• 한국환경과학회지
• /
• 제18권10호
• /
• pp.1071-1077
• /
• 2009

A novel pretreatment technique was applied to the conventional Pt/alumina catalyst to prepare for the highly efficient catalyst for the preferential oxidation of carbon monoxide in hydrogen-rich condition. Their performance was investigated by selective CO oxidation reaction. CO conversion with the oxygen-treated Pt/Alumina catalyst increased remarkably especially at the low temperature below $100^{\circ}C$. This result is promising for the normal operation of the proton exchange membrane fuel cell (PEMFC) without CO poisoning of the anode catalyst. XRD analysis results showed that metallic Pt peaks were not observed for the oxygen-treated catalyst. This implies that well dispersed small Pt particles exist on the catalyst. This result was continued by high resolution transmission electron microscopy (HRTEM) analysis. Consequently, it can be concluded that highly dispersed Pt nanoparticles could be prepared by the novel pretreatment technique and thus, CO conversion could be increased considerably especially at the low temperatures below $100^{\circ}C$.

• 한국재료학회지
• /
• 제6권12호
• /
• pp.1263-1269
• /
• 1996

반도체 메모리 소자에 이용되는 하부전극의 Pt 박막을 MOCVD 증착방법을 이용하여 SiO2(100nm)/Si 기판위에 증착하였다. 반응개스로 O2개스를 사용하였을 경우에 순수한 Pt 박막을 얻었으며 증착층은(11)우선방향을 가지고 성장하였다. 증착온도가 45$0^{\circ}C$에서는 결정립 경계에 많은 hole이 형성되어 박막의 비저항을 증가시켰다. MOCVD에 의해 얻어진 Pt 박막은 전 증착온도범위에서 인장응력을 가지고 있었으며 40$0^{\circ}C$이상의 온도에서 hole이 형성되면서 응력은 감소하였다. MOCVD-Pt 위에 PEMOCVD로 증착한 강 유전체 SrBi2Ta2O9박막은 균일하고 치밀한 미세구조를 보였다.

• Journal of Magnetics
• /
• 제10권1호
• /
• pp.28-32
• /
• 2005

The magnetic properties and ordering behavior of Nb-doped FePt alloy films prepared by dc-magnetron sputtering were investigated. It was found that Nb addition retarded the ordering reaction from the disordered face-centered-cubic (fcc) Al phase to the ordered face-centered-tetragonal (fct) L1₀ phase. The tetragonality (c/a ratio) of the ordered fct L1₀ phase increased with the Nb concentration. Nb addition hampered c-axis contraction during ordering, probably because the larger Nb atoms occupy Pt sites. Consequently, the coercivity and magnetocrystalline anisotropic energy of Nb-doped FePt alloy films are lower than those of un-doped FePt film under equivalent annealing conditions.

• 공업화학
• /
• 제9권4호
• /
• pp.486-490
• /
• 1998

콜로이드법을 이용하여 인산형 연료전지에서 전극촉매로 사용되는 Pt/C 분말을 제조하였다. 이 때 환원제로 사용되는 $Na_2S_2O_4$ (sodium hydrosulfite)로부터 유입되는 황성분이 연료전지의 장기운전시 촉매독으로 작용하는 것으로 알려져 었다. 따라서 다음의 3가지 방법을 이용하여 황을 제거하였다. 첫 번째, 열처리에 의한 황의 제거시 온도가 올라갈수록 황의 제거 효과가 좋지만 너무 높은 온도에서는 백금입자의 크기가 성장하여 입자의 크기가 $50{\AA}$ 이상이 되면 전극성능이 감소하였다. 최적의 열처리 온도는 $400^{\circ}C$ 이었으며, 이 때의 백금입자의 크기는 $35{\sim}40{\AA}$였으며, 반전지 측정시 0.7V의 전압에서 $360mA/cm^2$의 전류밀도를 나타내었다. $400^{\circ}C$에서 1시간, 3시간, 5시간 동안 처리하였을 경우 백금입자의 크기는 변함이 없었고 황제거율은 각각 비슷하였다. 두 번째, 환원성 분위기의 도가니 속에서 열처리를 했을 경우 $900^{\circ}C$의 같은 온도에서 수소분위기에서의 열처리보다는 황의 제거율은 떨어지나 같은 온도에서 백금입자의 성장이 작아 상대적으로 좋은 전극성능을 보여 주었다. 세 번째, 용매추출의 경우에는 초기에 일부의 황을 제거할 수 있음을 확인하였고 이 때의 전극성능은 서로 비슷하였다.

