코팅 액을 제조하였으며, 이를 에폭시/유리 섬유 복합재료로 얻어진 필름에 도포하고 경화시킨 후 base수지 중에 함유된 PDMS의 함량에 따른 물성을 측정하였다. 코팅 면의 접촉각을 측정한 결과 기존의 에폭시 수지로 코팅하여 얻은 코팅 면에 비해 접촉각이 $41^{\circ}$에서 $71^{\circ}$로 약 $30^{\circ}$정도 증가되고 있어 코팅 면에 PDMS가 나타나 있음을 확인할 수 있었다. 또한 접착력 및 표면 평활도 개선효과 측정 결과 에폭시 자체 코팅 액이나 일반적으로 많이 사용되고 있는 아크릴계 코팅 액 보다 5B 등급의 뛰어난 접착력을 나타내었고 평활도 개선 효과도 우수함을 나타내었다.

• 대한소아치과학회지
• /
• 제25권1호
• /
• pp.62-75
• /
• 1998

The main purpose of this study was to compare the anticariogenecity of glass ionomer restorative material polymerized by argon laser versus visible light, The results from the present study can be summarized as follows; 1. Under the polarized light microscope, the specimens of laser-cured group showed the shallower lesion body than that of visible-light cured group, both in the stage of lesion initiation and progression. 2. Glass ionomer material cured by visible light showed shallower body of lesion than that of composite resin cured by argon laser at the stage of lesion progression(p<0.05). It was suggested fluoride released from the glass ionomer might have the additive anticariogenic effect. 3. Statistical difference between groups on depth of lesion body was evident after lesion progression (p<0.05). It was suggested that anticariogenic effect by argon laser was more effective at the stage of lesion progression than the lesion initiation. 4. The increment of lesion body during progression was highest in group IV (p<0.05). 5. Based upon the above-mentioned results of this study, it can be concluded that the advantage of anticariogenic effect and short curing time of argon laser in glass ionomer polymerization should be considered in children and adolescents whose caries activity is relatively higher.

• Restorative Dentistry and Endodontics
• /
• 제29권3호
• /
• pp.281-287
• /
• 2004

The purposes of this study were to evaluate the effect of adhesive property on microtensile bond strength and to determine the failure mode. Flat occlusal dentin surfaces were prepared using low-speed diamond saw. The dentin was etched with 37％ phosphoric acid. The following adhesives were applied to the etched dentin to manufacturer's directions： Scotchbond Multi-Purpose in group SM, Prime＆Bond NT in group NT, Scotchbond Multi-Purpose followed by Tetric-flow in group TR. After adhesive application, a cylinder of resin-based composite was built up on the occlusal surface. Each tooth was sectioned vertically to obtain the $1{\;}{\times}{\;}1\textrm{mm}^2$ "sticks". Microtensile bond strength were determined. Each specimen was observed under stereomicroscope and scanning electron microscope (SEM) to examine the failure mode. Data were analyzed using one way ANOVA. The results of this study were as follows：1. The microtensile bond strength value were：group SM ($18.98{\pm}3.01MPa$). group NT ($16.01{\pm}4.82MPa$) and group TR ($17.56{\pm}3.22MPa$). No significant statistical differences were observed among the groups (P>0.05). 2. Most of specimens showed mixed failure. In group TR, there was a higher number of specimens showing areas of cohesive failure in resin.

