• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.4
• /
• pp.195-202
• /
• 2007

Corrosion resistance and torque of M10 bolt coated with Magni 565 were investigated. Corrosion protection mechanism were also studied with the microstructure of coating film. The bolts with the optimum conditions showed around $10{\mu}m$ layer thickness, a great corrosion resistance in salt spray test and a proper torque in torque/tension test. But torque coefficient k increased with the number of bolting and clamping force of M10 bolt showed significantly lower than that of specified value 28.3kN. It was thought that the repeated bolting made the coating film peel off and powdery. The sample coated with optimum coating conditions showed more higher polarization resistance and corrosion potential than the specimens of top and base coat only. The base coating film was composed of lamellar zinc flakes, which provides a large sacrificial cathodic protection. Meanwhile, the top coating film was composed of organic aluminium pigments layer, which provides barrier protection to the corrosion circumstances.

• The Korean Journal of Food And Nutrition
• /
• v.24 no.3
• /
• pp.442-450
• /
• 2011

Numerous studies have suggested that dietary flavonoids contribute to prevent cardiovascular disease. Onion contains many functional phytochemicals such as quercetin. The aim of this study was to examine whether onion peel extracts supplementation affect blood lipid profiles and blood coagulation in animal model. Total 48 Sprague-Dawley male rats at 5 weeks old were divided into 6 groups with different diets(C: control, HF: high fat diet, HFOE 0.01%: high fat+onion peel extract 0.01% diet, HFOE 0.02%, HFOE 0.05%, HFOE 0.1%) for 8 weeks. Onion peel extract supplementation significantly decreased serum levels of LDL-cholesterol and increased HDL-cholesterol, while total cholesterol and triglyceride levels were not affected. Hematological parameters(hematocrit, white blood cell, red blood cell, and platelet count) and blood coagulation parameters(prothrombin time, activated partial thromboplastin time, thrombin time, and fibrinogen) were not significantly different among 6 groups. However, activated partial thromboplastin time of HFOE 0.05% group was significantly longer than that of HF group. These results indicate that onion peel extract supplementation displays hypocholestrolemic effects but does not seem to have anti-coagulation effects in high fat fed SD rats.

• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.52-58
• /
• 2011

In this paper, the direct bonding process between FPCB and HPCB was studied. By using an ultrasonic horn which is mounted on the ultrasonic bonding machine, it is alternatively possible to bond the gold pads attached on the FPCB and HPCB at room temperature without an adhesive like ACA or NCA. The process condition for obtaining more bonding strength than 0.6 Kgf, which is commercially required, was carried out as 40 kHz of frequency, 0.6 MPa of bonding pressure and 2 second of bonding time. The peel off test was performed for evaluating bonding strength which results in more than 0.8 Kgf.

• Journal of Adhesion and Interface
• /
• v.13 no.1
• /
• pp.9-16
• /
• 2012

In order to describe external effects on the behavior of the adhesive tape, the semi-rigid body cylinder chain model for adhesive tape has been proposed as follows. Firstly the behavior of the tape is in detail investigated while it's being pulled off from the plate, and subsequently a relevant phenomenological model is designed. Then all the contributors affecting the force to peel out the tape from plate (hereafter, the pull out force) are clearly defined and their sensitivity analyses are made to set up the experimental reference condition, under which the angular dependence of the pull out force is measured in every $10^{\circ}$. The experimental data turn out to be in good agreement with the theoretical ones by our model within the measurement error, and the effects due to other factors are proved to be well explained from the phenomenological viewpoint. From these results, the concept of this study might be expected to be very useful for the test and evaluation of PSA types of adhesive tape.

