• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.267-267
• /
• 2015

본 연구에서는 에틸렌디아민을 착화제로 사용하여 전해도금으로 Ni-Pd 합금피막을 형성하였다. 염화팔라듐 농도 1~5 mM, 전류밀도 $0.2{\sim}1.5A/dm^2$ 구간에서 고용체 합금피막이 형성되었으며, 이의 격자상수는 X선회절 분석을 통하여 확인하였다. Pd 함량은 전류밀도가 증가할수록 감소하였고, 경도는 전류밀도가 증가할수록 증가하다가 전류밀도 $1.3A/dm^2$ 이후 급격히 감소하였다. 경도증가 원인은 결정립미세화이고, 전류밀도 $1.3A/dm^2$ 이후에서 잔류응력으로 인한 크랙 발생으로 사료되었다.

• Journal of Environmental Policy
• /
• v.9 no.1
• /
• pp.137-154
• /
• 2010

These objectives of this study were to compute heavy metal and accumulation carbon dioxide fixing quantity from urban green space(street trees and urban parks) in Cheong-ju city and Chungju-city and thus to estimate the effect of urban green space for improving the urban environment. The results are summarized below. 1. Results of the total accumulation of the carbon dioxide fixing quantity of street trees, Cheong-ju city and Chungju-city street tree was 1, 230,000kg-C, 1,270,000 kg-C, respectively. Total accumulation carbon dioxide fixing quantity of Balssan urban park had a 25,000kg-C in Cheong-ju city, Degami sports park had a 6,400kg-C in Chungju-city. 2. Results of heavy metal for street trees, fell in the order Zn > Cu > Cr > Ni >, the highest accumulated heavy metal was Zn, and the lowest was Ni. Total heavy metal concentration according to land-use area, was observed in order, for residental areas(157.26 mg/kg) > industrial areas(141.71 mg/kg) > commercial areas(118.55 mg/kg) > and greenspace areas(61.95 mg/kg) in Cheong-ju city. 3. Total heavy metal concentration for street trees fell in the order of commercial areas(84.48 mg/kg) > residental areas(83.70 mg/kg) > and greenspace(48.23 mg/kg) according to land-use area in Chungju-city. Comparatively, Cheong-ju city had more total heavy metal concentration than Chungju-city. 4. Heavy metal for soil that planted street trees was observed in order of Zn > Cu > Pb( > Ni > Cr > As > Cd), and Zn was highest, and Cd was lowest. Total heavy metal concentration for soil fell in the order commercial area(91.82mg/kg) > industrial area(85.96mg/kg) > residental area(67.55mg/kg) > greenspace(43.13mg/kg) according to land-use area in Cheong-ju city. 5. Heavy metal for soil that planted street trees was observed in order of Zn > Pb > Cu( > Ni > Cr > As > Cd, and Zn was highest. Total heavy metal concentration for soil fell in the order commercial area(87.66mg/kg) > greenspace(72.73mg/kg) $${\geq_-}$$ residental area(70.10mg/kg) in Chungju-city.

• Korean Journal of Environmental Agriculture
• /
• v.22 no.2
• /
• pp.87-93
• /
• 2003

Growth and mineral composition of young radish in soil amended with sewage sludge (ISS) with or without liming were investigated. Levels of EC, T-N, and micronutrients were increased in the ISS treatment (50 Mg/ha) compared to the NPK treatment but those of available P and exchangeable cations were decreased. Chlorosis was appear on the young radish leaf at the ISS treatment, but this phytotoxic symptom was corrected with lime amendment (3 Mg/ha). Yields of young radish leaf and root in the combined treatment of ISS and lime were increased about 29 and 48%, respectively, compared with those in the ISS treatment. Contents of P, K, Ca, and Mg in young radish were higher in the combined treatment to ISS and lime, whereas those contents in the ISS treatment were lower than those in the NPK treatment. Contents of Cu, Zn, and Ni in soil and young radish leaf were positively correlated with total N content in young radish leaf, while contents of P, K, Ca, and Mg were negatively correlated. Contents of Cu, Zn, and Ni in leaf were negatively correlated with yield of young radish. Contents of Cu and Zn in leaf corresponding with a 5% yield reduction of young radish were 22.4 and 349 mg/kg, respectively.