• Composites Research
• /
• 제12권3호
• /
• pp.84-90
• /
• 1999

HAC/PVA계 MDF시멘트 복합재료의 수분안정성 및 기계적 강도향상을 위하여 불용성 폴리머류(폴리우레탄, 페놀, 에폭시수지)와 탄소섬유(길이3mm)를 1-4wt% 보강하였다. 그리고 가압성형법으로 제조한 복합체의 수분침적 기간별 강도특성(수분안정성)과 계면 및 기계적 특성에 영향을 미치는 폴리머와 시멘트의 가교반응에 대하여 SEM 및 TEM 분석을 통하여 관찰하였다. HAC/PVA계 MDF 시멘트 복합체의 섬유함량에 따른 건조 굽힘강도는 섬유함량이 증가할수록 치밀화 구조가 저하되어 비례적으로 감소되었다. 또한 불용성 폴리머류를 사용한 경우에 건조 굽힘강도는 섬유함량이 증가될수록 저하되는 반면, 수분안정성은 크게 향상되었다. 에폭시 수지를 첨가한 경우에 수분안정성이 가장 우수하였으며, 섬유함량 4% 첨가의 경우에 3일 침적강도가 95%, 7일침적시 87%강도를 유지하였다. 이 점은 폴리머와 시멘트의 금속이온이 가교반응을 일으켜 섬유-메트릭스간 계면 부착강도를 크게 개선되었기 때문으로 추정된다. 반면 인장강도 특성은 모든 불용성 폴리머류 첨가 수준에서 섬유 함량이 증가할수록 비례적으로 증가되었으며, 역시 에폭시 수지 첨가의 경우에 강도특성이 가장 우수하였다. 그리고 섬유함량 4% 첨가된 경우에 있어서 인장강도는 섬유함량 0% 대비 약 30~80% 높게 나타났다.

• 대한소아치과학회지
• /
• 제26권3호
• /
• pp.554-563
• /
• 1999

심미적 수복재료인 복합 레진과 글래스 아이오노머 시멘트는 중합방식에 따라 화학중합형, 광중합형, 그리고 이 두 가지 중합방식을 겸비한 이중중합형으로 분류할 수 있다. 화학중합형과 광중합형에 대해서는 지금까지 다수의 보고가 있었으나, 충전용 복합 레진의 경우 이들과 이중중합형을 비교한 예는 아직 찾기 힘든 실정이었으므로, 이러한 관점에서의 연구가 필요할 것으로 사료되었다. 이 연구에서는 이중중합 수복재가 단일중합방식에 비해 어떠한 특성을 보이는지를 탐구하고자 하였다. 사용된 재료는 광중합형 복합 레진인 Veridonfil-Photo와 이중중합형인 Bis-core, 이중중합형의 글래스 아이오노머 시멘트인 Fuji II LC와 화학중합형인 Ketac-fil을 사용하였다. 가로 30mm, 세로 30mm, 높이 1mm와 3mm인 두 종류의 아크릴릭 몰드 중앙에 직경 7mm의 hole을 형성하여 여기에 4종의 수복재를 충전하였다. 충전 직후부터 시작하여 24시간 경과시까지 일정 시간의 간격으로 표면, 1mm, 3mm 깊이에서의 경도를 미세경도계(Shimadzu Micro Hardness Tester HMV-2000, Shimadzu Co. Japan)로 측정하였다. 측정치를 통계처리하여 얻은 결과는 다음과 같다. 1. 4 종의 수복재 모두에서, 중합직후에 비해 24시간 경과후의 미세경도가 증가되었다. 2. 중합 직후부터 24시간 경과시점까지의 미세경도를 측정한 결과, Ketac-fil을 제외한 나머지 수복재에서는 각 깊이간 경도의 차이가 있었다. 3. 각 수복제의 최종중합에 도달하는 시간을 조사한 결과, 이중중합형이 3min의 깊이에서 광중합형이나 화학중합형에 비해 중합이 더 오래 지속된 것으로 나타났다. 이상의 결과에서 조사광이 충분히 도달하지 못하여 중합이 현저히 떨어지는 수복재의 심부에도 이중중합방식을 사용할 경우에는 지속적인 중합반응이 일어나 중합도가 증가하는 것으로 나타났다.

