• 한국응용과학기술학회지
• /
• 제27권2호
• /
• pp.216-221
• /
• 2010

Polyvinyl acetate (PVAc) prepared by emulsion polymerization has broad applications for additive such as paint binder, adhesive for wood and paper due to its low glass transition temperature which help to plasticize substrate resins. Since emulsion polymerization has a disadvantage that surfactant and ionic initiator degrade properties of the product polymer, poly (vinyl acetate-eo-ethyl acrylate) (VAc-EA) was synthesized using potassium persulfate as catalyst and polyvinylalcohol (PVA) as protective colloid to prevent the degradation. The copolymer latex product was internally plasticized and has enhanced adhesion, water resistance during VAc-EA emulsion polymerization. No coagulation and complete conversion occur with the reactant mixture of 10 mmol/L potassium persulfate, 10 mmol/L poly ( vinyl alcohol) (PVA 17). As the concentrations of PVA increase, the viscosity becomes increase.

• 한국염색가공학회:학술대회논문집
• /
• 한국염색가공학회 2003년도 춘계학술대회 논문집
• /
• pp.192-196
• /
• 2003

폴리비닐알코올[poly(vinyl alcohol)(PVA)]은 1924년에 Herrmann과 Haehnel이 폴리아세트산비닐[(poly(vinyl acetate)(PVAc)]의 비누화 도중 처음 합성되었으며, 2차 세계대전 이후 일본에서 비닐론 섬유용 수지로 상업화되기 시작했다. PVAc의 비누화로부터 제조되는 PVA는 흰색의 분말상 고분자로 필름 및 섬유의 형성이 용이하고 표면 활성도가 높으며, 기계적 성질 및 접착 강도가 높고, 용해도와 화학적 반응성이 우수하다. (중략)

• 멤브레인
• /
• 제24권4호
• /
• pp.276-284
• /
• 2014

본 연구에서는 소수성 PVDF막 표면에 중성 친수성 고분자인 Poly(vinyl alcohol) (PVA)를 코팅한 후 순수 투과도를 측정하고 대표적인 단백질 오염물질인 bovin serum albumin (BSA)에 대하여 파울링 실험을 수행하였다. BSA 용액 20 ppm 조건에서 파울링 실험을 수행한 결과, 코팅 전 막에 비하여 순수 투과도는 감소하였지만 내오염성은 현저히 증가됨을 알 수 있었다. 코팅된 PVA의 분자량이 커질수록 순수 투과도는 감소하였으나, 내오염성이 증가하는 경향을 보였다. 또한, 코팅된 PVA의 농도가 높아질수록 순수 투과도는 감소하였고, 내오염성이 증가하였다. 이는 접촉각과 AFM 측정 결과와 관련하여 코팅 후 막 표면에 친수성의 증가와 거칠기가 감소했기 때문으로 여겨진다.

• 멤브레인
• /
• 제16권3호
• /
• pp.235-239
• /
• 2006

본 연구는 poly(vinyl alcohol) (PVA)와 가교제 poly(strene sulfonic acid-co-maleic acid) (PSSA-MA)을 이용하여 제조된 막을 물/에탄올 계에 대한 투과증발 실험을 25, 35 및 45$^{\circ}C$에서 수행하였다. 가교제의 함량은 7, 9, 11 wt.%를 사용하였으며, 원액의 조성은 무게비로 물 50, 20, 10 및 공비점인 4.4%에 대하여 조사하였다. 일반적인 투과증발 결과와 마찬가지로 가교제 함량의 증가 및 조업온도 증가에 따라 투과도 및 선택도에 대한 대표적 경향을 보여 주었다. 물 : 에탄올 = 10 : 90 조성에서 그리고 $45^{\circ}C$에서 선택도 12003와 투과도 $58.92g/m^2{\cdot}hr$를 PSSA-MA 11 wt%의 막이 보여 주었다.

• 공업화학
• /
• 제9권4호
• /
• pp.469-474
• /
• 1998

스티렌-무수말레인산 공중합체로 가교된 PVA막을 용액법으로 제조하였다. 투과증발공정에서 가교된 PVA/ PSMAn막에 대한 분리거동을 연구하기 위해 30~90 wt % 에탄올-물 혼합 조성에서 막에 대한 팽윤 및 수착 실험을 막내부로 수착되는 용액의 양과 조성을 측정할 수 있는 장치를 이용하여 수행하였다. 본 연구에서 제조된 막의 경우, 수착과 투과단계에서 물에 대해 좋은 선택성을 나타냈고, 공급액의 농도 50 wt % 이상에서 막의 투과선택도는 가교제의 함량에 따른 팽윤비 변화보다 수착선택도와 보다 많은 상관 관계를 나타내었다. 이러한 거동을 투과 선택도와 수착선택도과 관련된 용해-확산 모델로 고찰한 결과, 투과선택도는 막 내에서의 확산단계에서 보다 오히려 수착단계에서 결정됨을 결론지을 수 있다.

