• Analytical Science and Technology
• /
• v.17 no.1
• /
• pp.60-68
• /
• 2004

The core-shell polyolefin nonwovon fabric (PNF), wherein the PNF comprises at least about 60% of polyethylene having a melting temperature at ${\sim}132^{\circ}C$ and no more than about 40% of second polypropylene having a lower melting temperature at ${\sim}162^{\circ}C$. The sulfonic acid group for battery separators were prepared by radiation-induced grafting of styrene onto PNF and by the subsequent sulfonation of polystyrene graft chains. The sulfonated PNF was characterized by XPS, SEM, DSC, TGA and porosimeter. The electrochemical properties such as electrolyte retension, electrical resistance, and transport number of the $K^+ions$ were evaluated after sulfonation. It was found that the electrolyte retension increased, whereas the electrical resistance decreased with increasing sulfonic acid content. The transport number of $K^+$ in PNF with sulfonic acid of 0.22 ~ 3.60 mmol/g was to be 0.90 ~ 0.93.

• Proceedings of the Membrane Society of Korea Conference
• /
• 2004.11a
• /
• pp.199-203
• /
• 2004

Fibrous arsenic (As) adsorbent was synthesized by loading zirconium (Zr) on fibrous phosphoric adsorbent that was directly synthesized by radiation-induced graft polymerization of 2-hydroxyethyl methacrylate phosphoric acid on polyethylene-coated polypropylene nonwoven fabric. Zirconium reacted with phosphoric acid grafted in the polyethylene layer. Zirconium density of the resulting adsorbent was 4.1 mmol/g. The breakthrough curve of As(V) adsorption was independent of the flow rate up to $1300\;h^{-1}$ in space velocity. The total capacity of As(V) was 2.0 mmol/g-adsorbent at pH of 2. The adsorbed Zr(IV) could be evaluated by 0.4 M sodium hydroxide solution because negligible Zr(IV) could be found in the eluted solution.

• Textile Coloration and Finishing
• /
• v.21 no.6
• /
• pp.22-28
• /
• 2009

Oil-absorbable nonwovens were produced by melt-blown processing of polypropylene chips. The melt-blown processing conditions, such as air pressure, and gear pump speed, DCD. In this study, these three factors were chosen to produce samples. Experimental array and variance analysis of the design of experiment were used to increase the field repeatability and universality. The effect of the factors on oil absorption properties of melt-blown nonwoven fabric such as oil absorbency were evaluated. As a result, the fiber diameter decreased as gearpump speed decreased or air pressure increased. The oil absorbency increased as air pressure increased or gearpump speed decreased and with the DCD increasing the oil absorbency significantly increased.

• Journal of Fashion Business
• /
• v.6 no.1
• /
• pp.20-30
• /
• 2002

The purpose of this study was to provide the basic informations of disposable medical clothes and develop new disposable medical clothes which are not caused environmental pollutions. The staffs of Yuhan-Kimberly and doctors, nurses and personnel of four general hospitals in Seoul were interviewed individually in order to collect useful data of disposable clothes. Also the samples of disposable medical clothes were examined. The materials, designs, size of potential market and actual consumption conditions of disposable medical clothes were found out. New disposable medical clothes were made after having considered all the aspects examined above. Two kind of medical gowns and caps, a kind of medical apron, three kinds of patient robes and a kind of patient cap were made of Korean traditional paper with specific functions instead of nonwoven polypropylene fabric.

• Current Research on Agriculture and Life Sciences
• /
• v.28
• /
• pp.47-52
• /
• 2010

This study was carried out to investigate the availability of covering material used for raising seedlings in the rice nursery bed. The pre-germinated seeds of a rice cultivar 'Chilbo' were sown into seedling tray ($60{\times}30{\times}2.5cm$) on 20th April and 3rd May 2010. Polypropylene spunbonded fabric (PSF) and lagging were used for covering materials in rice nursery bed. The growth characteristics of seedlings were evaluated at 8, 15 and 25 days after sowing (DAS) in the nursery beds covered with PSF and lagging, respectively. The plant height of 8-day old seedlings grown in lagging nursery bed was longer by 2cm than those in PSF nursery bed when the seeds were sown on 20th April, but seedling quality grown in lagging nursery bed was poor compared with that in PSF nursery bed. The growth characteristics of 15-day old seedlings were similar to that of 8-day old seedlings. The plant height of 8, 15 and 25-day old seedlings grown in lagging nursery was longer than those in PSF nursery when the seeds were sown on 3rd May. The seedling quality grown in PSF nursery was better than that in lagging nursery. The seedlings grown in PSF nursery have more leaves and better seedling quality compared with that of lagging nursery. The seedling quality was remarkably decreased with the increase of nursery period in lagging bed but seedlings quality were recovered at 5 days after hardening treatment by removing the lagging.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.30 no.6 s.154
• /
• pp.981-991
• /
• 2006

The purpose of this study was to determine the practicability of an experimental protective clothing by identifying the human body's physiological responses to it as well as the human body's comfort level when wearing it, particularly with the use of a processed charcoal material. The experimental protective clothing came in two types: one whose outer side made use of polypropylene film, and the inner side, a non-woven rayon fabric; and one whose inner side made use of a non-woven fabric processed with charcoal with a 10% density. Experiments were conducted on five healthy adult women whose average age was 21. These experiments were conducted at a climatic chamber, in which the temperature and relative humidity were set below $28{\pm}1^{\circ}C\;and\;50{\pm}10%$, respectively, and were measured within a period of 60min, consisting of a 20-min rest period, a 20-min exercise period, and a 20-min recovery period. Based on the results of this study, the efficiency of the processed charcoal material was reviewed, and a database requiring the production of more functional and comfortable protective clothing materials was established.