• Restorative Dentistry and Endodontics
• /
• 제23권2호
• /
• pp.656-669
• /
• 1998

Hydrogen peroxide at high concentration during walking bleaching may cause damage to the tooth structure and to the surrounding periodontal tissues and may develop external root resorption. Clinically, It is so important to find a method of prevention or minimization of these complications. The efficacy of various chamber-irrigating agents to eliminate residual hydrogen peroxide after walking bleaching was examined and compared with water rinse in this study. Extracted human 46 premolars without any cementoenamel junction defects were treated endodontically and based with IRM to 1 mm below CEJ and totally bleached 3 times for each tooth with 30% hydrogen peroxide and sodium perborate. Upon completion of the 3rd walking bleaching procedure, the cervical portion and pulp chamber of each group of teeth were irrigated with catalase, 70% ethylalcohol, acetone, and distilled water. And then, a radicular hydrogen peroxide penetration was measured with spectrophotometer immediately after each bleaching and following treatment with each chamber-irrigating agents, and the significance of their eliminating efficacy of residual hydrogen peroxide was analyzed by Kruskal-Wallis test. The results were obtained as follows. 1. Cervical root penetration of hydrogen peroxide was increased as the bleaching procedure was repeated(P<.01). 2. The most effective irrigant that removed residual hydrogen peroxide was the catalase, and the least effective one was water rinsing (P<.01).; there was no significant difference between the acetone and ethanol group. 3. The Irrigation with antioxidant enzyme or water-displacement solutions can eliminate residual oxygen radicals from the pulp chamber effectively after walking bleaching. So, these agents can reduce adverse effects such as cervical external resorption and periapical inflammation and prevent residual $O_2$ from impeding composite resin polymerization, thus increase the bonding strength of composite resin. This, in turn reduces microleakage and discoloration of the esthetic restoration, extending its service-life.

• 대한소아치과학회지
• /
• 제48권2호
• /
• pp.168-175
• /
• 2021

이 연구는 깊은 와동에서 기저재로 사용되는 5개의 기저재용 재료를 대상으로 미세누출 및 압축강도 평가를 시행하였다. 미세누출 평가를 위해 발거된 영구 소구치 50개를 준비하여 베이스 재료에 따라 10개씩 군을 나누었다. 치아의 순면에 가로 5.0 mm, 세로 3.0 mm, 높이 3.0 mm 크기의 와동을 형성하였다. 형성된 와동에 1.0 mm 두께로 각 베이스 재료를 충전하였다. 이후 와동의 상방부를 composite resin으로 최종수복 시행하였으며, 시편을 2% 메틸렌블루 용액에 침적시킨 후 치아를 절삭하였고 실체현미경(× 30)을 이용해 미세누출 정도를 평가하였다. 압축강도 평가를 위해 각 재료 별로 5개씩의 원통형 시편을 제작하였다. 이후 만능시험기를 이용해 압축강도를 평가하였다. 미세누출 평가에서 Riva light cure^TM가 가장 큰 미세누출을 보였으며, Well-Root PT와 Biodentine이 가장 적은 미세누출을 보였다. 압축강도는 모든 군이 베이스 재료로서 받아들일 만한 강도를 보였다. Fuji II LC가 가장 높은 압축강도를 보였으며 Well-Root PT가 가장 낮은 강도를 보였다.

