• 한국세라믹학회지
• /
• 제33권12호
• /
• pp.1421-1425
• /
• 1996

Sintered Si3N4 and Inconel composed of Ni(58-63%) Cr(21-25%) Al(1-17%) Mn(<1%) fe(balance) were pressurelessly joined by using Ag-Cu-Ti brazing filler metal at 950℃ and 1200℃ under N2 gas atmosphere of 1atm and their interfacial structures were investigated. In case that the reaction temperature was low as 950℃ its interfacial structure was "Inconel metal/Ti-rich phase layer/brazing filler metal layer/Si3N4 " Ti used as reactive metal existed in between inconel steel and brazing metal and moved to the interface of between brazing filler metal nd Si3N4 according as reaction temperature increased up to 1200℃. The interfacial structure of inconel steel-Si3N4 reacted at 1200℃ was ' inconel metal/Ni-rich phase layer containing of Fe. Cr and Si/Cu-rich phase layer containing of Mn and Si/Si3N4 " Cr Mn, Ni and Fe diffused to the interface of between brazing filler metal and Si3N4 and reacted with Si3N4 The most reactive components of ingredients of inconel metal were Cr and Mn. On the other hand Ti added as reactive components to Ag-Cu eutectic segregated into Ni-rich phase layer,.

• Journal of the Korean Academy of Child and Adolescent Psychiatry
• /
• 제5권1호
• /
• pp.118-132
• /
• 1994

본 연구는 반응성 애착 장애아와 정상아의 의사소통 및 모자 상호작용 유형을 비교하기 위해 반응성 애착 장애아와 정상아 각 12명씩 그리고 그들의 어머니가 참석했다. 어머니와 아동은 이혜련 신경정신과 의원의 놀이치료실에 내원하여 가정에서 하듯이 놀이하라는 지시를 받고 15분간의 자유놀이를 하였고 이를 녹화하였다. 녹화된 테이프를 전사자료로 작성하여 의사소통 유형을 분석하였으며 상호작용 유형은 시간 표집 방법으로 분석하여 빈도자료를 얻었다. 이 자료는 t-검증 ,상관계수로 통계처리 되었다. 그 결과는 다음과 같았다. 1) 두 집단 아동의 비사소통 유형에서는 '수용적 발어', '정보요구', '기술', '자기기술'에서 의미있는 차이가 있었다. 2) 두 집단 어머니의 의사소통 유형에서는 '수용적 발어', '명명하기'에서 의미있는 차이가 있었다. 3) 두 집단의 상호작용 유형에서는 반응성 애착 장애아와 그들의 어머니 모두가 먼저 상호작용을시작하는 빈도가 적었고, 아동의 혼자놀이는 더 많았으며 혼자놀이 시의 어머니의 반응은 통제와 무반응이 정상아 집단보다 많았다. 4) 두 집단 아동과 어머니의 의사소통 유형과 상호작용 유형에서 의미있는 차이를 보였던 항목들간에 높은 상관을 보였는데 아동의 '수용적 발어', '정보요구', '기술'. '자기기술'은 '상호작용시작'과 정적인 상관을 보였으며 '혼자놀이', '통제', '무반응'과는 부적상관을 보였다.

• 한국산학기술학회논문지
• /
• 제16권12호
• /
• pp.8679-8683
• /
• 2015

세라믹은 고온에서 뛰어난 내마모성, 내부식성을 가지기 때문에 산업적 응용에 있어서 널리 사용된다. 세라믹은 금속과 비교해서 고온에서 더 큰 강도를 가지고 있고, 더 낮은 열전도도 및 열팽창 계수를 가진다. 그러나, 세라믹이 가진 취성의 성질은 전기전자산업과 고온에서의 구조적 적용에의 넓은 적용을 제한한다. Ti 활성금속과 STS304를 IBAD 기술을 이용해서 동시에 증착시켜 STS304 스테인레스강에 $Al_2O_3$(알루미나)의 브레이징 접합강도에 어떤 영향을 미치는지 알아보았으며, 시험편들은 Ti 타겟과 Ti+ STS304 타겟 두 종류를 이용하여 두께를 변화시켜가며 증착하였다. 브레이징 접합을 위한 삽입금속으로는 일반적으로 사용되는 Ag-Cu 공정조성의 합금이 사용되었다. 브레이징 접합품의 강도는 Ag-Cu 삽입금속과 알루미나 사이의 반응층의 두께와 반응 생성물 조직에 의해 결정되며, 본 실험에서는 계면 반응의 메커니즘을 보다 구체화하고 계면 반응에 의한 경사기능성의 접합계면을 더욱 향상시키는 결과를 얻고자 한다.