• Proceedings of the KSEEG Conference
• /
• 2003.04a
• /
• pp.241-244
• /
• 2003

유류오염 토양내 유류의 분해와 무기오염물질의 함량과의 관계성을 알아보기위해 부산 문헌지구의 유류 오염 토양 profile중 유류가 비교적 많은 두 층과 유기물이 다량 함유된 제주도 토양을 경유로 오염시킨 토양을 선택하여 유류가 분해 정도와 Pb, Zn, Cd, Ni의 함량을 측정 비교하였다. 토양 채취후 즉시 유류를 추출한 것, 15일간 별도의 미생물 영양원을 가하지 않고 습도와 통풍만을 행하여 토양내 존재하는 미생물들에 의하여만 유류가 분해되도록 한 것, $105^{\circ}C$에서 24시간 열처리를 행하여 미생물에 의한 분해보다는 물리적인 방법으로 비교적 강하게 처리한 것 세가지 경우에서 토양에서 추출한 유류를 분석한 결과 normal alkane이 서서히 상당량 분해되는 양상을 보여주었다. 토양내 Pb, Zn, Cd, Ni를 분석한 결과 부산 시료의 경우 두 층(B2, B3)모두 Cd은 검출한계 이하로, Ni의 경우 극소량의 함량을 보여주었다. Zn의 경우 B2는 28～29ug/g, B3는 12～14ug/g으로 세가지 경우 별 차이 없는 양상을 보여 주었다. 하지만, Pb의 경우 B2에서는 그 함량이 유류의 normal alkane의 분해와 함께 서서히 증가하는 경향을 확연히 보여주었으며, B3의 경우도 B2와 유사한 변화 양상을 보여주었다. 제주도 토양의 경우 Pb는 검출되지 않았고, Zn은 소량 검출되었다. Ba, Ni 함량은 normal alkane 분해에 따라 다소 증가하였다. 따라서, 본 예비실험을 통하여 유류오염 토양에서 유류의 분해와 일부 무기이온사이에는 관련성을 갖고 있으며, 이는 유류 분해정도를 파악하는 지시자로써 특정 무기 오염물질을 이용할 수 있을 가능성이 있으므로 좀더 이들 관계성에 대한 연구가 진행될 필요성이 있다고 판단된다.고 과학적으로 분석할 수 있는 방법이 될 수 있을 것으로 기대된다. 의미를 되새기는 것으로 짧은 연구를 시작하겠다. 등은 활성 값이 70% 이상으로 퇴적물 독성이 상대적으로 낮았다. 이중나선 DNA 함량은 28.4 % - 49%로 대조군에 비해서 감소가 크다. 대부분의 정점이 대조군의 30% 내외로 정점 간의 차이는 크지는 않다. 그러나 다른 측정자료와 같이 정점 22에서 18%로 최소치를 나타내고, 정점 2, 12에서 20% 내외의 값을 보인다. 종합적으로 볼 때 오염물질의 유입이 크고, 광양제철 인근 정점 들이 모두 다른 정점에 비해서 낮아서, 퇴적물 독성이 높은 정점으로 조사되었다.hiwo의 광합성 능력은 낮은 농도들에서는 대조구와 유사하였으나, 5 $\mu\textrm{g}$/l의 높은 농도에서는 초기에 매우 낮은 광합성 능력을 보이다가 시간이 경과하면서 대조군보다 더 높은 경향을 나타냈다. 이러한 결과는 식물플랑크톤이 benso[a]pyrene의 낮은 농도에서 노출될 때는 이 물질을 탄소원으로 사용할 가능성이 있음을 시사한다. 본 연구의 결과들은 연안해역에 benso[a]pyrene과 같은 지속성 유기오염물질이 유입되었을 때 내정여부에 따라 식물플랑크톤 군집내 종 천이와 일차생산력에 크게 영향을 미칠 수 있음을 시사한다.TEX>5.2개)였으며, 등급별 회수율은 각각 GI(8.5%), GII(13.4%), GIII(43.9%), GIV(34.2%)로 나타났다.ments of that period left both in Japan and Korea. "Hyojedo" in Korea is supposed to have been influenced by the letter design. Asite- is also considered to have been "Japan

