• Korean Journal of Materials Research
• /
• v.5 no.1
• /
• pp.112-122
• /
• 1995

Metal hydride alloys of TiFe based system have been produced by mechanical alloying(MA) method and their electrochemical characteristics have been evaluated for application for Ni/MH battery electrode. These alloys became amorphous after 36hrs ball milling and easily activated electrochemically. All MA amorphous alloys reached at the first charge/discharge cycle the maximum capacity which was 2-3 times higher than the crystalline state. But their cyclic lives were much inferior to the crystalline state. Alloying elements such as Ni, Co, Cr, Mo substituting Fe greatly improved the capacity and 180 mAh/g capacity was obtained in an alloy of TiFe_{0.6}Ni_{0.1}Co_{0.1}Cr_{0.1}Mo_{0.1}$.

• Journal of Korea Foundry Society
• /
• v.43 no.5
• /
• pp.230-240
• /
• 2023

The pitting corrosion behavior of 329LD cast lean duplex stainless steel and CF3M cast austenitic stainless steel was investigated in chloride environments. The pitting corrosion resistance of the 329LD alloy was superior to that of the CF3M alloy because the pitting potential, passive region, and critical pitting temperature of the low Ni-low Mo 329LD alloy were higher than those of the high Ni-medium Mo commercial CF3M alloy. There are two main reasons for the enhancement of the pitting corrosion resistance of high Cr-low Momedium N 329LD alloy compared to the low Cr-medium Mo CF3M alloy: First, the pitting resistance equivalent number (PREN_δ+γ) value of the 329LD alloy is higher than that of the CF3M alloy. Second, the passive region of the 329LD alloy is larger than that of the CF3M alloy. It indicates that the synergistic effect of the three elements by adding high Cr and low Mo-medium N to the 329LD alloy enhances the passivity of the passive film, thereby increasing the pitting corrosion resistance. It was verified that based on the PREN_γ of austenite (γ) and PREN_δ of ferrite (δ) values calculated using an N-factor of 16, the pitting corrosion of the 329LD alloy was selectively initiated at the γ-phases because PREN_γ value of austenite (γ) was smaller than that of ferrite (δ), and finally propagated from the γ-phase to the δ-phase.

• Nuclear Engineering and Technology
• /
• v.41 no.1
• /
• pp.107-112
• /
• 2009

Corrosion of nickel-base alloys (Hastelloy C-276, Inconel 625, and Inconel X-750) in $500^{\circ}C$, 25MPa supercritical water (with 10 wppb oxygen) was investigated to evaluate the suitability of these alloys for use in supercritical water reactors. Oxide scales formed on the samples were characterized by gravimetry, scanning electron microscopy/energy dispersive spectroscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. The results indicate that, during the 1000h exposure, a dense spinel oxide layer, mainly consisting of a fine Cr-rich inner layer ($NiCr_{2}O_{4}$) underneath a coarse Fe-rich outer layer ($NiFe_{2}O_{4}$), developed on each alloy. Besides general corrosion, nodular corrosion occurred on alloy 625 possibly resulting from local attack of ${\gamma}$" clusters in the matrix. The mass gains for all alloys were small, while alloy X -750 exhibited the highest oxidation rate, probably due to the absence of Mo.

• Journal of Welding and Joining
• /
• v.15 no.4
• /
• pp.78-89
• /
• 1997

This study has evaluated the weld metal solidification cracking behavior of several Ni base superalloys (Incoloy 825, Inconel 718 and Inconel 600). Austenitic stainless steels(304, 310S) were also included for comparison. In addition, a possible mechanism of solidification cracking in the fusion zone was suggested based on the extensive microstructural examinations with SEM, EDAX, TEM, SADP and AEM. The solidification cracking resistance of Ni base superalloys was found to be far inferior to that of austenitic stainless steels. The solidification cracking of Incoloy 825 and Inconel 718 was believel to be closely related with the Laves-austenite (Ti rich in 825 and Nb rich in 718) and MC-austenite eutectic phases formed along the grain boundaries during solidification. Cracking in Inconel 600 was always found along the grain boundaries which were enriched with Ti and P. Further, solidifidcation cracking resistance was dependent not only upon the type of love melting phases but also on the amount of the phases along the solidification grain boundaries.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.4
• /
• pp.461-471
• /
• 2000

This study evaluated the effect of degassing on the ceramic bond strength of two Ni-Cr alloys under varying holding time at the upper limit temperature and atmospheric conditions. Metal specimens were divided into 5 groups for each alloy according to degassing conditions prior to porcelain application no degassing, degassing under vacuum without hold, degassing under vacuum with hold for 5 min. and 10 min. respectively at the upper limit temperature and degassing in air. Total number of metal ceramic specimens was eighty and each group had eight specimens. The ceramic bond strength was measured by four-point flexural test using Instron and the fractured surface was examined under SEM. The results obtained were as follows. 1. Degassing in air improved the ceramic bond strength of Ni-Cr alloys. 2. In degassing under vacuum, hold at the upper limit temperature was advantageous to the ceramic bonding of Ni-Cr alloys. 3. After ceramic metal bond test, metal surfaces were partially covered with the thin porcelain layer, and the cohesive failures in porcelain were predominant in groups showing higher ceramic bond strength.