• 한국세라믹학회지
• /
• 제55권5호
• /
• pp.492-497
• /
• 2018

This paper reports the efficacy of tape casting using an Ag-10 wt% CuO filler for the successful joining of a sintered $Ce_{0.9}Gd_{0.1}O_{2-{\delta}}-La_{0.7}Sr_{0.3}MnO_{3{\pm}{\delta}}$ (GDC-LSM) ceramic with a SUS 460 FC metal alloy by reactive air brazing. The as-prepared green tape was highly flexible without drying cracks, and the handling was easy when used as a filler material for reactive air brazing. Heat treatment for the GDC-LSM/SUS 460 FC joint was performed at $1050^{\circ}C$ for 30 min in air. Microstructural observations indicated a reliable and compact joining. The room temperature mechanical shear strength of the as-brazed joints was $60{\pm}8MPa$ with a cohesive failure. The flexural strength of joints was measured from room temperature up to $850^{\circ}C$, where the strength retention revealed to be almost 100% at $500^{\circ}C$. However, the joints showed a degradation in strengths at 800 and $850^{\circ}C$, exhibiting strength retentions of 57% and 37%, respectively.

• 한국세라믹학회지
• /
• 제56권4호
• /
• pp.394-398
• /
• 2019

In this paper, the joining characteristics of GDC-LSM ceramics with Crofer 22 APU metal alloys was investigated at different brazing temperatures and holding times by reactive air brazing. Brazing was performed using Ag-10 wt% CuO filler, at three different temperatures (1000, 1050, and 1100℃ for 30 minutes) as well as for three different holding times (10, 30, and 60 minutes at 1050℃). The interfacial microstructures were examined by scanning electron microscopy and the joining strengths were assessed by measuring shear strengths at room temperature. The results show that with increasing brazing temperature and holding time, joint microstructure changed obviously and shear strength was decreased. Shear strength varied from a maximum of 100±6 MPa to a minimum of 18±5 MPa, depending on the brazing conditions. These changes were attributed to an increase in the thickness of the oxide layer at the filler/metal alloy interface.

• 한국세라믹학회지
• /
• 제35권9호
• /
• pp.939-944
• /
• 1998

실리콘함유 고분자(Polysiloxane)의 세라믹변환과정에서의 부피수축효과를 조절하기 위하여 활성화금속으로 중석을 첨가하여 열분해 및 합성반응을 통해 신 세라믹 복합체를 개발하고 이의 세라믹화 과정이나 물성을 조사하였다. 제조된 시편의 미세조직은 고분자로부터 야기된 $S_{1}$-O-C게열의 Glass기지상과, 분해잔여물(고상,기상)등과 활성화금속과의 반응르로 생성된 고경도의 탄호물로 이루어져 있어 향후 내마모재료로서의 응용을 기대할 수 있을 것이다. 제조된 복합체의 물성은 반응조건에 많이 의존함을 알 수 있었다. 1400~$1500^{\circ}C$에서 열분해 시켜 제조한 복합체의 밀도는 95% 이상의 상대밀도와, 경도 값은 7~8GPa 정도이고 탄성률은 220~230 GPa, 파괴인성응ㄴ 6~6.8$MPam^{1/2}$, 파괴강도는 380~470 MPs정도의 값을 나타내었다.