• Journal of Haehwa Medicine
• /
• v.13 no.2
• /
• pp.187-196
• /
• 2004

Now many sustitution and false articles is used in korea instead of shanyao. To use shanyao correctly, we will make a quilitative certificational plan of shanyao to investigate all of lieraturea, records and documents. And we could reach conclusions as folloews. 1) Source About a source of shanyao, though korea and china has a each other source, we think there is no problem in use of both. 2) Process In our country producing shanyao as medical use is a 'duanma', we can divide into peeling and non-peeling, drying at bulks and at briquets, steaming shanyao and fresh shanyao. Regardless of existence for peeling and steaming, a distributing shanyao is received a proper judgment. Like this result was expressed by insufficiency of standards about medical components or indicating components. We detected a reminding S02 more than 10 ppm. And this expresses that there ia a problum at a drying method. To suggest proper processing methods, a standard of quility will have to be made which the existence of peeling, difference of quility between 'changma' and 'duanma', drying method and exudation test with cutted thickness are adaptable. Besides, 'maoshanyao' and 'guangshanyao' of china is processed by various methods which decrease a medical effect such as too much soaking shanyao in water, steaming with a sulfur, too much peeling, So we must process shanyao like the next methods. (1) When harvesting, dig deeply not to cut off roots. (2) Not to peel, wash shanyao in a washing machine. (3) Dry to 50-60% degree at sunny place or drying machine. (4) To be easy for drying and exudation, cut off a thick piece with 5 mm (5) Dry perfectly at ding machine. 3) Quality3) Quality (1) Functional standards It is not Proper that 'guangshanyao' is used in china because it has a problem with quility on process of working, If they did not soak shanyao in water or heat with steam, it is the real situation that they cannot cutt off shanyao evenly. In conclusion, shanyao must be heavy, powdery with a perfectly non-peeling surface, section surface is yellow-white color, unequal and has no holes. (2) Physicochemical standards It is the real situation that we can not distinguish into quility of shanyao with established test because various workings which decrease medical effects is used. Therefore we suggest a testing standard of S02 which is used in bleaching. And testing standards relatived with decrease of medical effects must be established at once. It must that Dry on loss is less than 14.0%, content of ash is less than 6.0%. Content of acid-nonsoluble ash is less than 0.5%. Contens of heavy metal has to detect less than 30 ppm and there is no reminding agricultural medince.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.10
• /
• pp.113-123
• /
• 1990

Tungsten film was deposited on the single crystal silicon wafer in a low pressure chemical vapor deposition reactor from silane and tungsten hexafluoride in the temperature range of $250-400^{\circ}C$ Deposition rate was found to be determined by the mass transfer rate of reactants from the gas phase to the safter surface. It was found out that tungsten films deposited contained about 3 atomic $\%$ of silicon and that the crystallinity and the grain size increased as the deposition temperature was increased. The resistivity of the film was measured to be in the range of $7~25{\mu}{\Omega}-cm$ and decreased with increasing deposition temperature. The adhesion of the tungsten film on a silicon surface was measured by the tape peel off test and it was improved with increasing deposition temperature. From the analysis of the gas composition, the reaction pathway to form $SiF_{4}$ and $H_{2}$ was found to be more favorable than HF formation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.4
• /
• pp.395-403
• /
• 2012

This is direct bonding many of the metal bumps between FPCB and HPCB substrate. By using an ultrasonic horn mounted on an ultrasonic bonding machine, it is possible to bond gold pads onto the FPCB and HPCB at room temperature without an adhesive like ACA or NCA and high heat and solder. This ultrasonic bonding technology minimizes damage to the material. The process conditions evaluated for obtaining a greater bonding strength than 0.6 kgf, which is commercially required, were 40 kHz of frequency; 0.6MPa of bonding pressure; and 0.5, 1.0, 1.5, and 2.0 s of bonding time. The peel off test was performed for evaluating bonding strength, which was found to be more than 0.80 kgf.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.3
• /
• pp.47-54
• /
• 2008

To make up original defects of the wooden materials for decks, and to supply the wooden material for outdoor, we fabricated preservative treated plywood(PTP). Copper azole (CUAZ-1) preservative was treated with a normal full-cell process. Bond Strength of PTP was not affected after the preservative treatment. The anti-fungal efficiency and dimensional stability were obtained from PTP. A little discoloration of the surface was detected, but the dimensional change or peel bonded area off were not observed after accelerated weathering test. Although some strength of PTP was reduced after 17 months of field exposure, the PTP should be applicable for outdoor applications.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.31 no.6A
• /
• pp.457-464
• /
• 2011

An experimental study was performed to evaluate the possibility of using stiff type PolyUrea(PU) on RC slab as a strengthening material. Stiff type PU(STPU) was sprayed on the bottom surface of the slab specimens, which were then attached with CFRP or GFRP sheets. Also the evaluation of the bond capacity, the single most influential parameter on strengthening of RC structures, was carried out the flexural capacity evaluation test results showed that the load carrying capacity of the PU specimen was greater and less than the unstrengthened and FRP sheet attached specimens, respectively. The STPU specimens showed a ductile flexural behavior in the plastic displacement range. With respect to bond capacity, the bond strength of all of the specimen exceeded the code required bond strength of 1.5 MPa. Also, the STPU sprayed specimen without using epoxy resin did not peel off when the tensile grip was applied for testing. The stability of the PU bond failure indicate a good bond strength of PU when applied to concrete.