• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.61-64
• /
• 2008

Reinforced Concrete structures are constructed under the basic assumption of perfect bonding between steel and concrete. The corrosion of steel in the reinforced concrete columns results in the excessive cracks and gradual deterioration of concrete between steel and concrete. The cyclic loading test was conducted with the three corrosion rates in the laboratory. Throughout this test, it is investigated a bond behavior of reinforced concrete columns under a steel corrosion. Main variables of the test are a corrosion of steel reinforcement and a level of stress.

• Advances in concrete construction
• /
• v.8 no.4
• /
• pp.247-255
• /
• 2019

Several reinforced concrete structures that get deteriorated by rebar corrosion are retrofitted using Carbon Fiber Reinforced Polymer (CFRP). When rebar comes in direct contact with CFRP, rebar may corrode, as iron is more active than carbon. Progression of corrosion of rebar in strengthened RC structures has been carried out when rebar comes in direct contact with CFRP. The experimentation is carried out in two phases. In phase I, corrosion of bare steel bar is monitored by making its contact with CFRP. In phase II, concrete specimens with surface bonded CFRP were casted and subjected to the realistic exposure conditions keeping direct contact between rebar and CFRP. Progression of corrosion has been monitored by various parameters: Half-cell potential, Tafel extrapolation and Linear Polarisation Resistance. On termination of exposure, to find residual bond stress between rebar and concrete, pull-out test was performed. Rebar in contact with CFRP has shown substantially higher corrosion. The level of corrosion will be more with more area of contact.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.257-262
• /
• 1997

Reinforced concrete structures built on the seashore or in seawater are damaged from saltwater which cause to accelerate corrosion of reinforcing steel in concrete. Therefore, Corrosion of steel reinforcement of concrete structures become more and more serious, and prediction of service lives of concrete structures considering steel corrosion is needed much more. this research is to investigate basic physical properties of various corrosion inhibitors and to evaluate their corrosion resistance in concrete. The object of this study is develop appropriate corrosion protection systems so as to enhance the durability of concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04b
• /
• pp.633-636
• /
• 1998

This study is performed for the purpose of obtaining the fundamental datum to analyse the cause of steel corrosion in concrete and establish the repair strategies of deteriorated reinforced concrete structures due to steel corrosion. To investigate the degree of concrete deterioration, soluble chloride content in harden concrete, the depth of carbonation, cover depth and compressive strength are measured. The progress of corrosion of concrete bridge is electrochemically evaluated. The result shows that in approximately 43% of the structures below -350mV(vs. CSE), the exessive chloride contents is a direct cause of steel corrosion in reinforced concrete structures.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.5 no.1
• /
• pp.188-194
• /
• 2001

A reinforced concrete structure is complex structure that works as one body with bonding role of steel bar and concrete. The bonding action between steel bar and concrete makes possible the compound structure. The transmission of mutual strength of the steel bar with concrete in structure is determined by the bonding characteristic of steel bar and concrete surface. But the efficiency of bonding characteristic of steel bar is Questionable by the corrosion cause by the delay construction term, the wrong management, etc. So this study investigate bonding characteristic of reinforced concrete using pull-out test method which steel bar removed rust and the principal variables of this study are concrete compression strength and the degree of corrosion. The result showed that bonding strength tend to increase when removed rust of steel bar whereas it tend to decrease when not removed rust.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.755-758
• /
• 1999

Reinforced concrete is in general known as high durability construction material under normal environments due to strong alkalinity of cement. Marine and harbour concrete in the tidal and the splash zone at seashore are exposed to cyclic wet and dry saltwaters which cause to accelerate corrosion of reinforcing steel in concrete. If corrosion resistance of concrete gets to weaken due to carbonations and cracks in cover concrete, furthermore, concrete durability rapidly decreases by corrosion of reinforcement steel embedded in concrete. The objective of this study is to develop appropriate corrosion protection systems so as to enhance the durability of concrete by controlling the cover depth of concrete and by using corrosion inhibitors as concrete admixtures.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.821-826
• /
• 2000