• Transactions on Electrical and Electronic Materials
• /
• 제15권2호
• /
• pp.77-80
• /
• 2014

The effect of reactive diluents on the ac electrical treeing in epoxy/nanosilicate systems was studied, in a needle-plate electrode geometry. Diglycidyl ether of bisphenol A (DGEBA) type epoxy was used as a base resin, and layered silicate was used as a nano-sized filler. Polyglycol (PG) or 1,4-butanediol diglycidyl ether (BDGE) was introduced as a reactive diluent to the DGEBA/nanosilicate system, in order to decrease the viscosity of the nanocomposite system. PG acted as a flexibilizer, and BDGE acted as a chain extender, after the curing reaction. To measure the treeing propagation rate, a constant alternating current (ac) of 10 kV/4.2 mm (60 Hz) was applied to the specimen, in a needle-plate electrode arrangement, at $30^{\circ}C$ of insulating oil bath. When 10 kV/4.2 mm (60 Hz) was applied, the treeing propagate rate in the DGEBA system was $1.10{\times}10^{-3}$ mm/min, and that in the DGEBA/PG system was $1.05{\times}10^{-3}$ mm/min. As 1.5 wt% of nanosilicate was added to the DGEGA/PG system, the propagation rate was $0.33{\times}10^{-3}$ mm/min. This meant that the nano-sized layered silicates would act as good barriers to treeing propagation. The effect of chlorine content was also studied, and it was found that chlorine had a bad effect on the electrical insulation property of the epoxy system.

• 대한금속재료학회지
• /
• 제48권12호
• /
• pp.1056-1063
• /
• 2010

We present a new joining method for Pd-Cu membrane foils used as permeation tubes to collect $CO_2$. Since foils have poor mechanical strength, joining should be done at low temperatures to reduce residual stresses and without joining pressure. This contradicts the well known conditions for good contact between base materials that determines joint qualities. We selected Sn-Ag-Cu alloys that are highly reactive with Pd and Cu as a filler metal. As the filler melts at joining temperatures as low as $220{\sim}280^{\circ}C$, Pd and Cu are dissolved into the melt and react with the filler elements, which raises the melting temperature of the filler based on eutectic structures among the elements. Then, isothermal solidification progresses for the rest of the joining time. Intermetallic compounds (IMC) in the joints, one of the main factors for brittle joints, are inevitably formed. However, by optimizing both joining time and temperature, we balanced the wettability with IMC. Sealing test results confirmed that the joints are mechanically reliable during operation.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.101-102
• /
• 2006

Processing techniques for producing microcellular silicon carbide, mullite, and cordierite ceramics have been developed by a reaction method that incorporates a polysiloxane and reactive fillers. The techniques developed in this study offer substantial flexibility for producing microcellular ceramics whereby cell size, cell density, degree of interconnectivity, composition, and porosity can all be effectively controlled. It is demonstrated that the adjustment of filler composition enables the possibility of tailoring the composition and properties of the microcellular ceramics. The present results suggest that the proposed novel processing techniques are suitable for the manufacture of microcellular ceramics with high morphological uniformity.

• 폴리머
• /
• 제33권4호
• /
• pp.358-363
• /
• 2009

반응성기를 가지는 산무수물(maleic anhydride, MAH)을 폴리프로필렌(PP)에 도입함으로써 PP/극성 고분자의 블렌드 및 PP/filler의 복합소재 제조에서 계면과 계면 사이에 물리적 결합 이외의 화학적 결합을 향상시키고 기계적 특성 및 열적 특성을 극대화할 수 있다. 본 실험에서는 개시제(di-cumyl periofide, DCP)와 MAH 함량에 따른 그래프트율을 FT-IR과 화학적 적정법(chemical titration)을 이용하여 측정하였다. 그 결과 MAH의 함량이 증가할수록 그래프트율이 증가하였고 DCP의 함량이 0.06 wt% 일때에 가장 높은 그래프트율을 나타내었다. 또한, MAH의 함량에 따라 용융 흐름지수(melt index)가 증가하는 것을 볼 수 있었으며, 용융온도 및 열 분해 등의 열적 거동은 시차주사열량계(DSC) 및 열중량 분석기(TGA)를 이용하여 MAH 그래프트율에 따른 변화를 분석하였다.