• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2006년도 춘계학술대회
• /
• pp.63-66
• /
• 2006

A long term deactivation study was carried out with commercial MEA provided by Hyundai Motor Co. The deactivation phenomena were observed only at high voltage region where there is no diffusion-limited reaction. A rapid deactivation was observed up to 40h owing to the sintering of Pt particles. This was followed a gradual increase in the activity up to 300 h, which is probably caused by improvement in the electrode properties in the presence of current during the reaction. After 300 h, monotonic decrease in the activity was observed owing to dissolution of Pt particles especially in the cathode. The presence oxygen is the cause of oxidation and dissolution of Pt. The dissolution rate can be somewhat retarded by generation of current, which reduces Pt ion back to Pt in the cathode.

• 한국수소및신에너지학회논문집
• /
• 제23권3호
• /
• pp.256-263
• /
• 2012

We studied the degradation phenomenon of Pt catalyst in PEMFC. We used the electron microscope analysis technique including the ultra-microtome pretreatment method, FEG-SEM and TEM analysis methods for analysis of Pt nanoparticles. The Pt catalyst degradation is observed not only in electrode site but also in membrane site. We investigated these various degradation phenomena. The cathode electrode layer thickness is reduced. The size of the catalyst is increased much larger than initial size in membrane site. The catalyst moved from electrode layer to the electrolyte membrane. The rounded shape of catalyst was changed to the polygon. As a result, we found that the catalyst degradation processes of migration and coarsening occurred by the followings mechanisms; (1) dissolution of Pt ; (2) diffusion of Pt ion ; (3) Pt ion chemical reduction in membrane; (4) Coarsening of Pt particles (Ostwald ripening) ; (5) polygon shape change of Pt by {111} plane growth.

• Corrosion Science and Technology
• /
• 제9권6호
• /
• pp.281-288
• /
• 2010

This study examined the carbon corrosion at Pt/C interface in proton exchange membrane fuel cell environment. The Pt nano particles were electrodeposited on carbon substrate, and then the corrosion behavior of the carbon electrode was examined. The carbon electrodes with Pt nano electrodeposits exhibited the higher oxidation rate and lower oxidation overpotential compared with that of the electrode without Pt. This phenomenon was more active at $75^{\circ}C$ than $25^{\circ}C$. In addition, the current transients and the corresponding power spectral density (PSD) of the carbon electrodes with Pt nano electrodeposits were much higher than those of the electrode without Pt. The carbon corrosion at Pt/C interface was highly accelerated by Pt nano electrodeposits. Furthermore, the polarization and power density curves of PEMFC showed degradation in the performance due to a deterioration of cathode catalyst material and Pt dissolution.

• 한국재료학회지
• /
• 제28권11호
• /
• pp.646-652
• /
• 2018

During a long-term operation of polymer electrolyte membrane fuel cells(PEMFCs), the fuel cell performance may degrade due to severe agglomeration and dissolution of metal nanoparticles in the cathode. To enhance the electrochemical durability of metal catalysts and to prevent the particle agglomeration in PEMFC operation, this paper proposes a hybrid catalyst structure composed of PtCo alloy nanoparticles encapsulated by porous carbon layers. In the hybrid catalyst structure, the dissolution and migration of PtCo nanoparticles can be effectively prevented by protective carbon shells. In addition, $O_2$ can properly penetrate the porous carbon layers and react on the active Pt surface, which ensures high catalytic activity for the oxygen reduction reaction. Although the hybrid catalyst has a much smaller active surface area due to the carbon encapsulation compared to a commercial Pt catalyst without a carbon layer, it has a much higher specific activity and significantly improved durability than the Pt catalyst. Therefore, it is expected that the designed hybrid catalyst concept will provide an interesting strategy for development of high-performance fuel cell catalysts.

