• Journal of Advanced Marine Engineering and Technology
• /
• v.28 no.8
• /
• pp.1270-1278
• /
• 2004

This paper describes the effectiveness of laser pulse shaping in eliminating weld defects such as porosity, cracks and undercuts in pulsed Nd:YAG laser welding. A large porosity was formed in a keyhole mode of deeply penetrated weld metal of any stainless steel. Solidification cracks were present in STS 310S with above 0.017%P and undercuts were formed in STS 303 with about 0.3%S. The conditions for the formation of porosity were determined in further detail in STS 316. With the objectives of obtaining a fundamental knowledge of formation and prevention of weld defects, the fusion and solidification behavior of a molten puddle was observed during laser spot welding of STS 310S through a high speed video photographing technique. It was deduced that cellular dendrite tips grew rapidly from the bottom to the surface, and consequently residual liquid remained at the grain boundaries in wide regions and enhanced the solidification cracking susceptibility. Several laser pulse shapes were investigated and optimum pulse shapes were proposed for the reduction and prevention of porosity and solidification cracking.

• Laser Solutions
• /
• v.14 no.4
• /
• pp.9-13
• /
• 2011

The solar panel that consists of copper plate and copper tube was successfully welded by ultrasonic seam welding. However it was not only expensive the copper material but also ultrasonic welding has many problem such as high error rate, difficulty of dissimilar material welding, noise, etc. At this study, the laser welding of solar panel with aluminum plate instead of copper. The welding were carried out with the pulsed Nd:YAG laser and the weld bead geometry was measured with the variation of pulse energy. Consequently, there was no difference between the ultrasonic and the laser welding on the performance of heat transfer capacities. Also the formation of intermetalic compound such as CuAl2 was increased with the pulse energy.

• Proceedings of the KWS Conference
• /
• 1999.10a
• /
• pp.34-36
• /
• 1999

• Journal of Welding and Joining
• /
• v.22 no.1
• /
• pp.58-64
• /
• 2004

The control of the weld bead shape is important in laser welding of the small parts. The effects of laser welding parameters on the weld bead shape in the pulsed Nd:YAG laser welding of STS 304L material were investigated. Shielding gas type, flow rate, pumping voltage, pulse frequency, pulse width, focal position and overlap distance were selected as laser welding parameters. Experiments were designed and conducted using the Taguchi method which was a statistical experimental method. The weld bead width, penetration, area and aspect ratio were measured and analysed as the weld bead shape properties and the welding parameters were optimized to maximize the weld aspect ratio. Weld aspect ratio were greatly affected by the pulse width, pumping voltage and pulse frequency, and somewhat by the overlap distance, and little by the shielding gas type, flow rate and focal position. A confirmation experiment were conducted using the optimized welding parameters.

• Journal of Advanced Marine Engineering and Technology
• /
• v.30 no.6
• /
• pp.740-745
• /
• 2006

This study suggested the occurrence source of weld-defects and its solution methods in a welding of Electrolyte injection hole by pulsed Nd:YAG laser. In experiment, the ramp down was used in order that solidification crack was removed. Furthermore. shrinkage stress and heat input were reduced by changing of weld trajectory and defocused distance. As a results of a experiment, a sound weld bead shape and crack-free weld bead can be obtained. In conclusion this show that the welding stability is greatly affected by modulation of laser pulse shape for the same laser energy and welding parameters.

• International Journal of Korean Welding Society
• /
• v.3 no.1
• /
• pp.39-44
• /
• 2003

The welded specimens were made by butt welding of the 2 wires of 50mm length using the pulsed YAG laser. The laser welded wires were tested for investigating the shape memory effect and the ability of super elasticity. The fatigue properties of the welded wires were investigated using the rotary bending fatigue tester specially designed for wires. Moreover, the effect of defocusing distance during laser welding on the static and fatigue properties was Investigated. The shape memory effect and super elasticity of the laser welded wires were approximately identical with that of base metal at the test temperature below 353K. However, the welded wires were broken within elastic limit at the test temperature above 353k. Under the cyclic bending loading conditions, the welded wires could be useful only below the elastic limit, while the base metal had sufficient fatigue life even the stress induced M-phase region. The fatigue strength of the welded wires was about half of that of the base metal. The deterioration of the static and fatigue properties in the welded wires was proven to be from the large difference of the transformation behavior between the base metal and welded part that is caused by vaporization of Ni-content at the welded part during the welding process. The defocusing distance below 3mm acted more largely on lowering the strength of the welded wires than that of 6mm or 8mm.

