• Transactions of the Korean hydrogen and new energy society
• /
• v.27 no.1
• /
• pp.95-105
• /
• 2016

Spray-dried NiO-based oxygen carriers developed for chemical looping combustion required high calcination temperatures above $1300^{\circ}C$ to obtain high mechanical strength applicable to circulating fluidized-bed process. In this study, the effect of CBB ($CaO{\cdot}BaO{\cdot}B_2O_3$) addition, as a binder, on the physical properties and oxygen transfer reactivity of spray-dried NiO-based oxygen carriers was investigated. CBB addition resulted in several positive effects such as reduction of calcination temperature and increase in oxygen transfer capacity and porosity. However, oxygen transfer rate was considerably decreased. This was more apparent when a higher amount of CBB was added and MgO was added together. From the experimental results, it is concluded that CBB added NiO-based oxygen carriers are not suitable for chemical looping combustion and a new method to reduce calcination temperature while maintaining high oxygen transfer rate of NiO-based oxygen carriers should be found out.

• Applied Chemistry for Engineering
• /
• v.7 no.5
• /
• pp.913-924
• /
• 1996

In this study HDS(hydrodesulfurization) of thiophene was researched over nickel catalysts added with small amounts of neodymium which were prepared by different methods such as unsupported coprepricipitated NdNi catalysts, unsupported intermetallic $NdNi_5$ catalysts, and carbon supported NdNi catalyst. The HDS activity was remarkably increased when a small amounts of neodymium was added to unsupported coprecipitated Ni catalysts. Thus it was known that the role of Nd is important in HDS of thiophene of Ni catalysts. For the case of unsupported intermetallic $NdNi_5$, the intermetallic crystallinity was destroyed to oxide and sulfide after calcination and presulfidation respectively. The HDS activity of thiophene can be explained by surface area of unsupported catalysts. And Nd acts like as structural promoter keeping the high surface area of unsupported catalysts. The HDS activity was increased by each ten times based on 1 gr. of nickel in the order of unsupported intermetallic $NdNi_5$, unsupported coprecipitated NdNi, and carbon supported NdNi catalysts according to different preparation method of catalysts.

• The Journal of the Korean dental association
• /
• v.22 no.8 s.183
• /
• pp.705-714
• /
• 1984

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• v.y2005m4
• /
• pp.106-111
• /
• 2005

Failure mechanisms were investigated for the two layer thermal barrier coatings consisting of NiCrAlY bond coat and $ZrO_2-8wt.\% Y_{2}O_3$ ceramic coating during cyclic oxidation. $Al_{2}O_3$ developed at the ceramic coating/bond coat interface first, followed by the Cr/Ni rich oxides such as $NiCr_{2}O_4 and Ni(Al,Cr)_{2}O_4$ during cyclic oxidation It was observed that the spalling of ceramic coatings took place primarily within the NiCrAlY bond coat oxidation products or at the interface between the bond coat oxidation products and zirconia based ceramic coating or the bond coat. It was also observed that the fracture within these oxidation products occurred with the formation of $Ni(Cr,Al)_{2}O_4$ spinel or Cr/Ni rich oxides. It was therefore concluded that the formation of these oxides was a life-limiting event for the thermal barrier coatings.

• Korean Journal of Materials Research
• /
• v.5 no.2
• /
• pp.232-238
• /
• 1995

The thermal stress distribution of WC and Ni binder phases In WC-26st.%Ni and WC-6wt.%Ni composites has been investigated over the temperature range 100-900 K using a time-of-flight neutron diffractometer. To determine the stress distribution, the breadths of WC and Ni peaks in the reference powder and the composites were analyzed. The peak breadths were corrected for particle size effect using a procedure based on the integral peak breadth method of particle size-strain analysis. The result shows a broad range of strain, and thus stress, is present in the WC and Ni binder phases of the composites. The strain distribution of both phases broadens as the temperature decreases, and some fraction of total strain distribution of the WC phase remains tensile regardless of the temperature. The strain distribution of the WC phase broadens as the binder content increases, and that of Ni binder phase broadens as the binder content decreases, which means the strain distribution broadens as the absolute value of residual stress increase.