• Corrosion Science and Technology
• /
• v.2 no.1
• /
• pp.18-25
• /
• 2003

Effects of the precipitation of $\sigma$ phase on the metastable pitting as a precursor of stable pitting corrosion and also on the progress of stale pitting of the 25Cr-7Ni-3Mo-0.25N duplex stainless steel were investigated in chloride solution. Electrochemical potential and current noises of the alloy were measured in 10 % ferric chloride solution ($FeCl_3$) with zero resistance ammeter (ZRA), and then analyzed by power spectral density (PSD) and by corrosion admittance ($A_c$) spectrum. With aging at $850^{\circ}C$, the passive film of the alloy was found to get significantly unstable as represented by power spectral density (PSD) and a transition from metastable pitting state to stable one was observed. In the corrosion admittance spectrum, the number of negative $A_c$ corresponding to the state of localized corrosion increased with aging, suggesting that the precipitation of $\sigma$ phase considerably degraded the passive film by depleting Cr and Mo around it at $\alpha/\sigma$ or $\gamma/\sigma$ phase boundaries, thereby leading to the initiation of the pitting corrosion. However, the Cr and Mo at $\alpha/\sigma$ or $\gamma/\sigma$ phase boundaries which were once depleted due to the precipitation of the $\sigma$ phase were partly replenished by the diffusion of Cr and Mo from the surrounding matrix with aging time longer. The initiation of pitting seems to be associated with the precipitation density of the $\sigma$ phase with an effective size needed to induce the sufficient depletion of Cr and Mo around it.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2008.06a
• /
• pp.341-342
• /
• 2008

• Resources Recycling
• /
• v.27 no.4
• /
• pp.16-22
• /
• 2018

Inconel713C which of a commercial Ni super alloy have the compositions of 70 wt.% Ni, 12 wt.% Cr, 6 wt.% Al and 4 wt.% Mo. In this study, solvent extraction has been performed to separate Mo from the synthetic leaching solution, formation of Inconel713C alloy similarly and is found the optimum conditions of recovery of Mo from the leaching solution. The effects of some variables, such as the nature and concentration of the extractants, $H_2SO_4$ concentrations, and the presence of impurities were investigated. The extraction percentage of Mo by Cyanex272 is 96% in the condition of pH 1 and 4% of concentration of Cyanex272 but Alamine336 is 99% in the condition of the range of pH 1 to 4 and 1 wt.% of concentration of Alamine336. In the case of Alamine336, the extraction percentage of Mo is increased by increasing of the concentration of Alamine336. The optimum condition of this experiment is pH 1 in aqueous phase, 1% concentration of Alamine336 and activation ratio of $H_2SO_4$ 1:0.5.

• Transactions of Materials Processing
• /
• v.31 no.5
• /
• pp.273-280
• /
• 2022

Although the mechanical properties of high-entropy alloys depend on the annealing conditions, limited works were established to investigate the annealing effect on the mechanical properties of Mo-added high-entropy alloys. Therefore, in the present work, the annealing effects on the microstructural evolution and mechanical properties of Mo-added high-entropy alloy were investigated. As a result, incomplete recrystallization from the limited annealing time not only suppresses deformation-induced phase transformation during cryogenic tensile test but also induces a deformation instability that results into the ductility reduction compare with the fully recrystallized sample. This result represents adjustment of annealing time is useful to control both transformation-induce plasticity and deformation instability of high-entropy alloys, and this can be applied to control the mechanical properties of metallic alloys by combining pre-straining and subsequent annealing.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.56.1-56.1
• /
• 2012

The microstructures and mechanical properties of Co-29Cr-6Mo alloy with C and N additions, produced by additive manufacturing using electron beam melting (EBM) method, were studied using X-ray diffraction, electron back scatter diffraction, transmission electron microscope, Vickers hardness tests, and tensile tests, focusing on the influences on the build direction and the various heat treatments after build. It is found that the microstructures for the as built specimens were changed from columnar to equiaxed grain structure with average grain size of approximately $10-20{\mu}m$ due to the heat treatment employing the reverse transformation from a lamellar (hcp + $Cr_2N$) phase to an fcc. Our results will contribute to the development of biomedical Ni-free Co-Cr-Mo-N-C alloys, produced by EBM method, with refined grain size and good mechanical properties, without requiring any hot workings.