• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.6
• /
• pp.1056-1063
• /
• 2006

Thermal evaporated 10 nm-Ni/l nm-Ir/(or polycrystalline)p-Si(100) and 10 nm-$Ni_{50}Co_{50}$/(or polycrystalline)p-Si(100) films were thermally annealed using rapid thermal annealing fur 40 sec at $300{\sim}1200^{\circ}C$. The annealed bilayer structure developed into Ni(Ir or Co)Si and resulting changes in sheet resistance, microstructure, phase and composition were investigated using a four-point probe, a scanning electron microscopy, a field ion beam, an X-ray diffractometer and an Auger electron spectroscope. The final thickness of Ir- and Co-inserted nickel silicides on single crystal silicon was approximately 20$\sim$40 nm and maintained its sheet resistance below 20 $\Omega$/sq. after the silicidation annealing at $1000^{\circ}C$. The ones on polysilicon had thickness of 20$\sim$55 nm and remained low resistance up to $850^{\circ}C$. A possible reason fur the improved thermal stability of the silicides formed on single crystal silicon substrate is the role of Ir and Co in preventing $NiSi_2$ transformation. Ir and Co also improved thermal stability of silicides formed on polysilicon substrate, but this enhancement was lessened due to the formation of high resistant phases and also a result of silicon mixing during high temperature diffusion. Ir-inserted nickel silicides showed surface roughness below 3 nm, which is appropriate for nano process. In conclusion, the proposed Ir- and Co- inserted nickel silicides may be superior over the conventional nickel monosilicides due to improved thermal stability.

• Journal of the Microelectronics and Packaging Society
• /
• v.13 no.1 s.38
• /
• pp.1-5
• /
• 2006

We prepared 80 nm-thick TiSix on each 70 nm-thick amorphous silicon and polysilicon substrate using an RF sputtering with $TiSi_2$ target. TiSix composite silicide layers were stabilized by rapid thermal annealing(RTA) of $800^{\circ}C$ for 20 seconds. Line width of $0.5{\mu}m$ patterns were embodied by photolithography and dry etching process, then each additional annealing process at $750^{\circ}C\;and\;850^{\circ}C$ for 3 hours was executed. We investigated the change of sheet resistance with a four-point probe, and cross sectional microstructure with a field emission scanning electron microscope(FE-SEM) and transmission electron microscope(TEM), respectively. We observe an abrupt change of resistivity and voids at the silicide surface due to interdiffusion of silicide and composite titanium silicide in the amorphous substrates with additional $850^{\circ}C$ annealing. Our result implies that the electrical resistance of composite titanium silicide may be tunned by employing appropriate substrates and annealing condition.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.8 no.1
• /
• pp.25-32
• /
• 2007

We investigated the silicide reaction stability between 10 nm-Col-xNix alloy films and silicon substrates with the existence of 4 nm-thick natural oxide layers. We thermally evaporated 10 nm-Col-xNix alloy films by varying $x=0.1{\sim}0.9$ on naturally oxidized single crystal and 70 nm-thick polycrystalline silicon substrates. The films structures were annealed by rapid thermal annealing (RTA) from $600^{\circ}C$ to $1100^{\circ}C$ for 40 seconds with the purpose of silicidation. After the removal of residual metallic residue with sulfuric acid, the sheet resistance, microstructure, composition, and surface roughness were investigated using a four-point probe, a field emission scanning electron microscope, a field ion bean4 an X-ray diffractometer, and an Auger electron depth profiling spectroscope, respectively, to confirm the silicide reaction. The residual stress of silicon substrate was also analyzed using a micro-Raman spectrometer We report that the silicide reaction does not occur if natural oxides are present. Metallic oxide residues may be present on a polysilicon substrate at high silicidation temperatures. Huge residual stress is possible on a single crystal silicon substrate at high temperature, and these may result in micro-pinholes. Our results imply that the natural oxide layer removal process is of importance to ensure the successful completion of the silicide process with CoNi alloy films.