• Journal of the Korean institute of surface engineering
• /
• v.36 no.6
• /
• pp.461-465
• /
• 2003

The microstructures and magnetic properties of electrodeposited Fe-45 wt%Ni-P alloys have been investigated. The structures of electrodeposited Fe-45 wt%Ni alloy was FCC i.e. ${\gamma}$ phase and the size of crystallite was 10 nm. The structure of electrodeposited Fe-45 wt%Ni-1 wt%P alloy showed ${\gamma}$ phase and 7 nm sized nanocrystalline. The electrodeposited Fe-45 wt%Ni-P alloys containing 2∼3 wt% of P exhibited ${\gamma}$ ＋ $\alpha$ dual phases. The electrodeposited Fe-45 wt%Ni-P alloys above 3.5 wt% showed an amorphous structure. P in the alloys acted grain refining and phase changing element. The resistivity of the electrodeposited alloys increased with P contents. Effective permeability at high frequency (above 1 MHz) increased with P contents up to 2 wt% and this was ascribed to the easier magnetization rotation owing to the reduction of eddy current. Effective permeability decreased with P contents above 3 wt% and this was ascribed to the transformation of the ferromagnetism of Fe-45 wt%Ni alloy gradually into paramagnetism with the introduction of P into the electrodeposited alloy matrix.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.2
• /
• pp.57-63
• /
• 2010

In this study, thermal stability of the mechanical properties of Ni-P-B and Ni-P-Fe layers electroplated on Alloy 600 material was evaluated by measuring their microhardness, tensile strength, and elongation after heat treatment at $325^{\circ}C$ and $400^{\circ}C$. According to the results, there was no noticeable change in microhardness of the two electrodeposits before and after heat treatment at the temperatures for 30 days. In the case of a Ni-P-B electrodeposit, ultimate tensile strength (UTS) slightly increases with heat treatment time, while its elongation decreases, showing good thermal stability in the mechanical properties at high temperature. On the other hand, UTS and elongation of Ni-P-Fe decrease with heat treatment time, which is very unusual observation. This result was attributed to the bad microstructure of Ni-P-Fe having many defects in the deposit formed early stage of an electroplating process and their redistribution to link to become large ones during heat treatment.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.6
• /
• pp.437-443
• /
• 2003

The effects of additive(grain refiner, GR) on process efficiency of the Ni-Fe-P alloy electrodeposition and the material properties of the deposit were investigated. Electrochemical properties of the deposits were investigated using polarization and electrochemical impedance techniques, and the material properties of the deposits were characterized through inductively coupled plasma(ICP), spiral contractometer, XRD, SEM and TEM. When the additive was added into the electrodeposition bath, current efficiency, Ni content and corrosion resistance of the deposit increased, whereas residual stress, surface roughness and grain size of the deposit decreased.

• Corrosion Science and Technology
• /
• v.2 no.3
• /
• pp.148-154
• /
• 2003

The addition of Ni leads to the formation of protective rust layer on steel and subsequently high corrosion resistance of steel in $Cl^-$-containing environment. $\alpha$-FeOOH, $\beta$-FeOOH, $\gamma$-FeOOH and $Fe_3O_4$ are formed mainly on steels exposed to $Cl^-$-containing environment. As the first work of this kind, this study reports the influence of Ni on the oxidation behavior of $Ni_xFe_{1-x}(OH)_2$ in $Cl^-$-containing solution at two different pH regions(condition I under which the solution pH is allowed to decrease and condition I under which solution pH is maintained at 8) where $\gamma$-FeOOH and $Fe_3O_4$ are predominantly formed, respectively, upon oxidation of $Fe(OH)_2$, In the presence of Ni(II) in the starting solution, the formation of $\beta$-FeOOH was facilitated and the formation of $\gamma$-FeOOH was suppressed with increasing Ni(II) content and with increasing oxidation rate of Fe(II). Ni(II) was found to have $Fe_3O_4$-suppressing effect under condition II.

• Resources Recycling
• /
• v.13 no.2
• /
• pp.3-8
• /
• 2004

A basic study on the recovery of heavy metals such as Zn, Ni, Cu and Fe ions from wastewater was carried out with the spent iron oxide catalyst, which was used in the Styrene Monomer(SM) production company. The heavy metals could be recovered more than 98％ with the spent iron oxide catalyst. The alkaline components of the spent catalyst could be precipitated the metal ions of the wastewater as metal hydroxides at the higher pH 10.6 in Ni, pH 8.0 in Cu, pH 6.5 in Fe, pH 8.5 in Zn. But the metal ions are adsorbed physically on the surface of the spent catalyst in the range of the pH of the metal hydroxides and pH 3.0, which is the isoelectric point of the iron oxide catalyst.

