• 전기학회논문지
• /
• 제57권5호
• /
• pp.808-815
• /
• 2008

The composites were fabricated 61[vol.%] ${\beta}$-SiC and 39[vol.%] $TiB_2$ powders with the liquid forming additives of 8, 12, 16[wt%] $Al_2O_3+Y_2O_3$ as a sintering aid by pressureless annealing at 1650[$^{\circ}C$] for 4 hours. The present study investigated the influence of the content of $Al_2O_3+Y_2O_3$ sintering additives on the microstructure, mechanical and electrical properties of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Reactions between SiC and transition metal $TiB_2$ were not observed in the microstructure and the phase analysis of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Phase analysis of SiC-$TiB_2$ composites by XRD revealed mostly of ${\alpha}$-SiC(6H), ${\beta}$-SiC(3C), $TiB_2$, and In Situ YAG($Al_2Y_3O_{12}$). The relative density of SiC-$TiB_2$ composites was lowered due to gaseous products of the result of reaction between SiC and $Al_2O_3+Y_2O_3$. There is another reason which pressureless annealed temperature 1650[$^{\circ}C$] is lower $300{\sim}450[^{\circ}C]$ than applied pressure sintering temperature $1950{\sim}2100[^{\circ}C]$. The relative density, the flexural strength, the Young's modulus and the Vicker's hardness showed the highest value of 82.29[%], 189.5[Mpa], 54.60[Gpa] and 2.84[Gpa] for SiC-$TiB_2$ composites added with 16[wt%] $Al_2O_3+Y_2O_3$ additives at room temperature. Abnormal grain growth takes place during phase transformation from ${\beta}$-SiC into ${\alpha}$-SiC was correlated with In Situ YAG phase by reaction between $Al_2O_3$ and $Y_2O_3$ additive during sintering. The electrical resistivity showed the lowest value of 0.0117[${\Omega}{\cdot}cm$] for 16[wt%] $Al_2O_3+Y_2O_3$ additives at 25[$^{\circ}C$]. The electrical resistivity was all negative temperature coefficient resistance (NTCR) in the temperature ranges from $25^{\circ}C$ to 700[$^{\circ}C$]. The resistance temperature coefficient of composite showed the lowest value of $-2.3{\times}10^{-3}[^{\circ}C]^{-1}$ for 16[wt%] additives in the temperature ranges from 25[$^{\circ}C$] to 100[$^{\circ}C$].

• 멤브레인
• /
• 제24권1호
• /
• pp.31-38
• /
• 2014

지붕이나 여러 가지 방법과 장소에서 수집된 빗물을 처리하면 직접적 간접적으로 유익하게 사용될 수 있다. 이러한 빗물은 점점 더 높은 품질을 위해 고려되고 있고, 분리막은 이러한 빗물 처리를 위한 중요한 기술이다. 특히, 분리막은 고품질 물 생산, 높은 집적도 및 낮은 에너지 소비 등의 장점이 있다. 그럼에도 불구하고, 막오염은 수처리 및 폐수 재활용 부분과 마찬가지로 심각한 문제로 간주되고 있다. 본 연구에서는 빗물 처리에 정밀여과(MF)막을 적용하였고, 저압 자외선(LPUV) 처리를 정밀여과막의 전처리로 사용하였다. 유기물에 대한 UV의 영향을 정량화하기 위해 총 유기탄소(TOC) 및 UV 흡광도(UVA)를 모두 측정하였다. 또한 UV 전처리 효과에 따른 막의 오염 정도를 조사하였다. LPUV 전처리를 하고 실험을 한 결과 조류에 의해 오염된 빗물에서 막의 오염을 제어하는데 효과적임을 알 수 있었으며, 이것은 UV 처리 후 유기물의 양이 감소하고 특성이 변화하기 때문이었다. 따라서 UV/MF 처리는 마이크로 워터 그리드 시스템과 같은 수처리를 위한 유망한 옵션이 될 수 있을 것으로 생각된다.

