• 한국세라믹학회지
• /
• 제15권2호
• /
• pp.66-71
• /
• 1978

The cobalt blue spinel stains (main composition; CoO:$Al_2O_3$=1 : 1) in CoO-NiO-$Al_2O_$3 and $CoO-Al_2O_3-Cr_2O_3$ system were prepared by the calcination of each component oxides to be adequate for the factory. The color development, the change of the lattice constnat of the spinel and its application to colored glazes were studied. The results were summarized as follows. 1) In CoO-Al_2O_3$ spinel, the excess addition of each component hardly made any variation in lattice constantand alumina-rich spinel specimens caused the brilliant blue color fade. 2) An increase of $Ni^{2+}$ in $CoO-NiO-Al_2O_3$ system, made the lattice constnat of the $CoO-Al_2O_3$ spinel smaller, and an increase of $Cr^{3+}$ in $CoO-Al_2O_3-Cr_2O_3$, larger. 3) Glazed stains under lead glaze were colored nearly same dark blue color fade.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1997년도 특별강연 및 추계학술발표 개요집
• /
• pp.125-127
• /
• 1997

• 에너지공학
• /
• 제8권2호
• /
• pp.256-264
• /
• 1999

본 연구에서는 메탄의 부분산화반응에 미치는 base metal 의 영향을 살펴보기 위하여 6~l2wt%의 Mn, Cu, V, Co, Cr 그리고 Ba 등이 2 wt% Pt, 70 wt% Alumina, 28 wt% Ceria and Zirconia 와 함께 cordierite (2MgO.2Al$_2$O$_3$.5SiO$_2$)에 담지된 Pt-B/cordierite 촉매(B: base metal)를 사용하여 메탄의 부분산화반응 실험을 수행하였다. 메탄의 부분산화반응에 대한 활성은 Ba, Co그리고 Cr 담지 촉매는 Ni담지 촉매와 유사하게 Mn, Cu, V을 담지 했을 때 보다 우수한 것으로 나타났으나, 코크 생성에 대한 활성도 큰 것으로 나타났다. 또한 5wt% Ni/Al$_2$O$_3$촉매를 이용한 메탄의 부분산화반응 실험 후의 촉매에 대한 XRD 분석결과 Ni은 3가지 형태의 상으로 존재하는 것을 확인할 수 있었으며, 촉매층 전단에서는 주로 NiAl$_2$O$_4$와 NiO 형태로 존재하여 메탄의 산화반응이 일어나며, 그리고 촉매층 후단에서는 환원상태의 Ni로 존재는 것으로 보아 개질반응이 일어나는 것을 알 수 있었다.

• 한국표면공학회지
• /
• 제34권2호
• /
• pp.161-168
• /
• 2001

A Thermal Barrier Coating (TBC) can play an important role in protecting parts from harmful environments at high temperatures such as oxidation, corrosion, and wear in order to improve the efficiency of aircraft engines by lowering the surface temperature of the turbine blade. The TBC can increase the life span of the product and improve the operating properties. Therefore, in this study the mechanical and thermal properties of the TBC such as oxidation, fatigue and shock at high temperatures were evaluated. A samples of a bond coat (CoNiCrAlY) produced by the High Velocity Oxygen Fuel (HVOF) and Low Pressure Plasma Spray (LPPS) method were used. The thickness of the HVOF coating layer was approximately $450\mu\textrm{m}$ to 500$\mu\textrm{m}$ and the hardness number of the coating layer was between 350Hv and 400Hv. The thickness of the LPPS coating was about 350$\mu\textrm{m}$ to 400$\mu\textrm{m}$ and the hardness number of the coating was about 370Hv to 420Hv. The X-ray diffraction analysis showed that CoNiCrAlY coating layer of the HVOF and LPPS was composed of the $\beta$and ${\gamma}$phase. After the high temperature oxidation test, the oxide scale with about l0$\mu\textrm{m}$ to 20$\mu\textrm{m}$ thickness appeared at the coating surface on the Al-depleted zone was observed under the oxide scale layer.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2006년도 춘계학술발표회 초록집
• /
• pp.101-102
• /
• 2006

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2002년도 춘계연구발표회 논문개요집
• /
• pp.54-55
• /
• 2002

• 한국주조공학회지
• /
• 제20권1호
• /
• pp.21-28
• /
• 2000

Ni and Ni-Cr porous metals which are estimated to be easy to fabricate by squeeze casting are used as strengtheners for composite materials. As a matrix material, Al-7%wtSi-0.3 wt%Mg(AC4C) has been used. In case of Ni/AC4C and Ni-Cr/AC4C composite, $750^{\circ}C$ melt temperature and minimum 25 MPa squeezing pressure are needed to produce sound composite materials. The observation of interfacial reaction zone at various heat treatment condition showed that solutionizing temperature of above 520^{\circ}C$, the interfacial reaction zone increased proportionally with increasing heat treatment tim and reaction products formed by interfacial reaction are mainly composed of $Al_3Ni$ and $Al_3Ni_2$ phases. The tensile strength of Ni/AC4C and Ni-Cr/AC4C composite is lower than the matrix metal and this can be explained by the brittle intermetallic compounds formed at the interface of Ni and Ni-Cr reinforcements. But the properies of hardness, wear resistance and thermal expansion are better than the matrix due to the strengthening effect of Ni-Cr porous metals.

