• Bulletin of the Korean Chemical Society
• /
• v.33 no.8
• /
• pp.2523-2528
• /
• 2012

Green phosphors $(Zn_{1-a-b}M_aM^{\prime}_b)_xGa_yS_{x+3y/2}:Eu^{2+}$ (M, M' = alkali earth ions) with x = 2 and y = 2-5 were prepared, starting from ZnO, MgO, $SrCO_3$, $Ga_2O_3$, $Eu_2O_3$, and S with a flux $NH_4F$ using a conventional solidstate reaction. A phosphor with the composition of $(Zn_{0.6}Sr_{0.3}Mg_{0.1})_2Ga_2S_5:Eu^{2+}$ produced the strongest luminescence at a 460-nm excitation. The observed XRD patterns indicated that the optimized phosphor consisted of two components: zinc thiogallate and zinc sulfide. The characteristic green luminescence of the $ZnS:Eu^{2+}$ component on excitation at 460 nm was attributed to the donor-acceptor ($D_{ZnGa_2S_4}-A_{ZnS}$) recombination in the hybrid boundary. The optimized green phosphor converted 17.9% of the absorbed blue light into luminescence. For the fabrication of light-emitting diode (LED), the optimized phosphor was coated with MgO using magnesium nitrate to overcome their weakness against moisture. The MgO-coated green phosphor was fabricated with a blue GaN LED, and the chromaticity index of the phosphor-cast LED (pc-LED) was investigated as a function of the wt % of the optimized phosphor. White LEDs were fabricated by pasting the optimized green (G) and the red (R) phosphors, and the commercial yellow (Y) phosphor on the blue chips. The three-band pc-WLED resulted in improved color rendering index (CRI) and corrected color temperature (CCT), compared with those of the two-band pc-WLED.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.5
• /
• pp.437-441
• /
• 2006

The red emitting OLEDs using $Alq_3$:Rubrene-GDI4234 phosphors have been fabricated and characterized . In the device fabrication, 2- TNATA [4,4',4' - tris (2- naphthylphenyl - phenylamino ) - tripheny lamine] as the hole injection material and NPB [N,N'-bis (1-naphthyl)-N,N'-diphenyl-1,1'-biphenyl-4,4'-diamine] as the hole transport material were deposited on the ITO(indium tin oxide)/glass substrate by vacuum evaporation. And then, red color emissive layer was deposited using $Alq_3$ as the host material and Rubrene(5,6,11,12-tetraphenylnaphthacene)-GDI4234 as the dopants. finally, small molecule OLEDs with structure of ITO/2-TNATA/NPB/$Alq_3$:Rubrene-GDI4234/$Alq_3$/LiF/Al were obtained by in-situ deposition of $Alq_3$, LiF and Al as the electron transport material, electron injection material and cathode, respectively. Red OLEDs fabricated in our experiments showed the color coordinate of CIE(0.65, 0.35) and the maximum power efficiency of 2.1 lm/W at 7 V with the peak emission wavelength of 632 nm.

• Advances in materials Research
• /
• v.3 no.4
• /
• pp.227-232
• /
• 2014

$Ce^{4+}$, $Eu^{3+}$, $Tb^{3+}$ co-doped $Ca_3Si_3O_8F_2$ phosphor was synthesized via solid state reaction method using $CaF_2$, $CaCO_3$ and $SiO_2$ as raw materials for the host and $Eu_2O_3$, $CeO_2$, and $Tb_4O_7$ as activators. The luminescent properties of the phosphor was analysed by spectrofluorophotometer at room temperature. The effect of excitation wavelengths on the luminescent properties of the phosphor i.e. under near-ultraviolet (nUV) and visible excitations was investigated. The emission peaks of $Ce^{4+}$, $Eu^{3+}$, $Tb^{3+}$ co-doped $Ca_3Si_3O_8F_2$ phosphor lays at 480(blue band), 550(green band) and 611nm (red band) under 380nm excitation wavelength, attributed to the $Ce^{4+}$ ion, $Tb^{3+}$ ion and $Eu^{3+}$ ions respectively. The results reveal that the phosphor emits white light upon nUV (380nm) / visible (465nm) illumination, and a red light upon 395nm / 535nm illumination. RE ions doped $Ca_3Si_3O_8F_2$ is a promising white light phosphor for LEDs. The emission colours can be seen using Commission international de l'eclairage (CIE) co-ordinates. A single host phosphor emitting different colours under different excitations indicates that it is a potential phosphor having applications in many fields.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.177.2-177
• /
• 2003

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.565-570
• /
• 2011

The $Eu^{3+}$ doped $Y(P_x,V_{1-x})O_4$ (0 ${\leq}$ x ${\leq}$ 1) phosphors were synthesized by solid-state and impregnation method and investigated as potential red-emitting phosphors for a plasma display panel(PDP). The optimal substitution proportion of P for V was determined to be 60 mol%, for $Y(P_x,V_{1-x})O_4$ doped with 8 mol% $Eu^{3+}$. The VUV PL spectra and SEM for the synthesized phosphors were measured and compared against those of a commercial red-emission phosphor. The $Y(P_x,V_{1-x})O_4$:$Eu^{3+}$ phosphors exhibited strong red at around 592, 618 and 698 nm. The emission intensity and particle size of the phosphors were controlled by preparation conditions.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.286.1-286.1
• /
• 2013

Nowadays, the glare towards the light-emitting diode (LED) lighting source has much attention due to its eco-friendly nature, reduced energy consumption, and low CO2 emission. LEDs can show versatile colors by changing the composition ratio of semiconductors. Phosphors re-emit light by absorbing light from LED, which is the key factor for emission. The endeavor to make replica of natural white light is increasing day by day. Industrially, blue LED chip crowned with a yellow phosphor coated lens gives low quality white light. Newly, many researchers are introducing modern approaches, adding red phosphor to the yellow phosphor to increase the quality of white light. Here, we synthesized structurally and chemically stable europium doped oxyapatite Ca8Gd2(PO4)6O2 nano-crystalline structures by a hydrothermal method. The ultrafine structures were formed due to the effect of ethylenediaminetetraacetic acid, which is confirmed by the transmission electron microscope images. The structural properties were analyzed using the X-ray diffraction patterns.

