• 한국분말재료학회지
• /
• 제14권2호
• /
• pp.145-149
• /
• 2007

Nanocrystalline transient aluminas (${\gamma}$-alumina) were coated on core particles (${\gamma}$-alumina) by a carbonate precipitation and thermal-assisted combustion, which is environmentally friend. The ammonium aluminum carbonate hydroxide (AACH) as a precursor for coating of transient aluminas was produced from precipitation reaction of ammonium aluminum sulfate and ammonium hydrogen carbonate. The crystalline size and morphology of the synthetic, AACH, were greatly dependent on pH and temperature. AACH with a size of 5 nm was coated on the core alumina particle at pH 9. whereas rod shape and large agglomerates were coated at pH 8 and 11, respectively. The AACH was tightly bonded coated on the core particle due to formation of surface complexes by the adsorption of carbonates, hydroxyl and ammonia groups on the surface of the core alumina powder. The synthetic precursor successfully converted to amorphous- and ${\gamma}$-alumina phase at low temperature through decomposition of surface complexes and thermal-assisted phase transformation.

• 한국초전도ㆍ저온공학회논문지
• /
• 제1권1호
• /
• pp.7-14
• /
• 1999

Wekk oriented $Bi_{2} Sr_{2} CaCu_{2} O_{8}$ suppercondcting thick films were fabricared on copper tape by LiReac-PreCu (liquid reaction between a Cu-free precousor and Cu tape) method. Cu-free precursor power which is composed of $Bi_{2}Sr_{2}Ca_{5}$ was printed on a copper tape by screen printing and was heat-treated. The speciment were partially in a molten state at the heat treatment temperature (85$0^{\circ}C$~87$0^{\circ}C$). The heat heat treatments for the reaction were performed in air or low oxygen pressure in several stages. XRD analyses of the resulting Bi2Sr2CaCu2O8 superconducting tapes show that the $Bi_{2} Sr_{2} CaCu_{2} O_{8}$ phase is dominant and a small amount of $Bi_{2} Sr_{2} Cu_{2} O_{6}$ phase is detected. Both phases are aligned in the c-axis direction.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2000년도 제18회 학술발표회 논문개요집
• /
• pp.122-122
• /
• 2000

Magnesium oxide is thermodynamically very stable, has a low dielectric constant and a low refractive index, and has been widely used as substrate for growing various thin film materials, particulary oxides of the perovskite structure. There has been a considerable interest in integrating the physical properties of these oxides with semiconductor materials such as GaAs and Si. In this regard, it is considered very important to be able to grow MgO buffer layers epitaxially on the semiconductors. Various oxide films can then be grown on such buffer layers eliminating the need for using MgO single crystal substrates. Vapor phase epitaxy of magnesium oxide has been accomplished on Si(001) substrates in a high vacuum chamber using the single precursor methylmagnesium tert-butoxide in the temperature range 750-80$0^{\circ}C$. For the epitaxy of the MgO films, SiC buffer layers had to be grown on Si(001). The films were characterized by reflection high energy electron diffraction (RHEED) in situ in the growth chamber, and x-ray diffraction (XRD), x-ray pole figure analysis, scanning electron microscopy (SEM), and x-ray photoelectron spectroscopy (XPS) after the growth.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 1999년도 High Temperature Superconductivity Vol.IX
• /
• pp.315-318
• /
• 1999

Bi$_{2}Sr_{2}CaCu_{2}O_{\delta}$ superconducting films were rapidly fabricated on copper tape by liquid reaction between a Cu-free precursor and Cu tape (LiReac-PreCu) method. Those thick films were well oriented along the c-axis. The precursor was made by melt-quenched technology using twin roller. The melt-quenched films were transparent and glossy yellow in appearance. These films which were the compostion of Bi$_2SrCaO_y$, Bi$_3Sr_2CaO_z$ were placed on copper tape and then heated at various temperatures for several minutes in air. They were analyzed using X-ray powder diffraction, SEM, a DC four-probe method. The mechanism of superconducting phase formation . from the melt-quenched precursor on Cu tape was studied

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.732-734
• /
• 2003

A solvothermal synthetic method to $BaTiO_3$ nanoparticle has been investigated in toluene solution with $BaTi(OR)_6$ as precursor. A precursor prepared from barium metal with toluene, isopropanol and titanium isopropoxide was used as a starting material. Weight ratio of precursor to solvent prepared in the mixture are 5/100, 10/100, 20/100 and 50/100wt%. At the weight ratio of 50/100wt%, $BaTiO_3$ butterfly twin crystalline(${\fallingdotseq}100nm$) was obtained after synthesis at $250^{\circ}C$ for 20hrs in an autoclave. X-ray diffraction and transmission electron microscopy showed that the product of 50/100wt% has crystallization. At 5/100, 10/100, and 20/100wt%, however, red colloidal solution was obtained after synthesis and crystalline phase of $BaTiO_3$ was not produced.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.422-425
• /
• 1999

