• Bulletin of the Korean Chemical Society
• /
• v.35 no.11
• /
• pp.3249-3253
• /
• 2014

A novel triazole-functionalized phenolic resin was developed, and its thermal and flame-retardant properties were investigated. The triazole group was incorporated as a pendant unit on the phenolic resin via copper-mediated click chemistry between propargylated phenolic resin and benzyl azide. The newly-developed triazole-functionalized phenolic resin showed higher thermal stability and char yield, together with a reduced total heat release (THR), than the non-functionalized bare phenolic resin, indicating enhanced flame retardancy for the triazole-functionalized phenolic resin.

• Proceedings of the KSR Conference
• /
• 2004.06a
• /
• pp.277-283
• /
• 2004

The time to ignition, heat release rate characteristics and carbon monoxide yield of fiber reinforced and sandwich phenol resin were investigated with cone calorimeter. The fire characteristics of unsaturated polyester, mostly being applied to the existing passenger train, and phenolic resin were compared. Thermal gravimetric analysis(TGA) was used to monitor the degree of thermal decomposition for the phenolic resin. According to the cone calorimeter data, the time to ignition, heat release rate and CO yield was faster and higher as the external heat flux increase. Under the same heat flux, the time to ignition of sandwich type phenolic resin was shorter than that of fiber reinforced. The result of comparison between unsaturated polyester and phenolic resin was that phenolic resin was shown to have better fire resistance than that of unsaturated polyester.

• Korean Journal of Microbiology
• /
• v.35 no.3
• /
• pp.237-241
• /
• 1999

Phenolic resin wastewater contained 41,000 mglI phenol, 2,800 mg/l fonualdehyde and various chlorinated phenolic compounds. Candida tropicalis PW-51 isolated [rom the natural enVlfooment was able to degrade 1,000 mg/l phenol in the presence of 100 mglI formaldehyde, but it took much time to degrade phenol with the increase of formaldehyde in phenolic resin wastewater. %en the phenolic resin wastewater was diluted to 1/40, the initial concentration of phenolic compounds (phenols) was 882 mglI and degraded to 81 mglI by C tfVpicalis PW-51 in batch culture. In a continuous biological treatment, the phenolic resin wastewater was diluted to 40 (745 mglI), 20 (1,356 mglI), or 10 (2,875 mglI) times. The removal efficiency of phenols in 1/40- and lI20-diluted phenolic resin wastewater was about 92%, but the phenols in 1!1O-diluted wastewater were not degraded. The remained phenols in wastewater were absorbed by a mixture of activated carbon and rice bran (1:1, v:v) in the process of absorption which was connected to the biological treatment. The total removal efficiency of phenols in 1!40~ and l/20-diluted phenolic resin wastewater was 99.9%.

• Journal of the Korean Ceramic Society
• /
• v.48 no.4
• /
• pp.293-297
• /
• 2011

The thermodynamic behavior of phenolic resin was investigated to verify the relation between the properties of porous ceramics with $ZrO_2$-C system for submerged entry nozzle and the characteristics of phenolic resin with various relative humidity. The green and the sintered density were decreased between 25% and 50% relative humidity, whereas they were gradually enhanced above 50% relative humidity. The highest value of apparent porosity was 20.1% and the minimum compressive strength was 69MPa in the specimen using the powder exposed to 50% relative humidity. As a result of thermal analysis for phenolic resin, the shift of endothermic peak to low temperature and the reduction of exothermic peak were observed, and the peaks corresponded to melting and curing of phenolic resin, respectively. The melting and the curing of phenolic resin generate the change of green density, and it can affect the properties of submerged entry nozzle.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.57.1-57.1
• /
• 2011

The effects of relative humidity on the properties of the porous $ZrO_2$ ceramics were investigated in terms of the curing behavior of phenolic resin as a binder. The $ZrO_2$ powders containing 5wt% of phenolic resin were conditioned in a consistent chamber condition at a temperature of $50^{\circ}C$ and different humidity levels (25, 50, 75, and 95%) for 1 h. The exposure of humid atmosphere caused changes of density and microstructure in the green bodies. The higher level the powders were exposed to the humid atmosphere, the lower green density was obtained and the more irregular microstructure was observed due to aggregation by the curing of phenolic resin. After firing, the porosity of specimens has risen from 35.7% to 38.1% and Young's modulus has declined in response to the variation of green density. These results could be explained by the degree of resin cure which was associated with the area under the exothermic peak enclosed by a baseline of DSC thermogram curve. Also, the curing behavior of phenolic resin according to relative humidity has been confirmed by decrease of ether groups which have interacted with the phenolic-OH group and the hexamine as a curing agent. Consequently, it could be demonstrated that increase the relative humidity during fabrication of porous $ZrO_2$ diminished the compaction and properties of specimens after firing owing to curing of phenolic resin.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.10a
• /
• pp.145-146
• /
• 2012