• Journal of the Korean Electrochemical Society
• /
• v.20 no.4
• /
• pp.67-74
• /
• 2017

Layered Ni-rich NCM cathode materials $Li[Ni_xCo_{(1-x)/2}Mn_{(1-x)/2}]O_2$ ($x{\geq}0.6$) have advantages of high energy density and cost competitive over $LiCoO_2$. The discharge capacity of NCM increases proportionally to the Ni contents. However, there is a problem that it is difficult to realize the stable electrochemical performance due to cation mixing. In this study, synthesis conditions for the layered Ni-rich NCMs are investigated to achieve deliver the ones having good electrochemical performances. Synthesis parameters are atmosphere, lithium source, synthesis time, synthesis temperature and Li/M (M=transition metal) ratio. The degree of cation mixing gets worse as the Ni content is increased from $Li[Ni_{0.6}Co_{0.2}Mn_{0.2}]O_2$ (NCM6) to $Li[Ni_{0.8}Co_{0.1}Mn_{0.1}]O_2$ (NCM8). It is confirmed that higher level of cation mixing affects negatively on the electrochemical performance of NCMs. Optimum synthesis conditions are explored for NCMx (x=6, 7, 8) in order to reduce the cation mixing. Under optimized conditions for three representative NCMx, a high initial discharge capacity and a good cycle life are obtained for $180mAh{\cdot}g^{-1}$, 96.2% (50 cycle) in NCM6, $187mAh{\cdot}g^{-1}$, 94.7% (50 cycle) in NCM7, and $201mAh{\cdot}g^{-1}$, 92.7% (50 cycle) in NCM8, respectively.

• 한국신재생에너지학회:학술대회논문집
• /
• 2008.05a
• /
• pp.499-502
• /
• 2008

고정층반응기에서 니켈이 치환된 하이드로탈사이트($Ni_3Mg_3Al_2(CO_3)(OH)_{{16}{\cdot}n}H_2O$ ; n=3$\sim$5)를 합성하고 여기에 세리아를 첨가 후 소성하여 얻은 촉매를 사용하여($Ce_xNi_3$-HTlc ; x=0.3$\sim$1.2) 메탄의 부분산화 반응실험을 수행하였다. 세리아가 첨가되지 않은 촉매는 반응 초기 활성이 세리가가 소량 첨가된 ($Ce_{0.3}Ni_3$-HTlc) 촉매보다 우수하였으나 장시간 반응에서는 차차 활성이 저하되었으나, $Ce_{0.3}Ni_3$-HTlc의 활성은 30시간까지 일정하게 유지 되었다. 세리아 함량이 많아 질수록 촉매 활성은 점차 저하되었으며, $Ce_{1.2}Ni_3$-HTlc 는 촉매활성이 매우 낮았다.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.98-103
• /
• 2002

BGA(Ball Grid Array) 패키지의 솔더볼 패드 중의 하나인 Au/Ni-Co/Cu 금속층 위에 Bi가 첨가된 Sn-3.5Ag-$\chi$Bi 솔더볼을 리플로우시켰다. 리플로우한 후 130 $^{\circ}C$에서 열처리함에 따른 계면상 및 솔더 내부의 상변화를 관찰하였다. 계면에는 (Ni,Co)$_3$Sn$_4$외에 (Au,Ni,Co,Bi)Sn$_4$가 생성되었음을 관찰할 수 있었고, 솔더 내부에는 (Au,Ni,Co,Bi)SH$_4$, Ag$_3$Sn, Bi 상이 혼재되어 있었다. Nano-indentation에 의한 경도 측정 결과, Bi 함량 증가에 따라 경도는 증가하였으나, 볼전단(Ball Shear) 테스트 결과는 Bi가 증가됨에 따라 오히려 볼전단 강도값이 감소하였다. 이는 파면 검사 결과, 파괴 경로가 주로 계면의 금속간 화합물과 솔더 사이에서 진행함에 기인한 것이다. 솔더 내부의 파괴 경로를 가진 2.5Bi가 가장 우수한 볼전단 강도값을 나타내었는데, 이는 솔더내의 Bi의 고용강화에 기인한 것으로 보인다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.315-316
• /
• 2007

