• Clean Technology
• /
• v.24 no.1
• /
• pp.63-69
• /
• 2018

The reduction reaction characteristics and physicochemical properties were studied for the selection of oxygen carrier, which is the core of the chemical looping combustion (CLC) technology. Fuel conversion and $CO_2$ selectivity of oxygen carrier according to the concentration of reducing gas and the reduction temperature using three kinds of oxygen carrier (SDN70, N018-R2, N016-R4) were measured and compared. In addition, Attrition Index (AI) and BET surface area were measured to analyze the attrition resistance and the surface characteristics of the oxygen carrier. As a result, it was confirmed that all three kinds of oxygen carrier were suitable for use in chemical roofing combustion system, and the best particle was determined to be N016-R4.

• Journal of Magnetics
• /
• v.13 no.2
• /
• pp.61-64
• /
• 2008

We studied the effect of the variation of the lattice constant on the electrical properties of $SrRuO_3$ thin films. In order to obtain films with different volumes, we varied the substrate temperature and oxygen pressure during the growth of the films on $SrTiO_3$ (001) substrates. The films were grown using a pulsed laser deposition method. The X-ray diffraction patterns of the grown films at low temperature and low oxygen pressure indicated the elongation of the c-axis lattice constant compared to that of the films grown at a higher temperature and higher oxygen pressure. The in-plane strain states are maintained for all of the films, implying the expansion of the unit-cell volume by the oxygen vacancies. The variation of the electrical resistance reflects the temperature dependence of the resistivity of the metal, with a ferromagnetic transition temperature inferred form the cusp of the curve being observed in the range from 110 K to 150 K. As the c-axis lattice constant decreases, the transition temperature linearly increases.

• Journal of the Korean Ceramic Society
• /
• v.36 no.9
• /
• pp.982-990
• /
• 1999

YSZ/LSM composite cathode was fabricated by dip-coating of YSZ sol on the internal pore surface of a LSM cathode followed by sintering at low temperature (800-100$0^{\circ}C$) The YSZ coating significantly increased the TPB(Triple Phase Boundary) where the gas the electrode and the electrolyte were in contact with each other. Sinter the formation of resistive materials such as La2Zr2O7 or SrZrO3 was prevented due to the low processing temperature and TPB was increased due to the YSZ film coating the electrode resistance (Rel) was reduced about 100 times compared to non-modified cathode. From the analysis of a.c impedance it was shown that microstructural change of the cathode caused by YSZ film coating affected the oxygen reduction reaction. In the case of non-modified cathode the RDS (rate determining step) was electrode reactions rather than mass transfer or the oxygen gas diffusion in the experimental conditions employed in this study ($600^{\circ}C$-100$0^{\circ}C$ and 0,01-1 atm of Po2) for the YSZ film coated cathode however the RDS involved the oxygen diffusion through micropores of YSZ film at high temperature of 950-100$0^{\circ}C$ and low oxygen partial pressure of 0.01-0.03 atm.

• Journal of the Korean Ceramic Society
• /
• v.38 no.1
• /
• pp.84-92
• /
• 2001

(La,Sr)MnO$_3$(LSM)-YSZ 복합체 양극의 산소환원 반응기구에 대해 고찰하였다. YSZ를 첨가함에 따라 복합체 양극의 ohmic 저항이 증가하고, 분극 저항은 YSZ를 40 wt%~50 wt% 혼합하였을 때 최소값을 나타내었다. 또한 LSM-YSZ 복합체 양극의 산소환원 반응기구는 1가 산소이온의 표면확산과 산소이온전달반응에 의해서 지배됨을 알 수 있었다. 임피던스 분석 결과에 따르면 고주파수 영역에서 나타나는 반원은 산소이온전달반응으로 산소분압 의존성이 거의 없고, YSZ가 40 wt% 첨가되었을 때 최소값을 나타내었다. 중간주파수 영역에서 나타나는 반원은 1가 산소이온의 표면확산반응으로 산소분압 의존성은 약 1/4이고, YSZ가 40~50 wt% 첨가되었을 때 최소값을 나타냈다. 한편, 저주파수 영역에 나타나는 반원은 가스확산반응으로 산소분압 의존성이 1이고, 온도에 따른 의존성이 거의 없었다.

• Journal of Korean Vacuum Science & Technology
• /
• v.5 no.2
• /
• pp.47-51
• /
• 2001

To obtain high remnant polarization and good crystalinity of ferroelectric thin films in non-volatile memory devices, the high temperature treatment in oxygen ambient is inevitable. Severe problems that occur in this process are oxygen diffusion into substrate, oxidation of electrode and buffer layer, degradation of microstructure and so on. We made ruthenium dioxide thin film by reactive sputtering with oxygen and argon mixture atmosphere. Comparing quantitatively the core-level spectra of Ru and RuO$_2$ obtained by x-ray photoelectron spectroscopy(XPS), we found that chemical state of RuO$_2$ is very stable and of good resistance to oxygen diffusion and oxidation of adjacent layers. It opens the use of RuO$_2$ thin film as a multifunctional layer of good conducting electrode and resistive barrier for the diffusion and the oxidation. We also suggest a correct understanding of Ru 3d core-level spectrum for RuO$_2$ based on the scheme of final state screening and charge transfer satellites.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05b
• /
• pp.58-61
• /
• 2003

