• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.212-213
• /
• 2006

Polymer thick film resistor paste was fabricated using various materials. Inorganic materials of carbon black and graphite were selected as fillers and epoxy resin was selected as organic material. Solvent with high boiling temperature was applied to adjust viscosity. A designed test coupon pattern was used to evaluate fabricated resistors. Aspect ratio of 1 was selected for evaluating resistor values. Electrical properties of fabricated resistors were measured and their values analyzed in relation to paste composition. PTF fabricated using carbon black as fillers achieved resistor value of $530{\Omega}/sq$.

• Journal of Industrial and Engineering Chemistry
• /
• v.68
• /
• pp.209-219
• /
• 2018

Colloidally stable organic-inorganic (O-I) hybrid nanoparticles could be prepared using an alkoxysilanefunctionalized amphiphilic polymer (AFAP) precursor. O-I hybrid sols could maintain colloidal stability for six months even at 45% solid content and be coated onto glass as well as PET film to form transparent O-I hybrid films. The formation of O-I hybrid nanoparticles dispersed in cured coating films could be confirmed using scanning electron microscopy. The cured coating film showed 3H and 5H pencil hardness on PET and glass, respectively. Nanoindentation measurements also showed that their modulus and hardness was varied with the type of AFAP used in its preparation.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1999.10b
• /
• pp.41-44
• /
• 1999

• Fibers and Polymers
• /
• v.6 no.3
• /
• pp.200-205
• /
• 2005

Celite powder surface-modified with cationic surfactant was used to make polyethylene (PE) specialty film that can be contrasted with ordinary film in having high odor storing capacity and long odor lasting period. Mechanical properties of the films were sacrificed as more celite particles were included, whether celite surface was modified or not. The film with CTAS-modified celite showed the best odor storing and lasting properties for five different flavors of odor, three artificial and two natural ones, among the kinds of films developed. Comparisons among the different films are made, together with brief discussion about the reason for differences in odor lasting period and possible application to packaging industry.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.4
• /
• pp.297-302
• /
• 2009

We have successfully fabricated the alumina thick films using inkjet printing processes without a high temperature sintering process. Alumina suspension as dielectric ink was formulated by combining nano-sized alumina powders with an anionic polymer dispersant in formamide/water as co-solvent. The thickness of the printed alumina thick film was measured at around 5 um by field emission scanning electron microscope. The calculated packing density of 68.5 % from the printed alumina thick film was much higher than the same films fabricated by conventional casting or dip coating processes. Q factor of the dielectrics thick film infiltrated with cyanate ester resin was evaluated by impedance analyzer.

• Transactions of the Korean Society for Noise and Vibration Engineering
• /
• v.15 no.2 s.95
• /
• pp.239-247
• /
• 2005

This paper deals with the development of a contact-type counting device using a piezoelectric polymer film as a sensor. The piezoelectric and vibration characteristics of the film under a bending vibration were investigated theoretically and experimentally. A counting device, which includes filters, an amplifier, an analog-digital converter, and a display, was designed and fabricated. The performance of the piezoelectric polymer sensor was evaluated in the sense of the responses to contact force, contact frequency, and contact speed. The life and the temperature effect were also investigated for the piezoelectric film sensor.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.877-878
• /
• 2009

To realize the flexible audible display (FAD), polymer dispersed liquid crystal(PDLC) is deposited on PVDF(Poly-vinylidene fluoride) film with piezoelectric property. With applied audio signal, it makes sound more than 70 dB in 700 Hz-10kHz. In case of transparency it is opaque and transmittance is less than 10% at 550nm wavelength without bias voltage. It is turned to be transparent and show transmittance of 66% with driving voltage of 60V.

• Journal of Integrative Natural Science
• /
• v.6 no.4
• /
• pp.211-214
• /
• 2013

In this study, in order to investigate how consecutive treatments of glass surface with HF acid and water vapor/Ar plasma affect the quality of 3-aminopropyltriethoxysilane self-assembled monolayer (APS-SAM), poly(3,4-ethylenedioxythiophene) (PEDOT) thin films were vapor phase-polymerized immediately after spin coating of FeCl3 and poly-urethane diol-mixed oxidant solution on the monolayer surfaces prepared at various treatment conditions. For the film characterization, various poweful tools were used, e.g., FE-SEM, an optical microscope, four point probe, and a contact angle analyzer. The characterization revealed that HF treatment is not desirable for the synthesis of a high quality PEDOT thin film via vapor phase polymerization method. Rather, sole treatment with plasma noticeably improved the quality of APS-SAM on glass surface. As a result, a highly dense and smooth PEDOT thin film was grown on uniform oxidant film-coated APS monolayer surface.

• Tribology and Lubricants
• /
• v.25 no.2
• /
• pp.86-95
• /
• 2009

Adhesion tests were carried out in order to investigate the effect of temperature on the adhesion behavior between a PMMA film and a fused silica lens in the micro scale. For the tests, a microtribometer system was specially designed and constructed. The pull-off forces on the PMMA film were measured under atmospheric condition as the temperature of the PMMA film was increased from 300 K to 443 K and decreased to 300 K. The contact area between the PMMA film and the lens was observed during the test. The adhesion behavior was changed with the change of the PMMA surface state as the temperature increased. In glassy state below 363 K, the pull-off force did not change with the increase of temperature. In rubbery state from 383 K to 413 K, the pull-off force increased greatly as the temperature increased. In addition, the area of contact was enlarged. In viscous state above 423 K, the fingering instability was observed in the area of contact when the PMMA film contacted with the lens. It was also found that the adhesion behavior can be varied with the thermal history of the PMMA film. The residual solvent in the PMMA film could emerge to the PMMA surface due to the heating and reduced the pull-off force.

• Polymer(Korea)
• /
• v.38 no.6
• /
• pp.702-707
• /
• 2014

Corneal endothelium is mono-inner cell layer of cornea and lay on Descmet's membrane which comprised of various proteins called extracellular matrix such as fibronectin, collagen, laminin, and proteoglycan, etc. In this study, we fabricated transparent poly(lactic-co-glycolic acid) (PLGA) film because PLGA is widely used for tissue engineering based on their properties. We investigated the behaviors of rabbit corneal endothelial cells (rCEnCs) on PLGA film surfaces coated with various cell-adhesive molecules like fibronectin, laminin, collagen type I and IV and FNC coating mix. The morphologic images, proliferation and adhesion assay, immunofluorescence for ZO-1 and $Na^+/K^+-ATPase$ and RT-PCR for expression of specific markers were conducted. These results showed that PLGA film plays a role as CEnC carriers in vitro and the cell-adhesive molecules give positive effects on the behaviors of rCEnC.