In dental resin cement studies, viscosity is also an important factor in the adhesion of tooth defects and implants. This study used BisGMA and HPMA as the main ingredients, triethylene glycol dimethacrylate (TEGDMA) as a diluent, and benzoyl peroxide (BPO) as a photoinitiator. The physical properties of graphene oxide used as an additive for functionality were evaluated, and its use as a dental resin cement material was investigated.The rupture strength has the tendency to increase along with the increase of the ratio of graphene oxide that was added, which seemed to reflect the effect of the high strength property of graphene oxide. The flexural strength also has the tendency to increase when about 0.5% of graphene oxide was added the same as the increase of rupture strength.When graphene oxide was added, according to viscosity use, the utilization as high-quality dental resin cements will increase.

• Journal of Environmental Science International
• /
• v.28 no.5
• /
• pp.503-509
• /
• 2019

To prevent environmental pollution caused by leakage of leachate from waste landfill, vinyl acetate-ethylene (VAE) resin is applied to liner and cover materials to improve their performance. Styrene, styrene butadiene rubber, and VAE are widely used as polymer resins that have excellent water resistance and durability. Further, VAE resin is known to have additional advantages such as adhesion to nonpolar materials and resistance to saponification as a copolymer. In this study, the effect of VAE content on the properties of liner and cover materials was studied. The water and air content ratios, bending and compressive strengths, water absorption ratio, and coefficient of permeability of these materials were measured. The liner and cover materials with 4 wt% VAE showed good properties.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.164-165
• /
• 2021

To prepare the good-adherent and weather-resistant acrylic resin coatings, acrylic resin was prepared by a radical polymerization. Glass transition temperature(Tg) of the acrylic copolymer was fixed at 30℃ and the contents of tertiary amine monomer(DMAEMA) was varied to be 5, 10, 15, 20 wt% respectively. γ-Glycidoxypropyltrimethoxysilane(GPTMS) containing epoxy group was used for curing agents and di-n-butyltindilaurate(DBTDL) was used for drying accelerator. The equivalent ratio of amine to epoxy was 1:1. The prepared coatings exhibited excellent adhesion to various substrates, and various physical properties of the coatings were satisfactory. The gloss retention and color difference were improved at low tertiary amine concentration. The coatings containing 10wt% tertiary amine concentration have especially good weather resistant properties.

• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.643-649
• /
• 2012

Coatings composited with alumina and Perfluoro alkoxyalkane (PFA) resin were deposited on stainless steel plate (SUS304) to further improve corrosion resistance. Plate (ca. $10{\mu}m$) and/or nanosize (27~43 nm) alumina used as inorganic additives were mixed in PFA resin to make alumina-fluoro composite coatings. These coatings were deposited on SUS304 plate with wet spray coating and then the film was cured thermally. According to the amount and ratio of the two kinds of alumina having plate morphology and nano size, corrosion resistance of the film was evaluated under strong acids (HF, HCl) and a strong base (NaOH). The film prepared with the addition of 5~10 wt% alumina powders in PFA resin showed corrosion resistance superior to that of pure PFA resin film. However, for the film prepared with alumina content above 10 wt%, the corrosion resistance did not improve with the physical properties, such as surface hardness and adhesion. The film prepared with plate/nanosize (weight ratio = 1/2) alumina especially enhanced the surface hardness and corrosion resistance. This can be explained as showing that the plate and the nanosize alumina dispersed in PFA resin effectively suppressed the penetration of cations and anions due to the long penetration length and fewer defects that accompany the improved surface hardness under a serious environment of 10% HF solution for over 120 hrs.

• Restorative Dentistry and Endodontics
• /
• v.23 no.2
• /
• pp.607-617
• /
• 1998

The purpose of this study was to evaluate the apical sealing ability of lateral condensation method, vertical condensation method, and MicroSeal obturation system. Sixty-four extracted anterior teeth were instrumented to #40 using Profile. Three groups of 20 teeth were obturated by lateral condensation technique, vertical condensation technique, and and MicroSeal obturation system. Control group were not obturated. Teeth were immersed in resorcinol-formaldehyde resin for 5 days at $4^{\circ}C$, and the resin was allowed to polymerize completely for 4 days at room temperature. Teeth were ground horizontally at 1,5mm(level 1), 2.5mm(level 2), and 3.5mm(level 3) from the anatomic apex and examined with a stereomicroscope at X40 magnification. The photographs were taken a at X40 magnification of the filling in each level and scanned. The leakage area, which was filled with the resin, was measured at each of the three levels. Each ratio of leakage was evaluated by calculating the ratio of thearea of the resin to the total area of the canal and was analyzed statistically. The results were as followed: 1. Vertical condensation group had significantly higher percentage of the area which was obturated by gutta percha than other two technique at each level. 2. At the level 1, there was the greatest leakage in the lateral condensation group, but there was no statistically significant(P>0.05) 3. At the level 2, there was the least leakage in the MicroSeal group, and the most leakage in the lateral condensation group. There was statistically significant difference between the MicroSeal group and the lateral condensation group(P<0.05). 4. At the level 3, there was least leakage in the vertical condensation group, and the most leakage in the lateral condensation group. There was statistically significant difference between the vertical condensation group and the lateral condensation group(P<0.05).