• Journal of Pharmaceutical Investigation
• /
• 제18권1호
• /
• pp.15-21
• /
• 1988

An inclusion complex of phenytoin (PT) with ${\beta}-cyclodextrin\;({\beta}-CyD)$ in molar ratio of 1 : 1 was prepared, and the interaction between host and guest molecules was confirmed by infrared spectrometry, differential scanning calorimetry and X-ray diffractometry. Suppositories were prepared by the fusion method. PT and $PT-{\beta}-CyD$ complex were added to PEG 1540 and Witepsol H-15 under the vigorous stirring at $40^{\circ}C$. Content uniformity was tested for different formulations of the PT suppositories. The release rates were dependent on the K.P. V dissolution apparatus and the dialyzing tubing method. Then, the release rates were increased in the following order: $PT-{\beta}-CyD$ complex in PEG 1540>PT in PEG 1540>$PT-{\beta}-CyD$ complex in Witepsol H-15>PT in Witepsol H-15. The area under the curve and maximum blood concentration after rectal administration were increased in the following order: $PT-{\beta}-CyD$ complex in PEG 1540>PT in PEG 1540>$PT-{\beta}-CyD$ complex in Witepsol H-15>PT in Witepsol-15.

• 한국수소및신에너지학회논문집
• /
• 제26권4호
• /
• pp.318-323
• /
• 2015

For commercialization of fuel cell electric vehicles, one of the key objectives is to improve durability of MEA and electrocatalysts. Regarding electrocatalysts, the major issue is to reduce carbon corrosion and dissolution of Pt caused by harsh conditions, for example, SU/SD (Start-up/Shut-down). In this research, OER (Oxygen Evolution Reaction) catalyst has been developed improvement of durability. A modified polyol process is developed by controlling the pH of the solvent to synthesize the PtIr nanocatalysts on carbon supports. Each performance of the MEAs applying PtIr and Pt are equivalent because PtIrnanocatalysts have both ORR and OER activity. Breadboard test for catalyst durability in harsh conditions and high potentialsis found that the MEA applying PtIrnanocatalysts durability is improved more than the MEA applying Pt nanocatalysts.

• Korean Chemical Engineering Research
• /
• 제61권2호
• /
• pp.189-195
• /
• 2023

PEMFC(고분자 전해질 막 연료전지) cathode 촉매로 Pt-Co/C가 내구성 향상 때문에 최근에 많이 사용되는 추세이다. 연료전지에서 전극과 전해질은 상호 간에 성능과 내구성 면에서 밀접하게 영향을 준다. Pt/C 전극 촉매에서 Pt-Co/C로 대체되었을 때 고분자 전해질막의 전기화학적 내구성에 미치는 영향에 대해서 연구하였다. PEMFC 고분자막의 전기화학적 가속 열화 과정에서 Pt-Co/C MEA(막전극접합체)의 내구성이 Pt/C MEA 내구성보다 높았다. FER (불소유출속도)와 수소투과도를 분석한 결과 Pt-Co/C MEA의 고분자막 열화속도가 Pt/C MEA보다 낮음을 보였다. OCV(개회로전압) holding 과정에서 Pt-Co/C 전극의 활성면적 감소속도가 Pt/C 전극보다 낮고, 고분자막에 석출되는 Pt 양도 Pt-Co/C MEA가 Pt/C MEA보다 작았다. 고분자막 내부의 Pt는 라디칼을 생성해서 고분자막을 열화시킴으로 Pt 석출 속도가 높은 Pt/C MEA의 고분자막 열화속도가 높게 나타났다. Pt-Co/C 촉매를 사용하면 전극 내구성도 향상되고, 고분자막에 석출되는 Pt양도 감소해서 고분자막의 전기화학적 내구성을 향상시켰다.

