• 한국재료학회지
• /
• 제16권5호
• /
• pp.277-284
• /
• 2006

The alloys were prepared by a non-consumable vacuum arc melting and homogenized at $1050^{\circ}C$ for 24 hrs. Two kind of surface modifications were performed alkali treatment in 5.0M NaOH solution subsequent and heat treatment in vacuum furnace at $600^{\circ}C$, and were oxidizing treatment at the temperature range of 550 to $750^{\circ}C$ for 30 minutes. After surface modification, these samples were soaked in SBF which consists of nearly the same ion concentration as human blood plasma. Cytotoxicity tests were performed in MTT assay treated L929 fibroblast cell culture, using indirect methods. A porous and thin activated layer was formed on Titanium and Ti-8Ta-3Nb alloy by the alkali treatment. A bone-like hydroxyapatite was nucleated on the activated porous surfaces during the in vitro test. However, Ti-8Ta-3Nb alloys showed better bioactive properties than Titanium. According to XRD results, oxide layers composed of mostly $TiO_2$(rutile) phases. Cytotoxicity test also revealed that moderate oxidation treatment lowers cell toxicity and Ti-8Ta-3Nb alloy showed better results compared with Titanium.

• Advances in materials Research
• /
• 제2권3호
• /
• pp.141-153
• /
• 2013

Nanocrystalline Barium niobate ($BaNbO_3$) has been synthesized by a novel auto-igniting combustion technique. The X-Ray diffraction studies reveals that $BaNbO_3$ posses a cubic structure with lattice constant $a=4.071{\AA}$. Phase purity and structure of the nano powder are further examined using Fourier-Transform Infrared and Raman spectroscopy. The average particle size of the as prepared nano particles from the Transmission Electron Microscopy is 20 nm. The UV-Vis absorption spectra of the samples are recorded and the calculated average optical band gap is 3.74eV. The sample is sintered at an optimized temperature of $1425^{\circ}C$ for 2h and attained nearly 98% of the theoretical density. The morphology of the sintered pellet is studied with Scanning Electron Microscopy. The dielectric constant and loss factor of a well-sintered $BaNbO_3$ at 5MHz sample is found to be 32.92 and $8.09{\times}10^{-4}$ respectively, at room temperature. The temperature coefficient of dielectric constant was $-179pp/^{\circ}C$. The high dielectric constant, low loss and negative temperature coefficient of dielectric constant makes it a potential candidate for temperature sensitive dielectric applications.

• 한국세라믹학회지
• /
• 제38권10호
• /
• pp.953-957
• /
• 2001

완화형 강유전체인 $Pb(Mg_{1/3}Nb_{2/3})O_3$계의 상전이 주파수의존성을 조사하기 위해 낮은 전계와 높은 전계 하에서 측정된 물성들을 1 Hz부터 100 kHz에 이르는 주파수 범위에서 비교 분석하였다. $-40{\sim}90^{\circ}C$의 상전이 온도범위에 걸쳐 1 V/mm의 낮은 전계에서 측정된 유전특성의 온도의존성을 구하였고, 수 kV/mm의 강전계 하에서 측정된 유전이력곡선의 기울기로부터 계산된 유전상수의 온도의존성 및 초전전류의 온도의존성을 검토하였다. 모든 실험적 결과와 Vogel-Fulcher 관계식은 비교적 잘 일치되었다. 본 연구를 통하여 유전완화현상은 약전계 조건 뿐 아니라 강전계 조건 하에서도 동일한 거동을 보이는 것을 확인할 수 있었다.

• 한국재료학회지
• /
• 제12권3호
• /
• pp.182-189
• /
• 2002

The Zr-0.2Sn-0.8Nb-X(X = 0~200ppm Si, 0~0.4wt.% Mo and Mn respectively) ingots for test specimens were manufactured by a vacuum arc re-melting method to find out the effect of Si, Mo, and Mn on the corrosion characteristics of the Zr-0.2Sn-0.8Nb alloy. After being heat-treated and rolled repeatedly out to be flat materials, they were finally heat-treated at 51$0^{\circ}C$ for three hours and used as the specimens for corrosion tests. The corrosion behavior of the specimens was studied in both 40$0^{\circ}C$ steam for 200 days and in aqueous 70 ppm LiOH solution at 36$0^{\circ}C$ for 90 days. From the study it was found that Si from 80 to 200 ppm contributed to increasing the corrosion resistance of Zr-0.2Sn-0.8Nb alloy in both steam and LiOH solution. This study also showed that Mn from 0.1 to 0.4% caused to go up the corrosion resistance, whereas Mo played a apart in improving the corrosion resistance only between 0.05 and 0.2 wt.%.

