• 한국분말재료학회지
• /
• 제11권6호
• /
• pp.477-485
• /
• 2004

Monodispersed flaky silver powder was obtained by controlling the ratios of $H_{2}O_{2}/NH_{3}$ and Agin in a mixed solution of ethylene glycol and ammonia with an addition of PVP. The effects of $NH_{3}/Ag,\; H_{2}O_{2}/Ag\;and\;H_{2}PtCl_{6}/Ag$ on its morphology and size were investigated. In $H_{2}O_{2}-NH_{3}-AgNO_{3}\;system,\;NH_{3}/Ag$ molar ratio was found to be an important reaction factor for the nucleation and crystal growth of Ag powder. The synthesis of flaky powder was optimized at over 6 of $NH_{3}/Ag \;and\;5\;of\;H_{2}O_{2}/Ag\;under\;1.0{\times}10^{-3}\;of\;Pt/Ag.\;Moreover,\;as\;the\; NH_{3}/Ag$ molar ratio increased, the size of precipitates was increased regardless of the amount of Pt. In the absence of $H_{2}PtCI$, the morphology and size of reduced Ag powder were found to be irregular in shape $2-4{\mu}m$ in diameter. However, homogenized fine Ag powder was obtained due to heterogeneous nucleation when $H_{2}PtCI$ used as a cat-alyst, and flaky one was synthesized with the addition of Pt over $1.0{\times}10^{-3}$ of Pt/Ag.

• 센서학회지
• /
• 제6권3호
• /
• pp.207-213
• /
• 1997

$H^{+}$ 이온에 선택적으로 감응하는 field effect transistor(pH-ISFET)를 바탕소자로 하고, 그 gate 주위에 Ag/AgCl 기준전극을 형성한 다음, 이를 둘러싼 수화젤(hydrogel)막 및 기체투과막의 이중막 구조를 가진 용존이산화탄소($CO_{2(aq)}$) 센서소자를 사진식각(photolithography)법으로 제작하였다. PVA-SbQ 혹은 PVP-PVAc/감광제 형의 광가교형 감광액은 수화젤막 형성에 적합하지 않았으나, 2-hydroxyethyl methacrylate(HEMA) 및 acrylamide를 포함하는 광중합형 감광액을 사용할 경우에는 사진식각법에 의한 수화젤막이 좋은 해상도로 얻어졌다. 기체투과막은 urethane acrylate계 UV-oligomer를 주성분으로 한 감광액을 써서 사진식각법으로 수화젤막위에 형성할 수 있었다. 또한 수화젤막 및 기체투과막을 사진식각법으로 형성할 때 N,N,N',N'-tetramethyl ethplenediamine(TED) 을 $O_{2}$ quencher로서 감광액 중에 도입함으로써 UV 노광시에 polyester film을 부착하는 번거로운 공정을 생략할 수 있음을 알았다. 이렇게 제조된 $pCO_{2}$ 센서는 수용액 중에서 $10^{-3}{\sim}10^{0}\;mol/{\ell}$의 $CO_{2}$ 농도변화에 대하여 직선적인 검정곡선(calibration curve)을 얻을 수 있었다.

• 대한화학회지
• /
• 제47권4호
• /
• pp.339-344
• /
• 2003

Paraquat는 가장 효과적이고 널리 사용되는 제초제이지만 인간에게 매우 유독한 물질이다. 중독환자에 있어 뇨중 농도는 가장 중요한 인자중의 하나로 알려져 있으나 일반 검사실에서 이를 위한 정량검사는 거의 시행되지 않고 있다. 본 연구에서는 sodium dithionite를 이용하여 뇨중의 paraquat의 농도를 측정하는 새로운 방법의 진단 시험지를 개발하였다. 이 이차유도성 방식을 사용하여 paraquat의 농도를 측정한 결과 $0.5{\%}$ borate 완충용액(pH 8.0), 유도체 0.25 M $Na_2S_2O_4,\0.1~0.8{\%}$ PolyVinyl Pyrrolidone(PVP) 안정제, $1{\%}$ decanol의 구성비로 만들어진 진단시험지의 반응 색상이 안정하며 표준 비색표에 의한 육안적인 감별은 물론 화학 자동분석기에서의 응용성이 좋았다.