• Korean Chemical Engineering Research
• /
• 제61권3호
• /
• pp.341-347
• /
• 2023

PEMFC(Proton Exchange Membrane Fuel Cells)에서 PtCo/C 합금 촉매가 성능이나 내구성에서 우수하여 많이 사용되고 있다. 그러나 높은 전압에서(1.0~1.5 V) 평가되는 촉매 지지체 내구성에 관한 연구는 별로 보고 되지 않았다. 본 연구에서는 PtCo/C 촉매와 Pt/C 촉매에 촉매 지지체 가속 열화 프로토콜을 적용한 후 내구성을 비교하였다. 1.0↔1.5V 전압 변화 사이클 반복 후에 촉매 비활성도(Mass activity)와 전기화학적 활성면적(ECSA), 전기이중층 용량(DLC), Pt 용해와 입자 성장 등을 분석하였다. 전압변화 2,000 사이클 후 PtCo/C 촉매는 Pt/C 촉매에 비해 0.9 V에서 촉매 무게당 전류밀도가 1.5배 이상 감소하였다. 이와 같은 결과는 PtCo/C 촉매의 카본지지체의 열화 속도가 Pt/C 촉매보다 높기 때문이었다. Pt/C 촉매는 PtCo/C 촉매보다 촉매층의 ECSA 감소가 1.5배 이상 높았지만 Pt/C 촉매의 카본 지지체 부식이 작아 I-V 성능 감소가 작았다. PtCo/C 촉매의 고전압 내구성 향상을 위해서는 카본 지지체 내구성 향상이 필수적임을 보였다.

• Nuclear Engineering and Technology
• /
• 제54권3호
• /
• pp.965-974
• /
• 2022

Platinum anodes are widely used for metal oxides reduction in LiCl-Li₂O, however high-cost and low-corrosion resistance hinder their implementation. NiO-Li₂O ceramics is an alternative corrosion resistant anode material. Anode processes on platinum and NiO-Li₂O ceramics were studied in (80 mol.%) LiCl-(20mol.%)KCl and (80 mol.%)LiCl-(20 mol.%)KCl-Li₂O melts by cyclic voltammetry, potentiostatic and galvanostatic electrolysis. Experiments performed in the LiCl-KCl melt without Li₂O illustrate that a Pt anode dissolution causes the Pt²⁺ ions formation at 3.14 V and 550℃ and at 3.04 V and 650℃. A two-stage Pt oxidation was observed in the melts with the Li₂O at 2.40 ÷ 2.43 V, which resulted in the Li₂PtO₃ formation. Oxygen current efficiency of the Pt anode at 2.8 V and 650℃ reached about 96%. The anode process on the NiO-Li₂O electrode in the LiCl-KCl melt without Li₂O proceeds at the potentials more positive than 3.1 V and results in the electrochemical decomposition of ceramic electrode to NiO and O₂. Oxygen current efficiency on NiO-Li₂O is close to 100%. The NiO-Li₂O ceramic anode demonstrated good electrochemical characteristics during the galvanostatic electrolysis at 0.25 A/cm² for 35 h and may be successfully used for pyrochemical treating of spent nuclear fuel.

• Bulletin of the Korean Chemical Society
• /
• 제33권8호
• /
• pp.2539-2545
• /
• 2012

In the present study, we suggest a new way to reactivate performance of direct formic acid fuel cell (DFAFC) and explain its mechanism by employing electrochemical analyses like chronoamperometry (CA) and cyclic voltammogram (CV). For the evaluation of DFAFC performance, palladium (Pd) and platinum (Pt) are used as anode and cathode catalysts, respectively, and are applied to a Nafion membrane by catalyst-coated membrane spraying. After long DFAFC operation performed at 0.2 and 0.4 V and then CV test, DFAFC performance is better than its initial performance. It is attributed to dissolution of anode Pd into $Pd^{2+}$. By characterizations like TEM, Z-potential, CV and electrochemical impedance spectroscopy, it is evaluated that such dissolved $Pd^{2+}$ ions lead to (1) increase in the electrochemically active surface by reduction in Pd particle size and its improved redistribution and (2) increment in the total oxidation charge by fast reaction rate of the Pd dissolution reaction.