• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 봄 학술논문 발표대회
• /
• pp.67-68
• /
• 2023

After mixing the pozzolan-based powder and water repellent with porosity into the cement mortar, microanalysis and measurement of the water repellent contact angle confirmed that the NZS specimen using natural zeolite had the highest contact angle. The specific surface area is increased due to the porosity of natural zeolite, so the adhesion of silane-siloxane is relatively better than that of FA, and it is judged to have a uniform distribution inside the mortar.

• 한국의류산업학회지
• /
• 제14권4호
• /
• pp.641-647
• /
• 2012

This study investigates the sound properties of fabric frictional sound (SPL, ${\Delta}L$, ${\Delta}f$) according to the film type of PTFE laminated vapor-permeable water-repellent fabrics in order to understand the relationship between SPL and the basic properties of fabrics such as layer, yarn type, and thickness of fiber. This study accesses their mechanical properties and determines how to control them to minimize SPL. Eight PTFE laminated water-repellent fabrics, composed of four different film types (A, B, C, D) and with two different fabrics, were used as test specimens. Frictional sounds generated at 1.21m/s were recorded by using a fabric sound generator and SPLs were analyzed through Fast Fourier Transformation (FFT). The mechanical properties of fabrics were measured by KES-FB. The SPL value was lowest at 74.4dB in film type A and highest as 85.5dB in type D. Based on ANOVA and post-hoc test, specimens were classified into less Loud Group (A, B) and Loud Group (C, D). It was shown that SPL was lower when 2 layer (instead of 3 layer), filament yarn than staple, and thin fiber than thick were used. In Group I, shearing properties (G, 2HG5), geometrical roughness (SMD), compressional properties (LC, RC) and weight (W) showed high correlation with SPL however, elongation (EM) and shear stiffness (G) did with SPL in Group II.

• 임산에너지
• /
• 제21권2호
• /
• pp.34-42
• /
• 2002

천연물계의 유지를 목재에 처리하여 발수성능을 평가하였다. 시험에 사용한 유지는 아마인유, 피마자유, 올리브유, 콩기름, 들기름, 해바라기 씨 기름이다. 발수성 평가는 흡습성, 흡수성 시험과 접촉각 시험으로 하였다. 발수 처리한 목재를 빛과 수분에 의해 촉진열화 시킨 후에 열화정도를 색차계로 측정하였다. 촉진열화된 처리목재의 발수성능을 흡수성시험과 접촉각 시험을 통하여 비교 측정 하였다. 흡습성 시험결과, 흡습 초기에는 무처리에비하여 흡습량이 적으나 흡습처리 시간이 증가할수록 무처리의 흡습량에 가까워져 48시간 흡습처리 후에는 흡습비의 큰 차이는 없었다. 접촉각 시험의 결과, 처리재와 무처리재간의 결과가 큰 차이를 나타내었다. 유지의 농도와 종류에 따른 접촉각 변화는 흡습성 시험과 같이 큰 차이는 나타나지 않았다. 천연유지의 발수성능으로는 기상열화에 대한 안정성이 낮았다. 천연오일 단독처리만으로는 광열화에 대한 안정성을 기대하기 어려웠다.

• 한국건축시공학회지
• /
• 제15권6호
• /
• pp.607-614
• /
• 2015

일반적으로 건축물의 마감은 기본적인 발수성을 가진 수성페인트 마감으로 이루어진다. 이는 건축물 외벽에 작업시 적용하기 쉬우며, 건축물 유지 또한 쉬워 많은 장점을 가지고 있다. 하지만 자외선으로 인해 변색 또는 열화 되기 쉬워 그 효과는 기대에 미치지 못하고 있다. 따라서 본 연구는 외부 표면마감 재료로서 발수제를 직접 혼입한 수성페인트의 색 변화를 통한 내구성능을 분석하여 실제 현장에 적용하기 위한 실용성을 평가하고자 하였다. 촉진 시간에 따른 색 변화 및 색차를 측정하였으며, 적용가능성은 실험결과를 토대로 평가하였다. 색차, 명도 및 색도의 변화량을 실험결과에 따라 종합적으로 고려해 볼 때 본 연구에서 제안한 발수제를 혼입한 수성페인트 마감공법(혼입율 2, 5, 8%)은 충분히 사용 가능할 것으로 사료된다. 이는 건축물의 외부 표면을 수성페인트로 칠한 후 추가로 발수제를 도포하는 등의 기존 표면 마감방법에 비해 공사내용이 간편하며 시공성도 양호하여 폭넓은 활용이 기대된다. 또한 실제 현장에서는 원하는 색상으로 필요한 양만큼 제조하여 사용할 수 있으며, 전문 인력이 필요하지 않아 손쉽게 활용 가능할 것으로 기대된다.

