• Journal of the Korean Magnetics Society
• /
• v.13 no.2
• /
• pp.53-58
• /
• 2003

Annealing effects of exchange bias fields ($H_{2ex}$(top), $H_{lex}$ (bottom)) on composite type NiFe/[FeMn/Mn]$_{80}$/NiFe multilayers have been studied. Three samples with ultra-thin Mn inserted layers on glass/Ta(50 $\AA$)/NiFe(150 $\AA$)/[F $e_{53}$M $n_{47}$(1.25 $\AA$)/Mn(0 $\AA$, 0.11 $\AA$, 0.3 $\AA$)]$_{80}$/NiFe(90 $\AA$)/Ta(50 $\AA$) were prepared by ion beam sputtering. The average x-ray diffraction peak ratios NiFe(111) of FeMn (111) fcc textures for the Mn inserted total thicknesses of 0 $\AA$, 9 $\AA$, and 24 $\AA$ were about 0.65, 0.90, and 1.5, respectively. For the sample without Mn inserted layer, the $H_{2ex}$ of 260 Oe up to 300 $^{\circ}C$ disappeared at 350 $^{\circ}C$. For two multilayer samples with ultra-thin Mn layers of 0.11 $\AA$ and 0.3 $\AA$, the $H_{2exs}$ of 310 Oe and 180 Oe up to 300 $^{\circ}C$ endured of 215 Oe and 180 Oe at 350 $^{\circ}C$, respectively. The $H_{ex}$ (bottom)s of three samples decreased from 100 Oe to 70 Oe up to 250 $^{\circ}C$, while these values increased beyond 300 $^{\circ}C$. This observation can be attributed to less diffusive path of Mn atoms in bottom NiFe than top NiFe layer. The top and bottom coercive fields slightly varied about 5 Oe∼10 Oe. From these results, we could obtain the enhancement of exchange coupling intensity and thermal stability by an ultra-thin Mn inserted layer on NiFe/[FeMn/Mn]$_{80}$/NiFe Multilayers.

• Journal of the Korean Magnetics Society
• /
• v.13 no.5
• /
• pp.187-192
• /
• 2003

The magnetic and thermal properties of NiFe/[IrMn-Mn]/CoFe with Mn additions have been studied. As-deposited CoFe pinned layers with [IrMn-Mn]layer had dominantly larger exchange biasing field ( $H_{ex}$) and blocking temperature ( $T_{b}$) than those with pure I $r_{22}$M $n_{78}$ used. The $H_{ex}$ and $T_{b}$ improved with 76.8-78.1 vol% Mn, but those of the NiFe/IrMn/CoFe dropped considerably with more addition of 0.6 vol % Mn. The average x-ray diffraction peak ratios of fcc [(111)CoFe, NiFe]/(111)IrM $n_3$ textures for the Mn inserted total vol of 75.5, 77.5, and 79.3% were about 1.4, 0.8, and 0.6, respectively. For the sample without Mn inserted layer, the $H_{ex}$ between IrMn and CoFe layers was almost zero, but it increased to 100 Oe after annealing of 250 $^{\circ}C$. For as-grown two multilayers samples with ultra-thin Mn layers of 77.5 and 78.7 vol %, the $H_{ex}$s were 259 and 150 Oe, respectively. In case of IrMn with 77.5 vol% Mn, the $H_{ex}$ was increased up to 475 Oe at 350 $^{\circ}C$ but decreased to 200 Oe at 450 $^{\circ}C$, respectively. The magnetic properties and thermal stabilities of NiFe/[IrMn-Mn]/CoFe multilayer were enhanced with Mn additions. In applications where higher $H_{ex}$ and $T_{b}$ are required, proper contents of Mn can be used. be used. used.

• Journal of the Korean Magnetics Society
• /
• v.14 no.6
• /
• pp.228-231
• /
• 2004

We have studied local magnetization reversal and magnetic properties induced by Laser annealing method in the strip-patterned Ta/NiFe/FeMn/Ta and Ta/NiFe/FeMn/NiFe/Ta multilayers fabricated by ion-beam deposition. The films were exposed to the emission of the DPSS (Diode Pumped Solid State, Nd:YAG) laser under 600 G. The laser beam intensity increased up to 440 mW. When the laser illuminated the patterned film with the power of above 200 m W, the intensity of MR peak located in +87 Oe shrunk. A new MR peak was generated at -63 Oe. When the laser power is 400 mW, the location of positive MR peak(H$\sub$ex/) was changed slightly from +87 Oe to +76 Oe, and the MR ratio was decreased from 0.9% to 0.1 %. On the other hand, the new (negative) MR peak shifted from -63 Oe to -80 Oe, with the MR ratio increased up to 0.3%. As the illuminated area expanded, the intensity of opposite MR peak increased and it of negative MR peak decreased. This proved that the local reversal of exchange biasing should be realized by laser annealing.

• Journal of the Korean Magnetics Society
• /
• v.11 no.4
• /
• pp.141-145
• /
• 2001

The Mn$\_$80/Ir$\_$18.1/Pt$\_$1.9/ exchange bias layers (EBLs), which have a small amounts of Pt, exhibit a high value of H$\_$ex/. The Si/Ni-Fe/Mn$\_$80/Ir$\_$18.1/Pt$\_$1.9/ EBL shows the largest H$\_$ex/ of 187 Oe, which is equivalent to a exchange energy (J$\_$ex/) of 0.146 erg/cm$^2$. Mn$\_$80/Ir$\_$18.1/Pt$\_$1.9/ EBLS are estimated to have blocking temperature of about 250 $\^{C}$, which is higher than those of Mn-Ir EBLs and Mn-Ir-Pt EBLs with higher Pt contents. This result implies that a little addition of Pt element promotes thermal stability in the Mn-Ir-Pt EBLs. The chemical stability of Mn-Ir-Pt EBLs was characterized by potentiodynamic test, which was performed in 0.001 M NaCl solution. The current density of Mn-Ir-Pt films was gradually reduced with increasing Pt content. The present results indicate that the Mn-Ir-Pt with a small amount of Pt is suitable for an antiferromagnetic material for a reliable spin valve giant magnetoresistance device.