• Journal of Welding and Joining
• /
• v.15 no.5
• /
• pp.46-55
• /
• 1997

This study has evaluated the liquation cracking behavior in the heat affected zone of several Ni base superalloys (Incoloy 825, Inconel 718 and Inconel 600). 304 and 310S austenitic stainless steels were also included for comparison. In addition, the mechanism of liquation cracking in the HAZ was postulated based on the extensive microstructural examinations with SEM, EDAX and TEM. The liquation cracking resistance of Ni base alloys was found to be far inferior to that of austenitic stainless steels. The liquation cracking of Incoloy 825 and Inconel 718 was believed to be closely related with the Laves-austenite(Ti rich in 825 and Nb rich in 718) and MC-austenitic eutectic phases formed along the grain boundaries by constitutional liquation and incipient melting under rapid welding thermal contraction. Further, liquation cracking resistance of the HAZ was dependent not only upon the type and amount of low melting phases but also on the grain size.

• Structural Engineering and Mechanics
• /
• v.22 no.2
• /
• pp.241-262
• /
• 2006

NiTi-wire shape memory alloy (SMA) dampers, that utilize NiTi SMA wires to simultaneously damp tension, compression and torsion, was developed for structural control implementation in this study. First, eight reduced-scale NiTi-wire SMA dampers were constructed. Then tension, compression and torsion experiments using the eight reduced-scale NiTi-wire SMA dampers of different specification were done. The experimental results revealed all of the eight reduced-scale NiTi-wire SMA dampers had the ability to simultaneously supply tension-compression damping and torsion damping. Finally, mechanics analysis of the NiTi-wire SMA dampers was done based on a model of the SMA-wire restoring force and on tension-compression and torsion damping analysis. The damping analytical results were found to be similar to the damping experimental results.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.11a
• /
• pp.33-37
• /
• 2002

본 연구에서는 전해도금법을 이용하여 플립칩용 Ni, Ni-Cu 합금 UBM (Under Bump Metallurgy) 및 Sn-Ag 무연 솔더 범프를 형성하였다. 솔더 범프의 전해도금시 고속도금 방법으로 균일한 범프 높이를 갖도록 하는 도금 조건 및 도금 기판의 역할로서의 UBM의 영향을 조사하였다. Cu/Ni-Cu 합금/Cu UBM을 적용한 경우 음극시편의 전극 접점수를 증가시켰을 때 비교적 균일한 솔더 범프를 형성시킬 수 있었던 반면, Ni UBM의 경우는 접점수를 증가시켜도 다소 불균일한 솔더 범프를 형성하였다. 리플로 시간을 변화하여 범프 전단 강도 및 파단 특성을 조사하였는데 Ni UBM의 경우 Cu/Ni-Cu 합금/Cu UBM에 비해 전단강도가 다소 낮은 값을 가졌고 금속막이 웨이퍼에서 분리되는 파괴 거동이 관찰되었다.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.251-259
• /
• 2004

In the development of the advanced spent fuel management process based on the molten salt technology, it is essential to choose the optimum material for the process equipment handling molten salt. Corrosion behavior of Ni 200 and Ni-base alloys in molten salt of LiCl-$Li_2$O under oxidation atmosphere was investigated in the temperature range of $650～800^{\circ}C$ for 24～312 hrs. The order of corrosion rate was Ni 200 > Inconel 690 > Inconel 601 > Inconel 600. Inconel 600 alloy showed the highest corrosion resistance among the examined alloys, but Ni 200 exhibited the highest corrosion rate. Corrosion products of Inconel 600 and Inconel 601 were $Cr_2$$O_3$ and $NiFe_2$$O_4$. In case of Inconel 690, a single layer of $CrO_2$$O_3$ was formed in the early stage of corrosion and an outer layer of $NiFe_2$O$_4$ and inner layer of $Cr_2$$O_3$ were formed with increase of corrosion time. Inconel 600 showed local corrosion behavior and Inconel 601, 690 showed uniform corrosion behavior.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.953-954
• /
• 2006

Ti-Cu-Ni-Sn quaternary amorphous alloys of $Ti_{50}Cu_{32}Ni_{15}Sn_3$, $Ti_{50}Cu_{25}Ni_{20}Sn_5$, and $Ti_{50}Cu_{23}Ni_{20}Sn_7$ composition were prepared by mechanical alloying in a planetary high-energy ball-mill (AGO-2). The amorphization of all three alloys was found to set in after milling at 300rpm speed for 2h. A complete amorphization was observed for $Ti_{50}Cu_{32}Ni_{15}Sn_3$ and $Ti_{50}Cu_{25}Ni_{20}Sn_5$ after 30h and 20h of milling, respectively. Differential scanning calorimetry analyses revealed that the thermal stability increased in the order of $Ti_{50}Cu_{32}Ni_{15}Sn_3$, $Ti_{50}Cu_{25}Ni_{20}Sn_5$, and $Ti_{50}Cu_{23}Ni_{20}Sn_7$.