• 한국전기전자재료학회논문지
• /
• 제19권6호
• /
• pp.524-530
• /
• 2006

$xCa(Li_{1/4}Nb_{3/4})O_{3}-(1-x)CaTiO_{3}$ ceramics were sintered under the presence of zinc-borosilicate(ZBS) glass and resultant microwave dielectric properties were investigated with a view to applying the composition to low-temperature co-fired ceramic(LTCC) technology. The addition of $5{\sim}15wt%$ ZBS glass ensured successful sintering below $900\;^{\circ}C$. In general, increased addition of ZBS glass increased sinterability but it decreased the quality factor($Q{\times}f_{0}$) significantly due to the formation of an excessive liquid and second phases. As for the addition of $CaTiO_3$, the dielectric constant(${\epsilon}_r$) and temperature coefficient of resonant frequency(${\tau}_f$) increased, while the quality factor($Q{\times}f_{0}$) did not show an apparent change. The sintered $0.9Ca(Li_{1/4}Nb_{3/4})O_{3}-0.1CaTiO_{3}$ specimen at $900\;^{\circ}C$ with 10 wt% ZBS glass demonstrated 39.6 in dielectric constant(${\epsilon}_r$), 4,400 in quality factor$(Q{\times}f_{0}),\;and\;-11ppm/^{\circ}C$ in temperature coefficient of resonant frequency(${\tau}_f$).

• 대한금속재료학회지
• /
• 제50권4호
• /
• pp.285-292
• /
• 2012

Hot ductility behavior of precipitation-hardened low-carbon iron alloys containing 0.02 wt% Ti and 0.05 wt% Nb was characterized by a hot tensile stress test. Carbon (0.05, 0.1, 0.25 wt%) and boron (0.002 wt%) contents were varied to study the effect of precipitates on the high-temperature embrittlement of the alloys in the temperature range of $600{\sim}800^{\circ}C$. Ductility loss was observed at $700^{\circ}C$ for the tested alloys. The cause of the ductility loss was mainly attributed to the carbides and ferrite films formed at the grain boundaries during deformation. Although the carbon content tended to raise the total fraction of Nb (C, N), the precipitates were formed mostly in the grain interior as the precipitation temperature was raised above the deformation temperature by the high carbon content. Hence, carbon in excess suppressed the hot ductility loss. Meanwhile, boron addition improved the hot ductility of the alloys. The improvement is likely due to the boron atoms capturing carbon atoms and thus retarding the carbide formation.

• 한국결정성장학회지
• /
• 제5권4호
• /
• pp.318-331
• /
• 1995

Hologen lamp를 열원으로 한 적외선 집중가열 방식의 Floating zone법을 이용하여 조화융해조성(48.6 mol% $Li_2O : 51.4 mol% LiNbO_3$)의 $LiNbO_3$ 단결정과 여기에 5 mol%의 MgO를 첨가한 $LiNbO_3$:5mod%MgO 단결정을 c-축으로 성장시켰다. 고품질의 광학용 $LiNbO_3$ 결정을 성장시키기 위해 원료봉의 최적 소결조건 및 성장 분위이게 따른 원료봉/융액 계면에 대한 고찰을 하였고, 이를 바탕으로 하여 ga s flow rate, pulling rate, 원료봉과 종자정의 회전속도 등에 대한 최적의 결정성장 조건을 확립하였다. 성장된 결정에 대해서 chemical etching을 통한 etch pattern과 ICP(Inductively Coupled Plasma) 분석을 통한 조성 변동 및 불순물 Fe 함량을 조사하였고, 5 mol% MgO의 첨가에 따른 투과율과 굴절율의 변화를 관찰하였다. 또한 $LiNbO_3$의 비선형 광학특성에 대해서는 측정한 굴절율 값을 data로 하여 비선형 광학 굴절율 $n_2$를 계산하여 다른 광학물질과 비교하였고, 이와 관련하여 비선형 광학특성에 대한 전반적인 고찰을 하였다.