• 한국정보통신학회:학술대회논문집
• /
• 한국해양정보통신학회 2007년도 추계종합학술대회
• /
• pp.477-481
• /
• 2007

유비쿼터스 시대에 병원뿐만 아니라 가정과 요양 시설 내에서도 불규칙적이고 다양한 장소에서 발생하는 응급 환자는 신속한 처리가 이루어 져야 한다. 특히 노인 인구가 늘어나는 현${\cdot}$미래 시대에는 환자나 노인의 몸에 생체 신호 센서를 부착하여 환자의 상태를 실시간으로 모니터링 하여 환자나 노인의 몸에 이상이 생겼을 경우 실시간으로 대처하여 응급 환자에 대한 신속한 처리가 이루어지게 한다. 병원 내에서는 무선 네트워크 인프라를 최대한 이용하고 인프라를 보완하기 위해서는 근거리 무선 통신 프로토콜을 기반으로 하는 센서네트워크인 저 전력 지그비(ZigBee) 시스템을 활용한다. 전체적 시스템은 무선 통신망을 이용하고 심전도, 혈압, 혈당 그리고 체온 등의 바이오센서 모니터링을 위해 ZigBee(IEEE 802.15.4)를 이용하여 응급환자 및 노인 등의 이동시 생체신호를 모니터링 할 수 있게 한다. 본 논문에서는 환자 및 노인의 실시간 생체신호 전송 시스템을 구축하고 무선 센서 네트워크 구축 시 전송세션의 수와 노드 발생률에 따른 전송률 및 지연을 통해 그 효율성을 검증한다.

• 한국지리정보학회지
• /
• 제13권3호
• /
• pp.102-118
• /
• 2010

야산은 평지와 산지의 점이적인 지역이기 때문에 언제나 개발의 압력을 받고 있는 지역이다. 과거 야산은 산지에 비해 개발이 용이한 지역으로 인식되어 왔지만 이제는 산림 자원으로 인식하고 보전할 필요성도 있다. 현재 개간 현황 및 변화 과정에 대한 연구는 사례를 찾아보기 어렵다. 이에 본 연구에서는 시계열 자료를 활용하여 야산의 토지이용 변화를 정량적으로 파악하고자 하였다. 이를 위해 1915년, 1972년, 2002년, 2006년의 토지이용도를 작성하고 지리정보체계를 기반으로 공간분석을 수행하였다. 연구지역은 충청남도 당진군 면천면, 순성면, 합덕읍과 예산군 봉산면, 고덕면 경계 지역이며 야산의 총 면적은 3,034ha이다. 연구지역 야산의 산림 면적은 1915년~2006년 동안 50% 감소하였다. 2002년 이후 4년 사이의 산림 감소 면적은 그 이전 30년의 감소량과 비슷하다. 연구지역 야산의 산림감소는 논, 밭, 인공구조물, 나지 등 개간지의 증가로 이어졌다. 1915년부터 1980년대 말까지의 야산 개간은 1차 산업과 관련이 있으며, 그 이후의 야산 개간은 농공단지개발 등 2차 산업과 관련이 있다.

• Environmental Analysis Health and Toxicology
• /
• 제19권1호
• /
• pp.33-40
• /
• 2004

Benzoyl peroxide is a High Production Volume Chemical, which is produced about 1,371 tons/year in Korea as of 2001 survey. The substance is mainly used as initiators in polymerization, catalysts in the plastics industry, bleaching agents for flour and medication for acne vulgaris. In this study, Quantitative Structure-Activity Relationships (QSAR) are used for getting adequate information on the physical -chemical properties of this chemical. And hydrolysis in water, acute toxicity to aquatic and terrestrial organisms for benzoyl peroxide were studied. The physical -chemical properties of benzoyl peroxide were estimated as followed; vapor pressure=0.00929 Pa, Log $K_{ow}$ = 3.43, Henry's Law constant=3.54${\times}$10$^{-6}$ atm-㎥/mole at $25^{\circ}C$, the half-life of photodegradation=3 days and bioconcentration factor (BCF)=92. Hydrolysis half-life of benzoyl peroxide in water was 5.2 hr at pH 7 at $25^{\circ}C$ and according to the structure of this substance hydrolysis product was expected to benzoic acid. Benzoyl peroxide has toxic effects on the aquatic organisms. 72 hr-Er $C_{50}$ (growth rate) for algae was 0.44 mg/1.,48 hr-E $C_{50}$ for daphnia was 0.07mg/L and the 96hr-L $C_{50}$ of acute toxicity to fish was 0.24mg/L. Acute toxicity to terrestrial organisms (earth worm) of benzoyl peroxide was low (14 day-L $C_{50}$ = > 1,000 mg/kg). Although benzoyl peroxide is high toxic to aquatic organisms, the substance if not bioaccumulated because of the rapid removal by hydrolysis (half-life=5.2 hr at pH 7 at $25^{\circ}C$) and biodegradation (83% by BOD after 21 days). The toxicity observed is assumed to be due to benzoyl peroxide rather than benzoic acid, which shows much lower toxicity to aquatic organisms. One can assume that effects occur before hydrolysis takes place. From the acute toxicity value of algae, daphnia and fish, an assessment factor of 100 was used to determine the predicted no effect concentration (PNEC). The PNEC was calculated to be 0.7$\mu\textrm{g}$/L based on the 48 hr-E $C_{50}$ daphnia (0.07 mg/L). The substance shows high acute toxicity to aquatic organisms and some information indicates wide-dispersive ore of this substance. So this substance is, a candidate for further work, even if it hydrolysis rapidly and has a low bioaccumulation potential. This could lead to local concern for the aquatic environment and therefore environmental exposure assessment is recommended.

