A Study on the ENIG Surface Finish Process and Its Properties (ENIG 표면처리 공정 및 특성에 관한 연구)

  • Lee, Hong-Kee;Son, Seong-Ho;Lee, Ho-Young;Jeon, Jun-Mi
    • Journal of the Korean institute of surface engineering
    • /
    • v.40 no.1
    • /
    • pp.32-38
    • /
    • 2007
  • Ni coating layers were formed using a newly developed electroless Ni plating solution. The properties of Ni coating layer such as internal stress, hardness, surface roughness, crystallinity, solderability and surface morphology were investigated using various tools. Results revealed that internal stress decreased with plating time and reached $40N/mm^2$ at 20 minutes of the plating time. Hardness increased with increasing P content and thickness. Surface roughness of the pad decreased with Ni and Ni/Au plating. Crystallinity decreased with increasing P content. Solderability based on wettability decreased with Ni and Ni/Au plating. Based on surface morphology, it is expected that Ni coating layer formed using a newly developed electroless Ni plating solution is lower than that formed using a commercial electroless Ni plating solution in possibility of black pad occurrence.

Effects of the Electroplating Duration on the Mechanical Property of the Ni-Co-SiC Composite Coatings

  • Kim, Sung-Min;Lee, Hong-Kee
    • Journal of the Korean institute of surface engineering
    • /
    • v.43 no.6
    • /
    • pp.255-259
    • /
    • 2010
  • In this work, Ni-Co composites incorporated with nano-sized SiC particles in the range of 45-55 nm are prepared by electroplating. The effects of plating duration on the chemical composition, surface morphology, crystalline structures and hardness have been studied. The maximum hardness of Ni-Co-SiC composite coating is approximately 633 Hv at plating duration of 1 h. The hardness is gradually decreased with increasing plating duration, which can be attributed to the growth of crystalline size and the agglomerates of SiC nano-particles. It is therefore explained that the grain refinement of Ni-Co matrix and stable dispersion of SiC particles play an important role for strengthening, which indicate Hall-Petch relation and Orowan model were dominant for hardening of Ni-Co-SiC composite coatings.

Nano Crystalline Change by Heat Treatment

  • Sun, Yong-Bin
    • Journal of the Semiconductor & Display Technology
    • /
    • v.12 no.4
    • /
    • pp.55-59
    • /
    • 2013
  • Mold die sticking arises from silica filler abrasion to the cavity surface. Ni-P electroplating was examined to substitute conventional hard Cr plating. More than 4% of Phosphorus in the electroplated film produces nano crystal structure and annealing makes $Ni_3P$ precipitated to get hardness values equivalent to hard Cr.

Excellent Seam Weldable Nano-Composite Coated Zn-Ni Plating Steels for Automotive Fuel Tank

  • Jo, Du-Hwan;Yun, Sang-Man;Park, Kee-Cheol;Kim, Myung-Soo;Kim, Jong-Sang
    • Corrosion Science and Technology
    • /
    • v.18 no.1
    • /
    • pp.16-23
    • /
    • 2019
  • Steels for automotive fuel tank require unique properties such as corrosion resistance for fuel, welding for joining, forming for press, and painting for exterior. Recently, automakers have been requiring excellent seam weldable steels to enhance manufacturing productivity of fuel tank. Thus, POSCO developed a new type of functional steels coated with nano-composite thin layer on Zn-Ni plating steels. The nano-composite coating solution was prepared by mechanical fine dispersion of solutions consisting of polymeric resin and nano-composite materials in aqueous media. The composite solution was coated on the plating steel surface by using roll coater and cured through induction furnace. These new developed plating steels were evaluated for quality performances such as seam and spot weldability, press formability, and corrosion resistance. These new functional steels coated with nano-composite layer exhibited excellent seam weldability and press formability. Detailed discussion of coating solution and experimental results suggest that nano-sized composite dispersion as coating layer plays a key role in enhancing the quality performance.

