• Transactions of the Korean Society of Automotive Engineers
• /
• v.22 no.2
• /
• pp.141-147
• /
• 2014

This study aims to investigate the influence of bevel angles on the fatigue life of V-groove butt-welded joints with back-plates made by SM490A steel material, generally used for excavators, because changes in the geometry, material and surface properties of welded regions affect the fatigue life of welded structures. Butt type test specimens were prepared by the $CO_2$ welding of rolled steel plates (SM50A steel) with a thickness of 13.5 mm at a welding speed of 30 cm/min and these Butt type test specimens had two different groove angles, which are $40^{\circ}$ (A type) and $30^{\circ}$ (B type). In order to investigate differences in fatigue life between two types, 4-point bending fatigue tests were conducted with a stress ratio of R=0.1 under the cyclic loading environment at a frequency of 5 Hz at room temperature. The fatigue life of A type specimens was approximately 7% higher than that of B type specimens. The stress concentration factors calculated by finite element analysis were 2.16 for A type and 2.25 for B type, whose difference was caused by the influence of the back-plates of butt-welded structures. The current results could provide important guidelines to determine the V-groove angle of butt-welded joints with a satisfactory fatigue life, although under severe operating conditions.

• Journal of the Korean Institute of Gas
• /
• v.7 no.2 s.19
• /
• pp.22-32
• /
• 2003

Al-brass material is generally used at the state of plastic deformation, for example; bending, extension of bell mouth at shell and tube type heat exchanger. And SCC(stress corrosion cracking) of Al-brass material will be affected by residual stress as plastic deformation. SCC results from synergism between mechanical factor and corrosion environment. Mechanical factor is stress that directly relates with stress intensity factor at the crack tip. This paper was studied on the effect of stress on SCC of Al-brass tube under in $3.5\%$ NaCl. + $0.1\%\;NH_4OH$ solution by constant displacement tester. Increasing of acidified water flow into sea and speeds up corrosion rate of Al-brass which is used as a tube material of vessel heat exchanger by polluted coast seawater. The experimental results are as follow The latent time of SCC occurrence gets longer as the initial stress intensity factor($K_{Ii}$) gets lower The main crack was propagated as the initial stress intensity factor($K_{Ii}$) gets higher, and secondary cracks occurred by electro-chemical factor a(ter stage of released stress. Dezincification phase showed around the crack, and the range of dezincification gets wider as the initial stress intensity factor($K_{Ii}$) gets higher.

• Journal of Korean Society of Steel Construction
• /
• v.15 no.3
• /
• pp.299-311
• /
• 2003

This paper presents a finite element procedure to estimate the ultimate strength of space frames considering spread of plasticity. The improved displacement field is introduced based on the inclusion of second-order terms of finite rotations. All the non-linear terms due to bending moment, torsional moment, and axial force are precisely considered. The concept of plastic hinges is introduced and the incremental load/displacement method is applied for elasto-plastic analyses. The initial yield surface is defined based on the residual stress, and the full plastification surface is considered under the combined action of axial forces, bending and torsional moments. The elasto-plastic stiffness matrices are derived using the flow rule and the normality condition of the limit function. Finite element solutions for the ultimate strength of space frames are compared with available solutions and experimental results.

• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.3
• /
• pp.166-177
• /
• 1993

Bending fatigue strength tests were made for VC coated die steels which were coated by immersing in a molten borax bath and for hardened die steels which were quenched and tempered, in order to clarify the effect of VC coating at $1000^{\circ}C$ and $1025^{\circ}C$. The material used in this investigation was a representative cold and hot die steels STD11, STD61. The results obtained are as follows. 1) The endurance limit of VC coated die steels was a little lower than that of hardened die steels. It is considered to be mainly due to the decfl.lase of hardness in the substrates. Accordingly, the endurance limit reo covered almost to the level of hardened die steels by an additional diffusion treatment. 2) The initiation point of fatigue fracture of VC coated die steels in reversed bening was on the substrate just under the VC layer. Hence, the endurance limit is corrected to the hardness of this part. 3) But, there is a considerable scatter in this relationship and the endurance limit of VC coated die steels was a little lower than that of hardened die steels with equal hardness. These results suggest that the fatigue strength of VC coated die steels is determined not only by the hardness but also by other factors. For example. the residual stress in the substrate just under VC coating layer is one of the factors besides hardness which is mainly related to the retained austenite(${\gamma}_R$).

