The Object Directory Service(ODS) of the mobile RFID is the core technology of the object information service for the object information retrieval among objects with RFID tags. The ODS service returns an URL information of a specific object application service after recognizing the mRFID tag in real time. The general ODS service is suitable for the global mRFID environment, but it is not good in the local networks and private networks that information security is needed. This paper proposes a new ODS service algorithm for the improvement of the general ODS service algorithm.

• Journal of Powder Materials
• /
• v.17 no.2
• /
• pp.113-122
• /
• 2010

Two kinds of oxide-dispersion-strengthened (ODS) 316L stainless steel were manufactured using a wet mixing process(wet) and a mechanical alloying method (MA). An MA 316L ODS was prepared by a mixing of metal powder and a mechanical alloying process. A wet 316L ODS was manufactured by a wet mixing with 316L stainless steel powder. A solution of yttrium nitrate was dried after being in the wet 316L ODS alloy. The results showed that carbon and oxygen were effectively reduced during the degassing process before the hydroisostatic process (HIP) in both alloys. It appeared that the effect of HIP treatment on increase in impact energy was pronounced in the MA 316L ODS alloy. The MA 316L ODS alloy showed a higher yield strength and a smaller elongation, when compared to the wet 316L ODS alloy. This seemed to be attributed to the enhancement of bonding between oxide and matrix particles from HIP and to the presence of a finer oxide of about 20 nm from the MA process in the MA 316L ODS alloy.

• Proceedings of the Korea Information Processing Society Conference
• /
• 2005.05a
• /
• pp.599-602
• /
• 2005

본 논문에서는 운영 레거시 시스템으로부터 엔드 유저에까지 실시간으로 데이터를 전달하는 전체적인 프로세스를 정의한 ODS 레이어를 제시한다. ODS 의 레이어를 위하여 먼저 데이터 소스가 정의된다. 그 다음 데이터 소스로부터 ODS까지 데이터를 수집하는 방법이 정의된다. 마지막으로 엔드 유저 집단을 위한 ODS로의 데이터 접근을 준비한다. 운영 시스템과 ODS 간의 통합 레벨에 따른 ODS의 타입을 분류하고 특성을 요약한다.

• Proceedings of the Korea Information Processing Society Conference
• /
• 2008.11a
• /
• pp.1031-1034
• /
• 2008

현재 ODS(Object Directory Service) 검색 서비스는 글로벌한 모바일 RFID 환경에 적합하지만, 지역적인 로컬 네트워크 및 정보보안이 필요한 사설 네트워크에서는 불필요한 검색시간이 요구되고 효율성이 떨어지는 서비스 시스템이다. 따라서 본 논문에서는 기존의 ODS 검색 서비스 알고리즘을 개선하여 새롭게 로컬 환경에 적합한 ODS 검색 서비스 알고리즘을 제안하고, 개선된 ODS 검색 서비스 시스템의 성능평가 결과를 제시한다..

• Archives of Metallurgy and Materials
• /
• v.64 no.3
• /
• pp.921-924
• /
• 2019

In this study, ODS ferritic stainless steels were fabricated using a commercial alloy powder, and their microstructures and mechanical properties were studied to develop the advanced structural materials for high temperature service applications. Mechanical alloying and uniaxial hot pressing processes were employed to produce the ODS ferritic stainless steels. It was revealed that oxide particles in the ODS stainless steels were composed of Y-Si-O, Y-Ti-Si-O, and Y-Hf-Si-O complex oxides were observed depending on minor alloying elements, Ti and Hf. The ODS ferritic stainless steel with a Hf addition presented ultra-fine grains with uniform distributions of fine complex oxide particles which located in grains and on the grain boundaries. These favorable microstructures led to superior tensile properties than commercial stainless steel and ODS ferritic steel with Ti addition at elevated temperature.

• Proceedings of the KSME Conference
• /
• 2005.11a
• /
• pp.134.1-134.1
• /
• 2005

• Journal of Powder Materials
• /
• v.25 no.1
• /
• pp.36-42
• /
• 2018

In order to expand the application of oxide dispersion-strengthened (ODS) steel, a composite material is manufactured by adding mechanically alloyed ODS steel powder to conventional steel and investigated in terms of microstructure and wear properties. For comparison, a commercial automobile part material is also tested. Initial microstructural observations confirm that the composite material with added ODS steel contains i) a pearlitic Fe matrix area and ii) an area with Cr-based carbides and ODS steel particles in the form of a $Fe-Fe_3C$ structure. In the commercial material, various hard Co-, Fe-Mo-, and Cr-based particles are present in a pearlitic Fe matrix. Wear testing using the VSR engine simulation wear test confirms that the seatface widths of the composite material with added ODS steel and the commercial material are increased by 24% and 47%, respectively, with wear depths of 0.05 mm and 0.1 mm, respectively. The ODS steel-added composite material shows better wear resistance. Post-wear-testing surface and cross-sectional observations show that particles in the commercial material easily fall off, while the ODS steel-added material has an even, smooth wear surface.

• Nuclear Engineering and Technology
• /
• v.51 no.4
• /
• pp.1069-1074
• /
• 2019

A novel fabrication method of oxide dispersion strengthened (ODS) steel cladding tubes for advanced fast reactors has been investigated using the cold spray powder-based materials deposition process. Cold spraying has the potential advantage for rapidly fabricating ODS cladding tubes in comparison with the conventional multi-step extrusion process. A gas atomized spherical 14YWT (Fe-14%Cr, 3%W, 0.4%Ti, 0.2% Y, 0.01%O) powder was sprayed on a rotating cylindrical 6061-T6 aluminum mandrel using nitrogen as the propellant gas. The powder lacked the oxygen content needed to precipitate the nanoclusters in ODS steel, therefore this work was intended to serve as a proof-of-concept study to demonstrate that free-standing steel cladding tubes with prototypical ODS composition could be manufactured using the cold spray process. The spray process produced an approximately 1-mm thick, dense 14YWT deposit on the aluminum-alloy tube. After surface polishing of the 14YWT deposit to obtain desired cladding thickness and surface roughness, the aluminum-alloy mandrel was dissolved in an alkaline medium to leave behind a free-standing ODS tube. The as-fabricated cladding tube was annealed at $1000^{\circ}C$ for 1 h in an argon atmosphere to improve the overall mechanical properties of the cladding.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.227-234
• /
• 2000

AGV is very proper equipment for Port Automation. AGV must have Obstacle Detection System(ODS) for port automation. Obstacle Detection System must have some functions. It must be able to classify some specified object from background data. And it must be able to track classified objects. Finally, ODS must determine its next action for safe cruise whether it must do emergency stop or it must speed down or it must change its track. For these functions, ODS can have many different structures. In this paper, we will propose one structure among some possible ones. Our ODS has been being developed using proposed structure since last year. In this paper, we will introduce our system which is under construction.

• Analytical Science and Technology
• /
• v.6 no.5
• /
• pp.509-514
• /
• 1993

Benomyl, topsin-M and thiram been known as one of the seed disinfectant. For these studies benomyl, topsin-M and thiram simultaneously had been analyzed by high performance liquid chromatographic method using ODS cartridge, benomyl, topsin-M and thiram was chromatographed using an ODS column and eluent 40% Acetonitrile at a flow rate of 1ml/min. The UV Detector responses at 276nm.