• 한국진공학회지
• /
• 제9권4호
• /
• pp.315-320
• /
• 2000

본 연구에서는 강유전체 박막을 게이트 산화물로 사용한 $Pt/Sr_{0.8}Bi_{2.4}Ta_2O_{9}(SBT)/ZrO_2Si$(MFIS)와 Pt/SBT/Si(MFS)구조의 결정 구조 및 전기적 성질을 고찰하였다. XRD 및 SEM측정 결과 SBT/ZrO$_2$/Si 구조의 경우 SBT/Si구조에 비해 SBT 박막이 더 큰 결정립이 형성되었다. AES분석 결과 $ZrO_2$ 박막을 완충층으로 사용함으로써 SBT 박막과 Si 기판의 상호반응을 적절히 억제할 수 있음을 확인하였다. Pt/SBT/$ZrO_2/Pt/SiO_2$/Si와 Pt/SBT/Pt/$SiO_2$/Si 구조에서 Polarization-Voltage(P-V) 특성을 비교해 본 결과 $ZrO_2$ 박막의 도입에 따라 잔류분극값은 감소하였고 항전계값은 증가하였다. MFIS 구조에서 메모리 윈도우값은 항전계값과 직접적 관련이 있으므로 이러한 항전계값의 증가는 MFIS 구조에서의 메모리 윈도값이 증가할 수 있음을 나타낸다. Pt/SBT(210 nm)/$ZrO_2$/ (28 m)/Si 구조에서 Capacitance-Voltage(C-V) 측정 결과로부터 인가전압 4~6 V에서 메모리 윈도우 가 1~1.5V정도로 나타났다. Pt/SBT/ZrO$_2$/Si구조에서 전극을 갓 증착한 경우와 산소분위기 $800^{\circ}C$에서 후열처리한 경우의 전류 밀도는 각각 약 $8\times10^{-8} A/\textrm{cm}^2$와 $4\times10^{-8}A/\textrm{cm}^2$ 정도의 값을 나타내었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.214-215
• /
• 2009

This paper presents the fabrication and characteristics of microheaters, built on AlN(0.1 um)/3C-SiC(1 um) suspended membranes. Pt was used as microheater and temperature sensor materials. The results of simulated are shown that AlN/3C-SiC membrane has more large uniform-temperature area than $SiO_2$/3C-SiC membrane. Resistance of temperature sensor and power consumption of microheater were measured and calculated. Pt microheater generates the heat of about $550^{\circ}C$ at 340 mW and TCR of Pt temperature sensor is about 3188 ppm/$^{\circ}C$.

• 한국결정성장학회지
• /
• 제12권1호
• /
• pp.1-6
• /
• 2002

본 연구에서는 금속 알콕시드를 이용하여 0.9PMN-0.1PT 소결체를 제조하는데 있어 과량으로 첨가되는 $Mg(OC_2H5)_2$, Pb$(CH_3COO)_2{\cdot}3H_2O$ 등이 페로브스카이트 상의 생성량과 소결 밀도, 유전 상수 등에 미치는 영향을 검토하였다. 졸-겔법으로 0.9PMN-0.1PT 세라믹을 제조함에 있어 $Mg(OC_2H5)_2$를 과량 첨가하는 경우 페로브스카이트 상의 생성율을 증가시키는 효과가 나타났다. 0.9PMN-0.1PT 조성에 $Mg(OC_2H5)_2$를 5wt% 과잉 텀가한 시편을 $1,150^{\circ}C$에서 1시간 소결한 경우 페로브 스카이트 단일상을 얻었으며 이 때의 밀도는 이론 밀도의 98%인 것으로 확인되었다. $1.150^{\circ}C$에서 1시간 유지하여 소결한 시편의 유전 상수는 $Mg(OC_2H5)_2$를 5wt% 과잉 첨가한 경우 증가하였으며, 주파수 1 kHz에서 최대 유전 상수는 15,000의 값을 가졌다.