• Transactions on Electrical and Electronic Materials
• /
• v.15 no.2
• /
• pp.66-68
• /
• 2014

Most commercial white LED lamps use blue chip coated with yellow emitting phosphor. The use of blue excitable red and green phosphors is expected to improve the CRI. Several phosphors, such as $SrGa_2S_4:Eu^{2+}$ and $(Sr,Ba)SiO_4:Eu^{2+}$, have been suggested in the past as green components. However, there are issues of the sensitivity and stability of such phosphors. Here, we describe gallium substituted $YAG:Ce^{3+}$ phosphor, as a green emitter. YAG structures are already accepted by the industry, for their stability and efficiency. LEDs with improved CRI could be fabricated by choosing $Y_3Al_4GaO_{12}:Ce^{3+}$ (green and yellow), and $SrS:Eu^{2+}$ (red) phosphors, along with blue chip. Also, the effect of a slight change in chip wavelength is studied, for two phosphor-coated w-LEDs. The reduction in particle size of the coated phosphors also gives improved w-LED characteristics.

• Journal of Electrical Engineering and Technology
• /
• v.13 no.4
• /
• pp.1673-1681
• /
• 2018

In this paper, the fabrication of a white light-emitting diode (WLED) package capable of producing different color rendering indexes (CRI ($R_a$)) using different types of phosphors (YAG:Ce, Silicate, Nitride, LuAG) for the LEDs is presented. The color quality is evaluated based on the current and temperature variation conditions. The evaluation method for color quality compares the existing CIE 13.3 method and the new IES TM-30-15 method. The CRI ($R_a$) defined in the conventional CIE 13.3 has the disadvantage. This cannot offer any information relevant to the user's preference. However, the newly proposed IES TM-30-15 method suggests the additional measure related to user's preference such as Color Gamut ($R_g$). The present experimental results obtained using the IES TM-30-15 show that the color quality of the WLEDs using green and red phosphors are better than that of the WLEDs using yellow phosphor, but their luminous efficacies are lower. The color quality of WLEDs using green and red phosphors are more stable than that of the WLEDs using yellow phosphor, for current and temperature variations, and it is verified that the phosphor causes this change. The evaluation method for color quality, based on IES TM-30-15, is proved to be capable of overcoming the problems of the existing evaluation methods by this study.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.594-597
• /
• 1999

The new green and red phosphors for PDP application activated by T $b^{3+}$ and E $u^{3+}$ were synthesized, and their photoluminance properties were investigated. It was found that the brightness of $Al_3$Gd $B_4$ $O_{12}$ :T $b^{3+}$ green phosphor under 147nm VUV irradiation was higher than that of commercial Z $n_2$ $SiO_4$:M $n^{2+}$ phosphor. But the emitting intensity of A1$_3$Gd $B_4$ $O^{12}$ :E $u^{3+}$ red phosphor was inferior to the commercial (Y,Gd)B $O_3$:E $u^{3+}$. $Al_3$Gd $B_4$ $O_{12}$ Phosphor had a strong excitation band at 160nm associated with the host absorption, and also the photoluminance excitation intensity of $Al_3$Gd $B_4$ $O_{12}$ :T $b^{3+}$ was higher than that of Z $n_2$ $SiO_4$:M $n^{2+}$, but the intensity of $Al_3$Gd $B_4$ $O_{12}$ :E $u^{3+}$ phosphor was smaller than (Y,Gd)B $O_3$:E $u^{3+}$ phosphor In the VUV range. C $e^{3+}$ co-doping in A1$_3$Gd $B_4$ $O^{12}$ :E $u^{3+}$ and substitution of $Al^{3+}$ by G $a^{3+}$ A1$_3$Gd $B_4$ $O^{12}$ :E $u^{3+}$ phosphor were tried, but they did not improved the optical property .d the optical property .ty .

• Korean Journal of Materials Research
• /
• v.29 no.2
• /
• pp.116-120
• /
• 2019

We prepared $Y_3Al_5O_{12};Ce^{3+},Pr3^{+}$ transparent ceramic phosphor using a solid state reaction method. By XRD pattern analysis and SEM measurement, our phosphors reveal an Ia-3d(230) space group of cubic structure, and the transparent ceramic phosphor has a polycrystal state with some internal cracks and pores. In the Raman scattering measurement with an increasing temperature, lattice vibrations of the transparent ceramic phosphor decrease due to its more perfect crystal structure and symmetry. Thus, low phonon generation is possible at high temperature. Optical properties of the transparent ceramic phosphor have broader excitation spectra due to a large internal reflection. There is a wide emission band from the green to yellow region, and the red color emission between 610 nm and 640 nm is also observed. The red-yellow phosphor optical characteristics enable a high Color Rendering Index (CRI) in combination with blue emitting LED or LD. Due to its good thermal properties of low phonon generation at high temperature and a wide emission range for high CRI characteristics, the transparent ceramic phosphor is shown to be a good candidate for high power solid state white lighting.