• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.301-308
• /
• 2003

Glass-infiltrated alumina, which can be used as an all-ceramic dental crown, was prepared. The glasses in the system of SiO$_2$-B$_2$O$_3$-Al$_2$O$_3$-CaO-La$_2$O$_3$with various amount of $Al_2$O$_3$infiltrated into a porous sintered alumina. The effect of $Al_2$O$_3$on the infiltration characteristics and its mechanical strength were studied. The corrosion of the sintered alumina by infiltrated glasses was prevented by increasing the amount of $Al_2$O$_3$in the glass batches, this increased the bending strength of the glass infiltrated alumina composite. The crack like voids in the sintered alumina was a cause of the deteriorating the mechanical strength of the composite, and this can be eliminated by sintering the alumina at 130$0^{\circ}C$. Glass infiltration under the vacuum atmosphere enhanced the hording strength of the composite up to 453$\pm$31 MPa.

• Membrane Journal
• /
• v.10 no.4
• /
• pp.186-191
• /
• 2000

The recovery of three ethyl esters (aroma model compounds; ethyl acetate, ethyl propionate. ethyl butyrate) from aqueous solutions was studied for vapor permeation with surface-modified hydrophobic alumina membrane, Although the driving force of ethyl butyrate is the highest, the ethyl butyrate concentration in permeate is lower than those of propionate and acetate. Since the solubility of aroma compounds for water is very low, phase separation occurred in permeate, and we could obtain pure ethyl esters. The experimental results showed that the porous hydrophobic alumina membrane had high selectivity and permeation flux on the ester-model compounds.

• Journal of the Korean Ceramic Society
• /
• v.39 no.11
• /
• pp.1011-1016
• /
• 2002

Colloidal particles of silica (100 nm in size) were electrostatically dispersed and adsorbed on a glass substrate coated with silica sol or alumina sol. Stability of the suspensions and microstructure of the adsorbed particle layers were discussed in terms of total potential energies between the particles and the substrate. Well-dispersed suspension resulted in a layer with densely packed and regularly arranged particles, whereas less stable suspension resulted in a porous layer with loosely packed and irregularly arranged particles. Despite repulsive interactions between the particles and the substrate coated with silica sol, the observed adsorption can be attributed to chemical bonds formed at the interface between the particle and silica sol. In contrast, the adsorption of the particles on the substrate coated with alumina sol formed a layer with strongly adhered and densely packed particles, due to large attractive interactions between the particles and alumina sol.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2006.04a
• /
• pp.148-148
• /
• 2006

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.69.2-69
• /
• 2003

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.50.1-50
• /
• 2002

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.86.2-86
• /
• 2003

• Journal of the Korean Ceramic Society
• /
• v.41 no.12 s.271
• /
• pp.939-945
• /
• 2004

Glasses of $SiO_2-B_{2}O_3-Al_{2}O_3-CaO-La_{2}O_3$ with various amounts of $La_{2}O_3$ were infiltrated into a porous alumina to make an alumina-glass composite. The infiltration characterization and bending strength of the composite were examined in terms of glass composition. $La_{2}O_3$ in the glass decreased the high temperature viscosity and this enhanced the wetting behaviour of this glass to alumina, and made glass infiltration easier. The infiltrated glass dissolved the alumina skeleton, and $Al_{2}O_3$ component in the glass melt reprecipitated on the alumina. The grain growth occurred to a specific crystal direction. The glass containing $20mole\%$ of $La_{2}O_3$ was crystallized after infiltration, and this enhanced the bending strength of the composite.

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.70-78
• /
• 1997

3Y-TZP/SUS316 Functionally Graded Material (FGM) was fabricated by slip casting method. Alumina mold was used to overcome problems of gypsum mold in slip casting process, and the optimal dispersion con-ditions of 3Y-TZP/SUS316 binary slurries was determined using electrokinetic sonic amplitude and a viscometer, and observing sedimentation behavior. The properties of the specimens casted by gypsum mold and alumina mold were compared in terms of changes in shrinkage rate, drying and sintering conditions, and microstructure. It was found that the specimens obtaine from the alumina mold showed a clean surface, easier thickness control of each layer, and higher productivity. Especially, no degradation was observed in the SUS316 prepared using alumina mold. Thus it is desirable to use porous alumina mold rather than gyp-sum mold for the slip casting of 3Y-TZP/SUS316-FGM.

• Journal of Environmental Science International
• /
• v.9 no.4
• /
• pp.311-318
• /
• 2000

To improve $CO_2$pemselectivity, a modified silica membrane was prepared by chemical vapor deposition with tetraethoxysilane(TEOS)-ethanol-water, and TEOS-ethanol-water-HCI solution at 300-$600^{\circ}C$. The silica was effectively deposited in the mesopores of a ${\gamma}$-alumina film coated on a porous $\alpha$-alumina tube by evacuating the reactants through the porous wall. In this membrane, $CO_2$interacts, to some extent, with the pore wall, and $CO_2$/$N_2$selectivity then exceeds the value of the Knudsen diffusion mechanism, while the membrane derived from TEOS alone has no $CO_2$selectivity. The silica membrane prepared from TEOS-ethanol-water-HCI solution showed that $CO_2$permeance was $2.5$\times$10^{-7}mol/s^{-1}.m^{-2}.Pa^{-1} at 30{\circ}C$ and $CO_2$/$N_2$selectivity was approximately 3. The $CO_2$permeance and selectivity was improved by enlarging the surface diffusion with modification of chemical affinity of the silica pores.