• Composites Research
• /
• 제36권5호
• /
• pp.297-302
• /
• 2023

발포체를 성형하기 위한 방법으로는 여러 가지 방법이 있는데 일반적으로 가장 많이 사용되는 방법으로는 발포제를 섞은 레진을 고온, 고압상태에서 발포하는 가압발포 방법과, 압을 주지 않은 고온의 상태에서 발포하는 상압발포 방법이 있다. 발포에 사용되는 고분자들은 상압상태에서 발포를 시키기 위해서는 최적 발포조건에 대한 설계 및 분석이 필요하다. 친환경 바이오 기반 폴리머는 단독으로는 발포가 힘든 문제가 있어 기존의 발포체 제조가 가능한 수지를 혼합하여 발포체를 제조하는 연구가 진행되고 있다. 본 연구에서는 바이오 기반 고분자의 함량 변화에 따른 바이오 기반 고분자와 EVA 혼합 발포체의 특성변화에 대해서 연구하였으며 가교도에 따른 최적 발포 조건에 대해서 연구하였다. 발포체의 기계적 특성 분석을 통해서 발포특성과의 상관관계에 대해서 연구하였다. 이 연구를 통해 바이오 기반 폴리머의 함량이 바이오 기반 폴리머가 포함된 발포체의 물성에 어떤 영향을 미치는지 알 수 있었고 상압 및 가압 발포 공정에 따른 차이점을 확인할 수 있었다. 또한, 바이오 기반 폴리머-EVA 복합 발포체의 상용화 가능성을 확인하였다.

• 한국철도학회논문집
• /
• 제12권4호
• /
• pp.590-596
• /
• 2009

본 연구에서는 탄소, 유리, 케블라 및 탄소-케블라 하이브리드 섬유로 제작된 원형튜브를 이용하여 각 소재별 에너지 흡수특성과 파손메커니즘을 규명하였다. 이를 위해 각 튜브에 대한 10mm/min의 준정적 압축시험을 수행하였다. 시험결과 탄소섬유 튜브가 가장 에너지 흡수특성이 우수했으며 탄소-케블라 하이브리드 섬유 튜브가 가장 낮은 에너지 흡수율을 보였다. 또한, 각 소재별 에너지 흡수메커니즘을 분석한 결과 탄소 및 유리섬유튜브는 취성파괴 모드로 압축되었다. 또한, 케블라 섬유 튜브는 국부좌굴에 의한 접힘모드가 지배적이고, 탄소와 케블라 하이브리드 섬유 튜브의 경우 단층굽힘과 국부좌굴모드가 혼합되어 나타났다.

• 대한치과보철학회지
• /
• 제18권1호
• /
• pp.37-47
• /
• 1980

The purpose of this study was to investigate the stresses in different proximal margins and to measure, quantitatively, the effect of different modifications in the design of preparations on the stresses using two-dimensional photoelasticity. Photoelastic stress analysis is based on the phenomenon, exhibited by most transparent solids, of becoming birefringent, or doubly refracting, when strained. Two birefringent materials were used in this study, PSM-1 and PSM-5 in .standard sheet ($10'{\times}10'{\times}\frac{1}{4}'$ thickness), PSM-1(polyester) was used for constructing the substructure, and PSM-5(epoxy resin) was used in making the restorations to be investigated. Two birefringent materials were used in the construction of composite photoelastic model. Seven variable models were constructed. The peripheral dimensions of all model were constant and the models represent an occlusomesial section of a lower posterior molar. Model 1 represents the knife edge margin (shoulderless), Model 2 represents the chamfer, Model 3 represents a rounded shoulder(no sharp angle between the axial wall and gingival floor), Model 4 represents a flat shoulder (axial wall is a $90^{\circ}$ angle to the gingival wall), Model 5 represents $+15^{\circ}$ angulation, Model 6 has a $-15^{\circ}$ angulation, and Model 7 is the same as Model 4 except that it has a $45^{\circ}$ bevel. Improved artificial stone was used to represent dental cement in luting the composite photoelastic model. Static loading procedures(100 pounds) were used at preplanned sites. The results were as follows; 1. The stresses in the proximal portion of all tested models were compressive in nature when the proximal shoulders were loaded vertically on the same proximal marginal ridge. 2. The round and chamfered preparations were the optimum designs in proximoocclusal restorations. They showed the lowest stress concentration factor, i.e. 2.16 and 2.23, respectively. The knife edged shoulder had the highest value, K=5.39. Round type shoulder geometry experiments reduced the stress concentration factor (S.C.F.) 3. The gingival portion of proximal shoulder geometry was a critical location for stress concentration.