• 한국재료학회지
• /
• 제8권6호
• /
• pp.538-544
• /
• 1998

열차폐코팅층의 박리는 세라믹/금속접합층 계면에서 취성이 큰 스피텔의 생성, 금속과 세라믹의 열팽창계수의 차이, 세라믹층의 상변태, 코팅층의 잔류응력에 기인한다. 본 연구에서는 인코넬 713C에 전자빔 코팅 및 플라즈마 용사법으로 코팅된 안정화지르코니아/CoNiCrAIY 계면의 산화거동을 조사하기 위하여 $900^{\circ}C$에서 등온산화시험동안 생성되는 산화막층과 스피넬 생성 거동을 관찰, 분석하였다. 코팅 직후 코팅층에 고르게 분포하고 있는 Co,Ni,Cr,AI,Zr의 원소들이 산화시간에 따라 확산하여 산화반응을 하였다. 초기 20시간의 산화기시간에 안정화지르코니아/CoNiCrAIY 계면에 주요 성분이 $\alpha$-$AI_2O_3$인 산화막층이 생성되었고, CoNiCrAIY층에는 AI의 외부확산으로 인한 AI 결핍지역이 생성되었다. 산화시험동안 $\alpha$-AI2O층이 임계두께까지 성장한 후에 산화막층의 성장속도는 감소하였고, 안정화지르코니아/산화막층 계면에 스피넬, $Cr_2O_3$, $CO_2CrO_4$의 형성으로 인한 크랙이 관찰되었다.

• The Journal of Advanced Prosthodontics
• /
• 제6권2호
• /
• pp.138-145
• /
• 2014

Cobalt-Chromium (Co-Cr) alloys are classified as predominantly base-metal alloys and are widely known for their biomedical applications in the orthopedic and dental fields. In dentistry, Co-Cr alloys are commonly used for the fabrication of metallic frameworks of removable partial dentures and recently have been used as metallic substructures for the fabrication of porcelain-fused-to-metal restorations and implant frameworks. The increased worldwide interest in utilizing Co-Cr alloys for dental applications is related to their low cost and adequate physico-mechanical properties. Additionally, among base-metal alloys, Co-Cr alloys are used more frequently in many countries to replace Nickel-Chromium (Ni-Cr) alloys. This is mainly due to the increased concern regarding the toxic effects of Ni on the human body when alloys containing Ni are exposed to the oral cavity. This review article describes dental applications, metallurgical characterization, and physico-mechanical properties of Co-Cr alloys and also addresses their clinical and laboratory behavior in relation to those properties.

• 한국자기학회지
• /
• 제13권3호
• /
• pp.91-96
• /
• 2003

본 연구에서는 DC 마그네트론 스퍼터를 사용하여 Cr/Co/Al-Ox/Co/Ni-Fe 다층박막에 다양한 두께의 Cr 하지층을 삽입함에 따른 자기적 특성 및 전기적 특성에 관하여 연구하였다. 3 nm 두께의 Cr 하지층 증착시 자기저항비의 변화는 관찰할 수 없었고 적정한 Cr두께가 증가함에 따라 Co의 보자력이 크게 증가되었다 또한, 산화시간이 길수록 두 강자성층간에 보자력 차이 및 절연층의 저항이 점차 증가하였는데, 이는 산화시간에 따라 상부층 계면의 평탄성의 증가에 기인하는 것으로 생각되며 TEM을 통하여 확인할 수 있었다. Cr 하지층 유무에 관계없이 최고 자기저항비가 나타나는 절연층의 산화시간은 60~70초로 비슷하였지만 Cr 두께가 증가할수록 자기저항비는 감소하였다. 이는 전극간 계면의 거칠기의 증가로 인해 미반응 Al의 잔존 확률이 상대적으로 커짐에 따라 터널 전자의 산란이 증가함으로써 나타나는 것으로 생각된다. 이러한 결과로 Cr하지층의 두께는 3 nm로 고정하였으며 하지층의 증착 및 적정산화를 통하여 두 강자성층간에 큰 보자력 차이를 유도할 수 있었다. 이는 재현성에 있어서 가장 큰 문제점을 지닌 TMR 소자에 매우 긍정적인 해결방안을 제시할 수 있게 된다.̄