• Electrical & Electronic Materials
• /
• v.3 no.4
• /
• pp.325-331
• /
• 1990

본 연구는 텅스텐 소결에 저온 활성제로 작용하는 Ni-P 공정합금을 미량첨가하여 제조공정의 간단화를 통한 새로운 W-Cu계 전기접점제조를 목표로 하였다. 이를 위해 1회 용침공정을 통해 제조한 W(Ni-P)-Cu 합금에 대한 전기접점특성을 조사하여 접점의 미세구조 관점에서 논의하였다. Ni-P 합금첨가한 접점은 기존의 순수 W-Cu 합금에 비해 낮은 접촉저항 및 낮은 아크소모를 나타내는 우수한 접점성능을 보여주었다. 이것은 Ni-P합금이 Cu용침이 개시되기전 짧은 승온단계에서 분말간의 강한 결합과 Cu용침에 유리한 기공통로를 갖는 W 분말 골격체의 형성을 유도하기 때문인 것으로 판단된다.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.02a
• /
• pp.37-59
• /
• 2004

In the case of Ni/Au finished pad on the package side, the solder joint of SnAgCu system can bring brittle fracture under impact load such as drop test. Therefore, it's difficult to prevent the brittle fracture of lead-free solder, by controlling Cu content. The failure locus existing on the interface between $(Ni,Cu)_3Sn_4\;and\;(Cu,Ni)_6Sn_5$ IMC layers must be changed to other site in order to avoid brittle fracture due to impact load. It was not found any clear evidence that there were two IMC layers exist. But it was strongly assumed these were two layers which have different Cu-Ni composition. From the above analysis it was assumed that Cu atom in the solder alloy or substrate seemed to affect IMC composition and cause to IMC brittle fracture.

• Korean Journal of Materials Research
• /
• v.28 no.5
• /
• pp.295-300
• /
• 2018

Effects of annealing temperature on the microstructure and mechanical properties through thickness of a Cu-3.0Ni-0.7Si alloy processed by differential speed rolling are investigated in detail. The copper alloy with a thickness of 3 mm is rolled to a 50 % reduction at ambient temperature without lubricant and subsequently annealed for 0.5 h at $200-900^{\circ}C$. The microstructure of the copper alloy after annealing is different in the thickness direction depending on the amount of the shear and compressive strain introduced by the rolling; the recrystallization occurs first in the upper roll side and center regions which are largely shear-deformed. The complete recrystallization occurs at an annealing temperature of $800^{\circ}C$. The grain size after the complete recrystallization is finer than that of the conventional rolling. The hardness distribution of the specimens annealed at $500-700^{\circ}C$ is not uniform in the thickness direction due to partial recrystallization. This ununiformity of hardness corresponds well to the amount of shear strain in the thickness direction. The average hardness and ultimate tensile strength has the maximum values of 250 Hv and 450 Mpa, respectively, in the specimen annealed at $400^{\circ}C$. It is considered that the complex mode of strain introduced by rolling directly affects the microstructure and the mechanical properties of the annealed specimens.

• Journal of Advanced Marine Engineering and Technology
• /
• v.39 no.5
• /
• pp.536-541
• /
• 2015

Copper has been used extensively as an electric wire or as a base material in various types of machineries owing to its good electrical and thermal conductivity and good fabricating property, as well as its good corrosion resistance compared to iron. Furthermore, the copper-nickel alloy has significant corrosion resistance in severely corrosive environments. Although, cupro-nickel alloy shows better corrosion resistance than the brass and bronze series, this alloy also corroded in severely corrosive environments, including aggressive chloride ions, dissolved oxygen, and condition of fast flowing seawater. In this study, and annealing treatment at various annealing temperatures was carried out on the cupro-nickel (Cu-10%Ni) alloy, and the effects of annealing were investigated using electrochemical methods, such as measuring the polarization and impedance behaviors under flowing seawater conditions. The corrosion resistance increased by annealing compared to non heat treatment in the absence of flowing seawater. In particular, the sample annealed at $200^{\circ}C$ exhibited the best corrosion resistance. The impedance in the presence of flowing seawater showed higher values than in the absence of flowing seawater. Furthermore, the highest impedances was observed in the sample annealed at $800^{\circ}C$, irrespective of the present of flowing seawater. Consequently, the corrosion resistance of cupro-nickel (Cu-10%Ni) alloy in a severely corrosive environment can be improved somewhat by annealing.

• Journal of Sensor Science and Technology
• /
• v.13 no.6
• /
• pp.405-410
• /
• 2004

Compensation wires for Pt/Pd thermocouple was manufactured using Cu/Ni alloys. Their thermoelectric voltage has been tested from room temperature to about $150^{\circ}C$. Alloys of $Cu_{95.5}Ni_{4.5}$ and $Cu_{89.5}Ni_{10.5}$ introduced only small emf differences to Pt/Pd thermocouples, indicating a real possibility of industrial use. Above $1000^{\circ}C$, the temperature difference was expected to he small as ${\pm}0.5^{\circ}C$, and the difference would be minimized by adjusting the Ni content with a small amount.