• Fisheries and Aquatic Sciences
• /
• 제19권1호
• /
• pp.1.1-1.6
• /
• 2016

Although soft tunic syndrome (STS) in the ascidian is a serious disease, helpful measures have yet not been established. It was examined in this study by applying aniti-parasitic drugs to eradicate the causative protozoa Azumiobodo hoyamushi from infected ascidians. Formalin was synergistic in killing parasites in vitro when co-treated with hydrogen peroxide ($H_2O_2$) or bronopol, but not with chloramine-T or povidone-iodine (PVP-I), when tested with in vitro parasite culture. The synergistic effects did not change when $formalin-H_2O_2$ (or bronopol) ratios were changed. It was found that treatment periods less than 60 min achieved a sub-maximal efficacy. Increasing drug concentration while keeping 30 min period improved anti-parasitic effects. Anti-parasitic effects of $formalin(F)+H_2O_2$(H) were also assessed in an in vivo STS model infected with cultured parasites. It was observed that combined 50 (40F + 10H) and 100 (80F +20H) ppm were effective in partially preventing STS-caused mortality. In horizontally transmitted artificial STS model, significant prevention of ascidian mortality was also observed after 50 ppm. Marked reduction of living parasites were noted after drug treatments in vivo. The results provide a highly useful basis to develop a preventive or treatment measure against the currently uncontrollable STS in the ascidian.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.390-390
• /
• 2014

Soft-lithography 기술 중의 하나인 Micro-Contact Printing (${\mu}$-CP) 기술은 패턴이 형성된 mold 위에 고분자 물질을 코팅하고 기판과 접촉시켜, 패턴 된 부분만 기판으로 전사시켜 패턴을 형성하는 방법이다. ${\mu}$-CP 기술은 Imprint 방식과 비교하여 잔여물을 제거하기 위한 ashing 공정이 필요 없으며, 상대적으로 패턴이 전사되기 위한 공정 온도와 압력이 낮은 장점이 있다. 한편, 기존의 Photolithography 기술로 유기기판에 패턴을 형성하는 것은 제한이 있으며, 자외선에 의해 유기기판의 특성이 변화될 수 있다. 또한 패턴 형성 후 고분자 패턴을 제거하는 용매가 기판이 손상 받게 된다. 본 실험에서는 poly (1H,1H,2H,2H-perfluorodecyl methacrylate) polymer (PFDMA) films을 패턴 된 poly (dimethylsiloxane) (PDMS) mold 위에 코팅하고 ${\mu}$-CP 기술을 통해 poly (methylmethacrylate) (PMMA), poly (vinyl pyrrolidone) (PVP)등과 같은 유기기판 위에 고분자 패턴 형성을 하였다. 이때 전사 가능한 온도는 상온이며, 압력은 코팅된 PFDMA films이 기판과 접촉될 수 있는 정도만 필요하다. PFDMA가 상온에서 전사 가능한 이유는 유리전이온도가 상온보다 낮기 때문이다. 또한 접촉각을 측정하여 접착력을 계산하면 PFDMA와 기판과의 접착력이 상대적으로 높기 때문이다. PFDMA는 플루오르계 용매에 제거되기 때문에 유기기판의 손상을 최소화 할 수 있다. ${\mu}$-CP 기술을 이용한 PFDMA의 패턴 형성 방법은 물질의 특성으로 flexible 및 organic device 제작에 응용 될 수 있다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.154-154
• /
• 2012

Flexible complementary inverters based on thin-film transistors (TFTs) are important because they have low power consumption and high voltage gain compared to single type circuits. We have manufactured flexible complementary inverters using pentacene and amorphous indium gallium zinc oxide (IGZO) for the p-channel and n-channel, respectively. The circuits were fabricated on polyimide (PI) substrate. Firstly, a thin poly-4-vinyl phenol (PVP) layer was spin coated on PI substrate to make a smooth surface with rms surface roughness of 0.3 nm, which was required to grow high quality IGZO layers. Then, Ni gate electrode was deposited on the PVP layer by e-beam evaporator. 400-nm-thick PVP and 20-nm-thick ALD Al2O3 dielectric was deposited in sequence as a double gate dielectric layer for high flexibility and low leakage current. Then, IGZO and pentacene semiconductor layers were deposited by rf sputter and thermal evaporator, respectively, using shadow masks. Finally, Al and Au source/drain electrodes of 70 nm were respectively deposited on each semiconductor layer using shadow masks by thermal evaporator. The characteristics of TFTs and inverters were evaluated at different bending radii. The applied strain led to change in voltage transfer characteristics of complementary inverters as well as source-drain saturation current, field effect mobility and threshold voltage of TFTs. The switching threshold voltage of fabricated inverters was decreased with increasing bending radius, which is related to change in parameters of TFTs. Throughout the bending experiments, relationship between circuit performance and TFT characteristics under mechanical deformation could be elucidated.

