• E2M - 전기 전자와 첨단 소재
• /
• 제10권10호
• /
• pp.983-988
• /
• 1997

We investigated the structural and dielectric properties of PZT(20/80)/PZT(80/20) heterolayered thin films that fabricated by the alkoxide-based Sol-Gel method. PZT(20/80)/PZT(80/20) heterolayered thin films were spin-coated on the Pt/Ti/SiO$_2$/Si substrate with PZT(20/80) film of tetragonal structure and PZT(80/20) film of rhombohedral structure by turns. Each layers were dried to remove the organic materials at 30$0^{\circ}C$ for 30min and sintered at $650^{\circ}C$ for 1hr. This procedure was repeated several times to form PZT(20/80)/PZT(80/20) heterolayered films and thickness of the film obtained by one-times of drying/sintering process was approximately 80-90nm. PZt-1, 3, 5 films with top layer of PZT(20/80) film of tetragonal structure showed fine grain structure and PZT-2, 4, 6 films with top layer of PZT(80/20) film of rhombohedral structure showed the dense grain microstructure without rosette-type. Dielectric constant and dielectric loss of the PZT-6 film were approximaterly 1385 and 3.3% respectively. Increasing the number of coatings remanent polarization was increased and coercive field was decreased and the values of the PZT-6 film were 8.13$\mu$C/cm$^2$and 12.5kV/cm respectively.

• 한국전기전자재료학회논문지
• /
• 제11권11호
• /
• pp.990-995
• /
• 1998

본 연구에서는 PZT(20/80)과 PZT(80/20) 금속 alkoxide용액을 Pt/Ti/$SiO_2$/Si 기판위에 상호 반복시킨 강유전성 PZT(20/80)/PZT(80/20) 이종층 박막을 제작하였다. 건조와 소결을 한번 행한 PZT 이종층 박막의 평균 두께는 약 80~90 nm이었다. 제작된 모든 PZT 박막은 rosette상이 없는 치밀하고 균질한 미세구조를 나타내었으며, 하부의 PZT층은 열처리시 상부 PZT층은 열처리시 상부 PZT 박막의 페로브스카이트 형성에 대해 nucleation site로 작용하였다. 유전상수, 피로특성 및 누설전류특성 등은 단일 조성의 PZT(20/80), PZT(80/20) 박막에 비해 우수한 특성을 나타내었다.

• 한국산학기술학회논문지
• /
• 제21권8호
• /
• pp.222-227
• /
• 2020

페로부스카이트(Perovskite) 구조의 Pb(Zr,Ti)O₃(PZT)는 우수한 강유전 특성으로 인해 유전체, 압전체, 초전체 재료로 널리 사용된다. Pb_1.3(Zr_0.52Ti_0.48)O₃조성의 스퍼터링 타겟을 제조하여 RF 마그네트론 스퍼터링 공정으로 PZT박막을 형성하였다. PZT박막은 동일 스퍼터링 출력으로 연속 제조한 단층형 PZT와 2단계화한 스퍼터링 출력으로 제조한 2층형 PZT박막으로 구분하여 제조하였다. 2층형의 PZT는 저출력의 스퍼터링 조건으로 제작한 하부층과, 단층형 PZT와 동일한 조건으로 제작한 상부층으로 이루어진다. 제조한 박막에 대한 엑스선 회절분석결과, 단층형 PZT에서는 페로부스카이트상(Perovskite Phase)과 미소한 파이로클로르상(Pyrochlore Phase)이 혼합된 상태로 존재하나, 2층형 PZT에서는 페로부스카이트상만이 검출되었다. 전자현미경과 원자힘 현미경으로 표면상태를 관찰한 결과, 2층형 PZT박막의 상부는 단층형에 비해 치밀하고 평활한 표면상태를 나타냈으며, 단층형에 비해 낮은 표면거칠기값(RMS)을 보였다. 또한 이층형 PZT는 단층형에 비해 우수한 대칭성의 분극곡선형태를 보였고, 단층형에 비해 매우 저감된 1×10^-5 A/㎠ 이하수준의 누설전류 특성을 나타냈다. 이층형 PZT에서 보이는 이러한 현상은 치밀하게 형성한 하부 PZT층이 순차적으로 형성되는 상부PZT내의 미소 파이로클로르상 형성을 억제하여, 순수한 페로부스카이트상으로의 성장을 유도한 것으로 판단된다.

• 한국전기전자재료학회논문지
• /
• 제19권11호
• /
• pp.1014-1019
• /
• 2006

The influence of the number of solution coatings on the densification of the PZT thick films was studied. PZT powder and PZT precursor solution was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were (A) PZT(80/20)/PZT(20/80), (B) PZT(70/30)/PZT(30/70) and (C) PZT(60/40)/PZT(40/60), (D) PZT(52/48)/PT. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 moth and the number of coating was repeated from 0 to 6. The porosity of the thick films was decreased with increasing the number of coatings and the PZT thick films with 6-times coated showed the dense microstructure and thickness of about $60{\mu}m$. A grain size was increased with increasing the coating number. All PZT thick films showed the typical XRD patterns of a typical perovskite polycrystalline structure. The relative dielectric constant of PZT thick films was improved 30-100% as the number of coatings.