• Journal of Powder Materials
• /
• v.6 no.1
• /
• pp.36-41
• /
• 1999

The present work has attempted to investigate the dependence of Cu infiltration kinetics on in-situ structure modification of W powder skeleton in W-Cu system. In-situ structure modification of W skeleton by addition of 0.3wt%Ni-P eutectic alloy was designed to proceed during heat-up of the W compact for Cu infiltration process. It was found that the Ni-P added W skeleton underwent remarkable stucture change only during heating-up. its structure was composed of large necks of W particles above 0.5 in the ratio of neck to particle size and smooth pore channels. The infiltration experiment showed that the infiltration kinetics for the W-Ni-P followed well the linear relationship of h vs. $t^{1/2}$ the rate constant K of which was in good agreement with the theoretical value. On the other hand, in case of the pure W skeleton a lower K value by 20% than the theoretical one was obatined. Such discrepancy is discussed in terms of skeleton structure induced infiltration mechanics.

• Korean Journal of Materials Research
• /
• v.9 no.9
• /
• pp.905-912
• /
• 1999

Tensile properties of powder metallurgy (PM) processed Cu-7.5Ni-5Sn alloys, either as-received or additionally solution heat treated, were examined as a function of aging time. It was found that the as-received Cu-7.5Ni-5Sn alloys showed an abrupt increase in tensile strength after aging at $350^{\circ}C$ for 20 minutes, due to the metastable ${\gamma}$\\` precipitation and a marginal Spinodal decomposition. The resolutionized PM Cu-7.5Ni-5Sn alloys, on the other hand, showed a gradual increase in tensile strength from the very early stage of aging. The overall tensile strength of resolutionized PM Cu-7.5Ni-5Sn alloys, however, was lower than that of the as-received and aged counterparts, due to the grain growth during resolutionization. Afterprolonged aging for the as-received PM Cu-7.5Ni-5Sn alloys, a considerable amount of discontinuous precipitates formed along the grain boundaries. The formation and growth kinetics of such discontinuous precipitates appeared to be dependent on the heat treatment conditions, and affect the mechanical properties greatly.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.3
• /
• pp.125-130
• /
• 2002

An attempt was made for the application of porous reticular metal to a heat dissipation material in semiconductor process. For this aim, the electrodeposition of Fe/Ni alloy on the porous reticular Cu has been performed to minimize the thermal expansion mismatch between Cu skeleton and electronic chip. Preliminary tests for the electrodeposition of Fe/Ni alloy layer were conducted by using standard Hull Cell to examine the effect of current density on the composition of alloy layer. It seemed that mass transfer affected significantly the composition of Fe/Ni layer due to anomalous codeposition in the electrodeposition of Fe/Ni alloy. A paddle type stirring bath, which was employed to control the mass transfer of electrolyte in the work, was found to allow the electrodeposition Fe/Ni with a precise composition. result showed that the thermal expansion of Fe/Ni alloy layer was much lower than that of pure copper. From the tests of heat dissipation by using the apparatus designed in the work the heat dissipation material fabricated in the work showed the excellent heat dissipation capacity, namely, more than two times as compared to that of pure copper plate.

• Journal of Welding and Joining
• /
• v.12 no.4
• /
• pp.102-109
• /
• 1994

The thick and hard alloyed layer was formed on the surface of Aluminum Cast Alloy(AC2B) by PTA overlaying process with Cr, Cu and Ni metal powders under the condition of overlaying current 150A, overlaying speed 150mm/min and different powder feeding rate 5-20g/min. The characteristics of hardening and were resistance of alloyed layer have been investigated in relation to microstructure of alloyed layer. As a result, it was made clear that Cu powder was the most superier one in three metal powders used due to an uniform hardness distribution of Hv 250-350, good wear resistance and freedom from cracking in alloyed layer of which microstructure consisted of hypereutectic. On the contrary, irregular hardness distribution was usually obtained in Cr or Ni alloyed layers of which hardness was increased as Cr or Ni contents and reached to maximum hardness of about Hv 400-850 at about 60wt% Cr or 40wt% Ni in alloyed layer. However the cracking occurred in these alloyed layers with higher hardness than Hv 250-300 at more than 20-25wt% of Cr or Ni contents in alloyed layer. Wear rate of alloyed layer was decreased to 1/10 in Cu alloyed layer and 1/5 or 1/3 in Cr or Ni alloyed layer with same hardness of about Hv 300 in comparison with that of base metal at higher sliding speed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.246-249
• /
• 2000

The effects of Zr on the mechanical workability and tensile strength of Cu-Ni-Mn-Sn-Al alloys have been investigated and the following results were obtained. The mechanical workability of Cu-Ni-Mn-Sn-Al alloys are increased with addition of Zr. And the surface cracks of specimen were not produced in Zr added Alloys. Especially in condition of hot-worked beyond the 90% working ratio, Zr contained specimen showed intra-granule crack propagation but Zr-free specimen showed inter-granule mode. The tensile strength have maximum value in 0.05% Zr contained alloy. The aging mechanism of Cu-Ni-Mn-Sn-Al alloys were varied by Zr addition.