Ultrafine NiO/YSZ (Yttria-Stabilized Zirconic) composite powders were prepared by using a glycine nitrate process (GNP) for anode material of solid oxide fuel cells. The specific surface areas of synthesized NiO/YSZ composite powders were examined with controlling pH of a precursor solution and the content of glycine. The binding of glycine with metal ions occurring in the precursor solution was analyzed by using FTIR. The characteristics of synthesized composite powders were examined with X-ray diffractometer, a BET method with $N_2$ absorption, scanning and transmission electron microscopies. Strongly acid precursor solution increased the specific surface area of the synthesized composite powders. This is suggested to be caused by the increased binding of metal ions and glycine under a strong acid solution of pH=0.5 that lets glycine consist of mainly the amine group of NH$_3$$^{+}$ After sintering and reducing treatment of NiO/YSZ composite powders synthesized by GNP, the Ni/YSZ pellet showed ideal microstructure very fine Ni Particles of 3-5${\mu}{\textrm}{m}$ were distributed uniformly and fine pores around Ni metal particles were formed, thus, leading to an increase of the triple phase boundary among gas, Ni and YSZ.Z.

• 한국세라믹학회지
• /
• 제49권6호
• /
• pp.523-527
• /
• 2012

Silicon carbide (SiC) has recently drawn an enormous amount of industrial interest due to its useful mechanical properties, such as its thermal resistance, abrasion resistance and thermal conductivity at high temperatures. In this study, RF thermal plasma (PL-35 Induction Plasma, Tekna CO., Canada) was utilized for the synthesis of high-purity SiC powder from an organic precursor (hexamethyldisilazane, vinyltrimethoxysilane). It was found that the SiC powders obtained by the RF thermal plasma treatment included free carbon and amorphous silica ($SiO_2$). The SiC powders were further purified by a thermal treatment and a HF treatment, resulting in high-purity SiC nano-powder. The particle diameter of the synthesized SiC powder was less than 30 nm. Detailed properties of the microstructure, phase composition, and free carbon content were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), a thermogravimetric (TG) analysis, according to the and Brunauer-Emmett-Teller (BET) specific surface area from N2 isotherms at 77 K.

• 한국초전도ㆍ저온공학회논문지
• /
• 제10권1호
• /
• pp.1-5
• /
• 2008

The effect of $BaCeO_3$ doping on the critical current density of YBCO film by TFA-MOD method was studied. $BaCeO_3$ doping was made by two method; one is direct addition of $BaCeO_3$ nano-sized powder prepared by citrate process followed by grinding with planetary ball mill for 10 hours. Another is addition of Ba-Ce precursor solution prepared with Ba-acetate and Ce acetate dissolved in TFA to the YBCO-TFA precursor solution. The film was made by standard dip coating and heat treatment process with conversion temperature of $790^{\circ}C$ in 1000 ppm oxygen containing moisturized Ar gas atmosphere. The direct addition of $BaCeO_3$ powder resulted in YBCO film with good epitaxial growth and no evidence of second phase formation. The addition through precursor solution resulted in the increase of critical current density upto 30 at% doping and uniform dispersion of $BaCeO_3$ fine inclusion was confirmed by SEM-EDX.

• 한국세라믹학회지
• /
• 제26권2호
• /
• pp.221-227
• /
• 1989

To investigate the development and densification YBa2Cu3O7-x(1-2-3) superconducting phase, the 1-2-3 phase powders have been prepared by citrate and nitrate processes with changing calcination temperature. Nearly pure 1-2-3 phase peaks have been obtained by calcining the precursor in air at 90$0^{\circ}C$ for 2.5h in citrate process but at 95$0^{\circ}C$ for 2.5h in nitrate process. The sintering density of citrate derived sample calcined at 80$0^{\circ}C$ has been about 4% higher than that calcined at 90$0^{\circ}C$, although the compacting density has been lower at 80$0^{\circ}C$ calcination. This can be explained that the 1-2-3 phase particles formed at 80$0^{\circ}C$ have reactive sub-micron size which has good sinterbililty.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1997년도 추계학술대회 논문집
• /
• pp.298-301
• /
• 1997

This paper describes the thermally stimulated current(TSC) measurements arachidic acid(AA) and polyamic acid alkylamine salts(PAAS) LB film, which is a precursor of polyimide(PI). The measurements were performed from room temperature to about 250$^{\circ}C$ and the temperature was increased at a rate of 0.02 $^{\circ}C$/s linearly[4]. It shows that peaks of TSC are observed at about 80$^{\circ}C$ in the arachidic acid and about 80$^{\circ}C$, 160$^{\circ}C$ in the PAAS LB films. The DSC and TGA of PAAS, arachidic acid are measure. Monolayer phases on the water subphase such as Langmuir(L) films and the phase transitions from gas phase to solid phase via liquid phase are observed using Brewster angle microscopy(BAM). BAM is also used to observe the Langemuir-Blodgett(LB) films.