Newly structured metal-supported solid oxide fuel cell was fabricated and characterized by impedance analysis and galvanodynamic experiment. Using a cermet adhesive, thin ceramic layer composed of anode(Ni/YSZ) and electrolyte(YSZ) was joined with STS430 metal support of which flow channel was fabricated. $La_{0.8}Sr_{0.2}Co_{0.4}Mn_{0.6}O_3$ perovskite oxide was used as cathode material. Single cell performance was increased and saturated at operating time to 300hours at 800$^{\circ}C$ because of cathode sintering effect. The sintering effect was reinvestigated by half cell test and exchange current density was measured as 0.005A/$cm^2$. Maximum power density of the cell was 0.09W/$cm^2$ at 800$^{\circ}C$. Numerical analysis was carried out to classify main factors influencing the single cell performances. Compared to experimental IV curve, simulated curve based on experimental parameters such as exchange current density was in good agreement.

• Korean Chemical Engineering Research
• /
• 제59권4호
• /
• pp.557-564
• /
• 2021

페로브스카이트 구조를 갖는 Sr_0.92Y_0.08Ti_1-xV_xO_3-δ (SYTV)는 고체산화물 연료 전지(Solid oxide fuel cell, SOFC)에서 H₂S를 포함하는 연료를 사용하기 위한 대체 연료극으로 연구되었다. Sr_0.92Y_0.08TiO_3-δ (SYT)의 전기화학적 성능을 향상시키기 위해 페로브스카이트의 B-사이트에 위치한 티타늄을 바나듐으로 치환하였다. 페치니법을 통해 합성된 SYTV는 작동 온도 조건에서 추가적인 부산물의 형성 없이 YSZ(yttria-stabilized zirconia) 전해질과 화학적으로 안정했다. 바나듐의 치환량이 증가함에 따라 산소 공공 결함(Oxygen vacancy)이 증가하였으며, 생성된 산소 공공 결함으로 인해 연료극의 이온 전도도가 증가했다. 전지 성능은 850 ℃ 순수한 H₂ 연료 조건에서 바나듐 치환 정도에 따라 1 mol.%의 바나듐이 치환된 경우 19.30 mW/cm² 이고 7 mol.%의 바나듐이 치환된 경우 34.87 mW/cm²이다. 1000 ppm의 H₂S를 포함하는 H₂ 연료조건에서 cell의 최대 전력밀도는 1 mol.%의 경우 22.34 mW/cm²이고 7 mol.%의 경우 73.11 mW/cm²로 증가하였다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 춘계학술대회 초록집
• /
• pp.139-139
• /
• 2010

LSM is widely used as a cathode material in SOFC, because of its high electrochemical activity, good stability and compatibility with YSZ electrolyte at high temperature. However, LSM in traditional cathode materials will not generate a satisfactory performance at intermediate temperature. In order to reduce the polarization resistance of cell with the operating temperature of SOFC system, the cathode material of LSCF is one of the most suitable electrode materials because of its high mixed ionic and electronic conductivity. In this report, cathode material, $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_3$ powder for intermediate temperature SOFC was synthesized by Pechini method using the starting materials such as nitrate of La, Sr, Co and Fe including ethylene glycol, etc. As a result, the synthesized powder that calcined above $700^{\circ}C$ exhibits successfully perovskite structure, indicating phase-pure of LSCF. Moreover, the particle size, surface area, crystal structure and morphology of the synthesized oxide powders were characterized by SEM, XRD, and BET, etc. In order to evaluate the electrochemical performance for the synthesized powder, slury mixture using the synthesized cathode material was coated by screen-printing process on the anode-supported electrolyte which was prepared by a tape casting method and co-sintering. Finally, electrochemical studies of the SOFC unit cell, including measurements such as power density and impedance, were performed.

• 한국세라믹학회지
• /
• 제47권1호
• /
• pp.26-38
• /
• 2010

Degradation in Solid Oxide Fuel Cell performance can be ascribed to the following fundamental processes from the materials chemical point of view; that is, diffusion in solids and reaction with gaseous impurities. For SOFC materials, diffusion in solids is usually slow in operation temperatures $800\sim1000^{\circ}C$. Even at $800^{\circ}C$, however, a few processes are rapid enough to lead to some degradations; namely, Sr diffusion in doped ceria, cation diffusion in cathode materials, diffusion related with metal corrosion, and sintering of nickel anodes. For gaseous impurities, chromium containing vapors are important to know how the chemical stability of cathode materials is related with degradation of performance. For LSM as the most stable cathode among the perovskite-type cathodes, electrochemical reduction reaction of $CrO_3$(g) at the electrochemically active sites is crucial, whereas the rest of the cathodes have the $SrCrO_4$ formation at the point where cathodes meet with the gases, leading to rather complicated processes to the degradations, depending on the amount and distribution of reacted Cr component. These features can be easily generalized to other impurities in air or to the reaction of nickel anodes with gaseous impurities in anode atmosphere.

