• Journal of Powder Materials
• /
• v.27 no.1
• /
• pp.8-13
• /
• 2020

In this study, we investigated the effects of precipitates and oxide dispersoids on the high-temperature mechanical properties of oxide dispersion-strengthened (ODS) Ni-based super alloys. Two ODS Ni-based super alloy rods with different chemical compositions were fabricated by high-energy milling and hot extrusion process at 1150 ℃ to investigate the effects of precipitates on high-temperature mechanical properties. Further, the MA6000N alloy is an improvement over the commercial MA6000 alloy, and the KS6000 alloy has the same chemical composition as the MA6000 alloy. The phase and microstructure of Ni-based super alloys were investigated by X-ray diffraction and scanning electron microscopy. It was found that MC carbide precipitates and oxide dispersoids in the ODS Ni-based super alloys developed in this study may effectively improve high-temperature hardness and creep resistance.

• Journal of Powder Materials
• /
• v.26 no.2
• /
• pp.101-106
• /
• 2019

Ni-based oxide dispersion strengthened (ODS) alloys have a higher usable temperature and better high-temperature mechanical properties than conventional superalloys. They are therefore being explored for applications in various fields such as those of aerospace and gas turbines. In general, ODS alloys are manufactured from alloy powders by mechanical alloying of element powders. However, our research team produces alloy powders in which the $Ni_5Y$ intermetallic phase is formed by an atomizing process. In this study, mechanical alloying was performed using a planetary mill to analyze the milling behavior of Ni-based oxide dispersions strengthened alloy powder in which the $Ni_5Y$ is the intermetallic phase. As the milling time increased, the $Ni_5Y$ intermetallic phase was refined. These results are confirmed by SEM and EPMA analysis on microstructure. In addition, it is confirmed that as the milling increased, the mechanical properties of Ni-based ODS alloy powder improve due to grain refinement by plastic deformation.

• Journal of Powder Materials
• /
• v.5 no.2
• /
• pp.122-128
• /
• 1998

NiAl based ODS (Oxide Dispersion Strengthened) intermetallic alloys have been produced by mechanical alloying (MA) process and consolidated by hot extrusion. Subsequent thermomechanical treatments have been applied to induce secondary recrystallization in an attempt to improve creep resistance in this material. The creep behavior of secondary recrystallized MA NiAl has been investigated and compared with those of as-extruded condition. Minimum creep rate were shown to be approximately two orders of magnitude lower than that in as-extruded condition. The improvement in creep resistance is believed due to the grain coarsening, restricting of dispersoid coarsening as well as increase in grain aspect ratio. Creep threshold stress behavior, below which no measurable creep rate can be detected, has been discussed on the basis of particle-dislocation interaction theory. The threshold stress becomes negligible after secondary recrystallization in MA NiAl, presumably due to dispersoid coarsening and a decrease in grain boundary area during secondary recrystallization.

• Journal of Powder Materials
• /
• v.25 no.4
• /
• pp.331-335
• /
• 2018

This study investigates the directional recrystallization behavior of Ni based oxide dispersion strengthened (ODS) alloy according to the zone annealing velocity. The zone annealing temperature is set as $1390^{\circ}C$, while the zone velocities are set as 2.5, 4, 6, and 10 cm/h, respectively. The initial microstructure observation of the as-extruded sample shows equiaxed grains of random orientation, with an average grain size of 530 nm. On the other hand, the zone annealed samples show a large deviation in grain size depending on the zone velocities. In particular, grains with a size of several millimeters are observed at 2.5-cm/h zone velocity. It is also found that the preferred orientation varies with the zone annealing velocity. On the basis of these results, this study discusses the role of zone velocities in the directional recrystallization of Ni base ODS alloy.

• Nuclear Engineering and Technology
• /
• v.45 no.6
• /
• pp.821-826
• /
• 2013

In the present study, the effects of various heat treatments on the microstructure and mechanical properties of dual phase ODS steels were investigated to enhance the high strength at elevated temperature. Dual phase ODS steels have been designed by the control of ferrite and austenite formers, i.e., Cr, W and Ni, C in Fe-based alloys. The ODS steels were fabricated by mechanical alloying and a hot isostatic pressing process. Heat treatments, including hot rolling-tempering and normalizing-tempering with air- and furnace-cooling, were carefully carried out. It was revealed that the grain size and oxide distributions of the ODS steels can be changed by heat treatment, which significantly affected the strengths at elevated temperature. Therefore, the high temperature strength of dual phase ODS steel can be enhanced by a proper heat treatment process with a good combination of ferrite grains, nano-oxide particles, and grain boundary sliding.