• 한국자기학회지
• /
• 제8권3호
• /
• pp.156-160
• /
• 1998

고주파 마그네트론 스퍼링법에 의하여 두께 약 2000$\AA$으로 제조한 (Mn0.5-ZSb0.5+Z)100-yPty(0$0^{\circ}C$의 진공중에서 열처리한 후, X-선회질장치, 토크자려계, kerr 효과 즉정장치를 이용하여 결정구조 및 자기광학적 특성을 조사하였다. 열처리 후, MnSbPt 합금막은 FDD의 Clb-형구조를 갖으나, MnSbAg 합금막은 HCP의 NiAs-형구조를 갖고 c-축이 막면에 수직하여 배향하는 이방성조직이 형성되나 열처리시간이 길어지면 등방성조직으로 바뀐다. 30$0^{\circ}C$에서 3시간 동안 dufcjflgksMnSbAg 합금막에서 우수한 수직자기이방성이 관측되었으며 Mn47.4Sb47.5Ag5.1 합금막으로부터 K1=6.6$\times$105 erg/cm3, K2=1.9$\times$105 erg/cm3의 수직자기이방성값을 얻었다. 입사파장 700~100nm 범위에서 MnSbpt 합금막의 Kerr 회전각은 입사파장이 감소할수록 증가하나 MnSgAg 합금막은 반대경향을 보인다. 입사파장 λ=700nm에서 Mn41.1Sb44.9Pt14.0 및 Mn47.4Sb47.5Pt5.1 합금막의 Kerr 회전각 $\theta$k는 각각 1.7$^{\circ}$와 0.2$^{\circ}$이고 λ=1000nm에서는 각각 0.6$^{\circ}$와 0.97$^{\circ}$이다.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2005년도 동계학술연구발표회 및 2차 아시안포럼
• /
• pp.101-101
• /
• 2005

• 대한한방내과학회지
• /
• 제21권1호
• /
• pp.156-161
• /
• 2000

The unripe fruit of Poncirus trifoliata Raf has been used for the treatment of allergic disease. Recently it was reported that the fruit inhibits passive cutaneous anaphylaxis and histamine release at mast cell. Type I immediate hypersensitivity of anaphylactic type is caused by released mediate chemical at mast cell. Histamine is also known as one of potent mediate chemical. Also release of mediate chemical is affected by specific stimulation of IgE combined with mast cell. Activation of mast cell is known to be stimulated by compound 48/80 and inhibited by increase of cAMP. In this experiment, the effect of water extract of Poncirus trifoliata Raf fruit (PT) on a histamine release, cAMP concentration and IgE production was measured. Compound 48/80 was administrated to the mouse peritoneal cell which was pretreated with PT. PT dosedependently inhibited histamine release at peritoneal mast cell and the serum level of histamine induced by compound 48/80. PT also instantly increased cAMP level of peritoneal mast cell right after it was added and the level gradually decreased. Production of IgE induced by antigens at mouse peritoneal cell was inhibited by PT. The IgE synthesis is induced by IL-4 and it is known that lipopolysaccharide(LPS) plus IL-4 cause an increase in IgE secretion by murine B cells. The effects of PT inhibited the production of IgE activated by LPS plus IL-4 at human U266B1 cells. These results indicate that PT has antiallergic activity by Inhibition of IgE production from B cells and histamine release by increase of cAMP.