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.96-101
• /
• 2004

Conventionally, SMAW process was applied to join pipes of RCL, which caused lot of loss in time and cost due to excessive heat input and defects in joining section. Recently, narrow-gap welding(NGW) process was introduced to overcome the disadvantages of SMAW. However, the application of NGW to nuclear power plant is not yet common because safety of NGW process is not proven. In present paper, the welded coupons are made of carbon steel. They are manufactured under different processes; general welding(GW), post-weld heat treatment(PWHT) after GW, repair welding after GW and PWHT with repair welding after GW in carbon steel. Performed are various mechanical tests investigation of microstructure, hardness test, tensile test at room and high temperature, bending test, impact test and J-R test. It is verified that the mechanical properties of carbon steel are greatly changed after repair welding process due to applied heat flux, and that the effect of PWHT is beneficial.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.12
• /
• pp.153-159
• /
• 1997

A thermally-driven polysilicon microactuator has been fabricated using surface micromachining techniques. It consists of P-doped polysilicon as a structural layer and TEOS(tetraethylorthosilicate) oxide as a sacrificial layer. The polysilicon was annealed for the relaxation of residual stress which is the main cause to its deformation such as bending and buckling. And newly developed HF GPE(gas-phase etching) process was also employed to eliminate the troublesome stiction problem using anhydrous HF gas and CH$_{3}$OH vapor, and successfully fabricated the microactuators. The actuation is incurred by the thermal expansion due to the current flow in the active polysilicon cantilever, which motion is amplified by lever mechanism. The moving distance of polysilicon microactuator was experimentally conformed as large as 21 .mu. m at the input voltage level of 10V and 50Hz square wave. The actuating characteris- tics are also compared with the simulalted results considering heat transfer and thermal expansion in the polysilicon layer. This microactuator technology can be utilized for the fabrication of MEMS (microelectromechanical system) such as microrelay, which requires large displacement or contact force but relatively slow response.

• Journal of Korean Society of Steel Construction
• /
• v.21 no.5
• /
• pp.483-492
• /
• 2009

In this study, nonlinear analysis of steel plane frame was performed using the refined plastic hinge method of advanced analysis techniques. In deterioration of stiffness in plastic zone, influences by flexural bending, residual stress, geometrical non-linearity, and semi-rigid connection are considered. And also, further reduced tangent modulus was used for geometrical non-linearity, top and seat angle were chosen for semi-rigid connection. Furthermore, 3 parameter power model was used for moment-rotation behaviour of beam to column connection. The loading conditions are combined with axial and lateral force and the inverse triangle distribution of lateral and eight type of analytical models were used in analysis. The results of analyses were compared with semi-rigid and rigid connection on behaviour of numerical analysis models. And also, the behaviors of frame with changes of semi-rigidity were analyzed by using the results obtained from MIIDAS-GENw.

• Structural Engineering and Mechanics
• /
• v.76 no.2
• /
• pp.175-191
• /
• 2020

In this study, the effect of Nano silica (SiO2) on the buckling strength of the glass fiber reinforced laminates containing the machining process causes holes were investigated. The tests have been applied on two status milled and non-milled. To promote the mechanical behavior of the fiber-reinforced glass epoxy-based composites, Nano sio2 was added to the matrix to improve and gradation. Nano sio2 is chosen because of flexibility and high mechanical features; the effect of Nanoparticles on surface serenity has been studied. Thus the effect of Nanoparticles on crack growth and machining process and delamination caused by machining has been studied. We can also imply that many machining factors are essential: feed rate, thrust force, and spindle speed. Also, feed rate and spindle speed were studied in constant values, that the thrust forces were studied as the main factor caused residual stress. Moreover, entrance forces were measured by local calibrated load cells on machining devices. The results showed that the buckling load of milled laminates had been increased by about 50% with adding 2 wt% of silica in comparison with the neat damaged laminates while adding more contents caused adverse effects. Also, with a comparison of two milling tools, the cylindrical radius-end tool had less destructive effects on specimens.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.04a
• /
• pp.146-150
• /
• 1996

A thermal micro actualtor has been fabricated using surface micromachining techniques. It consists of doped ploysilicon as a moving part and TEOS(Tetra Ethyl Ortho Silicate) as a sacrificial layer. The polysilicon was annealed for the reduction of residual stress which is the main cause to its deformation such as bending and buckling. And the newly developed HF VPE(vapor phase etching)process was also used as an effective release method for the elimination of sacrificaial layer. With noliquid involved during any of the steps for relasing, unlike other reported relase techniques, the HF VPE pocess has produced polysilicon microstructures with virtually no process-induced stiction problem. The actuation is incured by the thermal expasion due to current flow in active polysilicon cantilever, which motion is amplified bylever mechanism. The thickness of pllysilicon is 2 .mu. m and the length of active and passive polysilicon cantilever are 500 .mu. m, respectively. The moving distance of polysilicon actuator was experimentally conformed as large as 21 .mu. m at the input voltage level of 10 V and 50Hz square wave. These micro actuator technology can be utilized for the fabrication of MEMS (microlectromechanical system) such as microrelay, which requires large displacement or contact force but relatively slow response.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.3
• /
• pp.190-195
• /
• 2009

All the failure in fatigue of torsion, bending and rolling contact, and in sliding wear begins mostly from surface. So much efforts have been invested to the surface technology which deal these problems during past decades, but the industrial demand keeps growing and more significant requirements are added to researchers and engineers. Nano crystal surface modification technology which makes the surface layers into nano crystalline, induces big and deep compressive residual stress, increases surface hardness, improves surface hardness, and make micro dimples structure on surface is an emerging technology which can break limits of current surface technology and relieve the burden of researchers and engineers. In this study, a nano crystal surface modification technology which is calling UNSM(Ultrasonic nano crystal surface modification) technology, is introduced and how it has been applied to industry to solve these failure problems is explained.