• Journal of the Korean Ceramic Society
• /
• v.32 no.3
• /
• pp.305-312
• /
• 1995

Thin films of Pb(Mg, Zn)1/3Nb2/3O3 were fabricated by spin coating the Pb-Mg-Zn-Nb-O complex alkoxide sols on(111) Pt-coated MgO (100) planes. It was observed that the content of H2O and the rheological characteristics of sol greatly influenced the orientation of perovskite grains after thin-film formation. A strong preferential orientation of (100)-type planes of the perovskite grains was obtained for the sol aged for 15 days with the molar ratio of H2O to total metal alkoxides=2. As small angle X-ray scattering experiment in the Porod region was performed to correlate the observed preferential orientation with the network structure of precursors at various stage of aging. It was shown that the degree of branching of the Pb-Mg-Zn-Nb-O precursor chain had a direct effect on the preferred oreintation, and weakly branched precursor systems led to highly oriented grains after thin-film formation.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.2
• /
• pp.114-121
• /
• 1996

Thin film Ba$^{0.7}Sr^{0.3}TiO^{3}$ (BST) capacitors were fabricated on SiO$_{2}$/Si substrates by RF magnetron sputtering method and characterized at microwave frequencies ranging from 40 MHz to 1GHz to examine the dielectric dispersion of the capacitors. The BST thin films were electrode material of BST thin films capacitor which is known as one of the best electrode materials for BST films. 50$\AA$-thick titanium (Ti) layers were introduced to increase adhesion between bottom Pt and SiO$_{2}$. The leakage current density of the capacitors was about 1.7${\times}10^{7}A/cm^{2}$ at 1.5V and the dielectric constant was about 140 at 1MHz. Microwave measurement patterns having a coplanar waveguide type were fabricated and their S parameters were measured using network analyzer. After de-embedding parasitic components in microwave measurement patterns nearly frequency-invariant dielectric constant of about 120 was extracted in the measurement range of 40 MHz to 1 GHz.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.49-52
• /
• 2003

The role of gas ratio with the crystallization behavior and electrical properties in $Bi_{3.25}La_{0.75}Ti_3O_{12}$(BLT) thin films by rf magnetron sputtering method has not been precisely defined. In this work, the ferroelectric properties of these films with gas variation was investigated. BLT thin films were deposited on the Pt/Ti bottom electrode by rf magnetron sputtering method and then they were crystallized by rapid thermal annealing (RTA). The experiment showed that all BLT films indicated perovskite polycrystalline structure with preferred orientation (020) and (0012). And no pyrochlore phase was observed. The fabricated film annealed with $O_2$ of 15 sccm showed that value of leakage current was $9.67{\times}10^{-7}A/cm^2$ at 50kV /em, and the value of remanent polarization (2Pr=Pr+-Pr-) was $11.8{\mu}C/cm^2$. Therefore we induce access to memory device application by rf-magnetron sputtering method in this report.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.94-98
• /
• 2000

Polycrystalline SBTN ferroelectric thin films were prepared by sol-gel method with various Nb mole ratios on Pt/ $SiO_2$/Si (100) substrates. The films were annealed at different temperatures and characterized in terms of phase and microstructure. Relatively a well saturated hysteresis pattern was obtained at x =0.2 in S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin films. At an applied voltage of 5V, the dielectric constant ($\varepsilon$$_{r}$) and dissipation factor (tan $\delta$) of typical S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin film (x=0.2) were about 236.2 and 0.034. Measured remanent polarization (2Pr) and coercive field (Ec) were 4.28C/c $m_2$, and 38.88kv/cm respectively. No fatigue was observed up to 6$\times$10$_{10}$ switching cycles at 5V and the normalized polarization reduced by a factor of only 4%.%. 4%.%. 4%.%.%.%.%.

• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.754-762
• /
• 1995

Strontium titanate(SrTiO$_3$) thin film was prepared on Si substrates by RF magnetron sputtering for a high capacitance density required for the next generation of LSTs. The optimum deposition conditions for SrTiO$_3$thin film were investigated by controlling the deposition parameters. The crystallinity of films and the interface reactions between SrTO$_3$film and Si substrate were characterized by XRD and AES respectively. High quality films were obtained by using the mixed gas of Ar and $O_2$for sputtering. The films were deposited at various bias voltages to obtain the optimum conditions for a high quality file. The best crystallinity was obtained at film thickness of 300nm with the sputtering gas of Ar+20% $O_2$and the bias voltage of 100V. The barrier layer of Pt(100nm)/Ti(50nm) was very effective in avoiding the formation of SiO$_2$layer at the interface between SrTiO$_3$film and Si substrate. The capacitor with Au/SrTiO$_3$/Pt/Ti/SiO$_2$/Si structure was prepared to measure the electric and the dielectric properties. The highest capacitance and the lowest leakage current density were obtained by annealing at $600^{\circ}C$ for 2hrs. The typical specific capacitance was 6.4fF/$\textrm{cm}^2$, the relative dielectric constant was 217, and the leakage current density was about 2.0$\times$10$^{-8}$ A/$\textrm{cm}^2$ at the SrTiO$_3$film with the thickness of 300nm.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.481-485
• /
• 2001