Effect of Plating Parameters on the Electrodeposition of Ni-alumina Nanocomposite

  • Gyawalia, Gobinda;Woo, Dong-Jin;Lee, Soo-Wohn
    • Journal of the Korean institute of surface engineering
    • /
    • v.43 no.4
    • /
    • pp.165-169
    • /
    • 2010
  • $Ni-Al_2O_3$ nanocomposite coatings were fabricated by conventional electrodeposition technique using nickel sulfamate bath. Effect of plating parameters on electrodeposition of $Ni-Al_2O_3$ nanocomposite were studied. The properties of the nano composite were investigated by using SEM, XRD, and Vicker's microhardness test. The results demonstrated that $Al_2O_3$ incorporation in the composite coatings was found to be increased by increasing stir rate and $Al_2O_3$ content in plating bath. Microhardness of the composite coatings was also increased with increasing content of the nano particles in the plating bath. The surface morphologies of the nanocomposite coatings were found to be varied with varying pH, current densities as well as alumina content in the plating bath.

Properties of Ni-P-SiC Composite Coating Layers Prepared by Electroless Plating Method (무전해도금법으로 형성한 Ni-P-SiC 복합도금막의 특성)

  • Lee, Hong-Kee;Lee, Ho-Young;Jeon, Jun-Mi
    • Journal of the Korean institute of surface engineering
    • /
    • v.40 no.2
    • /
    • pp.70-76
    • /
    • 2007
  • Ni-P-SiC composite coating layers were prepared by electroless plating method and their deposition rate, codeposition of SiC, morphology, surface roughness, hardness, wear and friction properties were investigated. The deposition rate was kept almost constant independent of the concentration of SiC in the plating solution and the codeposition of SiC in the composite coating layer increased with increased concentration of SiC in the plating solution except the early stage. Vickers microhardness increased with respect to the increased codeposition of SiC and the heat treatment at $300^{\circ}C$ in air for 1 hour. It was found that the wear volume decreased with increased up to 50 wt.% of SiC codeposition, and that friction coefficient increased gradually with increased codeposition of SiC. Considering the wear and the friction behaviors, the composite coating layer obtained by using 50 wt.% of SiC codeposition is desirable for the practical application for anti-wear and anti-friction coatings.

The Surface Improvement by Supercritical Nano Plating (슈퍼크리티컬 나노 플레이팅에 의한 표면개질)

  • Kim, Yun-Hae;Bae, Chang-Won;Kim, Do-Wan;Moon, Kyung-Man;Kim, Dong-Hun;Jo, Young-Dae;Kang, Byung-Yoon
    • Transactions of the Korean Society of Mechanical Engineers A
    • /
    • v.33 no.9
    • /
    • pp.913-921
    • /
    • 2009
  • In this study, supercritical nano plating was performed to observe its effect on materials. Using supercritical carbon dioxide as a solvent, we observed how different pressures and temperatures of the supercritical fluid affected the process and its outcome. The plating current increases as pressure increases from 8 MPa to 16 MPa, but it decreases after that. Similarly, the plating current increases as temperature is increased from $35^{\circ}C$ to $45^{\circ}C$, but the current decreases after that. Also, the thickness of the wet electrolyte plating is about $35\sim50{\mu}m$, while the thickness of the plating done using supercritical fluid is about $20\sim25{\mu}m$. At the results, It to it is considered that supercritical nano plating enable to form more thin and stable plating than wet electroplating methods. Also both of the electroplating methods could be affected plating quality by surface condition, and the supercritical nano plating has been confirmed to product more uniform plating surface than wet electroplating.

Sintering of Ni-Based Amorphous Alloy Powders by Plasma Activated Sintering Process (PAS법을 이용한 Ni기 비정질 분말의 소결)

