• 한국농공학회논문집
• /
• 제51권6호
• /
• pp.97-103
• /
• 2009

This study was performed to evaluate the strength and durability properties of recycled polymer concrete using unsaturated polyester resin and recycled aggregates. Unsaturated polyester resin, natural and recycled aggregates and fly ash were used. The mix proportions were determined to satisfy the requirement for the workability and slump according to aggregate sizes (5-10 and 5-25 mm) and unit binder contents (10% and 12%). Tests for the compressive and flexural strength, freezing and thawing and durability for 20% sulfuric solution were performed. The compressive and flexural strength of recycled polymer concrete were in the range of 85~97 MPa and 17.9~20.8 MPa, respectively. The strengths of recycled polymer concrete using recycled aggregate have similar or slightly decreased compared to polymer concrete using natural aggregate. After 300 cycles of freezing and thawing, weight decrease ratio and durability factor of recycled polymer concrete were in the range of 0.13~1.42% and 94~99, respectively.

• 한국농공학회논문집
• /
• 제58권3호
• /
• pp.21-27
• /
• 2016

This study was performed to evaluate engineering properties of carbon and glass fiber reinforced recycled polymer concrete. Fiber reinforced recycled polymer concrete were used recycled aggregate as coarse aggregate, natural aggregate as fine aggregate, $CaCO_3$ as filler, unsaturated polyester resin as binder, and carbon and glass fiber as fibers. The compressive and flexural strength of carbon fiber reinforced recycled polymer concrete were in the range of 68~81.5 MPa and 19.1~21.5 MPa at the curing 7days. Also, the compressive and flexural strength of glass fiber reinforced recycled polymer concrete were in the range of 69.4~85.1 MPa and 19~20.1 MPa at the curing 7days. Abrasion ratio of carbon and glass fiber reinforced recycled polymer concrete were decreased 21.6 % and 11.6 % by fiber content 0.9 %, respectively. After impact resistance test, drop numbers of initial and final fracture were increased with increase of fiber contents. Accordingly, carbon fiber and glass fiber reinforced recycled polymer concrete will greatly improve the hydraulic structures, underground utilities and agricultural structures.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.316-319
• /
• 2004

Resins using recycled PET offer the possibility of a lower source cost of materials for making useful polymer concrete products. The purposed of this paper is to propose the model for the stress-strain relation of recycled-PET polymer concrete at monotonic uniaxial compression and is to investigate for the stress-strain behavior characteristics of recycled-PET polymer concrete with different variables(strength, resin contents, curing conditions, addition of silane and ages). The maximum stress and strain of recycled-PET polymer concrete was found to increase with an increase in resin content, however, it decreased beyond a particular level of resin content. A ascending and descending branch of stress-strain curve represented more sharply at high temperature curing more than normal temperature curing. In addition, results show that the proposed model accurately predicts the stress-strain relation of recycled-PET polymer concrete.

• 한국농공학회:학술대회논문집
• /
• 한국농공학회 2003년도 학술발표논문집
• /
• pp.411-414
• /
• 2003

This study is performed to examine the physical and mechanical properties of recycled polymer concrete using recycled coarse aggregate and recycled fine aggregate. Tests for compressive strength, flexural strength and pulse velocity with replacement ratio of recycled coarse aggregate and recycled fine aggregate are performed. As a result, compressive strength, flexural strength and pulse velocity of polymer concrete containing recycled coarse aggregate are in the range of $826{\sim}849kgf/cm^2,\;192{\sim}200kgf/cm^2\;and\;3,932{\sim}4,000m/s$, respectively. Compressive strength, flexural strength and pulse velocity of polymer concrete containing crushed stone only are $805kgf/cm^2,\;197kgf/cm^2$ and 3,931 m/s, respectively. Accordingly, recycled aggregates is expected that can be utilizing as an aggregate of polymer concrete.