• 한국진공학회지
• /
• 제21권6호
• /
• pp.328-332
• /
• 2012

Ag (silver)의 일함수는 T-OLED (Top Emission Organic Light Emitting Diode)의 전극소자로 사용하기에는 다소 낮다는 단점이 있다(~4.3 eV). 이러한 단점을 해결하기 위한 대안으로 Ag 박막의 표면을 플라즈마, UV, 열처리를 통하여 일함수를 높이는 연구가 진행되어 왔다(~5.0 eV). 하지만 현재의 대부분 연구는 후 처리된 박막의 일함수에 초점을 맞춰 연구가 진행되어, 박막의 mechanical property에 대한 연구는 매우 부족하며 이는 T-OLED의 효율과 수명 등의 연구에 매우 중요하다. 본 논문에서는 Ag와 $AgO_x$ 박막의 mechanical property에 초점을 맞춰 분석을 실시하였다. Ag는 유리기판 위에 rf-magnetron sputter를 이용하여 100 W의 power에서 150 nm 두께로 증착되었다. 증착된 박막은 UV 램프를 이용하여 다양한 시간동안 UV 처리되었다(0~9분). 본 논문에서는 처리된 박막의 면저항을 측정하고 nano indenter, Scanning Probe Microscopy의 Atomic Force Microscopy mode를 이용하여 mechanical property를 분석하였다. 실험 결과 UV 처리 시간이 3분을 넘어가는 시편과 3분 이내의 시편은 면저항값 및 경도 값에 큰 차이가 있었다. 이러한 결과는 Ag 박막의 후처리에 따른 Ag 물질의 산화 및 결합상태에 따라 박막 내에 존재하는 stress의 영향으로 예상되어진다.

• 환경영향평가
• /
• 제23권4호
• /
• pp.315-322
• /
• 2014

근대 산업혁명 이후 도시 내 하천은 개발의 압력에 의해 점차 복개되고 사라져 도시 자연생태계의 기반이 되는 기능이 훼손되기 시작하였다. 중랑천 현지조사에서 조사지역내에 3회에 걸쳐 조사한 식물목록은 총 64과 179속 230종 36변종 1품종 1아종 등으로 총 268분류군으로 조사되었다. 연구대상지 출현식물의 상대 우점도를 분석한 결과 2차 조사에서는 참새귀리 22.97, 쑥 16.76, 개망초 15.89 등으로 나타났으며, 3차 조사에는 바랭이 26.78, 단풍잎돼지풀 16.29, 미국쑥부쟁이 14.31 등으로 조사되었다. 현지조사를 통해 연구대상지에 출현한 귀화식물은 총 54종이었다. 분석 결과 1년생 23분류군(43%), 2년생 11분류군(20%), 다년생 17분류군(31%), 목본 3분류군(6%) 등으로 나타나 우리나라 귀화식물 생활형과 유사한 값을 보였다. 귀화식물을 원산지별로 분석한 결과 북미와 유럽의 귀화종 비율이 76%이상이었다. 귀화도 5가 22분류군(41%)로 가장 높게 나타났고, 귀화도 3이 19분류군(35%), 귀화도 2가 8분류군(15%), 귀화도 4가 5분류군(9%) 순으로 조사되었다. 중랑천의 식물상은 아직도 10여년 전의 모습과 변화가 없다. 중랑천은 시민들을 위한 편의시설 확충과 수질개선은 이루어졌으나, 중랑천의 자연환경과 친수경관적 측면에서는 시급히 생물 다양성을 높이기 위한 노력이 필요하다고 판단된다.