최근 전자제품의 경박단소화와 고성능화에 대한 관심이 증가하면서 내장형 수동소자 (Embedded Passive Device)에 대한 연구가 활발히 진행되고 있다. 본 연구에서는 Ni-coated $BaTiO_3$와 PMMA의 함량 변화에 따른 복합체의 유전적 특성을 연구하였다. Ni-coated $BaTiO_3$첨가량을 0~50%까지 증가시키며 유전율을 측정하였으며, 코팅되지 않은 $BaTiO_3$-PMMA복합체의 유전율과 결과를 비교하였다. 본 연구결과 Ni 코팅에 의한 유전율 증가를 관찰할 수 있었으며, 코팅 상태는 코팅공정시의 시간과 온도 등에 의존한다는 것을 확인하였다. 본 논문에서는 이러한 실험결과를 개선된 혼합법칙을 바탕으로 해석하고자 한다.

• Korean Chemical Engineering Research
• /
• v.45 no.5
• /
• pp.506-514
• /
• 2007

To select the best oxygen carrier particle for syngas fueled chemical-looping combustor, the reduction reactivity and carbon deposition characteristics were determined in a thermogravimetric analyzer. Four kinds of oxygen carrier particles (NiO/bentonite, $NiO/LaAl_{11}O_{18}$, $Co_xO_y/CoAl_2O_4$, $NiO/NiAl_2O_4$) were tested with the simulated syngas (30% $H_2$, 10% $CO_2$, 60% CO) as a reduction gas. With each of these particles, the maximum conversion and oxygen transfer capacity increase with increasing the reduction temperature At the given experimental range, the optimum operating temperature to maximize oxygen transfer rate is found to be $900^{\circ}C$ and carbon deposition on the particles could avoid at the temperature above $800^{\circ}C$. Among four kinds of oxygen carrier particles, the NiO-based particles exhibits better reactivity than the CoO-based particle. Moreover, the NiO/bentonite particle produces the best reactivity based on the oxygen transfer rate and the degree of carbon deposition. The measured oxygen transfer rate increases as the metal oxide content in NiO/bentonite particle is increased thereby higher metal oxide contents could provide stable operation of chemical-looping combustor.

• Corrosion Science and Technology
• /
• v.22 no.1
• /
• pp.64-72
• /
• 2023

Ni-Ti shape memory alloy for dental nerve treatment devices was prepared by adding Mo to Ni-Ti alloy to improve flexibility and fatigue fracture characteristics and simultaneously increase corrosion resistance. Surface properties of the alloy were evaluated. Microstructure analysis of the Ni-Ti-xMo alloy revealed that the amount of needle-like structure increased with increasing Mo content. The shape of the precipitate showed a pattern in which a long needle-like structure gradually disappeared and changed into a small spherical shape. As a result of XRD analysis of the Ni-Ti-xMo alloy, R-phase structure appeared as Mo was added. R-phase and B2 structure were mainly observed. As a result of DSC analysis, phase transformation of the Ti-Ni-Mo alloy showed a two-step phase change of B2-R-B19' transformation with two exothermic peaks and one endothermic peak. As Mo content increased, R-phase formation temperature gradually decreased. As a result of measuring surface hardness of the Ti-Ni-Mo alloy, change in hardness value due to the phase change tended to decrease with increasing Mo content. As a result of the corrosion test, the corrosion potential and pitting potential increased while the current density tended to decrease with increasing Mo content.