• 전기화학회지
• /
• 제2권1호
• /
• pp.38-45
• /
• 1999

Electrochemical lithium intercalation into a PECVD (plasma enhanced chemical vapour deposited) carbon film electrode was investigated in 1 M $LiPF_6-EC$ (ethylene carbonate) and DEC (diethyl carbonate) solution during lithium intercalation and deintercalation, by using cyclic voltammetry supplemented with ac-impedance spectroscopy. The size of the graphitic crystallite in the a- and c-axis directions obtained from the carbon film electrode was much smaller than those of the graphite one, indicating less-developed crystalline structure with hydrogen bonded to carbon, from the results of AES (Auger electron spectroscopy), powder XRD (X-ray diffraction) method, and FTIR(Fourier transform infra-red) spectroscopy. It was shown from the cyclic voltammograms and ac-impedance spectra of carbon film electrode that a threshold overpotential was needed to overcome an activation barrier to entrance of lithium into the carbon film electrode, such as the poor crystalline structure of the carbon film electrode showing disordered carbon and the presence of residual hydrogen in its structure. The experimental results were discussed in terms of the effect of host carbon structure on the lithium intercalation capability.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1994년도 추계학술대회 논문집
• /
• pp.171-174
• /
• 1994

The drive towards ultra-large-scale integrated circuits a continuous intermetal dielectric films for multi layer interconection. Optimum condition of remote plasma enhanced chemical vapour deposition(RPECVD) was achieved by orthogonal array method. Chracteristics of SiO$_2$ films deposited by using remote PECVD with N$_2$O gas were investigated. Etching rate of SiO$_2$ films in P-echant was about 6[A/s] that was the same as the thermal oxide. The films a showed high breakdown voltage of 7(MV/cm) and a resistivity of Bx10$\^$13/[$\Omega$cm] at 7(MV/cm). The interface Trap density of SiO$_2$ has been shown excel lent properties of 5x10$\^$10/[/$\textrm{cm}^2$eV]. It was observed that the dielectric constant dropped to a value of 4. 29 for 150 [W] RF power.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1992년도 추계학술대회 논문집
• /
• pp.22-27
• /
• 1992

Phosphorus doped hydrogenated microcrystalline silicon (${\mu}c$-Si:H) thin films were deposited by PECVD (Plasma Enhanced Chemical Vapour Deposition) method using 10.2% $SiH_4$ gas (diluted in Ar) and 308ppm $PH_3$ gas (diluted in Ar). The structural, optical and electrical properties of the films were investigated as a function of substrate temperature(15 to $400^{\circ}C$) and RF power(10 to 120W). The thin film deposited by varing substrate temperature had columnar structure and microcrystalline phase. The volume fraction of microcrystalline phase in the films deposited at RF power of 80W, increased with increasing substrate temperature up to $200^{\circ}C$, and then decreased with further increasing substrate temperature. Volume fraction of microcrystalline phase increased monotonously with increasing RF power at substrate temperature of $250^{\circ}C$. With increasing volume fraction of microcrystalline, electrical resistivity of films decreased to 0.274 ${\Omega}cm$.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 춘계학술대회 초록집
• /
• pp.63.2-63.2
• /
• 2010

삼중접합 태양전지에 상부전지로 이용되는 a-SiO:H 태양전지는 PECVD(Plasma Enhanced Chemical Vapour Deposition)을 이용하여 증착하였다. i a-SiO:H는 $CO_2/SiH_4$ 비율을 변화하여 밴드갭을 조절하였다. $CO_2/SiH_4$가 0에서 0.43으로 증가 할수록 밴드갭이 1.74 eV에서 1.94 eV로 증가하는 경향을 보였다. 이는 FTIR에서 나타난 결과인 Si-O-Si 결합의 증가 때문인 것으로 판단한다. 그에 반해서 광 전도도는 감소하는 경향을 보였다.그러나 암전도도와 광전도도의 비율인 광민감도는 $10^5$에서 $10^4$의 값으로 비정질 태양전지에 적용가능한 값을 보였다. 이러한 박막 특성을 가진 i a-SiO:H를 이용하여 비정질 실리콘 태양전지를 제작한 결과 $CO_2/SiH_4$의 비율이 증가함에 따라 태양전지의 $V_{oc}$가 0.8 V에서 0.5 V로 현저하게 감소하였고, $J_{sc}$와 FF 역시 11 $mA/cm^2$에서 4 $mA/cm^2$, 69%에서 50%로 감소하였다. 단위박막 결함을 측정하는 CPM(Constant Photocurrent Method)을 이용하여 i a-SiO:H 내부에 $10^{16}cm^{-3}$ 정도의 내부 결함을 관찰하였고 이는 태양전지의 특성 감소와 관련이 있는 것으로 판단한다.