• International Journal of Railway
• /
• v.5 no.2
• /
• pp.89-92
• /
• 2012

Effective notch stress, as an approach to evaluate the local stress at a notch (weld toe or root), is defined as the total stress assuming linear-elastic material behavior. This method can be effectively used to evaluate the fatigue performance of welded joints. In this study, finite element analysis results using the effective notch stress method were correlated with fatigue test results of rib-to-deck welded joints in a steel orthotropic bridge deck. Effective notch stress approach provided a good correlation with the crack pattern observed in the full-scale fatigue test. A higher effective notch stress at the critical weld toe than at the weld root was consistent with the dominant crack pattern observed at the weld toe during testing. The effective notch stress at the toe on the deck plate was about 80% higher than that on the rib; no cracks at the weld toe on the rib in the testing were observed. Maximum effective notch stress at the weld root occurred on the upper side of the root notch, which indicates that cracks are more likely to propagate into the deck plate, not into the weld metal. This is also consistent with the observed crack pattern in which the crack from the root propagated upward into the deck plate. No such crack pattern, propagating into the weld metal, was observed in the testing.

• Journal of Adhesion and Interface
• /
• v.7 no.4
• /
• pp.18-23
• /
• 2006

The influence of the notch length on the stress distribution of mid-bondline and adherend was investigated using elasto-plastic finite element method. The results from the simulation showed that peak stress of mid-bondline decreased markedly as adherend with notch in the middle of lap zone, and the stress in the middle of joint with low stress originally increased evidently. All the peak stresses decreased firstly and increased again as the length of notch increased. The relative higher peak stress appeared at the point near the notch of adherend where might be failed previously during the loading procedure.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.1358-1361
• /
• 2003

In this study, intrinsic static/dynamic fracture toughness of Al 7175-T74 are evaluated from the apparent static/dynamic toughness of notched specimen. The notch/crack critical average stress fracture model is suggested to establish the relationship to predict the intrinsic fracture toughness from the apparent fracture toughness of a notched specimen. The notch/crack critical average stress fracture model is established using the relation between the notch root radius and the effective distance calculated by finite element analysis. It is conclude that the true fracture toughness can be estimated from test results of apparent fracture toughness measured by using a notched specimen. Also, critical notch root radius can be predicted by notch/crack critical average stress fracture model.

• Journal of the Society of Naval Architects of Korea
• /
• v.47 no.4
• /
• pp.573-579
• /
• 2010

The notch effects on the fatigue strength of welded joints are both stress concentration and fatigue strength reduction. In the notch stress approach, the notch effects are usually approximated by introducing weld-bead parameters for the local detailed weld joints. In this paper, well-known notch stress approaches - critical distance method, area method and fictitious rounding method are presented for the fatigue strength of cruciform joints. The estimated results of the present methods are applied to the experiments performed in this study and reported in the references. The results of the application show that the fatigue-life scatterness of the experimental data expressed in the nominal stress is significantly reduced by introducing the effective fatigue stress of the present study.

• Journal of Biosystems Engineering
• /
• v.1 no.1
• /
• pp.64-72
• /
• 1976

This experimental work was carried out to investigate the fatigue bending strength on various shapes and sizes of notches of the domestically manufactured steel plate. The notch types tested were a circular hole, U-and V-notches. The S-N diagram for different notch shapes were discussed in relation to plan bending strength and stress concentration factor of notches .The results of the experiments are summarized as follows : (1) The difference between stress concentration factor and notch factor was greater as the radium of notch root became smaller, and these values approached to an identical value as the radium of notch root increased. (2) It was shown that the plane bending fatigue limit of bar without notch for the hotrolled steel having the tensile strength of 33.1kg/$mm^2$was 17.0kg/$mm^2$. (3) U-and V-notch had a greater effect of stress concentration factor on the endurance limit, but O-hole showed the same effect only for $\o\pm2mm$. (4) For the same radius of notch root, U-notch showed a lower value of fatigue limit compared to V-notch and O-hole.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.8 no.2
• /
• pp.127-132
• /
• 1984