Reinforced concrete is in general known as high durability construction material under normal environments due to strong alkalinity of cement. Marine concrete specimens in the tidal and the splash zone at seashore have been exposed to cyclic wet and dry saltwaters which cause to accelerate corrosion of reinforcing steel in concrete. If corrosion resistance of concrete gets to weaken de to carbonations and cracks in cover concrete, furthermore, concrete durability rapidly decreases by the corrosion of reinforcement steel embeded in concrete. The objective of this study is to develop appropriate corrosion protection systems of marine concrete so as to enhance the durability of concrete by establishing pertinent cover depth of concrete and by using corrosion inhibitors as concrete admixtures.

• Computers and Concrete
• /
• v.27 no.5
• /
• pp.395-406
• /
• 2021

This study experimentally and analytically investigates the shear behavior of corroded reinforced concrete (RC) beams repaired using steel fiber-reinforced concrete (SFRC) in the flexural zone. The experimental parameters are the corrosion degree (0%, 12%, and 17%) and the steel fiber volume in the SFRC (1.0%, 1.5%, and 2.0%). The test results reveal that corrosion degree significantly affects the shear resistance of the beams. The shear capacity of the beam with the corrosion degree of 17% was higher than that of the uncorroded beam, whereas the shear capacity of the beam with the corrosion degree of 12% was lower than that of the uncorroded beam. The shear efficiency of damaged beams can be recovered by repairing them using SFRC that contains a reasonable amount of steel fibers. In addition, two methods to estimate the shear capacity of the repaired beams are developed using the modified truss analogy and strut-and-tie models. The estimated shear capacity of the beam using the modified truss analogy model agrees well with the experimental data.

• International Journal of Concrete Structures and Materials
• /
• v.5 no.1
• /
• pp.65-73
• /
• 2011

Corrosion of steel bars embedded in concrete admixed with 0%, 2% and 4% calcium nitrite (CN), having compressive strengths of 20 and 46 MPa was investigated. Reinforced concrete specimens were immersed in 3% NaCl solutions for 1, 7 and 15 days where 0.4A external current was applied to accelerate the chemical reactions. Corrosion rate was measured by retrieving electrochemical data via potentiodynamic polarization technique. Pull-out tests of reinforced concrete specimens were then conducted to assess the corroded steel-concrete bond characteristics. Experimental results showed that corrosion rate of steel bars and steel-concrete bond strength were dependent on concrete strength, amount of CN added and accelerated corrosion period. As concrete strength increased from 20 to 46 MPa, corrosion rate of embedded steel decreased. The addition of 2% CN to concrete of 20 MPa was not effective in retarding corrosion of steel at long time of exposure. However, the combination of higher strength concrete and 2% or 4% CN appear to be a desirable approach to reduce the effect of chloride-induced corrosion of steel reinforcement. After 1 day of corrosion acceleration, specimens without CN showed higher bond strength in both concrete mixes than those with CN. After 7 and 15 days of exposure, the higher concentration of CN, the higher bond strength in both concrete mixes achieved, except for the concrete specimen of 20 MPa compressive strength with 2% CN that recorded the highest deterioration in bond strength at 15 days of exposure.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.13 no.6
• /
• pp.557-569
• /
• 2011

Steel Fiber Reinforced Concrete (SFRC) is widely used for tunnel structures such as shotcrete and segments. Corrosion of steel fibers and steel reinforcements may affect on the long-term durability of the concrete structures with steel fibers and reinforcement. Therefore, a study on the feasible method to evaluate corrosion possibility and permeability of the concrete structures is required. This experimental study examines the effect of steel fibers and internal reinforcement on the surface resistivity. Steel fiber mix ratio and corrosion of internal reinforcement were considered as variables. In the results, steel fibers significantly reduce the surface resistivity due to those conductive characteristic. In the case of 3% mix ratio, it was difficult to evaluate rate and permeability of corrosion due to the great reduction of resistivity by mixing of steel fibers.