  • Koo, Ja-Min;Shin, Kee-Sam;Kim, Yoon-Bae;Bae, Jong-Soo;Hur, Sung-Kang
    • Korean Journal of Materials Research
    • /
    • v.15 no.12
    • /
    • pp.765-772
    • /
    • 2005
  • PAS(Plasma Activated Sintering) process was tried to apply for the fabrication of BMG(Bulk Metallic Glasses) of $Ni_{57}Zr_{20}Ti_{18}Si_5}\;and\;Ni_{57}Zr_{20}Ti_{18}Si_3Sn_2$ from the as-atomized amorphous powder. Compressive strength for the BMG(bulk Metallic Glasses) of $Ni_{57}Zr_{20}Ti_{18}Si_5$ were lower than those of BMG rods produced by warm extrusion ,or copper mold casting method. Microstructural examination by optical microcope, SEM ana EDS showed that oxidation had occurred during PASintering. In order to prevent the powder from the oxidation during PASintering, Ni coating for $Ni_{57}Zr_{20}Ti_{18}Si_5$ amorphous powder by electroless-plating method was performed. Microstructural examination for Ni coated layers after PASintering indicated that the Ni coating had been so effective to prevent powder from oxidation during PASintering. Sintering behaviors of $Ni_{57}Zr_{20}Ti_{18}Si_3Sn_2$ represent the same as those of $Ni_{57}Zr_{20}Ti_{18}Si_5$.

DMAB Effects in Electroless Ni Plating for Flexible Printed Circuit Board (DMAB첨가량에 따른 연성회로기판을 위한 무전해 Ni 도금박막에 관한 연구)

  • Kim, Hyung-Chul;Rha, Sa-Kyun;Lee, Youn-Seoung
    • Korean Journal of Materials Research
    • /
    • v.24 no.11
    • /
    • pp.632-638
    • /
    • 2014
  • We investigated the effects of DMAB (Borane dimethylamine complex, C2H10BN) in electroless Ni-B film with addition of DMAB as reducing agent for electroless Ni plating. The electroless Ni-B films were formed by electroless plating of near neutral pH (pH 6.5 and pH 7) at $50^{\circ}C$. The electroless plated Ni-B films were coated on screen printed Ag pattern/PET (polyethylene terephthalate). According to the increase of DMAB (from 0 to 1 mole), the deposition rate and the grain size of electroless Ni-B film increased and the boron (B) content also increased. In crystallinity of electroless Ni-B films, an amorphization reaction was enhanced in the formation of Ni-B film with an increasing content of DMAB; the Ni-B film with < 1 B at.% had a weak fcc structure with a nano crystalline size, and the Ni-B films with > 5 B at.% had an amorphous structure. In addition, the Ni-B film was selectively grown on the printed Ag paste layer without damage to the PET surface. From this result, we concluded that formation of electroless Ni-B film is possible by a neutral process (~green process) at a low temperature of $50^{\circ}C$.

Research on the Solution and Properties of Ni-P/n-$Al_2O_3$ Electroless Composite Plating

  • Huang, Yan-bin;Liu, Fei-fei;Zhang, Qi-yong;Ba, Guo-zhao;Liang, Zhi-jie
    • Corrosion Science and Technology
    • /
    • v.6 no.5
    • /
    • pp.257-260
    • /
    • 2007
  • In order to further improve the corrosion resistance and wear resistance of the Ni-P coatings of electroless plating, electroless Ni-P/n-$Al_2O_3$ composite deposits were prepared by adding some nano $Al_2O_3$ Particles in Ni-P plating bath. The bath composition and proproties were studied in this paper. The orthogonal test was applied in order to get the new composite solution, taking the initial stable potential as evaluation standard and considering the elements correlation at the same time. The processing parameters have been optimized by single factor experiment in which the depositing speed was chosen as the evaluation standard. The results showed that the process is stable and the composite Ni-P/n-$Al_2O_3$ deposits werebright and smooth, whose hardness and corrosion resistance are much better than simple Ni-P coatings. Furthermore the surface appearance and structure of the composite Ni-P/n-$Al_2O_3$ coating were investigated by SEM and XRD method. It was proved that the coating surface is typical cystiform cells and its structure is amorphous. All test results ofcomposite coating showed that all various physical coating properties had been improved by adding nano-particles. The hardness of optimal coating is more than 600HV and increases to 1000HV after heat-treating, and its hardness is 20~50% higher than Ni-P coating. The rust points appeared in 200 hour by immersing the coating into the 10%HCl solution and the corrosive speed is $3{\times}10^{-3}mg/(cm^2{\cdot}h)$which was obtained after 300 hour. In the same condition Ni-P coating is $5.6{\times}10^{-3}mg/(cm^2{\cdot}h)$. The salt spray resistance of the layers can exceed 600h with the thickness $20{\mu}m$.