• 마이크로전자및패키징학회지
• /
• 제22권2호
• /
• pp.33-39
• /
• 2015

타이타늄산바륨($BaTiO_3$)은 대표적인 강유전 물질로 유전상수가 200 이상의 값을 나타내는 물질이다. 타이타늄산바륨을 나노입자화하면 나노커패시터(nanocapacitors)와 강유전체 메모리(ferroelectric random access memories)와 같이 여러 용도로 응용 가능하다. 하지만, 나노입자의 합성방법에 따라 나노입자의 분산특성이 달라지며 이에 활용할 수 있는 분야가 달라질 수 있다. 본 연구에서는 타이타늄산바륨 나노입자를 옥살레이트법(oxalate method)과 sol-gel법(ambient condition sol method)으로 합성하고 각 방법에 따른 나노입자의 크기와 분산상태를 확인하였다. 각각의 공정에 사용한 캡핑 에이전트(capping agent)는 poly vinyl pyrrolidone (PVP)을 옥살레이트법에 이용하였고 sol-gel법에는 tetrabutylammonium hydroxide (TBAH)를 이용하였다. 합성된 나노입자의 X-선 회절 분석 패턴을 분석하여 cubic 결정구조를 갖는 타이타늄산바륨을 확인하였다. 푸리에(Fourier) 변환 적외선 분광분석을 이용하여 나노입자의 캡핑 에이전트 결합상태와 시차주사현미경과 입도분석기를 이용한 나노입자의 크기 및 뭉침 변화를 확인하였다.

• 멤브레인
• /
• 제29권6호
• /
• pp.348-354
• /
• 2019

최근 유기용매나노분리막(OSN) 기술의 응용분야가 확대되고 있으며 그에 따른 분리막 성능향상이 요구되고 있다. 본 연구에서는 박막복합막 형태의 OSN 분리막을 제조하여 용매의 투과성능을 측정하였다. 먼저 비용매상전이법(NIPS)을 활용하여 한외여과막 지지체를 제조하였고, 지지체의 성능을 최적화하기 위해 고분자(PSf or PES)와 기공형성제(PVP or Pluronic F-127)의 종류 및 조성의 영향을 확인하였다. 지지체 표면에 MPD와 TMC 단량체를 계면중합하여 폴리아미드 박막을 형성하였다. 제막된 박막복합막 OSN 분리막의 용매투과성능과 배제율을 측정하여 평가하였다. OSN 지지체로는 PSf 대비 PES 지지체의 성능이 안정적이었으며 Pluronic F-127보다 PVP를 도프용액에 첨가하였을 때 성능이 더 향상되었다. 기존 TMC-MPD 반응을 활용하여 박막복합막을 제조하였을 때 Acetonitrile 용매의 투과성능이 EtOH보다 월등히 높은 것을 확인할 수 있었다.

• 식물조직배양학회지
• /
• 제22권1호
• /
• pp.7-11
• /
• 1995

종자발아 후 5일된 양배추 그린챌린져 배축으로부터 분리된 원형질체로부터 완전한 식물체를 재분화 시켰다. Kao배지와 B5 배지를 기본으로 한 기존의 몇가지 배지에서 원형질체를 배양한 결과 변형시킨 BS배지에서 Plating efficiency는 낮았으나 식물체 재분화율은 가장 높게 나타나 거의 원형질체 배양배지 조성, 생장조절제 농도 등이 재분화에 상당한 영향을 주는 것으로 나타났다. 또한 사용된25가지 종류의 재분화 배지중에서 MS배지에 l% sucrose zeatin 3 mg/L, 1.6% T.C. agar가 첨가된 배지에서 재분화율이 가장 좋았다. 식물체 재분화에 미치는 PVP (polyvinyl Polypyrrolidone)와 agar 농도의 영향으로는 PVP는 큰 효과가 없었고 agar농도를 1.6%로 2배 증가시켰을 때 재분화율이 다소 높아졌다. 현재까지 재분화된 식물체는 150여 개체로서 포장에서 재배중에 있다.

• 한국재료학회지
• /
• 제21권6호
• /
• pp.327-333
• /
• 2011

Nanostructured cobalt materials have recently attracted considerable attention due to their potential applications in high-density data storage, magnetic separation and heterogeneous catalysts. The size as well as the morphology at the nano scale strongly influences the physical and chemical properties of cobalt nano materials. In this study, cobalt nano particles synthesized by a a polyol process, which is a liquid-phase reduction method, were investigated. Cobalt hydroxide ($Co(OH)_2$), as an intermediate reaction product, was synthesized by the reaction between cobalt sulphate heptahydrate ($CoSO_4{\cdot}7H_2O$) used as a precursor and sodium hydroxide (NaOH) dissolved in DI water. As-synthesized $Co(OH)_2$ was washed and filtered several times with DI water, because intermediate reaction products had not only $Co(OH)_2$ but also sodium sulphate ($Na_2SO_4$), as an impurity. Then the cobalt powder was synthesized by diethylene glycol (DEG), as a reduction agent, with various temperatures and times. Polyvinylpyrrolidone (PVP), as a capping agent, was also added to control agglomeration and dispersion of the cobalt nano particles. The optimized synthesis condition was achieved at $220^{\circ}C$ for 4 hours with 0.6 of the PVP/$Co(OH)_2$ molar ratio. Consequently, it was confirmed that the synthesized nano sized cobalt particles had a face centered cubic (fcc) structure and with a size range of 100-200 nm.