• Environmental Engineering Research
• /
• v.23 no.3
• /
• pp.330-338
• /
• 2018

This study investigated the possibility of using potassium titanate oxide ($K_2Ti_4O_9$) and acrylic acid-grafted polypropylene fabric (PP-g-AA) as adsorbents capable of removing strontium from aqueous solutions. $K_2Ti_4O_9$ showed the highest rate of strontium removal in the weak alkaline range, while the PP-g-AA increased strontium removal in the neutral range. Moreover, the adsorption capacity of the $K_2Ti_4O_9$ was not affected by the coexistence of K and Na ions, while the adsorption capacity decreased when Ca and Mg ions were present at the same concentration as that of strontium. When coexisted at the same concentration as strontium, Na, K, Ca, and Mg ions strongly reduced the adsorption capacity of the PP-g-AA. The results also indicated that the adsorption of strontium on $K_2Ti_4O_9$ was consistent with both the Langmuir and Freundlich adsorption isotherms. In contrast, the adsorption of strontium on the PP-g-AA was more consistent with the Langmuir isotherm model. Moreover, the adsorption equilibrium time of $K_2Ti_4O_9$ was generally 12 h, while that of the PP-g-AA was 5 h, indicating that the adsorption rates were consistent with the pseudo-second order kinetics model. $K_2Ti_4O_9$ and the PP-g-AA could be regenerated by simple washing with 0.5 N HCl.

• Polymer(Korea)
• /
• v.32 no.6
• /
• pp.509-515
• /
• 2008

The aminated polypropylene melt blown ion exchange fibers were synthesized with acrylic acid monomer onto polypropylene melt blown fibers by radiation-induced polymerization and subsequent amination. Degree of grafting was increased with increasing the acrylic acid monomer concentration and total dose. The highest degree of grafting was obtained 140% at a monomer concentration of 20 v/v% acrylic acid and total dose of 4 kGy. Optimum condition of Mohr's salt was 5.0 $\times10^{-3}$ M. Degree of amination was increased with increasing degree of grafting. Water content was about 1.5 times higher than that of trunk polymer. The maximum ion-exchange capacity was 7.3 meq/g which was 2$\sim$3 times higher than a commercial ion exchange fiber. The average pore size was decreased and BET surface area was increased in order of PPmb, PPmb- g- AAc and APPmb- g- AAc. The average pore size and BET surface area of synthesised fibers were $366.1\;{\AA},\;3.71m^2/g,\;143.3\;{\AA},\;4.94m^2/g,\;40.97\;{\AA},\;8.98m^2/g$, respectively.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.24 no.8
• /
• pp.1115-1124
• /
• 2000

The purpose of this study was 1) to determine physical properties, and subjective evaluation of sensation of sports socks with various type of fiber content and fabric structure, and 2) to develop regression equations for predicting each sensation from physical properties of socks. Thirty healthy male students participated in the wear test with ten replications. The ANOVA, Duncans multiple test, and multiple regression, and paired-t test were used in the statistical analysis, using an SAS package. The results of this study are as follows: 1. 100% cotton socks had higher absorbency and wickability among five different socks. Comfort sensation, tactile sensation and fit sensation of socks were significantly influenced by types of fiber content. People felt that polypropylene socks were less comfortable & slightly tighter, and cotton socks were drier than the other socks. Terry socks were warmer than single jersey socks. 2. The results of the regression analysis showed that tactile sensation of socks after exercise can be predicted from the cube of moisture permeability($R^2$=0.99), and fit sensation can be predicted from drop absorbency, moisture permeability, wickability in wale and weight($R^2$=-0.98).

• Textile Coloration and Finishing
• /
• v.30 no.2
• /
• pp.90-97
• /
• 2018

Hydrophilic reactive hot-melt polyurethane adhesive(HRHA) using a hydrophilic polyol having different molecular weight and NCO index was synthesized. This HRHA was synthesized using Polyethylene glycol(PEG) as a hydrophilic polyol, Polypropylene glycol(PPG) and Polycaprolactone diol(PCL) as hydrophobic polyols, and Methylene diphenyl diisocyanate(MDI) as an isocyanate. The changes in IR spectrum, viscosity and thermal properties of HRHA with different PEG molecular weights and NCO index were investigated, and the tensile strength and elongation of the HRHA casting film and the peel strength, moisture permeability and water pressure of the HRHA coated fabric were confirmed. In this experiment, as the molecular weight of PEG and NCO index increased, the adhesive strength, tensile strength, elongation and moisture permeability was increased but viscosity and Tg was decreased.