• Journal of the Korean Wood Science and Technology
• /
• 제47권4호
• /
• pp.418-424
• /
• 2019

Densification is a process for improving the strength properties of wood from the felling of young trees, which is a common harvest practice in community forests. A series of experiments was conducted to refine the process with particular regard to the determination of suitable pretreatment and treatment conditions. Samples of pine and gmelina measuring $23cm(L){\times}20cm(W){\times}2cm(T)$ underwent pretreatment through immersion in a 1:1 $CH_3COOH-H_2O_2$ solution at concentrations of 15%, 20%, and 30%. Samples pretreated with the 20% solution showed the greatest improvement in strength; further experiments were conducted to determine the optimum treatment conditions in terms of temperature and duration following immersion. Test samples with the same dimensions as those in the pretreatment experiment were soaked in a 1:1 20% $CH_3COOH-H_2O_2$ solution and warmed in a water bath. The test samples were then individually hot pressed to the target thickness, which was 30% less than the original thickness and held at $150^{\circ}C$ or $170^{\circ}C$ for 15 or 30 minutes. The treated samples were cut for an analysis of their density, recovery of set, and bending strength. Pine and gmelina exhibited the best characteristics after treatment at $150^{\circ}C$ for 30 and 15 minutes, respectively. The results suggest that the modified densification process had increased the bending strength of the wood, but the temperature and duration of treatment must be carefully considered for different wood species.

• Bulletin of the Korean Chemical Society
• /
• 제33권8호
• /
• pp.2642-2646
• /
• 2012

Pretreatment of spent FCC catalyst and its application in remove trace olefins in aromatics were investigated in this research. The most effective pretreatment route of spent FCC catalyst was calcining at $700^{\circ}C$ for 1 h, washing with 5% oxalic acid solution in ultrasonic reactor and dried. Treated spent FCC catalyst was modified with metal halides, then to prepare catalyst to remove trace olefins in aromatics. X-ray diffraction, Pyridine-FTIR, $N_2$ adsorption-desorption and inductively coupled plasma optical emission spectrometer (ICP-OES) were used to investigate the pretreatment process. The result showed that the performance of the treated spent FCC catalyst was much greater than that of the spent FCC catalyst, which indicted the possibility and improvement of this research.

• 패션비즈니스
• /
• 제9권3호
• /
• pp.99-113
• /
• 2005

Recently, problems related to the natural dyeing have been addressed. Severer problems have been posed by the elution at metallic ions and dyestuff tram dyed fabrics. In order to prevent the elution tram the dyed fabrics, it is needed to improve the fastness. Especially, it is the most important measure to improve the fastness to perspiration in terms at human body safety. In this study, we employed chitosan pretreatment method bet ore the dyeing process, anticipating that the pretreatment might improve the fastness. We used Al, Sn, and Cu as mordants and investigated the fastness to light and perspiration of the chitosan treated and dyed fabric specimens. By the chitosan pretreatment, the fastness to perspiration improved, while the fastness to light did not.

• Environmental Engineering Research
• /
• 제14권1호
• /
• pp.48-52
• /
• 2009

Solubilization of sewage sludge creates favorable conditions for anaerobic microorganisms to produce biogas. In this paper, we quantify the effect of heating pretreatment on the degree of solubilization of sewage sludge. The pretreatment process was carried out using a lab-scale industrial microwave unit (2450 MHz frequency). Response surface analysis was applied to determine the combination of temperature-increase rate (ramp rate) (2.9 to 17.1 ${^{\circ}C}$/min) and terminal temperature (52 to 108${^{\circ}C}$). Both ramp rate and temperature significantly affected the solubilization degree of sludge. Within the design boundaries, the conditions predicted to maximize the solubilization degree of 15.8% were determined to be 2.9 ${^{\circ}C}$/min and 104${^{\circ}C}$.

• 대한본초학회지
• /
• 제30권4호
• /
• pp.71-79
• /
• 2015

Objectives : These present study was designed to investigate the relaxation effects of Alpiniae Oxyphyllae Fructus(AOF) on isolated corpus cavernosum smooth muscle.Methods : Rabbit corpus cavernous tissues were prepared in strip. Then relaxation responses of AOF at 0.01-3 ㎎/㎖ in contracted strips induced by phenylephrine(PE) were measured. To evaluate mechanisms, indomethacin(IM) tetraethylammonium chloride(TEA), Nω-nitro-L-arginine(_L-NNA), methylene blue(MB) were treated before AOF extract(0.1-3 ㎎/㎖) infused into precontracted strips induced by PE. And 1 mM Ca²⁺was infused into precontracted strips after pretreatment of AOF extract(3 ㎎/㎖) in Ca²⁺-free krebs-ringer solution. NO concentration was measured by Griess reagent system. Ratio of smooth muscles to collagen fibers and eNOS positive reaction were measured by histocheminal and immunohistochemical process.Results : The cavernous strips were significantly relaxed by AOF extract 0.1, 0.3, 1, 3 ㎎/㎖ and the pretreatment with IM 10 μM,_L-NNA 100 μM, MB 10 μM inhibited relaxation of AOF compared to non-pretreatment, but the pretreatment with TEA 100 μM didn't affect relaxation of AOF. In a Ca²⁺-free solution, pretreatment with AOF reduced increase on contraction of strips by Ca²⁺supply than non-pretreatment. On HUVEC, NO concentration was increased. On corpus cavernosum of penis in Spontaneous Hypertensive Rat, ratio of smooth muscles to collagen fibers and eNOS positive reaction in AOF group were increased compared to PE groupConclusions : Taken this results, we can suggest that AOF extract exerts a relaxation effects on rabbit corpus cavernosum smooth muscle in part by suppressing influx of extracellular Ca²⁺throughout prostacyclin, the NO-cGMP system.