• Journal of the Korean Vacuum Society
• /
• v.4 no.1
• /
• pp.67-76
• /
• 1995

자기저항헤드용 Ni-Fe-Co/Cu/Ni-Fe-Co/Fe-Mn 다층박막에서 자기적 성질과 전기적 성질에 관하여 조사하였다. 저 포화자계에서 고 자기저항을 나타내는 스핀 밸브형 다층박막을 제작하기 위하여 Borond이 도핑된 p-type Si(100)기판위에 Ni-Fe-Co 단층박막과 Si/Ni-Fe-Co/Cu/Ni-FeCo, Si/Ni-Fe-Co/Fe-Mn 구조의 다층막을 제작하여 자기적 특성을 조사하였다. Ni-Fe-Co 단층박막의 자기적 특성은 고정된 아르곤 분압에서 박막의 두께 등에 의존성이 있는 것으로 나타났다. 또한 Si/Ni-Fe-Co($70AA$)/Fe-Mn 구조에서 Ni-Fe-Co와 Fe-Mn 계면에서의 두 자성층의 이방성 차이에 의해서 발생되어지는 교환자기이방성이 존재하였으며, 교환자기이방성자계값은 Fe-Mn 두께가 $150\AA$일 때 가장 큰 값을 나타내었다. Ni-Fe-Co texture와 교환자기이방성자계값은 Fe-Mn 두께가 $150\AA$일 때 가장 큰 값을 나타내었다. Ni-Fe-Co texture와 교환자기이방성자계값의 의존성을 알아보기 위하여 Ti, Cu를 바닥층으로 사용하였다. Ti을 바닥층으로 사용하였을 경우, 교환자기이방성자계값은 23.5 Oe 정도의 가장 큰 값을 나타내었다. XRD 분석결과, Ti 바닥층이 Cu 바닥층이나, 바닥층이 없는 경우와 비교하여 성막된 Ni-Fe-Co 자성층의 강한 fcc(111) texture를 형성하는 것으로 나타났다. 각각의 단층박막과 다층박막에서의 자기적 특성을 측정한 후, Si/Ti($50\AA$)/Ni-Fe-Co($70\AA$)/Cu($23\AA$)/Ni-Fe-Co($70\AA$)/Fe-Mn(150$\AA$)/Cu(50$\AA$)의 스핀밸브구조를 갖는 다층박막을 제작하였으며, 11 Oe의 낮은 포화자계값에서 4.1%의 고 자기저항값을 얻을 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.123.2-123.2
• /
• 2017

Fe-Ni-Cu 합금 전주를 위하여 황화물 용액에의 상의 열역학적 안정도를 작성하고 전주 조건을 선정하였다. $Fe-Ni-Cu-S-H_2O$ 용액의 열역학적 상의 안정도를 전산모사하기 위한 프로그램은 C#으로 작성하였다. JANAF 자료를 근거한 적정 전주 조건은 $130mA/cm^2$, $50{\sim}55^{\circ}C$, pH 2.4 이었다. XRF을 이용한 Fe-Ni-Cu의 합금 도막의 평균 조성은 Fe-42Ni-1Cu [wt.%] 이었다, 전류밀도가 낮아질수록 Ni과 Cu량은 증가하였다. 구리 농도가 증가하면 표면조도는 60 nm로 변화하였다.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.5
• /
• pp.225-232
• /
• 2013

The influence of aging treatment, addition elements and rolling reduction ratio on the microstructure, mechanical, electrical and bendability properties of Cu-Ni-Si-P-x (x = Fe, Sn, Zn) alloys for connector material application was investigated. SEM/EDS analysis exhibited that Ni2-Si precipitates with a size of 20~100 nm were distributed in grains. Fe, Sn, Zn elemnets in Cu-Ni-Si-P alloy imporved the mechanical strength but it was not favor in increasing of electrical conductivity. As higher final rolling reduction ratio, the strength and electrical conductivity is increased after aging treatment, but it indicated excellent bendability. Especially, Cu-2Ni-0.4Si-0.5Sn-0.1Fe-0.03P alloy show the tensile strength value of 700MPa and the electrical conductivity was observed to reach a maximum of 40%IACS. It is optimal for lead frame and connector.

• 한국전기화학회:학술대회논문집
• /
• 2004.04a
• /
• pp.32-32
• /
• 2004

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.10-10
• /
• 2001

In this paper, initial depositing process of electroless Ni-Cu-P alloy was investigated by means of SEM, TEM and AES. The results show that the initial deposition is inhomogeneous and there exist different transition layers between different coatings and substrates, which are decided by the structures and compositions of the bath. For Ni-P binary alloy, its deposition takes place superiorly at grain boundary and on some grains with beneficial texture, the thickness of transition layer composed of Ni-Fe-P reaches 2000 angstrom. But during initiation of Ni-Cu-P trinary alloy, only at grain boundary is prIor to be deposited electrolessly, transited layer contains Ni-Fe-Cu-P and is decreased to about 500 angstrom. The structures of the films of Ni-P and Ni-Cu-P are crystalline at the initial depositing stage. The mechanisms of the process are put forward in this paper.