• The Journal of Advanced Prosthodontics
• /
• v.8 no.4
• /
• pp.275-284
• /
• 2016

PURPOSE. The aim of this study was to evaluate the influence of different surface treatment methods on the microtensile bond strength of resin cement to resin nanoceramic (RNC). MATERIALS AND METHODS. RNC onlays (Lava Ultimate) (n=30) were treated using air abrasion with and without a universal adhesive, or HF etching followed by a universal adhesive with and without a silane coupling agent, or tribological silica coating with and without a universal adhesive, and divided into 6 groups. Onlays were luted with resin cement to dentin surfaces. A microtensile bond strength test was performed and evaluated by one-way ANOVA and Tukey HSD test (${\alpha}$=.05). A nanoscratch test, field emission scanning electron microscopy, and energy dispersive X-ray spectroscopy were used for micromorphologic analysis (${\alpha}$=.05). The roughness and elemental proportion were evaluated by Kruskal-Wallis test and Mann-Whitney U test. RESULTS. Tribological silica coating showed the highest roughness, followed by air abrasion and HF etching. After HF etching, the RNC surface presented a decrease in oxygen, silicon, and zirconium ratio with increasing carbon ratio. Air abrasion with universal adhesive showed the highest bond strength followed by tribological silica coating with universal adhesive. HF etching with universal adhesive showed the lowest bond strength. CONCLUSION. An improved understanding of the effect of surface treatment of RNC could enhance the durability of resin bonding when used for indirect restorations. When using RNC for restoration, effective and systemic surface roughening methods and an appropriate adhesive are required.

• Journal of Digital Convergence
• /
• v.18 no.4
• /
• pp.309-314
• /
• 2020

Polymethyl methacrylate (PMMA) is concerned with promoting oral infection due to its low antibacterial activity. To overcome this, the nanoparticles of Ag-MSN, nGO, and CNP were mixed with MMA liquid in a weight ratio of 0, 0.25, 0.5, 1.0, 2.0% compared to resin powder using Orthocryl from Dentarum, a calibration resin, and then instructed by the manufacturer. Accordingly, a specimen for calibration was prepared by mixing PMMA: MMA (1.2: 1) ratio, and physical properties of the calibration resin, antifungal experiments, and statistical analysis were performed. As a result of antibacterial experiments, the antibacterial properties of Ag-MSN increased. In nGO, the antibacterial adhesive effect increased hydrophilicity, not a change in surface roughness. The higher the CNP concentration, the higher the antibacterial activity. This suggests its potential usefulness as an antibacterial dental material for orthodontic devices and temporary restorations.

• Journal of Electrical Engineering and Technology
• /
• v.13 no.3
• /
• pp.1166-1172
• /
• 2018

Degradation due to delamination occurs frequently in the high temperature superconductors (HTS) coil of rotating machines made with 2nd generation (2G) HTS wire, and the authors have observed other similar cases. Since an HTS field coil for a rotating machine is required to have stable current control and maintain a steady state, co-winding techniques for insulation material and epoxy resin for shape retention and heat transfer improvement are applied during coil fabrication. However, the most important limiting factor of this technique is delamination, which is known to be caused by the difference in thermal expansion between the epoxy resin and 2G HTS wire. Therefore, in this study, the experimental results of mixing the ratio of epoxy resin and alumina ($Al_2O3$) filler were applied to the fabrication of small and large test coils to solve the problem of degradation. For the verification of this scheme, eight prototypes of single pancake coils with different shapes were fabricated. They showed good results. The energization and operation maintenance tests of the stacked coils were carried out under liquid neon conditions similar to the operation temperature of an MW-class rotating machine. In conclusion, it was confirmed that the alumina powder mixed with epoxy resin in an appropriate ratio is an effective solution of de-lamination problem of 2G HTS coil.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.346-356
• /
• 1998

The purpose of this study was to evaluate the sealing ability of various canal filling methods. Palatal roots of ninety extracted human maxillary molar teeth were resected at cementoenamel junction. Eighty of them were randomly assigned to four experimental groups, ten were served as positive and negative controls. All canals were prepared to # 40 using Profile. Experimental groups were obturated by lateral condensation technique, Thermafil technique, Continuous Wave of Condensation Technique, and down-pack & back-fill technique of Obtura-II, each with root canal sealer. Control groups were not obturated. Teeth were immersed in resorcinol-formaldehyde resin for 5 days at $4^{\circ}C$, and the resin was allowed to polymerize completely for 4 days at room temperature. Teeth were then ground horizontally at 1.5mm(level 1), 2.5mm(level 2), 3.5 mm(level 3) from the anatomical apex and examined with a stereomicroscope at ${\times}40$ magnification. The gap between the canal wall and the filling material, which was filled with the resin, was measured at each of the three levels. Each ratio of leakage was obtained by calculating the ratio of the area of the resin to the total area of the canal and was analyzed statistically (Rank-sum test). The results were as follows : 1. At the level 1, there was the greatest leakage in the Thermafil group and Obtura-II group, and the difference between the Obtura-II group and Continuous Wave of Condensation Technique group was statistically significant(p<0.05). 2. At the level 2, there was the least leakage in the Continuous Wave of Condensation Technique group, but there was no statistically significant difference between each group (p>0.05). 3. At the level 3, there was no statistically significant difference between each group(p>0.05).

• Composites Research
• /
• v.24 no.2
• /
• pp.30-37
• /
• 2011

Analysis of wettability between epoxy resin and glass fabric was studied. The mixing ratios of epoxy resin and anhydride hardener were varied as 1:0.5, l:l and l:1.2. Catalyst content was fixed as 0.1wt% of the mixed resin. A curing analysis by differential scanning calorimeter(DSC) showed a possible impregnation of the mixed resin at the room temperature. An effective contact angle of the mixed epoxy resin drop onto the glass fabric being preset on a flat glass plate was measured as a function of time. The wet area of the epoxy resin drop was also measured. Behaviors of the contact angle, the droplet height, the neat wet area and the coefficient of wettability were used to evaluate the wettability of the epoxy resin onto the glass fabric. It was concluded that the equivalent ratio of 1: 1.2 was the most suitable for the wettability.