• 한국재료학회지
• /
• 제5권6호
• /
• pp.748-753
• /
• 1995

NaNb $O_3$70 mol%와 SrTi $O_3$30 mol%의 고용체인 ($Na_{0.7}$S $r_{0.3}$)( $Ti_{0.3}$N $b_{0.7}$) $O_3$는 완전 고용에 의한 one phase의 페로브스카이트 구조를 형성하였으며 온도변화에 대한 유전 특성 측정 결과 100K 부근에서 완만한 유전 피크가 관찰되었다. 유전 피크를 전후한 상온과 12K에서 결정 구조 해석을 Rietveld법을 이용하여 수행하였으며 결과 상온에서는 단순 페로브스카이트의 a, b 그리고 c격자를 2배로 하는 격자를 격자 상수로 갖는 사방정계의 단위포를 형성하며 공간군은 Pmmm이였고, 12K로 온도를 낮추었을때 역시 단순 페로브스카이트의 a, b 그리고 c격자를 2배로 하는 격자를 격자 상수로 갖는 사방정계 단위포를 형성하나 공간군은 Pnma로 바뀌었다. 이러한 결정 구조의 변화는 c축 방향의 (Ti, Nb)-O-(Ti, Nb) 결합 각도에는 거의 변화가 없이 팔면체 중심의 (Ti, Nb)-O간의 결합 거리가 대칭성이 낮아지는 방향으로 변화하고 이로인해 산소 팔면체가 distortion되어 생기는 것이라는 것을 알 수 있었다. 따라서 l00K 부근에서의 완만한 유전 피크는 산소 팔면체의 distortion에 의한 구조상전이 결과라는 것을 알 수 있었다.수 있었다.다.

• 한국재료학회지
• /
• 제11권8호
• /
• pp.708-712
• /
• 2001

($Pb_{0.2}$$Ca_{0.8}$ )[($Ca_{1}$3$Nb_{2}$3/)$_{1-x}$ $Ti_{x}$ ]O$_{3}$ 세라믹스의 $^{4+}$ 치환량 변화에 따른 마이크로파 유전특성을 고찰하였다. $Ti^{4+}$ 치환량이 증가함에 따라 x=0.05부터 x=0.15까지의 조성범위에서는 단일상의 페롭스카이트상을 얻을 수 있었으며, x=0.2이상에서는 $Ti_2$와 $CaNb_2$$O_{6}$ 가 제 2상으로 존재하였고, 결정구조는 x=0.05에서 사방정(orthorhombic) 구조가 x=0.35에서 이방정(cubic) 구조로 전이하였다. 유전상수(K)는 $Ti^{4+}$ 치환량의 증가에 따라 rattling 효과의 증가로 인하여 증가되었으며, B-자리 양이온의 평균이온반겨의 세제곱의 반비례하였다. 그러나 결정립 크기의 감소와 제 2상의 존재로 인하여 Qf값은 감소하였다. $Ti^{4+}$ 치환량이 증가됨에 따리 tolerance factor(t)와 B-자리 결합원자가의 영향으로 공진주파수의 온도계수(TCF)는 -27.36ppm/$^{\circ}C$값으로부터 +18ppm/$^{\circ}C$r값으로 조절되었다. $1350^{\circ}C$d서 3시간 소결한 ($Pb_{0.2}$ $Ca_{0.8}$ )[(Ca$_{1}$3$Nb_{2}$3)$_{1-x}$ /$Ti_{x}$]$O_{3}$ 시편에서 K=51.67, Qf=7268(GHz), TCF=0 ppm/$^{\circ}C$의 우수한 특성을 얻을 수 있었다.

• 한국재료학회지
• /
• 제4권1호
• /
• pp.44-54
• /
• 1994

Ti, Nb B를 합금원소로 첨가한 알루미늄 킬드 극저탄소 고강도 강판의 재결정 집합조직에 미치는 코일링처리시의 냉각속도, 냉간가공도, 연속어닐링처리등의 효과를 조사하였다. 집합조직계수비 TC(222)/TC(200)는 코일링시의 냉각속도 감소와 냉간압연시의 입하율 증가에 따라 증가하는 경향을 나타내었다. 그러나 압하율이 80%에서 90%로 증가됨에 따라 집합조직계수비가 오히려 감소하는 경향을 나타내는데, 이것은 주집합조직이 {554}<225>로부터 {111}<112>로부터 {111}<112>로 바뀌기 때문인것으로 보여진다. 집합조직계수비를 최대로 만들기위한 최적의 강판제조 공정 조건을 제시하면, 코일링처리시 노냉하고, 냉간압연시의 압하율은 80%로 하며, 연속열처리시 $800^{\circ}C$에서 1분간 유지한다음 $20^{\circ}C$로 수냉하고 다시 $450^{\circ}C$에 5분간 과시효처리하는 것이다.