In this paper, stress concentration factor and distribution of slotted or notched plate which is subjected to uniaxial tensile load are studied. The experimental measurements have shown the following; (1)The stress around slot or notch of slotted or notched plate which is subjected to uniaxial tensile load is state of biaxial stress, which is mainly varied to notch radius and depth. (2)The stress concentration factor around slot or notch is mainly influenced by the .sigma.$_{yy}$ , it is varied with notch radius and depth. (3)For the notched specimen, there is a notch depth where stress concentration factor is maximum. On the other hand, for the slotted specimen, stress concentration factor increases as the notch depth increases. An investigation of the relationship between fracture and stress concentration factor due to the slot or notch will be presented on the later paper, for reference.

• Journal of Ocean Engineering and Technology
• /
• v.25 no.5
• /
• pp.47-51
• /
• 2011

This paper analyzes the fatigue-life of welded joints using the notch stress approach. In the notch stress approach, the notch effects are usually approximated by introducing weld-bead parameters for the local detailed weld joints. The actual bead shape is complex and 3-dimensional. It may also greatly influence the fatigue strength. In this study, the welded shape was modeled using a 3D-scanner. The critical distance method was adopted in the evaluation of the fatigue effective notch stress for the weldments. Fatigue life tests were performed to verify the present method of fatigue life estimation for two types of welded plates with longitudinal attachments. The estimated results of the present methods were applied to the results of the experiment. The results of the analysis showed that the scatter of fatigue-life for the experimental data expressed in the nominal stress was significantly reduced by applying the effective fatigue stress of the present study.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.10a
• /
• pp.795-798
• /
• 1997

This study is about the dynamic behavior of steel(SM45C). Dynamic tests were performed using SHPB(Split Hopkinson Pressure Bar) which is designed and modified to be used in both tensile and compressive modes. Quasi-static compression tests were also carried out for the comparison to the dynamic results. Not only the dynamic mechanical properties but also the effect of the notch of the specimen on stress-strain curve were investigated. The dynamic test results reveal that strain and stress are sensitively affected by the notch. The depth and the number of notch increase the stress and decrease the strain.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.145-150
• /
• 2002

It has been well known that ductile fracture of steels is accelerated by triaxial stresses. The characteristics of ductile crack initiation in steels are evaluated quantitatively using two-parameters criterion based on equivalent plastic strain and stress triaxiality. It has been demonstrated by authors using round-bar specimens with circumferential notch in single tension that the critical strain to initiate ductile crack from specimen center depends considerably on stress triaxiality, but surface cracking of notch root is in accordance with constant strain condition. In order to evaluate the stress/strain state in the specimens, especially under dynamic loading, a thermal, elastic-plastic, dynamic finite element (FE) analysis considering the temperature rise due to plastic deformation has been carried out. This study provides the fundamental clarification of the effect of strength mismatching, which can elevate plastic constraint due to heterogeneous plastic straining, loading mode and loading rate on critical condition to initiate ductile crack from notch root using equivalent plastic strain and stress triaxiality based on the two-parameter criterion obtained on homogeneous specimens under static tension. The critical condition to initiate ductile crack from notch root for strength mismatched bend specimens under both static and dynamic loading would be almost the same as that for homogeneous tensile specimens with circumferential sharp notch under static loading.

• Journal of the Society of Naval Architects of Korea
• /
• v.35 no.4
• /
• pp.46-54
• /
• 1998

In this paper, the erect of notch geometries on dynamic stress concentration was investigated by using the dynamic photoelasticity and the drop weight loading system Dynamic stress fields arisen by elastic wave through the loading system around various types of notch geometries were captured by using $10^6/sec$ frame rate Cranz-Shardin camera system with 12 photographic frames. We found that dynamic stress concentrations around the notch tip and comer were highly dependent on the change in notch geometries. The elders of dynamic stress singularity ware determined with respect to varying geometries of notches and we explained dynamic stress concentration in terms of the orders of dynamic stress singularity.