• 대한기계학회논문집A
• /
• 제26권6호
• /
• pp.1001-1007
• /
• 2002

To improve the performance of the PZT thin flms, each PZT and PT layer was alternately deposited on a Pt/Ti/Si$_3$N$_4$/SiO$_2$/Si substrate by a modified sol-gel solid precursor technique. For comparison, PZT thin films were also prepared with an identical method under the same conditions. XRD measurement revealed that the diffraction pattern of the multilayer film was due to the superimposition of the PZT and PT patterns. At 1㎑, a dielectric constant of 389 and 558, a dielectric loss of 1.2% and 1.1% were obtained for the PZT/PT and PZT thin films, respectively. If we consider the PT dielectric constant to be 260, it is clear that the dielectric constant of alternately deposited PZT/PT thin films was well adjusted. The PZT/PT thin film showed a low dielectric constant and a similar dielectric loss compared with those of the PZT film. The figures of merit on detectivity for the PZT/PT and PZT thin films were 20.3$\times$10$\^$-6/㎩$\^$-$\sfrac{1}{2}$/, and 18.7$\times$10$\^$-6/㎩$\^$-$\sfrac{1}{2}$/, and the figures of merit on voltage response were 0.038㎡/C and 0.028 ㎡/C, respectively. The high figures of merit for the PZT/PT film were ascribed to its relatively low dielectric constant when compared to the PZT thin films.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권2호
• /
• pp.98-102
• /
• 2000

Ferroelectric PZT heterolayered thin films were fabricated by spin coating method on the Pt/Ti/SiO2/Si substrate using PZT(10/90) and PZT(90/10) m7etal alkoxide solutions. All PZT heterolayered films showed a homogeneous grain structures without presence of rosette structure. It can be assumed that the lower PZT layers played a role of nucleation site for the formation of the upper PZT layer. Pb-deficient PZT phase was formed at PZT/Pt interface due to the diffusion of Pb element into a Pt bottom electrode. The relative dielectric constant and the dielectric loss of the PZT-6 film were 567 and 3.6%, respectively. Increasing the number of coatings, remanent polarization and coercive field were decreased and the values of the PZT-6 heterolayered film were $7.18\muC/cm^2$ and 68.5kV/cm, respectively. Leakage current densities were increased with increasing the number of coatings, and the value of the PZT-4 film was about $7\times10-8A/cm^2$ at 0.05MV/cm.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제48권7호
• /
• pp.514-520
• /
• 1999

Ferroelectric PZT(30/70)/PZT(70/30) heterolayered thin films were fabricated by spin-coating method on the $Pt/Ti/SiO_2Si$ substrate alternately using(30/70) and PZT(70/30) alkoxide solutions prepared by sol-coating method. The coating and heating procedure was repeated six times to form PZT heterolayered films, and thickness of the film obtained by one-times drying/sintering process was about 40-50 nm. All PZT heterolayered films, showed dense and homogeneous structure without the presence of rosette sturctrue. The relative dielectric constant, remanent polarization and leakage current density of PZT heterolayered films were superior to those of single composition PZT(30/70) and PZT(70/30) films, and those values for the PZT-6 film were 975, $21 \muC/cm^2\; and\; 8\times10^{-9}\; A/cm^2$, respectively. And the PZT-6 heterolayered film showed fairly good fatigue characteristics of remanent polarization and coercive field after application of $10^8$ switching cycles.

• 한국세라믹학회지
• /
• 제25권2호
• /
• pp.125-130
• /
• 1988

The characteristics of the PZT/PMM and PZT/Butadiene composites with 3 dimensional network structure have been investigated as a function of the PZT volume fraction. The dielectric constants of the PZT composites increased linearly as the PZT volume fraction increased. However, they are not significantly affected by the polymer compliance. The piezoelectric d33 coefficients of the PZT/Butadiene are largest than the PZT/PMM because of the high elastic compliance which promotes stress transfer. The values of the mechanical quality factor adn frequency factor of the PZT/PMM composite are slightly larger, while the planar coupling factor is smaller, than the PZT/Butadiene composite. These results are due to strong interaction and mechanical coupling between PZT and PMM.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 제37회 하계학술대회 논문집 D
• /
• pp.2209-2210
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coaled on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field wore 16.48 ${\mu}C/cm^2$ and 35.48kV/cm, respectively.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 제37회 하계학술대회 논문집 D
• /
• pp.2211-2212
• /
• 2006

Ferroelectric PZT (70/30) thick films were fabricated by the screen printing method. And the PZT (30/70) precusor solution were infiltrated by the spin-coating method on the PZT thick films to obtain a densification. All PZT thick films were sintered at $1050^{\circ}C$ for 10 min. Structural properties, such as crystalline structure, microstructures and compositional ratio, of PZT thick films were investigated with the variation of the number of sol coatings using XRD, SEM and EDS, respectively. All PZT thick films exhibited a perovskite polycrystalline structure without a pyrochloer phase. The thickness of PZT thick films, 4-times screen-printed, was approximately $60{\mu}m$. And the densification of the PZT thick films increased with increasing the number of sol coatings.