The small-scale electroplating device was designed and fabricated for Ni-63 sealed source (foil type) with a high specific activity needed for production of betavoltaic battery. The condition of Ni electroplating was optimized by using fabricated electroplating device to establish a Ni-63 electroplating condition on the Ni foil. The results showed that the optimum surface morphology and thickness of Ni deposit was obtained for 1,758 seconds at a current density of $15mA{\cdot}cm^{-2}$ with 0.5% tween 20. Radioisotope Ni-63 electroplating was implemented under established condition. The radioactivity of Ni-63 sealed source was calculated to $28mCi{\cdot}cm^{-2}$, and the thickness of Ni-63 deposit was about $2.4{\mu}m$.

• Journal of Surface Science and Engineering
• /
• v.50 no.1
• /
• pp.29-34
• /
• 2017

Chloride plating solution was fabricated by dissolving metal Ni powders in a mixed solution with HCl and de-ionized water. Effects of $Ni^{2+}$ and saccharin concentrations in the plating baths on current efficiency, residual stress, surface morphology and microstructure of Ni films were studied. In the case of $0.2M\;Ni^{2+}$ concentration, current efficiency was decreased to about 65 % with increasing saccharin concentration, but, in the case of $0.7M\;Ni^{2+}$ concentration, it was shown more than 90 % with the increase of saccharin concentration. Residual stress of Ni thin film was appeared to be about 400 MPa up to 0.0244 M saccharin concentration at the $0.2M\;Ni^{2+}$ concentration and surface morphology with severe cracks was observed in the range of 0.0487~0.0975 M saccharin concentration. Residual stress of Ni thin films was measured to be about 750 MPa without saccharin addition and 114~148 MPa at the range of 0.0097~0.0975 M saccharin concentration for the $0.7M\;Ni^{2+}$ concentration. Relatively low residual stress values (114~148 MPa) of the Ni films at the range of 0.0097~0.0975 M saccharin concentration may be resulted from codeposition of S from saccharin. Ni films at $0.7M\;Ni^{2+}$ concentration showed smooth surface morphology and were independent of saccharin concentration. Ni films at $0.7M\;Ni^{2+}$ concentration consist of FCC(111), FCC(200), FCC(220) and FCC(311) peaks and the intensities of FCC(111) and FCC(200) peaks increased with increasing saccharin concentration. Also, the average grain size decreased with increasing saccharin concentration from about 30 nm to about 15 nm.

• Journal of Surface Science and Engineering
• /
• v.52 no.2
• /
• pp.78-83
• /
• 2019

Chloride baths for electrodeposited Ni thin films were fabricated by dissolving metal Ni powders with the mixed solution consisting of HCl and de-ionized water. Current efficiency, residual stress, surface morphology and microstructure of Ni films with the change of metal ion ($Ni^{2+}$) concentrations in the plating solution were studied. Current efficiency was measured to be more than 90% with increasing $Ni^{2+}$ concentrations in the plating solution. Residual stress of Ni thin film was increased from about 400 to 780 MPa with increasing $Ni^{2+}$ concentration from 0.2 to 0.5 M. It is gradually decreased to 650 MPa at 0.9 M $Ni^{2+}$ concentration. Smooth surface morphologies were observed over 0.3 M $Ni^{2+}$ concentration, but nodule surface morphology at 0.2 M. Ni films consist of FCC(111), FCC(200), FCC(220) and FCC(311) peaks in XRD patterns. Preferred orientation of FCC(111) was observed and its intensity was slightly decreased with increasing $Ni^{2+}$ concentration. The average grain size was slightly increased at 0.3 M $Ni^{2+}$ concentration and then slightly decreased with increasing $Ni^{2+}$ concentration.

• Journal of Surface Science and Engineering
• /
• v.48 no.3
• /
• pp.73-81
• /
• 2015

Chloride plating solution was fabricated by dissolving metal Ni powders in solution with HCl and deionized water. Effects of deposition conditions on the properties of Ni films electrodeposited from chloride baths were studied. Current efficiency of Ni films electrodeposited from the baths containing saccharin was decreased with increasing the current density. Residual stress of Ni thin films ware measured to be about 230 ~ 435 MPa in the range of current density of $10{\sim}25mA/cm^2$. Cathode current efficiency in baths without saccharin was initially increased with increasing pH, while it was decreased with increasing pH further. Cathode current efficiency in baths with saccharin (except at pH 2) exhibited less 10 ~ 20% than that in baths without saccharin. Residual stress of Ni films electrodeposited from baths without saccharin was measured to be 388 ~ 473 MPa in the range of pH 2 ~ pH 5 and then was increased to 551 MPa at pH 6. On the other hand, residual stress of Ni films electrodeposited from baths with saccharin was increased with increasing pH. Surface morphology was strongly affected by the change of current density, but slightly by solution pH and addition of saccharin.