• Journal of Welding and Joining
• /
• v.14 no.5
• /
• pp.59-68
• /
• 1996

This study was aimed to characterize the laser cutting process for the cold rolled stainless steel sheet. The principal process parameters of the cutting process were applied to both the continuous wave form and the pulsed wave form for the laser output mode. The laser-oxygen cutting process and the laser-nitrogen cutting process were also considered to characterize the quality and efficiency of the cutting process. The laser-oxygen cutting process revealed the better productivity than the laser-nitrogen cutting process, since the laser energy and the exothermic oxidation energy exerted on the laser-oxygen cutting process simultaneously during the entire cutting process. However, the straightness of the cutting section, which was considered as the most important factors, was inferior to that of the laser-nitrogen cutting process due to the formation of chromum oxide on the cutting surface. Frequency and duration of the pulsed wave form act as the main factors for the better quality, When the frequency increased from 100 Hz to 200 Hz and the duty increased from 20% to 40%, the quality factors such as the height of dross and the surface roughness were improved remarkably. The increase in the frequency from 200 Hz to 300 Hz, on the other hand, revealed the less effective in the cutting quality.

• Laser Solutions
• /
• v.15 no.1
• /
• pp.10-14
• /
• 2012

Pulse laser welding was performed on C22 metal bellows. The results can be summarized as follows: Laser welded metal bellows had less thermal distortion, narrow HAZ, high aspect ratio in comparison with other welding processes like TIG, Plasma welding. Laser welded bellows has higher tensile strengths than that C22 base metal. The value of hardness in laser weld metal was measured 100-120 Hv, it was decreased compared to the base metal. It is reasoned that due to the annealed by heat input during the laser welding.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.1
• /
• pp.99-104
• /
• 2010

Magnesium and magnesium alloys, the lightest structural materials, have been received plenty of global attention recently. These alloys could be applied in various fields, especially the electronics industry, because of their excellent electromagnetic interference shielding. However, the welding technique of magnesium alloys has not been established. This study is related to the welding of AZ31B magnesium alloy by a short-pulsed a Nd:YAG laser. Two types of pulse waves, square pulse and variable pulse, were used to control weld defects. Results show that the crack and porosity, generated in the weld, had not been controlled by general square pulse. But through the application of variable pulse, the defects could be prevented and the good weld zone was obtained.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.139-144
• /
• 2002

Ti-50.9at%Ni wires were welded using pulsed YAG laser. The laser welded wires were tested for investigating the shape memo교 effect and the ability of super elasticity. The fatigue properties of the welded wires were investigated using the rotary bending fatigue tester specially designed for wires. Moreover, the effect of defocusing distance during laser welding on the static and fatigue properties was investigated. The shape memory effect and super elasticity of the laser welded wires were approximately identical with that of base metal at the test temperature below 353K. However, the welded wires were broken within elastic limit at the test temperature above 353k. Under the cyclic bending loading conditions, the welded wires could be useful only below the elastic limit, while the base metal had sufficient fatigue life even the stress induced M-phase region. The fatigue strength of the welded wires was about half of that of the base metal. The deterioration of the static and fatigue properties in the welded wires was proven to be from the large difference of the transformation behavior between the base metal and welded part that is caused by vaporization of Ni-content at the welded part during the welding process. The defocusing distance below 3mm acted more largely on lowering the strength of the welded wires than that of 6mm or 8mm.