• 한국세라믹학회지
• /
• 제45권12호
• /
• pp.755-759
• /
• 2008

New cathode materials $LaNi_{1-x}{Cu_x}{O_3}$ (typically $LaNi_{0.8}Cu_{0.2}O_3$) were synthesized using a co-precipitation method. The structure and morphology of the powders were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The composite material [$Ce_{0.8}Sm_{0.2}O_{2-\ddot{a}}$(SDC) and carbonate (${Na_2}{CO_3},{Li_2}{CO_3}$)], NiO and $LaNi_{1-x}{Cu_x}{O_3}$ were used as the electrolyte, anode and cathode, respectively. The electrochemical performance of La-Ni-Cu-O perovskite oxide at low temperatures ($400{\sim}550^{\circ}C$) was studied. The results showed that $LaNi_{0.8}Cu_{0.2}O_3$ precursor powder prepared through a co-precipitation method and calcined at $860^{\circ}C$ for 2 h formed uniform grains with diameters in the range of $400{\sim}500\;nm$. The maximum power density and the short circuit current density of the single cell unit at $550^{\circ}C$ were found to be $390\;mW/cm^2$ and $968\;mA/cm^2$, respectively.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 춘계학술발표대회
• /
• pp.45.1-45.1
• /
• 2011

Cobalt-free $La_xSr_{4-x}Fe_6O_{13}$ ($0{\leq}x{\leq}2$) oxide have been synthesized and investigated as a potential cathode material for solid oxide fuel cells (SOFCs). $Sr_4Fe_6O_{13}$ consists of alternating perovskite layers ($Sr_4Fe_2O_8$) containing iron cations in octahedral oxygen coordination and $Fe_4O_5$ layers where iron cations have 5-fold coordination of two types-square pyramids and trigonal bipyramids. Our preliminary electrochemical testes of pristine $Sr_4Fe_6O_{13}$ show a rather high area specific resistance ($0.47{\Omega}cm^2$ at $700^{\circ}C$) for ~20 ${\mu}m$ thick layers with CGO electrolyte. The electrochemical performances are improved by La addition up to x=1 ($La_1Sr_3Fe_6O_{13}$, $0.06{\Omega}cm^2$ at $700^{\circ}C$). In addition, thermal expansion coefficient (TEC) values of $La_1Sr_3Fe_6O_{13}$ specimen demonstrated $15.1{\times}10^{-6}\;^{\circ}C^{-1}$ in the range of 25-900$^{\circ}C$, which provides good thermal expansion compatibility with the CGO electrolyte. An electrolyte supported (300-${\mu}m$-thick) single-cell configuration of $La_1Sr_3Fe_6O_{13}$/CGO/Ni-CGO delivered a maximum power density of 584 $mWcm^{-2}$ at $700^{\circ}C$. In addition, an anode supported single cell by YSZ electrolyte (10-${\mu}m$-thick) with a porous CGO interlayer between the cathode and the electrolyte to avoid undesired interfacial reactions exhibited 1,517 $mWcm^{-2}$ at $800^{\circ}C$. The unique composition of $La_1Sr_3Fe_6O_{13}$ with low thermal expansion coefficient and higher electrochemical properties could be a good cathode candidate for intermediate temperature SOFCs with CGO and YSZ electrolyte.

• 한국세라믹학회지
• /
• 제51권4호
• /
• pp.271-277
• /
• 2014

To overcome the limitations of the solid oxide fuel cells (SOFCs) due to the high temperature operation, there has been increasing interest in proton conducting fuel cells (PCFCs) for reduction of the operating temperature to the intermediate temperature range. In present work, the perovskite $BaCe_{0.85-x}Zr_xY_{0.15}O_{3-\delta}$ (BCZY, x = 0.1, 0.3, 0.5, and 0.7) were synthesized via solid state reaction (SSR) and adopted as an electrolyte materials for PCFCs. Powder characteristics were examined using X-ray diffraction (XRD), thermogravimetric analysis (TGA) and Brunauer, Emmett and Teller (BET) surface area analysis. Single phase BCZY were obtained in all compositions, and chemical stability was improved with increasing Zr content. Anode-supported cell with $Ni-BaCe_{0.55}Z_{0.3}Y_{0.15}O_{3-\delta}$ (BCZY3) anode, BCZY3 electrolyte and BCZY3-$Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-\delta}$ (BSCF) composite cathode was fabricated and electrochemically characterized. Open-circuit voltage (OCV) was 1.05 V, and peak power density of 370 ($mW/cm^2$) was achieved at $650^{\circ}C$.