• Journal of the Korean institute of surface engineering
• /
• v.41 no.5
• /
• pp.181-188
• /
• 2008

A.C. impedance properties of HA/Ti compound layer coated Ti-30Ta-($3{\sim}15$)Nb alloys have been studied by electrochemical method. Ti-30Ta binary alloys contained 3, 7, 10 and 15 wt% Nb were manufactured by the vacuum furnace system. And then specimen was homogenized at $1000^{\circ}C$ for 24 hrs. The sample was cut and polished for corrosion test and coating. It was coated with HA/Ti compound layer by magnetron sputter. The non-coated and coated morphology of Ti alloy were analyzed by X-ray diffractometer (XRD), energy X-ray dispersive spectroscopy (EDX) and filed emission scanning electron microscope (FE-SEM). The corrosion behaviors were investigated using A.C. impedance test (PARSTAT 2273, USA) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. Ti-30Ta-($3{\sim}15\;wt%$)Nb alloys showed the ${\alpha}+{\beta}$ phase, and $\beta$ phase peak was predominantly appeared in the case of increasingly Nb contents. The microstructures of Ti alloy were transformed from needle-like structure to equiaxed structure as Nb content increased. From the analysis of coating surface, HA/Ti composite surface uniformed coating layer with 750 nm thickness. The growth directions of film were (211), (112), (300) and (202) for HA/Ti composite coating on the surface after heat treatment at $550^{\circ}C$, whereas, the growth direction of film was (110) for Ti coating. The polarization resistance ($R_p$) of HA/Ti composite coated Ti-alloys were higher than those of the Ti and HA coated samples in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. Especially, corrosion resistance of Ti-Ta-Nb system increased as Nb content increased.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.4
• /
• pp.151-155
• /
• 2007

Quasi-phase-matched (QPM) second harmonic generation (SHG) waveguide devices for a green light generation were fabricated by a periodically patterned electrode on the +Z crystal surface and homogeneous LiCl solution using a 5 mol% MgO doped congruent z-cut lithium niobate crystals. Using selective chemical etching, we confirmed the periodic (${\sim}6.8{\mu}m$) domain inverted structure and measured SHG properties of fabricated periodically poled MgO : $LiNbO_3$ ridge-type waveguides.

• Corrosion Science and Technology
• /
• v.7 no.4
• /
• pp.233-236
• /
• 2008

Halide-activated pack cementation was utilized to deposit B-doped silicide coating. The pack powders were consisted of $3Wt.c/oNH_4Cl$, 7Wt.c/oSi, $90Wt.c/oAl_2O_3+TiB_2$. B-doped silicide coating was consisted of two layers, an outer layer of $NbSi_2$ and an inner layer of $Nb_5Si_3$. Isothermal oxidation resistance of B-doped silicide coating was tested at $1250^{\circ}C$ in static air. B-doped silicide coating had excellent oxidation resistance, because continuous $SiO_2$ scale which serves as obstacle of oxygen diffusion was formed after oxidation.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.2
• /
• pp.152-164
• /
• 1995

$xPb(Fe_{1/2}Nb_{1/2})O_3 - (1 - x)Pb(Mg_{1/3}Nb_{2/3})O_3$ powders were synthesized by the molten salt synthesis method using the NaC!- KCI flux with 1 : 1 molar ratio, and their powders and dielectric properties were investigated. The synthesized powders showed less agglomerated shape with the average particle size of less than $2 \mu\textrm{m}$. The composition $x0.3Pb(Fe_{1/2}Nb_{1/2})O_3-0.7Pb(Mg_{1/3}Nb_{2/3})O_3$ could be sintered at $1000{\times}C$ and its dielectric constnat was over 11, 000.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.1
• /
• pp.39-48
• /
• 2001

Fe-Cr-Al alloy has been studied for application in automobile muffler materials due to good corrosion and oxidation resistance. In order to develop the automobile muffler materials, corrosion behaviors of electron beam physical vapor deposition (EB-PVD) coated surface of muffler matericls of muffler materials were investigated using potentiostat. For 0.1M NaCl solution, corrosion potential and pitting potential of Fe-20Cr-10Al was higher than that of Fe-5Cr- 10Al samples. Especially, in the case of Ti and Nb coated samples, pitting potential increased remarkably compared with non-coated samples. For 0.1M $CaCl_2$ solution, Ti-coated Fe-20Cr-10Al showed remarkably improved pitting corrosion resistance in comparison with non-coated Fe-20Cr-10Al and Fe-5Cr-10Al. The number and size of pits were decreased in the case of Ti coated samples in the 0.1M NaCl and 0.1M $CaCl_2$ solution.

• Journal of the Korean Ceramic Society
• /
• v.22 no.3
• /
• pp.19-24
• /
• 1985

The phtoelectrochemical porperties of $Nb_2O_5$, $Sb_2O_3$ and $V_2O_5$ doped and pure $SrTiO_3$ ceramic electodes were investigated. Shapes of I-V and I-λ characteristics of the pure $SrTiO_3$ ceramic electrode are similar to those of SrTiO3 single crystal electorde ; the anodic current strats at -0.9V (vs. Ag/AgCI) in 1 N-NaOH aqueous solution and the photoresponse appears at a wavelength of about 390nm and the quantum efficiency is about 3.5% at wavelength of 390nm under 0.5V vs. Ag/AgCl. Photocurrents of $Nb_2O_5$, $Sb_2O_3$ and $V_2O_5$ doped electrodes and $V_2O_5$ doped ceramic electrode appears at wavelength of 390nm and 500nm respectively.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.9
• /
• pp.2851-2852
• /
• 2012

• Bulletin of the Korean Chemical Society
• /
• v.32 no.8
• /
• pp.2525-2526
• /
• 2011

• Bulletin of the Korean Chemical Society
• /
• v.29 no.9
• /
• pp.1781-1783
• /
• 2008

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.112-112
• /
• 2015

The purposed of this work was to determine nanotube shape variation on the Ti-xNb alloys with alloying elements and applied potentials. Samples were prepared by arc melting, followed by followed by homogenization for 12 hr at $1000^{\circ}C$ in argon atmosphere. This study was evaluated the phase and microstructure of Ti-xNb alloys using an X-ray diffraction (XRD) and optical microscopy (OM). The morphology of the samples was investigated with a field-emission scanning electron microscope (FE-SEM) and energy dispersive X-ray spectroscopy (EDS). The nanotube on the alloy surface was formed in 1 M $H_3PO_4$ with small additions of NaF 0.8 wt.%. All anodization treatments were carried out using a scanning potentiostat (Model 362, EG&G, USA) at constant voltage 30 V for 120 min, respectively. The morphology of the samples was investigated with a field-emission scanning electron microscope (FE-SEM) and energy dispersive X-ray spectroscopy (EDS). Surface characteristics of nanotbue formed on Ti-xNb alloys was investigated by potentiodynamic test and potentiostatic in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. It was observed that the changed ${\alpha}$ phase to ${\beta}$ phase with Nb content.