In this study, a series of fatigue tests are carried out in order to estimate quantitatively the characteristics of fatigue crack growth rate for high strength steels of SM570, POSTEN60, and POSTEN80 steel, that is, the influence on fatigue crack growth rate according to the welding line, the characteristics of fatigue crack growth according to the welding method and the kinds of steel, and the characteristics of fatigue crack growth for base metal, heat affected zone and weld metal. From the test results, in case that the notch if parallel to welding line, it knows that the retardations of fatigue crack growth rate in crack tip at early stage increase remarkably than in case that the notch is perpendicular to welding line due to compressive residual stress. And the characteristics of fatigue crack growth rate according to welding method are that the dispersion of fatigue crack growth rate in case of FCAW method is smaller than that of SAW method. Also, it knows that the fatigue crack growth rate converges in high stress intensity factor range.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.6 no.2
• /
• pp.34-40
• /
• 2007

Antifatigue failure technology take an important part of current industries. Currently, the shot peening is used for removing the defect from the surface of steel and improving the fatigue strength on surface. Therefore, this paper the effect of compressive residual stress and corrosion of spring steel(SAE 5155)by shot-peening on fatigue crack growth characteristics in stress ratio(R=0.05)was investigated with considering fracture mechanics. By using the methods mentioned above, We arrived at the following conclusions. The fatigue crack growth rate(da/dN) of the shot-peening material was lower than that of the un-peening material. And in stage I, ${\Delta}Kth$, the threshold stress intensity factor, of the shot-peen processed material is high in critical parts unlike the un-peening material. Also m, fatigue crack growth exponent and number of cycle of the shot-peening material was higher than that of the un-peening material. That is concluded from effect of da/dN. Finally fracture of shot-peening material and un-peening material was identified and discussed in this study.

• Journal of Welding and Joining
• /
• v.15 no.4
• /
• pp.70-77
• /
• 1997

Welding is one of the most important and popular joining techniques employed in structures. In spite of, weld designs depend on the rules and regulations. Moreover, the study to optimize a shape of welding joint not may be sufficient and systematic on the theoretical and experimental sides. Therefore, in this study, a computer program based on thermal elasto plastic theory is developed for optimizing(minimizing) shape of weld joints. By the results, study is made on the characteristics of the distributions of welding residual stresses and plastic strains, and their production mechanisms. Also, Various kinds of tests are carried out to find out mechanical characteristics due to shape of weld joints. As a result of this optimization(minimization) of weld joints, the productivity and the reliability will be improved.

• Proceedings of the KIEE Conference
• /
• 1997.11a
• /
• pp.612-614
• /
• 1997

Silicon based micro mirror array is a highly efficient component for use in optical applications such as adaptive optical systems and optical correlators. A micro mirror array designed, fabricated and tested here is consisted of $5{\times}5$ single layer polysilicon, electrostatically driven actuators. In this paper, deflection characteristics and pull-in behavior of the actuators for analog control was studied and particularly, the influence of the residual stress in flexure beams for the restorative force of actuators was considered. The springs are modeled as a residual stress-free spring and a spring with residual stress. In calculation, a mirror with the residual stress-free springs has 30.3N/m spring constant and 31.1V pull-in voltage. On the other hand, a mirror with the stressed springs has 23.6N/m and 27.4V respectively. The experimental result, which is 20.5N/m and 25.5V, shows that the stressed springs ore well modeled.

• Journal of Ocean Engineering and Technology
• /
• v.21 no.1 s.74
• /
• pp.64-68
• /
• 2007

Recently, there has been considerable research in the field of application of Laser-Arc hybrid welding for superstructures, such as ship-structures, transport vehicles etc. However, the study on heat distribution and welding residual stress of hybrid weld by numerical simulation leaves much to be desired. Therefore, in this study, an optimized welding condition and numerical simulation for hybrid welding, using previous numerical analysis to calculate the heat source for hybrid welding, has been analyzed. For this purpose, fundamental welding phenomena of the hybrid process, using Laser and, is investigated. In order to calculate temperature and residual stress distribution in hybrid welds, a finite element heat source model is developed on the basis of experimental results and characteristics of temperature. Residual stress distribution in hybrid welds are understood from the result of simulation, and compared with the experimental values.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.319-324
• /
• 2004

In this study, the high strength and superior toughness spring steels as the suspension material, used for automobile and railroad industries were utilized to carry out the following investigations. Corrosion times were controlled in 7, 14, 30 and 60days to examine the relation between corrosion pit and compressive residual stress in the static corrosion environment after shot peened. And then corrosion current and corrosion potential were measured for every 24 hours to investigate the corrosion mechanism. Shot peened material shows the low or rate of corrosion current as compared with unpeened material. In case of peened material which has the highest residual stress, it has a low corrosion current density.

• Journal of the Korean Society of Safety
• /
• v.18 no.1
• /
• pp.1-7
• /
• 2003

The objective of this paper was to investigate the welding characteristics according to the restraint condition. the pass number, and the shield gas quantity with titanium commonly using in power stations, aircrafts, ships, and so forth. The residual stress distribution was measured under restraint and nonrestraint welding conditions. The tensile strength and elongation of the 4 pass welded specimen were shown higher about 10% and 30% than those of the 7 pass welded specimen at the same welding conditions respectably. Also, the more shield gas quantity and the shorter natural cooling time, the higher tensile strength and the lower elongation.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.8 no.1
• /
• pp.142-149
• /
• 1999

A machine frame has been manufactured by casting. However, due to the development of the industrial society, 3-D duties was refused. Especially, the declination of the casting industry makes it difficult to produce the frame. Many companies still manufacture the small casting products. The large casting products are extremely limited and manufactured for their own use. Therefore, it is difficult to keep the term of order. In this study, the characteristics of steel structure which is produced by welding were identified in the view of mechanical strength of steel structure which is produced by welding were identified in the view of mechanical strength to substitute steel structure for casting frame. But welding structure has the residual stress, HAZ and welding deformation. Residual stress and HAZ especially cause crack growth. The proposed steel structure, based on the simulation and experiment(tensile curve and S-N curve), can reduce not only the producting term but also the weight of the frame.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.1
• /
• pp.21-26
• /
• 1993

A study on the fatigue fracture at electro discharge machined(E.D.M) surface has been made with special emphases on the microstructure variation and the residual stress distribution at the E.D.H heat affected zone. Results obtained are summarized as follows. (1) E.D.M brings about a variation of microstructure in heat affected zone, structures of molten, quenching, tempering are formed in order of formation from E.D.M surface. (2) Residual stress generated by E.D.M reduces the fatigue strength of the material through the influencing fatigue crack initiation and growth. (3) Magnitude of the residual stress existed in a microscopic area is approximately estimated by a COD measurement method which was originally suggested by authors.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.11a
• /
• pp.959-963
• /
• 1996

Hardened layer and compressive residual stress created by carburized treatment effect on bending fatigue strength of gear massively. Also, shot peening treatment improves the strength of carburized gear as it does the hardness and residual stress of surface layer. In these days shot peening techniques are welcomed as one of physical improvement ways around the surface of materials. It is used widely because qualitative analysis of shot peening has become possible and surface treatment can be done with very little costs compared to other surface improvement methods. Therefore this study investigates the effect of shot peening in surface shape and bending fatigue strength after doing many kinds of shot peening treatments, then doing fatigue test and also explained characteristics of shot peening gear.