• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.45 no.6
• /
• pp.30-35
• /
• 2013

To conserve wood resources for papermaking, chemical compositions of the hemp (Cannabis sativa L.) bast fiber cultivated in Korea such as holocellulose, ${\alpha}$-cellulose, lignin, alcohol-benzene extractives, hot and cold water extractives, and ash contents were investigated to manufacture the specialty packaging paper effectively. Significantly very low klason lignin content of 3.3% was accomplished by removing of the outer shell of bark. Laboratory soda pulping method which is very useful for the nonwood fiber was adapted, and it was found that there was no significant difference in both kappa number and H-factor between 25% and 30% NaOH charge. Hemp pulp cooked with the laboratory digester in 25% NaOH at $170^{\circ}C$ were mixed together with the wood pulp(NBKP:LBKP=1:1) in order to find the optimum mixture ratio which exhibited acceptable paper strength properties such as tensile index, burst index, and tear strength. When 10% of hemp soda pulps was mixed with 90% of wood pulps comprised of SwBKP and HwBKP (1:1), all physical strength increased significantly. The physical strength decreased as the amount of hemp pulp increased because the cell wall of bast fiber is very thick which causes low conformability and low fiber-fiber bonding. These results showed that paper made of hemp-wood pulp can be used for the specialty packaging paper which requires both the characteristic surface properties and the high physical strength of hemp fiber.

• Ecology and Resilient Infrastructure
• /
• v.5 no.3
• /
• pp.118-124
• /
• 2018

Social infrastructures and industrial complexes have been actively constructed in South Korea since the 1960 s as part of the economic development plan, resulting in rapid industrialization. However, side-effects due to the industrialization have occurred. An increase in industrial by-products or wastes is a typical problem. Although some industrial by-products are recycled in Korea as well as worldwide, some wastes are landfilled or dumped in the sea. Although many researchers have executed various technologies for the disposal of industrial wastes, economic and environmental technologies have not been developed. Thus, this study aims to activate paper and fly ashes during the crush process to overcome the drawback of simple concrete mixed with paper and fly ashes, which cause a reduction in workability and strength, derive an optimal content and replacement ratio of concretes mixed with Energetically Modified Material (EMM), and evaluate the material performance. In addition, the basalt fiber is mixed simultaneously to achieve the reduction of cracks and improve the tensile strength.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.6
• /
• pp.475-489
• /
• 2013

This work was conducted to investigate the effect of the addition of binders, such as rapeseed flour, coffee waste, bark, pine cone and lignin powder, on the fuel characteristics of the pellets fabricated with larch and tulip tree sawdust. Moisture content, bulk density and higher heating value of most pellets fabricated with the binders exceeded the 1st-grade pellet standard designated by Korea Forest Research Institute, but ash content of the pellets fabricated with rapeseed flour or bark of 10 wt% on the dry weight basis of sawdust was satisfied with just the 2nd- or 3rd-grade standard. The durability of tulip tree-pellets was positively influenced by the addition of rapeseed flour, coffee waste or lignin powder and increased with increasing the amount of the binders. For larch-pellets, the increase of binders did not greatly affect the durability, and even the durability reduced with the increase of bark or pine cone. From the microscopic observation, the obvious feature of pellet surfaces was not identified by the type of binder but by the addition amount of the binder. In summary, the addition of binders contributed to the fuel characteristics of wood pellets, and particularly the characteristics of wood pellets fabricated with coffee waste improved greatly. Therefore, if the binders are secured sufficiently with a reasonable cost, it might be possible to commercialize wood/binder pellets, which have better fuel characteristics than conventional wood pellets.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.42 no.2
• /
• pp.67-74
• /
• 2010

This study was carried out to investigate the pulping and papermaking characteristics of lotus (Nelumbo nucifera G.) leafstalk for the development of high performance paper. Anatomical and chemical properties of the lotus leafstalk were analyzed. The pulping and papermaking properties of the lotus leafstalk by conventional alkali and sulfomethylated pulping processes were also evaluated. The length and width of fibers were 0.06-3.32 mm (av. 1.23 mm) and 3.47-25.6 ${\mu}m$ (av. 20.7 ${\mu}m$), respectively. The length and width of vessel elements were 0.07-0.78 mm (av. 0.20 mm) and 14.1-330.0 ${\mu}m$ (av. 54.13 ${\mu}m$), respectively. The fiber length/fiber width ratio was 60.20. The extractives (cold water, hot water, 1% NaOH and ethanol-benzene) and lignin content of lotus leafstalk were higher than those of plant bast fiber. The contents of holocellulose, lignin, and ash were 73.8%, 24.3%, and 4.3%, respectively. The pulp yields based on pulping methods were sulfomethylated pulping av. 52%, and alkaline pulping av. 42%. The conventional alkaline pulping shows better pulp and sheet properties than the sulfomethylated pulping which was modified pulping processes. But the sulfomethylated pulping shows higher brightness than alkali pulping. In the consequence of FE-SEM observation, lotus leafstalk pulp consists of various kinds of thin walled fibers which have large amount of small pits.