• 한국지반공학회논문집
• /
• 제18권3호
• /
• pp.87-94
• /
• 2002

최근 들어 국내에서는 경제적이고 효율적인 지하굴착공법으로 쏘일네일링 벽체와 지하구조물 외벽을 합벽처리하는 사례가 많아지고 있으며, 이같은 지하외벽 일체식 쏘일네일링 공법은 기존의 지보공법과 비교해 볼 때 굴착면적을 최소화하고 시공성을 개선할 수 있는 특징 이 있다. 또한 지하외벽 일체식 쏘일네일링 공법은 지하외벽의 단면 축소와 지하수에 의한 양압력의 영향에도 대처할 수 있는 장점이 있으나 아직까지는 이에 대한 연구가 미흡하여 보수적으로 설계되고 있는 실정이다. 이를 위해 본 연구에서는 실내모형실험을 통해 전면벽체의 강성에 따른 쏘일네일링 보강토체의 거동 및 네일의 두부에 작용하는 인발력을 분석하여 전면벽체의 강성에 따른 쏘일네일링 벽체의 파괴유형을 규명하고 사용상태 및 한계상태에서의 변위양상 및 네일 두부에서의 인장력 분포를 분석하였다. 또한 전면판의 강성이 쏘일네일링 벽테의 전체 안정성에 미치는 영향을 분석하였으며, 향후 전면벽체의 강성에 따른 지반-네일의 상호작용에 대한 모델개발에 필요한 기초적인 자료를 제공하고자 한다.

• 대한치과보철학회지
• /
• 제37권4호
• /
• pp.454-464
• /
• 1999

The metal ceramic crown is currently the most popular complete veneer restoration in dentistry, but in many cases, the metal cervical collar at the facial margin is unesthetic and unacceptable. Facial porcelain margin has been used in place of it. But this dose not solve the problems, such as dark gingival discoloration and cervical opaque reflection of porcelain veneer. Recently, metal copings which were designed to terminate its labio-cervical end on the axial walls coronal to the shoulder have been clinically used to solve the esthetic problem of metal ceramic crown. But in this design, porcelain veneer of labio-cervical area which is not supported by metal may not be able to resist the stress during cementation and mastication. The purpose of this study was to evaluate fracture strength and fractured appearance of crowns according to different coping designs. A resin maxillary left central incisor analogue was prepared for a metal ceramic crown, and metal dies were made with duplication mold. Metal copings were made and assigned to one of four groups based on facial framework designs: group 1, coping with 0.5mm metal collar; group 2, metal extended to the shoulder; group 3, metal extended to 1mm coronal tn the shoulder: group 4, metal extended to 2mm coronal to the shoulder. Copings and crowns were adjusted to be same size and thickness, and cemented to metal dies with zinc phosphate cement by finger pressure. Fracture strength was measured with Instron Universal Testing Machine. Metal dies were anchored in Three-way-vice at 3mm below finish line and at $130^{\circ}$ inclined to the long axis of the crown. Load was directed lingually at 2mm below midincisal edge. Load value at initial crack and at catastrophic fracture was recorded. The results obtained were as follows : 1. Fracture strength values at initial crack were higher in groups 1, 2 than in groups 3, 4 but this difference was not statistically significant(P<0.05). 2. Conventional metal collared crown had greater catastrophic fracture strength than any other collarless crowns. 3. The greater the labial metal coping reduction, the lower the catastrophic fracture strength of crowns but when more than 1mm of labial metal reduction was done, the difference in strengths was not statistically significant(p<0.05). 4. The strongest collarless coping design was group 2.

• 대한화학회지
• /
• 제17권5호
• /
• pp.337-345
• /
• 1973

$0^{\circ}C\sim1200^{\circ}C$ 온도범위와 $10^{-4}\sim10^2mmHg$ 산소압력하에 산화철계의 무게감소를 석영마이크로 천평을 사용하여 측정하므로써 산화철계의 비화학양론에 대한연구를 실시하였다. 이를 측정하기 위한 종래의 방법으로 시료를 급냉시킨 후 분석을 하는 방법을 피하고 직접측정하여 $FeO_{1+Y}$의 Y값을 구하였다. log Y 대 $log Po_2$(혹은 $log Y=_nlog Po_2$)의 Plot은 직선관계가 성립된다. 이의 기울기에서 n값을 구한결과 $1000^{\circ}C$에서는 $n=\frac{1}{10}$을 얻을 수 있고 이로부터 산화반응기구와 비화학양론적 반응기구의 차이를 설명하였다. 화학양론적 FeO(Fe:O = 1:1)를 형성하는 기준조건을 $1200^{\circ}C$와 $10^{-3}mmHg$ 산소압력으로 하였으며 표준조건에서의 이산화철계의 조성은 $FeO_{1.11185}$로 표시된다. 일반적으로 낮은온도와 높은산소압력하에서 더 많은 산소가 산화물계에 용해되어 화학양론적 FeO로부터 편기가 크다. 산화철계의 전기전도도를 Y값과 비교해보면 전기전도의 전이점이 산화철계의 완전한 상전이를 동반하지 않음을 알 수 있었다.