• 한국염색가공학회지
• /
• 제11권6호
• /
• pp.24-35
• /
• 1999

This study was carried out to investigate the changes of surface characteristics of polyester fabrics on the deposition and the removal of oily soils from polyester fabrics in detergency, The relations between the removal of soil and the changes of surface properties of polyester fabrics treated with water- and oil-repellent agents were discussed before and after various wash cycles. Two kinds of fluoropolymers were selected as water-and oil-repellent finishing agents. The effects of water- and oil-repellent finishes were determined by the water repellency and oil repellency. The surface properties of untreated and treated polyester fabrics were evaluated with respect to contact angle and wicking time. The treatment of polyester fabrics with fluoropolymers improved efficiently water repellency, oil repellency, contact angle and wicking time. But those properties were greatly decreased after 3 times of wash cycles in detergency The deposition of oily soils on the untreated fabrics was drastically increased with increasing of wash cycles. The deposition and the removal of oily soils from fabrics treated with fluoropolymer having hydrophobic components were very low after various wash cycles. The deposition and the removal of oily soils on the fabrics treated with fluoropolymer having hydrophilic components were high comparatively after various wash cycles. Even though the surface properties of treated fabrics were greatly decreased with the increasing of wash cycles, the remains of oily soils on the fabrics were lower than those of untreated fabrics in various wash cycles. But the remains of soils were drastically increased after 10 times of wash cycles in any cases.

• 한국유기농업학회지
• /
• 제26권2호
• /
• pp.259-268
• /
• 2018

The study investigated the efficacy of four different essential oils on the repellent responses of large black chafer (Holotrichia parallela) Motschulsky (Coleoptera: Scarabaeidae) in organic pear (Pyrus pyrifolia) orchards. Cinnamon, pine, peppermint, and eucalyptus oils were used, and the behavioral responses and repellent effects against H. parallela were investigated under laboratory and field conditions. Adult beetle responses to different oils were examined using a Y-tube olfactometer in the laboratory and four absorbent blocks with each oil in the field. The repellent responses rates of H. parallela were 100% for cinnamon oil; however, only 67% of adult beetles avoided peppermint and eucalyptus oil in the Y-tube olfactometer bioassay. In the field tests, the least damage to leaves was observed on trees treated with cinnamon oil, whereas the most damage was observed in the control (non-treated) trees and those treated with peppermint oil, followed by eucalyptus and pine oil. Therefore, cinnamon oil can be used as a repellent to avoid damage form large black chafers in organic pear orchards.

• Korean Chemical Engineering Research
• /
• 제56권3호
• /
• pp.327-334
• /
• 2018

출발물질로서 테트라에톡시실란(TEOS)과 메틸트리메톡시실란(MTMS)을 사용하여 졸-겔법에 의해 발수성 코팅용액을 제조하였다. 이 용액을 냉연강판 위에 스핀 코팅하고 열처리하여 비불소계 발수 코팅 도막을 제조 하였다. 이 과정 중 MTMS/TEOS의 몰 비, 물 농도 및 암모니아 농도가 코팅 도막의 발수성에 미치는 영향을 연구하였다. MTMS/TEOS의 몰 비를 1~20으로 변화시켜 제조 한 코팅 도막의 접촉각은 MTMS/TEOS 몰 비가 10 일 때 최대 수치인 $108^{\circ}$를 나타내었다. 반면에 물의 첨가량을 증가시킴에 따라 코팅 도막의 접촉각이 증가하여 발수성이 향상되었다. 또한 암모니아의 첨가량이 커질수록실리카입자의 크기가커져 실리카입자의표면 거칠기가증가하므로 발수성이 증가하였다.