• 한국농공학회논문집
• /
• 제47권4호
• /
• pp.25-32
• /
• 2005

This study was performed to evaluate the strength properties of polymer concrete using recycled aggre-gate. The compressive strength, splitting tensile strength, flexural strength and pulse velocity of polymer concrete were decreased with increasing the content of recycled aggregate. At the curing age of 7days, the compressive strength was $80.5\~88.3$ MPa, the splitting tensile strength was $9.1\~10.6$ MPa, the flexural strength was $19.2\~21.5$ MPa and the pulse velocity was $3,931\~4,041$ m/s, respectively. Also, the compressive strength, splitting tensile strength, flexural strength and pulse velocity of concrete using recycled fine aggregate were higher than that of the silica sand. Therefore, these recycled aggregate polymer concretes were estimated for high strength concrete without major problem.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.437-440
• /
• 2005

The effects of polymer-cement ratio and recycled aggregate content on the continuous void ratio, coefficient of permeablity, compressvie, tensile and flexural strengths of water-permeable polymer-modified concretes using recycled aggregate are examined. As a result, the continuous void ratio and coefficient of permeablity of the water-permeable polymer-modified concretes tend to decrease with increasing polymer-binder ratio. Regardless of the recycled aggregate content, the compressvie, tensile and flexural strengths of the water-permeable polymer-modified concretes wtend to increase with increasing polymer-cement ratio.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.320-323
• /
• 2004

In general, polymer concrete has more excellent mechanical properties and durability than Portland cement concrete, but very sensitive to heat and has large deformations. In this study, the long-term creep behaviors was predicted by the short-term creep test, and then the characteristic of creep of recycled-PET polymer concrete was defined by material and experimental variables. The error in the predicted long-term creep values is less than 5 percent for all polymer concrete systems. The filler carry out an important role to restrict the creep strains of recycled PET polymer concrete. The creep strain and specific on using the CaCO3 were less than using fly-ash. the creep increases with an increase in the applied stress, but not proportional the rate of stress increase ratio. The creep behavior of polymer concrete using recycled polyester resin is not a linear viscoelastic behavior.

• 한국건설순환자원학회논문집
• /
• 제7권4호
• /
• pp.445-451
• /
• 2019

본 연구에서는 콘크리트 교면포장 재료로서 사용되는 라텍스의 단점인 경제성을 보완하고 자원재활용을 위해 괭생이모자반 기반의 자원순환형 폴리머 혼입에 따른 내구성능을 분석하였다. 본 연구 범위의 모든 배합조건에서 슬럼프 및 공기량은 품질기준은 만족하는 것으로 나타났으나, 분말 형태의 자원순환형 바이오 폴리머 적용시 슬럼프가 일부 저하되는 경향을 나타내었다. 압축강도 시험결과, 라텍스 혼입시 강도가 감소되었지만 바이오 폴리머 대체시 혼입율에 따라 6.3~24.4%의 강도 개선효과를 나타내었다. 내구성능 시험결과, 합성 폴리머 혼입시 가장 우수한 내구성능을 나타내었고, 바이오 폴리머 혼입시에는 혼입율이 증가할수록 내구성능이 우수한 경향을 나타내었지만 라텍스보다는 미소하게 낮은 것으로 확인되었다.

• 한국농공학회:학술대회논문집
• /
• 한국농공학회 2003년도 학술발표논문집
• /
• pp.415-418
• /
• 2003

This study is performed to examine properties of polymer permeability concrete using recycled coarse aggregate and blast furnace slag for application of structures needed permeability. Tests for compressive strength, flexural strength and pulse velocity with replacement ratio of recycled coarse aggregate are performed. As a result, compressive strength, flexural strength and coefficient of permeability of polymer permeability concrete containing recycled coarse aggregate are in the range of $180{\sim}200kgf/cm^2,\;58{\sim}64kgf/cm^2\;and\;4.6{\times}10^{-2}{\sim}6.9{\times}10^{-2}cm/s$, respectively. Compressive strength, flexural strength and pulse velocity of polymer concrete containing crushed stone only are $192kgf/cm^2,\;65kgf/cm^2\;and\;6.1{\times}10^{-2}cm/s$, respectively. Accordingly, recycled coarse aggregate is expected that can be utilizing as an aggregate of polymer permeability concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.719-722
• /
• 2004

Resins using recycled PET offer the possibility of a lower source cost of materials for making useful polymer concrete products. The purposed of this paper is to form a part of reducing the damage of sulfuric acid, through investigating recycled PET polymer concrete, . immersed at sulfuric acid solution for 84 days. Recycled PET PC is excellent chemical resistance, resulting in the role of unsaturated polyester resin which consists of polymer chain structure accomplishes bond of aggregates and filler strongly. Also, Recycled PET PC, used fly-ash as filler, is stronger resistance of sulfuric acid corrosion than $CaCO_3$, because it is composed of $SiO_2$ and very strong glassy crystal structure. Therefore, Recycled PET PC, used fly-ash as filler, is available under corrosion circumstances like sewer pipe or waste disposal plant.