• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.7
• /
• pp.551-556
• /
• 2001

In this work, the recovery of etching damage in the etched PZT thin film with $O_2$ annealing has been studied. The PZT thin films were etched as a function of Cl$_2$/Ar and additive CF$_4$ into Cl$_2$(80%) /Ar(20%). the etch rates of PZT thin films were 1600$\AA$/min at Cl$_2$(80%)/Ar(20%) and 1970 $\AA$/min at 30% additive Cf$_4$ into Cl$_2$(80%)/Ar(20%). In order to recover the characteristics of etched PZT thin films, the etched PZT thin films were annealed in $O_2$ atmosphere at various temperatures. From the hysteresis curves, ferroelectrical properties are improved by $O_2$ annealing process. The improvement of ferroelectric behavior is consistent with the increase of the (100) and (200) PZT phase revealed by x-ray diffraction (XRD). From x-ray photoelectron spectroscopy (XPS) analysis, intensities of Pb-O, Zr-O and Ti-O peak increase and the chemical residue peak is reduced by $O_2$ annealing. From the atomic force microscopy (AFM) images. it shows that the surface morphology of re-annealed PZT thin films after etching is improved.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1301-1302
• /
• 2007

The multilayered $Pb_{1.1}(Zr_{0.4}Ti_{0.6})O_{3}$/$Pb_{1.1}(Zr_{0.6}Ti_{0.4})O_{3}/Pb_{1.1}(Zr_{0.4}Ti_{0.6})O_{3}$[PZT(4060)/(6040)/(4060)] thin films were deposited by RF sputtering method on the Pt/TiO2/SiO2/Si substrate. We investigated the effects of deposition conditions on the structural and electrical properties of the multilayered PZT thin films. All the multilayered PZT thin films showed dense and homogeneous structure without the presence of the rosette structure. The dielectric properties such as dielectric constant, loss, remanent polarization of the multilayered PZT thin film were superior to those of single composition PZT(4060) and PZT(6040) films, and those values for the multilayered PZT(10/20/10) thin film were 903, 1.01% and $25.60{\mu}C/cm^2$. This study suggests that the design of the multilayered PZT thin films capacitor with tetragonal and rhombohedral phase should be an effective method to enhance the dielectric and ferroelectric performance in devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.56-59
• /
• 2000

In this study, Ferroelectric $Pb(Zr_x,Ti_{1-x})O_3$(x=0.53) thin films were fabricated by the spin-coating on the Pt/Ti/$SiO_2$/Si substrate using the PZT metal alkoxide solutions with various excess Pb contents. Etching of PZT film was performed using planar inductively coupled Ar(20)$/Cl_2/BCl_3$ plasma. The etch rate of PZT film was 2450 ${\AA}/min$ at Ar(20)$/BCl_3$(80) gas mixing ratio and substrate temperature of $80^{\circ}C$. The leakage current densities of before etching and after etching PZT thin film were $6.25\times10^{-8}A/cm^2$, $8.74\times10^{-7}A/cm^2$ with electric field of 0.07MV/em, respectively.

• Journal of Industrial Technology
• /
• v.25 no.A
• /
• pp.157-162
• /
• 2005

In this study, the fabrication of PZT films was performed from a multilayer structure comprising $TiO_2$, $ZrO_2$ and PbO thin films prepared by rapid themal chemical vapor deposition(RTMOCVD). $TiO_2$, $ZrO_2$ and PbO are the component layers of oxide multilayer system for a single phase PZT thin film. The composition control of PZT thin film was done by the thickness control of individual component layer. The composition ratio of Pb:Ti:Zr with thickness were 1:0.94:0.55. Occurrence of a single-phase of PZT was initiated at around $550^{\circ}C$ and almost completed at $750^{\circ}C$ under the fixed time of 1hr. As the concentration of Pb increased, the roughness and crystallization in the film increased. From the as result of using XPS and TEM, the single phase formation through annealing is evident. The electrical properites of the prepared PZT thin film(Zr/Ti=40/60, 300 nm) on a Pt-coated substrate were as follow: dielectric constant ${\varepsilon}_r=475$, coercive field Ec=320 kV/cm, and remanant polarization $P_r=11{\mu}C/cm^2$ at an applied voltage of 18 V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.528-531
• /
• 2000

Deposition of PZT with UV laser ablatio was applied for realization of thin film sensors and actuators. Deposition rate of more than 20nm/min was attained by pulsed KrF excimer laser deposition, which is fairly better than those obtained by the other methods. Perovskite phase was obtained at room temperature deposition with Fast Atom Beam(FAB) treatment and annealing. Smart MEMS(Micro electro-mechanical system) is now a suject of interest in the field of micro optical devices, micro pumps, AFM cantilever devices etc. It can be fabricated by deposition of PZT thin films and micromachining. PZT films of more than 1 micron thickness is difficult to obtain by conventional methods. This is the reason why we applied excimer laser ablation for thin film deposition. The remanent polarization Pr of 700nm PZT thin film was measured, and the relative dielectric constant was determined to about 900 and the dielectric loss tangent was also measured to be about 0.04. XRD analysis shows that, after annealing at 650 degrees C in 1 hour, the perovskite structure would be formed with some amount of pyrochlore phase, as is the case of the annealing at 750 degrees C in 1 hour.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1240_1241
• /
• 2009

In this paper, sol-gel-spin coated $Pb(ZrTi)O_3$ thin film with $ZrO_2$ buffer-layer and $PbTiO_3$ seed-layer was investigated for vibration MEMS energy harvester to scavenge power from ambient vibration via d33 piezoelectric mode. Piezoelectric thin film deposition techniques on insulating layer is the important key for $d_{33}$ mode of piezoelectric vibration energy harvester. $ZrO_2$ buff-layer was utilized as an insulating layer. $PbTIO_3$ seed-layer was applied as an inter-layer between PZT and $ZrO_2$ layer to improve the crystalline of PZT thin film. The fabricated PZT thin film had a remanent polarization of 5.3uC/$cm^2$ and the coercive field of 60kV/cm. The fabricated energy harvester using PZT thin film with PTO seed-layer generated 1.1uW of electrical power to $2.2M{\Omega}$ of load with $4.4V_{pvp}$ from vibration of 0.39g at 528Hz.

• Proceedings of the KIEE Conference
• /
• 2006.07d
• /
• pp.2209-2210
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coaled on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field wore 16.48 ${\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.07a
• /
• pp.577-578
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coated on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at 650f showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field were 16.48${\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.07b
• /
• pp.1243-1244
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coated on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field were $16.48{\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.07c
• /
• pp.1703-1704
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coated on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field were $16.48{\mu}C/cm^2$ and 35.48kV/cm, respectively.