• 한국안광학회지
• /
• 제19권1호
• /
• pp.1-8
• /
• 2014

목적: 플라스틱 렌즈의 온도에 의한 영향을 조사하고자 열 충격을 주어 렌즈 재질과 코팅의 변화를 살펴보았다. 방법: 본 연구에서는 굴절률이 다른 3 가지의 렌즈(2 종류의 thiourethane계열 렌즈, 한 종류의 allyl diglycol carbonate, ADC 렌즈)를 5 시간 동안 고온(50, 80, 그리고 $100^{\circ}C$)에 노출시켰을 때 각각의 코팅(반사방지코팅, 하드 코팅, 그리고 수막방지코팅)의 변화를 측정하였다. 결과: 그 결과 고굴절률 렌즈들에서는 경도의 변화가 미미하였으나 중굴절률 렌즈는 고온의 열에 노출될수록 경도가 점차 감소하여 하드코팅이 손상됨을 확인하였다. 모든 렌즈의 광투과율이 $80^{\circ}C$ 이상의 열 충격 시 큰 감소가 나타나 멀티코팅 층이 파괴됨을 유추할 수 있었다. 렌즈에 열 충격이 가해질수록 표면 접촉각이 작아져 $80^{\circ}C$ 이상 가열 시 수막발수코팅이 손상되기 시작함을 보였다. 결론: 굴절률이 다른 3가지 렌즈 모두에서 $80^{\circ}C$ 이상의 열 충격을 받았을 때 발수코팅을 포함한 멀티코팅이 손상되었고 고분자 재료 소재에 따라 기계적, 물리적 특성 변화정도가 다르게 나타났다.

• 한국의류학회지
• /
• 제17권4호
• /
• pp.577-586
• /
• 1993

Pesticide protective clothing has not been frequently worn due to its lack of thermal comfort. It is important to develop fabrics which can allow the wearer to work in comfort. One of the possible way to achieve the goal is to produce fabrics with a water- and oil-repellent finish which would resist pesticide penetration but maintain some breathability. The purpose of this study were to evaluate the pesticide barrier properties of untreated and water- and oil-repellent finished nonwoven fabrics. Three types of nonwoven fabrics(Tyvek, Sontara and Kimlon) were used as test specimens. By pad-dry-cure method, each of the specimen was treated with fluorocarbon. The pesticide barrier properties (amount of pesticide penetration and residue) were measured by the gas chromatography. The performance properties of untreated and treated specimens were evaluated with respects to water pepellency(KS K 0590), oil repellency(AATCC 118), water resistance(KS K 0591, AATCC 42), water vapor transmission (KS A 1013) and air permeability(KS K 0570). The results of this study were as follows : 1) The untreated Sontara showed much more amount of pesticide penetration than untreated Tyvek and Kimlon, while the treated Sontara showed little amount of pesticide penetration. 2) After laundering, the amount of pesticide residue in the untreated and treated Sontara was less than that in Tyvek and in Kimlon. 3) Water- and oil-repellent finish improved water repellency, oil repellency, and water resistance of specimens. 4) The untreated Sontara and Kimlon showed higher water vapor transmission and air permeability than untreated Tyvek. Water vapor transmission and air permeability of treated specimen decreased compared to those of untreated.

• 한국염색가공학회지
• /
• 제6권3호
• /
• pp.27-36
• /
• 1994

In order to produce a water repellent surface on polyester fabric, samples were treated in the atmosphere of $CF_4$ glow discharge plasma. The samples used in the study were ployester fabric and poyester film. The purpose of film treatment is for the comparison of hydrophobicity with fabric sample at same treatment condition. Radio frequency(13.56MHz) generator was used as electric source and its in put power is 100 Watt. Water repellency was evaluated by contact angle measurement. Result obtained are as follows. 1) Fiber interstice of original fabric was ana lysed as 0.43$\mu$m, and this value was sufficiently ideal for making water repellent fabric. 2) The most favorable setting position of substrate was the center area between two electrodes. 3) Fabric contact angle was higher than film contact angle at same treatment condition, and its difference was more than 50${\circ}$. And it was incapalbe of fabric contact angle measurement when the film contact angle was less than 90${\circ}$. because the fabric is susceptible to absorption of water by the capillary effect. 4) Fabric contact angle can not revealed the precise defferences of surface hydrophobicity, however, the film contact angle showed the real hydrophobic nature. 5) It was not sufficient method to evaluate the hydrophobicity of fabric surface by merely measure of the water contact angle. 6) It showed high water repellent nature at 0.06 torr of $CF_4$ plasma gas pressure and duration of 45 seconds treatment, and it can not be anticipated more improved nature if the pressure and duration of treatment time were increased.