• Journal of the Korean Society of Hazard Mitigation
• /
• v.4 no.2 s.13
• /
• pp.29-34
• /
• 2004

The time to ignition, heat release rate characteristics, and carbon monoxide yield of fiber reinforced and sandwich phenol resin were investigated with cone calorimeter. The fire characteristics of unsaturated polyester, mostly being applied to the existing passenger train, and phenolic resin were compared. DSC & TGA was used to monitor the degree of thermal decomposition and weight loss for the phenolic resin. According to the cone calorimeter data, the time to ignition was shorter, heat release rate, and CO yield was higher as the external heat flux increased. Under the same heat flux, the time to ignition of sandwich type phenolic resin was shorter than that of laminated. The result of comparison between unsaturated polyester and phenolic resin was that phenolic resin was shown to have better fire resistance than unsaturated polyester.

• Journal of Powder Materials
• /
• v.26 no.6
• /
• pp.502-507
• /
• 2019

Macro-porous carbon foams are fabricated using cured spherical phenolic resin particles as a matrix and furfuryl alcohol as a binder through a simple casting molding. Different sizes of the phenolic resin particles from 100-450 ㎛ are used to control the pore size and structure. Ethylene glycol is additionally added as a pore-forming agent and oxalic acid is used as an initiator for polymerization of furfuryl alcohol. The polymerization is performed in two steps; at 80℃ and 200℃ in an ambient atmosphere. The carbonization of the cured body is performed under Nitrogen gas flow (0.8 L/min) at 800℃ for 1 h. Shrinkage rate and residual carbon content are measured by size and weight change after carbonization. The pore structures are observed by both electron and optical microscope and compared with the porosity results achieved by the Archimedes method. The porosity is similar regardless of the size of the phenolic resin particles. On the other hand, the pore size increases in proportion to the phenol resin size, which indicates that the pore structure can be controlled by changing the raw material particle size.

• Journal of the Korea Furniture Society
• /
• v.14 no.2
• /
• pp.21-29
• /
• 2003

This study was carried out to investigate characteristics of plywood overlaid with softwood veneers densified by resin impregnation and compression. The resin impregnability of Korean pine veneer under atmospheric pressure soaking was greater than that of larch, and impregnability of melamine resin was slightly greater than phenolic resin. It was suggested that resin impregnation ratio was affected by density and thickness of veneer. The largest melamine resin impregnation ratio of 50.7% was obtained with 1.26mm thick Korean pine veneer, and the lowest phenolic resin impregnation ratio of 11.7% with 3.41mm thick larch veneer. Therefore, it was suggested that the vacuum-pres sure-soak treatment is required at thick larch veneer. In densifying resin-impregnated veneers, densification ratio from 13.4 to 31.2% was obtained by high pressure from 15.6 to $20.8kgf/cm^2$. Impregnation of melamine resin also showed relatively greater at densification than that of phenolic resin. So it showed the degree of densification of about 20% or greater. It was seemed that adhesive bonding strength of plywood(base panel) which was directly pressed and overlaid with resin-impregnated veneer was affected by resin tackiness after resin impregnation followed by semi-drying. In laboratory scale, melamine resin impregnation was more favorable for the development of adhesive bonding strength owing to moisture control.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.1
• /
• pp.1-7
• /
• 2004

This paper describes the carbonization characteristics of a phenolic resin deteriorated by tracking under the environment of a fire. In the experiment, a liquids droplet of 1[％] NaCl was dripped on the phenolic resin to cause a tracking with 110[V], 220[V] voltages applied. It can be addressed from the experimental results that when an insulator is carbonized by an external fire, its structure is amorphous. If an insulator is carbonized by electrical cause, on the other hand, its structure would be crystalline. In order to observe the surface change of the phenolic resin, the tracking process was analyzed by using SEM. In the case that the materials are carbonized under heat or fire, the exothermic peak appears around 500[$^{\circ}C$]. This is one of the important factors to determine the cause of fires. As a result of DTA, the exothermic peaks of an untreated sample showed at 333.4[$^{\circ}C$], 495.7[$^{\circ}C$] but those of a sample deteriorated by tracking appeared at 430.6[$^{\circ}C$], 457.6[$^{\circ}C$] in a voltage of 110[V], and at 456.2[$^{\circ}C$], 619.7[$^{\circ}C$] in a voltage of 220[V]. It is possible, therefore, to distinguish a virgin sample from carbonized samples(graphite) by the exothermic peak.