• 한국연소학회:학술대회논문집
• /
• 2006.10a
• /
• pp.282-292
• /
• 2006

Various kinds of coals are supplied for coal fired power plants as the coal market situations are fluctuated with the high prices of oil and coals over the world. The quality of coal is decreasing as coal consumption increased and some specifications of coals are out of boiler design criteria. It could make combustion troubles such as coal clogging, spontaneous combustion, coal firing in the coal handling equipments, ash slag and clinker issues, etc. This paper covers combustion troubles, issues and countermeasures in the biggest coal fired power plant in Korea.

• 한국연소학회:학술대회논문집
• /
• 2006.10a
• /
• pp.168-174
• /
• 2006

A pilot scale (200kg/hr) pyrolysis melting incineration system is designed and constructed in Korea Institute of Industrial Technology. The incineration process is composed of pyrolysis, gas combustion, ash melting, gas stabilization, waste heating boiler, and bag filter. For each unit process, experimental approaches have been conducted to find optimal design and operating conditions. Especially, a pyrolysis is very important process in that it is a way of energy recirculation and minimizing the waste products. This paper presents major results of the most efficient operating conditions in a pilot scale pyrolysis melting incinerator.

• Journal of the Korea Institute of Building Construction
• /
• v.3 no.1
• /
• pp.139-146
• /
• 2003

The special requirements of high-performance concrete(HPC) could be enhanced property over others such as compressive strength, durability, and construction practices. In order to satisfy these requirements a series of laboratory trial mixes and following mock-up test of reinforced concrete wall at field were performed in this study. The objective of this study was to quantitatively evaluate the workability, compressive strength, and the increased heat of hydration caused by the increase of the specific weight of cement according to various variables. Six example series designed about a minimum compressive strength of 500kgf/$\textrm{cm}^2$ at 28 days, and an approximately slump and slump flow of 25cm and 60cm respectively were tested. The selection process of the specific weight of water and the percentage of fly-ash transposition determined to be most suitable for the production of HPC is presented in the following paper.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.431-436
• /
• 2002

In this paper, to seek a solution of reducing autogenous shrinkage three types of bar restricted concrete specimens which have similar compressive strength were tested. The three type of concrete were plain concrete-P25 type, $10^{\circ}C$ fly-ash replaced concrete-F10 type, and $1^{\circ}C$ expansion admixture replaced concrete-SP1 type, and with the test result an experimental study was conducted to gain the tensile stress of concrete. From the result of P25, SP1, F10 tests, it was found that by the age of 14 the ratios of tensile stress to tensile strength of three specimens are $75^{\circ}C$, $47^{\circ}C$, $52^{\circ}C$ respectively. so we came to a conclusion that the SP1-type concrete has better capacity to reduce autogenous shrinkage than F10-type concrete at similar compressive strength condition.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.11a
• /
• pp.137-138
• /
• 2015

The use of the cement and increased with the recent development of the construction industry. If the cement is the environmental problems caused by generating a large quantity of CO₂ and the production process. Accordingly, this study is the test to determine the sulfuric acid and hydrochloric acid resistance properties of the Light weight matrix product of blast furnace slag-based light. A result, the compression strength of the sulfuric acid and hydrochloric acid immersion showed alower strength than the Plain.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.386-391
• /
• 1998

Recently, high performance concrete developed has a good quality at fresh and hardened state, but high binder contents results in spending much money on manufacturing and many cracks by drying and autogenous shrinkage. Therefore, in this paper, not only prevention of cracks caused by drying and autogenous shrinkage, but improvement of quality and accmplishment of economy by applying F.A(fly ash), S.F(silica fume) and CSA(calcium sulfa aluminate) expansive additives as an inorganic admixtures in W/B 35% are discussed. According to the experimental results, when 5% of CSA Expansive additives and 15:5 (F.A:S.F)are replaced at unit cement content, high performance concrete with both good compensation of drying and autogenous shrinkage at hardened state is accomplished.