• 한국대기환경학회지
• /
• 제26권3호
• /
• pp.286-297
• /
• 2010

This study deals with the effect of pretreatment on the $CO_2$ adsorption capacity of zeolitic adsorbents including a commercial A-type zeolite and cation exchanged adsorbents. The pre-heating could change the intrinsic properties such as specific surface area and adsorption capacity of the adsorbent. As a result of the experiment, the moisture previously filled inside might affect the potential adsorption capacity of the adsorbent, and could be disappeared throughout the heat treatment. An optimum pretreatment temperature for the test adsorbent was found to be $400^{\circ}C$, at which temperature enabled more than 90% refreshment. Precise examination through the TPD test showed that the TSA (Temperature Swing Adsorption) process would be desirable in dry adsorption of $CO_2$.

• Environmental Engineering Research
• /
• 제16권2호
• /
• pp.103-109
• /
• 2011

This work experimentally determined the effect of thermal and microwave pretreatments on the anaerobic digestion of mixtures of municipal primary and secondary sludges in semi-continuous mesophilic digesters at hydraulic retention times (HRT) of 20, 15, 10, 7, and 5 days. The ratio of soluble chemical oxygen demand (COD) to total COD in thermally pretreated and microwaved sludges at $80^{\circ}C$ was 2.7 and 3.2 times higher than that of raw sludge, respectively. The volatile solids (VS) and COD removal efficiencies in all three digesters fed with raw (control), thermally pretreated (TM), and microwaved (MW) sludges decreased as the HRT was reduced. The highest relative improvement in VS removal compared to the control occurred at the HRT of 5 days in the TM and MW (29 and 41% higher than the control, respectively). At this HRT, improvement in the COD removal efficiencies in the TM and MW compared to the control was 28 and 53%, respectively. Improvements in biogas production compared with the control increased in both the TM and MW as the HRT was reduced to 5 days. The relative improvement in daily biogas production compared to the control from the TM and MW was 33 and 53% higher than the control at the HRT of 5 days, respectively. The results show that microwave pretreatment is more effective than thermal pretreatment in increasing the solubilization degree and mesophilic anaerobic biodegradability of sewage sludge.

• 한국진공학회지
• /
• 제22권6호
• /
• pp.277-284
• /
• 2013

아세틸렌과 수소기체를 원료기체로 하고 육불화황을 첨가기체로 하여 열화학 기상 증착하에서 탄소코일을 합성하였다. 이 때 산화실리콘 기판위의 니켈막을 탄소코일 성장의 촉매로 사용하였다. 성장된 탄소코일의 생성밀도, 형상, 기하구조 등을 수소 플라즈마 전처리의 유무에 따라 조사하였다. 상대적으로 짧은 시간(1분)의 수소 플라즈마 전처리는 탄소 마이크로 코일을 우세하게 성장시켰다. 긴 시간(30분)동안의 수소플라즈마 전처리는 탄소마이크로 성장 축을 따라 수많은 탄소 나노코일이 들어붙어 있는 특이한 구조를 보였다. 이 특이한 구조는 매우 작은 니켈 촉매의 알갱이를 효과적으로 지지할 수 있는 촉매 지지대로서의 역할을 할 수 있을 것으로 예견되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제29권4호
• /
• pp.103-110
• /
• 2001

목재 내 리그닌의 선택적 분해 특성을 지닌 백색부후균 중, Phanerochaete chrysosporium KCCM 34740 균주를 현사시나무 목재 칩에 전처리하여 bio-kraft pulping 적용 가능성을 실험적으로 평가하였다. 전처리 결과, 무처리 대조구에 비해 펄프의 정선수율은 전처리 10일에서 최고 약 2%의 증가를 보였으며, 전처리 기간의 증가에 따라 여수도의 감소, WRV의 증가 경향을 나타냈다. 또한 수초지의 물성 개선에도 효과가 있었으며, 주사전자현미경 관찰을 통하여 이러한 효과가 백색부후균의 생물고해 작용, 즉 펄프 섬유의 미세섬유화 및 다공질화에 기인한 것임을 확인할 수 있었다. 이러한 결과로써 향후 kraft 증해 약액 및 제지공정상의 고해 동력에너지의 소비를 절감할 수 있을 것으로 기대한다.

• 한국재료학회지
• /
• 제26권3호
• /
• pp.109-116
• /
• 2016

To achieve the fabrication of high-quality Ag-coated Cu particles through a wet chemical process, we reported herein pretreatment conditions using an ammonium-based mixed solvent for the removal of a $Cu_2O$ layer on Cu particles that were oxidized in air for 1 hr at $200^{\circ}C$ or for 3 days at room temperature. Furthermore, we discussed the results of post-Ag plating with respect to removal level of the oxide layer. X-ray diffraction results revealed that the removal rate of the oxide layer is directly proportional to the concentration of the pretreatment solvent. With the results of Auger electron spectroscopy using oxidized Cu plates, the concentrations required to completely remove 50-nm-thick and 2-nm-thick oxides within 5 min were determined to be X2.5 and X0.13. However, the optimal concentrations in an actual Ag plating process using Cu powder increased to X0.4 and X0.5, respectively, because the oxidation in powder may be accelerated and the complete removal of oxide should be tuned to the thickest oxide layer among all the particles. Back-scattered electron images showed the formation of pure fine Ag particles instead of a uniform and smooth Ag coating in the Ag plating performed after incomplete removal of the oxide layer, indicating that the remaining oxide layer obstructs heterogeneous nucleation and plating by reduced Ag atoms.