We investigated the structural and electrical properties of the Ba ($Zr_{x}$ $T_{il-x}$ )$O_3$ (BZT thin films with a mole fraction of x=0.2 and thickness 150 nm for the application in MLCC (Multilayer Ceramic Capacitor). BZT films were prepared on $Pt/SiO_2$/Si substrate at various substrate temperatures by the RF-magnetron sputtering system. When the substrate temperature was above $500^{\circ}C$, we could obtain multi-crystalline BZT films oriented at (110), (111), and (200) directions. The crystallization of the film and high dielectric constant were observed with the increase of substrate temperature. Capacitance of the film deposited at high temperature is more sensitive to the applied voltage than that of the film deposited at low temperature. This paper reports surface morphology, dielectric constant, dissipation factor, and C-V characteristics for BZT films deposited at three different temperatures. The BZT film deposited at 40$0^{\circ}C$ shows stable electrical properties but a little small dielectric constant for MLCC application.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.80-81
• /
• 2008

Schottky barrier thin film transistors (SB-TFT) on polycrystalline silicon(poly-Si) are fabricated by platinum silicided source/drain for p-type SB-TFT. High quality poly-Si film were obtained by crystallizing the amorphous Si film with excimer laser annealing (ELA) or solid phase crystallization (SPC) method. The fabricated poly-Si SB-TFTs showed low leakage current level and a large on/off current ratio larger than $10^5$. Significant improvement of electrical characteristics were obtained by the additional forming gas annealing in 2% $H_2/N_2$ ambient, which is attributed to the termination of dangling bond at the poly-Si grain boundaries as well as the reduction of interface trap states at gate oxide/poly-Si channel.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1097-1104
• /
• 2000

MOD(Metal-Organic-Decomposition)법에 의해 $Y_2$O$_3$버퍼층에 Pt/TiO$_2$/SiO$_2$/Si 기판 위에 제조한 후, 그 표면 위에 졸-겔 방법으로 YMnO$_3$박막을 형성하였다. 기판의 종류와 수화조건 변화가 YMnO$_3$박막의 결정화 거동에 미치는 영향을 고찰하였으며, 또한 $Y_2$O$_3$버퍼층 유.무에 따른 Mn의 산화상태를 확인하고 이에 따른 유전특성 변화를 연구하였다. $Y_2$O$_3$버퍼층을 삽입하지 않고 직접 기판 위에 형성한 YMnO$_3$박막의 결정상은 기판의 종류 및 Rw 변화에 관계없이 orthorhombic 구조임이 확인되었다. 반면, $Y_2$O$_3$버퍼층 위에 형성된 YMnO$_3$박막의 경우에는 Rw($H_2O$/alkoxide mole ratio)가 0~6 범위 내에서 낮아질술고 hexagonal 결정상 성장에 유리하였으며, 또한 Pt(111)/TiO$_2$/SiO$_2$/Si 기판이 Ptd(200)/TiO$_2$/SiO$_2$/Si에 비하여 결정상 형성에 용이하였다. $Y_2$O$_3$버퍼층은 YMnO$_3$결정상 내에서 $Mn^{4+}$ 이온형성을 억제함으로써 누설전류밀도가 크게 감소되는 효과를 주었으며, 동시에 강유전 특성을 지닌 hexagonal 결정상 형성에 유리하게 작용하였다. 결론적으로, $Y_2$O$_3$는 Pt가 코팅된 Si 기판 위에 YMnO$_3$박막 제조시 그 강유전 특성을 향상시켜주는 우수한 버퍼층 재료임을 확인하였다.

• Korean Journal of Materials Research
• /
• v.9 no.7
• /
• pp.735-739
• /
• 1999

In this study we investigated stress development and shrinkage of thickness for a single $PbTiO_3$(PT) layer prepared by sol-gel processing. Changes of microhardness for multideposited PT layers with temperatures are also monitored to understand the densification of thin films. Single PT layer shrank rapidly from room temperature to$ 220^{\circ}C$ yielding 83% of total shrinkage observed up to $500^{\circ}C$. A tensile stress of ~75MPa developed in an as-spun layer, and increased steadily beyond $130^{\circ}C$ until it reaches the maximum value of 147MPa at $250^{\circ}C$. The significant decrease of tensile stress in the film beyond $370^{\circ}C$ indicates that thermal expansion mismatch between the film and the substrate dominates the stress behavior in this temperature range. Microhardness of the multideposited coatings also increased rapidly above $300^{\circ}C$ regardless of the pyrolysis temperatures used. Large amount of perovskite phase formed in multideposited coatings after $550^{\circ}C$ may be due partly to enhanced homogeneous nucleation in the thicker coating.

• Journal of the Korean Vacuum Society
• /
• v.16 no.6
• /
• pp.446-452
• /
• 2007

[ $(Pb_{1.1},La_{0.08})(Zr_{0.65}.Ti_{0.35})O_3$ ] thin films on the $Pt/Ti/SiO_2/Si$, $TiO_2(interlayer)/Pt/Ti/SiO_2/Si$ substrate were fabricated by the R.F. magnetron-sputtering method and considered their characteristics depending on $TiO_2$ interlayer. Changing the deposition conditions of $TiO_2$ interlayer, we obtained $TiO_2$ anatase single phase and rutile single phase. PLZT was deposited on these substrates and analyzed by x-ray diffraction(XRD) for there crystallinity and orientation. To investigate $PLZT-TiO_2$, $TiO_2-Pt$ interface, glow discharge spectrometer(GDS) analysis was carried out and we performed electrical measurements for dielectric properties of PLZT thin films. The PLZT thin film on $TiO_2$ anatase interlayer was found to have (110)-preferred orientation and 12.6 ${\mu}C/cm^2$ remaining polarization value.