• 방사선산업학회지
• /
• 제5권2호
• /
• pp.119-124
• /
• 2011

Silver nano-particles (AgNPs) have attracted much attention for centuries due to their unique optical properties, electrical conductivities, oxidative catalysis, and antibacterial effect. In this study, AgNPs have been prepared by using aqueous $AgNO_3$ solution in the poly(vinyl alcohol) (PVA)/poly(ethylene glycol) (PEG) hydrogels. PVA and PEG powders were dissolved in deionized water, and then irradiated by a gamma-ray with a radiation dose of 50 kGy to make hydrogels. PVA/PEG hydrogels were dipped into $1.0{\times}10^{-2}M$ $AgNO_3$ solution for 1 hour. After that, the swollen hydrogels were irradiated by gamma-ray for the formation of AgNPs. FE-SEM is used to observe the formation of AgNPs as a function of the content of PEG and the irradiation dose. Also, AgNPs in the PVA/PEG hydrogels were monitored by UV-Vis. It is observed that the content of PEG and gamma-ray irradiation in the hydrogel is crucial to the formation of AgNPs. Finally, antibacterial tests indiacted that the hydrogel containing silver nanoparticle has antibacterial activity.

• 폴리머
• /
• 제30권6호
• /
• pp.545-549
• /
• 2006

폴리(비닐 알코올) (PVA)과 폴리아크릴산-말레산-공중합체(PAM)의 블렌드를 수용액 상태로 얻은 후 점토인 사포나이트(SPT)를 분간시켜 필름 형태인 PVA/PAM/SPT의 나노복합재료를 합성하였다. 용액 삽입법을 이용하여 점토 함량을 0-9 wt%의 다양한 농도로 변화시켜 얻은 나노복합재료에 대해 분산도, 모폴로지 및 열적-기계적 성질 등을 각각 조사하였다. 점토 함량이 3 wt%일 때 점토 입자는 PVA/PAM 블렌드에 잘 분산되었으며, 점토함량이 7 wt%보다 많을 경우에는 고분자 모체에 일부 뭉친 구조가 관찰되었다. 나노복합재료의 열적 안정성은 점토함량이 9 wt%로 증가할 때까지 꾸준히 증가하였다. 인장 강도와 초기인장 탄성률은 점토 함량이 7 wt%일 때 최고값을 나타내었으나 그 이상의 점토 농도에서는 오히려 감소하였다. 본 연구 결과로부터 소량의 점토 첨가는 PVA/PAM 나노복합재료 필름의 열적, 기계적 성질을 증가시키는데 도움이 된다는 것을 알았다.

• 한국인쇄학회지
• /
• 제16권2호
• /
• pp.61-74
• /
• 1998

Some photopolymer, poly(vinyl cinnamoyl acetate)(PVCiA) was synthesized by esterification of polymer(vinyl alcohol)(PVA) with monochloroacetic acid, followed by reaction poly(vinyl monochloroacetate)(PVAhA) and potassium cinnamate. When esterification of PVA with monochloroacetic acid was reacted in the dimethyl sulfoxide(DMSO), in the synthesis of PVChA, it is very good yield and the successive cinnamoyl acetoxyl esterification of PVCiA can be successfully synthesized. But PVCiA is low photosensitive polymer if net added photosensitizing dyes. Here, we synthesized photosensitizing dyes.

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 2003년도 가을 학술발표회 논문집
• /
• pp.52-54
• /
• 2003

Poly(vinyl alcohol) (PVA) obtained by the saponification of poly(vinyl ester) is a linear semicrystalline polymer; these polymers have been widely used as fibers for clothes and industries, binders, films, membranes, medicines for drug delivery system, and cancer cell-killing embolic materials. PVA fibers have high tensile and compressive strength, tensile modulus, and abrasion resistance because of the highest crystalline lattice modulus. (omitted)

• Fibers and Polymers
• /
• 제3권2호
• /
• pp.73-79
• /
• 2002

Nanoscaled PVA fibers were prepared by electrospinning. This paper described the electrospinning process, the processing conditions fiber morphology, and some potential applications of the PVA nato-fibers. PVA fibers with various diameters (50-250 nm) were obtained by changing solution concentration, voltage and tip to collector distance (TCD). The major factor was the concentration of PVA solution which affected the fiber diameter evidently. Increasing the concentration, the fiber diameter was increased, and the amount of beads was reduced even to 0%. The fibers were found be efficiently crosslinked by glyoxal during the curing process. Phosphoric acid was used as a catalyst activator to reduce strength losses during crosslinking. Scanning electron micrograph (SEM) and differential scanning calorimetric (DSC) techniques were employed to characterize the morphology and crosslinking of PVA fibers. It was fecund that the primary factor which affected the crosslinking density was the content of chemical crosslinking agent.