ITO (indium tin oxide) thin films on PET (polyethylene terephthalate) substrate have been deposited by a dc reactive magnetron sputtering without heat treatments such as substrate heater and post heat treatment. Each sputtering parameter during the sputtering deposition is an important factor for the high quality of ITO thin films deposited on polymeric substrate. Particularly, the material, electrical and optical properties of as-deposited ITO oxide films are dominated by the ratio of oxygen partial pressure. As the experimental results, the excellent ITO films are prepared on PET substrate at the operating conditions as follows: operating pressure of 5 mTorr,target-substrate distance of 45 mm, dc power of 20-30 W, and oxygen gas ratio of 10 %. The optical transmittance is above 80 % at 550 nm, and the sheet resistance and resistivity of films are $24\;{\Omega}$/square and $1.5{\times}10^{-3}\;cm$, respectively.

• The Korean Journal of Malacology
• /
• v.22 no.2
• /
• pp.151-155
• /
• 2006

Proportion of Tegillarca granosa surviving after 2-6 hrs air exposure with 12 hrs interval at $20^{\circ}C$ and $28^{\circ}C$ for 20 days showed 85-100%, 80-100%, respectively. The survival rate was somewhat lower at high temperature but not significant (p < 0.05). Subsequent exposures for 7-9 days showed survival rate of 8.0-24.1% at $20^{\circ}C$ and $28^{\circ}C$. Oxygen consumption rates and filtration rates were significantly higher for 4 to 6 hrs exposures, compared with the preceding exposures. On the other hand, at $28^{\circ}C$, oxygen consumption rates in adult granular ark for 6 hrs exposure during 20 days had significantly decreased. Filtration rates in study groups increased a little over extended period of exposure, compared with those in control groups, and were similar irrelevant to the time of exposure and size of experimental animals. It is concluded, in view of their viability and oxygen consumption rate during air exposure, that ark shells have quite a high resistance to air exposure with their limited range of responses.

• Journal of Korean Society on Water Environment
• /
• v.27 no.1
• /
• pp.44-53
• /
• 2011

Membrane bio-reactor (MBR) has several advantages over the conventional activated sludge process, including a high biomass, low sludge production, and better permeate quality. Therefore, the MBR have gained popularity for municipal and industrial wastewater treatment. However the MBR usually were used for sewage and low streng th wastewater treatment because of membrane fouling problem and limitation of oxygen transfer into biomass. In this study, the hybrid process combining MBR and pure oxygen was tested for high strength organic wastewater treatment in the COD loading range from 2 to $10kgCOD/m^3{\cdot}day$. The hybrid process, membrane coupled pure oxygen high compact reactor (MPHCR), had been operated for one year and operation parameters, the effect of COD loading, MLSS concentration and the location of membrane module were studied for membrane fouling characteristic. Also membrane resistance test and the component of foulant was analyzed to investigate what is specific foulant in the MBR.

• Corrosion Science and Technology
• /
• v.5 no.2
• /
• pp.45-51
• /
• 2006

Properties of the anode for cathodic protection need low overvoltage for oxygen evolution and high corrosion resistance. It is well known that DSA (Dimensionally Stable Anode) has been the best anode ever since. DSA is mainly composed of $RuO_2$, $IrO_2$, $ZrO_2$, $Co_2O_3$, and also $Ta_2O_5$, $TiO_2$, $MnO_2$ are added to DSA for better corrosion resistance. The lifetime of DSA for cathodic protection is also one of the very important factors. $RuO_2$, $IrO_2$, $RhO_2$, $ZrO_2$ are well used for life extension, and many researches are focused on life extension by lowering oxygen evolution potential and minimizing dissolution of oxide coatings. This work aims to evaluate the influence of constituents of MMO and coating cycles and $ZrO_2$ coating on the electrochemical properties and lifetime of DSA electrodes. From the results of lifetime assessment in the anodes coated with single component, $RuO_2$ coating was more effective and showed longer lifetime than $IrO_2$ coating. Also, an increased coating cycle and an electrochemically coated $ZrO_2$ could enhance the lifetime of a DSA.

• Journal of the Korean Institute of Gas
• /
• v.17 no.1
• /
• pp.35-41
• /
• 2013

In this study, flame retardancy of polyurethane foam and phenolic foam were investigated by addition of phosphorous flame retardants. The thermal degradation behavior of polyurethane foam and phenolic foam in the presence of flame retardants has been studied by thermogravimetric analysis(TGA). Heat release rate(HRR), mean HRR, mass loss rate(MLR), total smoke released(TSR) and limited oxygen index(LOI) were tested by cone calorimeter. From the test results, Phenolic foam showed low HRR, MLR and TSR than polyurethane foam.