Ferroelectric PZT heterolayered thin films were fabricated by spin coating method on the Pt/Ti/SiO$_2$/Si substrate using PZT(10/90) and PZT(90/10) metal alkoxide solutions. All PZT heterolayered films showed a homogeneous grain structure without presence of the rosette structure. It can be assumed that the lower PZT layers a role of nucleation site or seeding layer for the formation of the upper PZT layer. Zr and Ti diffusion into the Pt electrode were mainly distributed at the surface of Pt electrode beneath the PZT/Pt interface. The PZT/Pt interfacial layer showed a microstructure characterized by a grain phase surrounded by a Pb-deficient pyrochlore matrix phase. The relative dielectric constant and the dielectric loss of the PZT-6 film were 567 and 3.6, respectively.

• Electrical & Electronic Materials
• /
• v.9 no.3
• /
• pp.251-258
• /
• 1996

Sol-Gel derived ferroelectric Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ thin films have been fabricated on Pt/Ti/ $SiO_{2}$/Si substrate. Two kinds of fast annealing methods, F-I (six times of intermediate and final annealing) and F-II(one final annealing after six times of intermediate annealing) were used for preparation of multi-coated PZT thin films. As the annealing temperature was increased, high capacitance could be obtained, for instance, 2700.angs.-thick PZT thin film annealed at 680.deg. C had a capacitance value of approximately 20nF at 1kHz. In addition, it is found that the dielectric constant is a function of the perovskite phase fraction. In case of F-I method, PZT thin film had a remanent polarization(Pr) of 8-15.mu.C/c $m^{2}$ and a coercive field( $E_{c}$) of 35-44kV/cm according to annealing temperature, whereas PZT film fabricated by F-II method had as high as 24-25.mu.C/c $m^{2}$ and 48-59kV/cm, respectively. As a result of measuring Curie temperature, PZT thin film had a range of 460-480.deg. C by F-I method and more or less higher range of 525-530.deg. C by F-II method, which implied that different microstructures could cause the different Curie temperature. Through I-V measurement, leakage current of PZT thin film fabricated by F-I and F-II methods was 64nA/c $m^{2}$ and 2.2.mu.A/c $m^{2}$ in the electric field of 100kV/cm, respectively.y.y.y.

• Electrical & Electronic Materials
• /
• v.9 no.8
• /
• pp.836-850
• /
• 1996

In this study, we have analyzed structural analysis and measured ferroelectric characteristics of PZT thin films prepared by sol gel process with different sintering conditions and different Zr/Ti mot%. When the Zr mot% of PZT thin film was increased, it was found that the remanent. polarization and coercive field were decreased and increased, respectively. Also, the maxium dielectric constant of PZT(50/50) thin film was 786.8. We got double hysteresis(anti-fcrroelectric) curve from PbZrO$_{3}$ thin film. As heating rate goes up, pyrochlore phase of PZT thin film was decreased and dielectric and ferroelectric characteristics were improved. As a result of variation of sintering temperature and time 500.deg. C-800.deg. C and 5 sec.-8 hours, respectively, we got optimal sintering temperature and time. The optimium sintering temperature and time of conventional furnace method and rapid thermal processing method were 650.deg. C-700.deg. C for 30-60 minutes and 700.deg. C/20 seconds-2 minutes, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.247-250
• /
• 1998

Ferroelectric PZT(10/90)PZT(90/10) heterolayered thin films were fabricated by spin-coating method on the Pt/Ti/SiO$^2$/Si substrate alternately using PZT(10/90) and PZT(90/10) metal alkoxide solutions. The coating and heating procedure was repeated six times to form PZT heterolayered films. The surface, cross-sectional microstructures and thickness of the films were observed using scanning electron microscope(SEM). The relative dielectric constant and dielectric loss of the 5-coated PZT heterolayered films were 1331 and 4.8% respectively.

• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.51 no.2
• /
• pp.77-81
• /
• 2002

In this study, PZT thin films were fabricated using sol-gel processing onto Si/$SiO_2$/Ti/Pt substrates. PZT sol with different Zr/Ti ratio(20/80, 30/70, 40/60, 52/48) were prepared, respectively. The films were fabricated by using the spin-coating method on substrates. The films were heat treated at $450^{\circ}C$, $650^{\circ}C$ by rapid thermal annealing(RTA). The preferred orientation of the PZT thin films were observed by X-ray diffraction(XRD), and Scanning electron microscopy(SEM). All of the resulting PZT thin films were crystallized with perovskite phase. The fine crystallinity of the films were fabricated. Also, we found that the ferroelectric properties from the dielectric constant of the PZT thin films were over 600 degrees, P-E hysteresis constant. And the leakage current densities of films were lower than $10^{-8}A/cm^2$. It is concluded that the PZT thin films by sol-gel process to be convinced of application for ferroelectric memory device.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.11a
• /
• pp.10-10
• /
• 1994

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.11a
• /
• pp.126-126
• /
• 1999

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.11a
• /
• pp.116-116
• /
• 1999

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.05a
• /
• pp.89-89
• /
• 1998

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.36-36
• /
• 2003